JP2018162199A - セメント組成物及びその製造方法 - Google Patents
セメント組成物及びその製造方法 Download PDFInfo
- Publication number
- JP2018162199A JP2018162199A JP2017061522A JP2017061522A JP2018162199A JP 2018162199 A JP2018162199 A JP 2018162199A JP 2017061522 A JP2017061522 A JP 2017061522A JP 2017061522 A JP2017061522 A JP 2017061522A JP 2018162199 A JP2018162199 A JP 2018162199A
- Authority
- JP
- Japan
- Prior art keywords
- dust
- mass
- cement composition
- amount
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
・ダスト1:電気集塵ダスト
・ダスト2:電気集塵ダストと塩素バイパスダストとの混合ダスト
・ダスト3:電気集塵ダストと脱塩ダストとの混合ダスト
・ダスト4:塩素バイパスダストと脱塩ダストとの混合ダスト
・ダスト5:電気集塵ダストと塩素バイパスダストと脱塩ダストとの混合ダスト
・ダスト1:電気集塵ダスト
・ダスト2:電気集塵ダストと塩素バイパスダストとの混合ダスト
・ダスト3:電気集塵ダストと脱塩ダストとの混合ダスト
・ダスト4:塩素バイパスダストと脱塩ダストとの混合ダスト
・ダスト5:電気集塵ダストと塩素バイパスダストと脱塩ダストとの混合ダスト
・電気集塵ダスト(電気集塵ダストの質量基準)
SiO2含有量:5〜20質量%
Al2O3含有量:2〜8質量%
Fe2O3含有量:0.1〜5質量%
CaO含有量:30〜50質量%
塩化物イオン量:0.05〜2質量%
・塩素バイパスダスト(塩素バイパスダストの質量基準)
SiO2含有量:1〜30質量%
Al2O3含有量:0.1〜10質量%
Fe2O3含有量:0.1〜5質量%
CaO含有量:1〜65質量%
塩化物イオン量:4〜35質量%
・脱塩ダスト(脱塩ダストの質量基準)
SiO2含有量:5〜30質量%
Al2O3含有量:1〜15質量%
Fe2O3含有量:0.1〜5質量%
CaO含有量:15〜65質量%
塩化物イオン量:0.1〜2質量%
・セメント組成物の全質量基準で塩化物イオン量が0.01〜0.2質量%である。
・ダストからセメント組成物に持ち込まれる塩化物イオン量がセメント組成物の全質量基準で0.01〜0.2質量%である。
本実施形態に係るセメント組成物は、セメントクリンカーと、石膏と、混合材と、ダストとを含み、混合材として石灰石及び高炉スラグの少なくとも一方を含み、ダストとして以下のダスト1〜5からなる群から選ばれる一種を含む。
・ダスト1:電気集塵ダスト
・ダスト2:電気集塵ダストと塩素バイパスダストとの混合ダスト
・ダスト3:電気集塵ダストと脱塩ダストとの混合ダスト
・ダスト4:塩素バイパスダストと脱塩ダストとの混合ダスト
・ダスト5:電気集塵ダストと塩素バイパスダストと脱塩ダストとの混合ダスト
・C3S量(質量%)=4.07×CaO(%)−7.60×SiO2(%)−6.72×Al2O3(%)−1.43×Fe2O3(%)−2.85×SO3(%)…[1]
・C2S量(質量%)=2.87×SiO2(%)−0.754×C3S(%)…[2]
・C3A量(質量%)=2.65×Al2O3(%)−1.69×Fe2O3(%)…[3]
・C4AF量=3.04×Fe2O3(%)…[4]
・塩基度(JIS)=(CaO+MgO+Al2O3)/SiO2
・塩基度(TiO2換算)=(CaO+MgO+Al2O3)/SiO2−(0.13×TiO2)
・塩基度(Bm)=(CaO+MgO+Al2O3)/SiO2−(0.13×TiO2)−MnO
・ダスト1:電気集塵ダスト
・ダスト2:電気集塵ダストと塩素バイパスダストとの混合ダスト
・ダスト3:電気集塵ダストと脱塩ダストとの混合ダスト
・ダスト4:塩素バイパスダストと脱塩ダストとの混合ダスト
・ダスト5:電気集塵ダストと塩素バイパスダストと脱塩ダストとの混合ダスト
上記セメント組成物の製造方法は、セメントクリンカーと、石膏と、特定の混合材(石灰石及び高炉スラグの少なくとも一方)と、特定のダスト(ダスト1〜5のいずれか一種)とを混合することによってセメント組成物を得る工程を含む。これらの混合は例えばボールミルを使用すればよく、より具体的にはボールミルによって所望のブレーン比表面積となるように粉砕混合すればよい。なお、ボールミルに各成分を投入する順序は特に限定されず、ボールミルを使用して予め粉砕されたセメント組成物に対して特定のダストを添加することによってセメント組成物を得てもよい。ボールミルの代わりに他の種類の粉砕機を使用してもよい。
・塩基度(JIS)=(CaO+MgO+Al2O3)/SiO2
・塩基度(TiO2換算)=(CaO+MgO+Al2O3)/SiO2−(0.13×TiO2)
・塩基度(Bm)=(CaO+MgO+Al2O3)/SiO2−(0.13×TiO2)−MnO
セメント組成物の配合(セメント組成物の全質量基準)を表11に示す。第一工程として、各材料(セメントクリンカー、排脱二水石膏(排煙脱硫二水石膏)、石灰石及び高炉スラグ)を直径5mm以下に粗砕し、試験ボールミルでブレーン比表面積が3700±100cm2/gになるように粉砕して、各ダスト添加する前のセメント組成物を得た。第二工程として、第一工程で得たセメント組成物にダストを所定量添加し、ロッキングミキサーで20分間にわたって混合することにより、表11に示す配合のセメント組成物を得た。
Claims (10)
- セメントクリンカーと、石膏と、混合材と、ダストとを含むセメント組成物であって、
前記混合材として石灰石及び高炉スラグの少なくとも一方を含み、当該セメント組成物の全質量基準で石灰石及び高炉スラグの合量が20質量%超であり且つ40質量%以下であり、
前記ダストとして以下のダスト1〜5からなる群から選ばれる一種を含む、セメント組成物。
・ダスト1:電気集塵ダスト
・ダスト2:電気集塵ダストと塩素バイパスダストとの混合ダスト
・ダスト3:電気集塵ダストと脱塩ダストとの混合ダスト
・ダスト4:塩素バイパスダストと脱塩ダストとの混合ダスト
・ダスト5:電気集塵ダストと塩素バイパスダストと脱塩ダストとの混合ダスト - 塩化物イオン量が当該セメント組成物の全質量基準で0.01〜0.2質量%である、請求項1に記載のセメント組成物。
- 前記ダストから当該セメント組成物に持込まれる塩化物イオン量が当該セメント組成物の全質量基準で0.01〜0.2質量%である、請求項1又は2に記載のセメント組成物。
- 前記電気集塵ダストは、当該電気集塵ダストの質量基準で、SiO2含有量が5〜20質量%であり、Al2O3含有量が2〜8質量%であり、Fe2O3含有量が0.1〜5質量%であり、CaO含有量が30〜50質量%であり、塩化物イオン量が0.05〜2質量%である、請求項1〜3のいずれか一項に記載のセメント組成物。
- 前記塩素バイパスダストは、当該塩素バイパスダストの質量基準で、SiO2含有量が1〜30質量%であり、Al2O3含有量が0.1〜10質量%であり、Fe2O3含有量が0.1〜5質量%であり、CaO含有量が1〜65質量%であり、塩化物イオン量が4〜35質量%である、請求項1〜4のいずれか一項に記載のセメント組成物。
- 前記脱塩ダストは、当該脱塩ダストの質量基準で、SiO2含有量が5〜30質量%であり、Al2O3含有量が1〜15質量%であり、Fe2O3含有量が0.1〜5質量%であり、CaO含有量が15〜65質量%であり、塩化物イオン量が0.1〜2質量%である、請求項1〜5のいずれか一項に記載のセメント組成物。
- 当該セメント組成物の全質量基準で、0.1〜18質量%の前記電気集塵ダスト、0.05〜5質量%の前記塩素バイパスダスト及び/又は0.1〜20質量%の前記脱塩ダストを含む、請求項1〜6のいずれか一項に記載のセメント組成物。
- 前記電気集塵ダストと、前記塩素バイパスダストと、前記脱塩ダストとの合量が、セメント組成物の全質量基準で、0.1〜20質量%である、請求項1〜7のいずれか一項に記載のセメント組成物。
- セメントクリンカーと、石膏と、混合材と、ダストとを混合することによってセメント組成物を得る工程を含む、セメント組成物の製造方法であって、
前記セメント組成物は、前記混合材として石灰石及び高炉スラグの少なくとも一方を含み、当該セメント組成物の全質量基準で石灰石及び高炉スラグの合量が20質量%超であり且つ40質量%以下であり、前記ダストとして以下のダスト1〜5からなる群から選ばれる一種を含む、セメント組成物の製造方法。
・ダスト1:電気集塵ダスト
・ダスト2:電気集塵ダストと塩素バイパスダストとの混合ダスト
・ダスト3:電気集塵ダストと脱塩ダストとの混合ダスト
・ダスト4:塩素バイパスダストと脱塩ダストとの混合ダスト
・ダスト5:電気集塵ダストと塩素バイパスダストと脱塩ダストとの混合ダスト - 前記セメント組成物は、前記ダストとして、当該セメント組成物の全質量基準で、0.1〜18質量%の前記電気集塵ダスト、0.05〜5質量%の前記塩素バイパスダスト及び/又は0.1〜20質量%の前記脱塩ダストとを含む、請求項9に記載のセメント組成物の製造方法。