JP2018518567A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2018518567A5 JP2018518567A5 JP2017562065A JP2017562065A JP2018518567A5 JP 2018518567 A5 JP2018518567 A5 JP 2018518567A5 JP 2017562065 A JP2017562065 A JP 2017562065A JP 2017562065 A JP2017562065 A JP 2017562065A JP 2018518567 A5 JP2018518567 A5 JP 2018518567A5
- Authority
- JP
- Japan
- Prior art keywords
- minutes
- composition
- weight
- properties
- viscosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
この組成物は、任意の相溶化剤及び添加剤を用いてまたは用いずに、過酸化物との以下の架橋反応速度を有する。
(1)押出条件における耐スコーチ性の尺度:140℃におけるts1(トルクの1lb−inの増加時間)が、≧30分、好ましくは≧35分、最も好ましくは≧40分、
(2)連続加硫ステップにおける架橋性の尺度:MH(182℃での最大トルク)−ML(182℃での最小トルク)が、≧0.7lb−in、好ましくは≧1.3lb−in、最も好ましくは≧1.8lb−in。
(1)押出条件における耐スコーチ性の尺度:140℃におけるts1(トルクの1lb−inの増加時間)が、≧30分、好ましくは≧35分、最も好ましくは≧40分、
(2)連続加硫ステップにおける架橋性の尺度:MH(182℃での最大トルク)−ML(182℃での最小トルク)が、≧0.7lb−in、好ましくは≧1.3lb−in、最も好ましくは≧1.8lb−in。
組成物は、任意の相溶化剤及び添加剤を用いてまたは用いずに、架橋後に以下の特性を有する。
(1)ゲル含有量が、≧40%、好ましくは≧50%、最も好ましくは≧60%、
(2)曲げ弾性率、2%セカント(MPa)が、(≦)220以下、好ましくは≦200、最も好ましくは≦180、
(3)ホットクリープ(200℃)が、≦175%、好ましくは≦125%、最も好ましくは≦100%、
(4)130℃、60Hzでの誘電正接(DF)が、≦5%、好ましくは≦2%、最も好ましくは≦1%、ならびに
(5)AC破壊強度(エージングしていない及びエージングした)が、≧28kV/mm、好ましくは≧29kV/mm、最も好ましくは≧30kV/mm。
(1)ゲル含有量が、≧40%、好ましくは≧50%、最も好ましくは≧60%、
(2)曲げ弾性率、2%セカント(MPa)が、(≦)220以下、好ましくは≦200、最も好ましくは≦180、
(3)ホットクリープ(200℃)が、≦175%、好ましくは≦125%、最も好ましくは≦100%、
(4)130℃、60Hzでの誘電正接(DF)が、≦5%、好ましくは≦2%、最も好ましくは≦1%、ならびに
(5)AC破壊強度(エージングしていない及びエージングした)が、≧28kV/mm、好ましくは≧29kV/mm、最も好ましくは≧30kV/mm。
特性
組成物の特性を以下の表に示す。実施例1〜7は、100rad秒−1及び120℃または135℃でのせん断粘度≦1600Pa・s(押出加工性のため)ならびに140℃におけるts1≧30分(押出中の予備成熟架橋に対する耐性のため)と組み合わせた、それぞれの比較例よりもより高い、1のヘンキーひずみでの伸張粘度(押出条件における耐タレ性を高めるため)を示す。100rad秒−1 (120℃または135℃)でのせん断粘度≦1600Pa・sを維持するためのポリプロピレンの最大許容充填量は、13重量%(すなわち、14重量%未満)である。さらに、組成物中のポリプロピレンがわずか1重量%であっても、(曲げ弾性率及び/または溶融せん断粘度の増大を最小限に抑えながら)溶融伸長粘度を有意に高めることができた。
組成物の特性を以下の表に示す。実施例1〜7は、100rad秒−1及び120℃または135℃でのせん断粘度≦1600Pa・s(押出加工性のため)ならびに140℃におけるts1≧30分(押出中の予備成熟架橋に対する耐性のため)と組み合わせた、それぞれの比較例よりもより高い、1のヘンキーひずみでの伸張粘度(押出条件における耐タレ性を高めるため)を示す。100rad秒−1 (120℃または135℃)でのせん断粘度≦1600Pa・sを維持するためのポリプロピレンの最大許容充填量は、13重量%(すなわち、14重量%未満)である。さらに、組成物中のポリプロピレンがわずか1重量%であっても、(曲げ弾性率及び/または溶融せん断粘度の増大を最小限に抑えながら)溶融伸長粘度を有意に高めることができた。