JP2018140945A - 人工爪用組成物、人工爪、除去液、及び人工爪用キット - Google Patents
人工爪用組成物、人工爪、除去液、及び人工爪用キット Download PDFInfo
- Publication number
- JP2018140945A JP2018140945A JP2017034911A JP2017034911A JP2018140945A JP 2018140945 A JP2018140945 A JP 2018140945A JP 2017034911 A JP2017034911 A JP 2017034911A JP 2017034911 A JP2017034911 A JP 2017034911A JP 2018140945 A JP2018140945 A JP 2018140945A
- Authority
- JP
- Japan
- Prior art keywords
- artificial nail
- composition
- meth
- nail
- artificial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記アニオン性モノマーは、LogPが10.0以下であることが好ましく、4.0以下であることがさらに好ましい。アニオン性モノマーのLogPが10.0以下であることにより、人工爪用組成物から形成された人工爪をアルカリ性水溶液によってより短時間で除去できるという利点がある。
上記のごとき人工爪用組成物は、上記の重合によって硬化して形成された人工爪を除去するときに、アルカリ性の水溶液たる除去液(後述)によって除去される用途で使用される。
(A)[アニオン性モノマー]
(A−1)メタクリロイルオキシエチルコハク酸
(製品名「NKエステルSA」(新中村化学工業社製))
(A−2)メタクリロイルオキシプロピルヘキサヒドロフタル酸
(製品名「NKエステルCB−23」(新中村化学工業社製))
(A−3)リン酸基含有(メタ)アクリレート 成分名「ジ(2−ヒドロキシエチルメタクリレート)ホスフェート」
(製品名「ライトエステルP−2M」(共栄社化学社製))
(B)[アニオン性モノマー以外の重合性化合物]
(B−1)ウレタンアクリレートオリゴマー(アクリレートを分子中に2つ有する)
(製品名「NKオリゴUA−160TM」(新中村化学工業社製))
(B−2)ウレタンアクリレートオリゴマー(アクリレートを分子中に2つ有する)のフェノキシジエチレングリコールアクリレート希釈物[「ウレタンアクリレートオリゴマー」(80質量%)が「フェノキシジエチレングリコールアクリレート」(20質量%)で希釈されている]
(製品名「NKオリゴU−122P」(新中村化学工業社製))
(B−3)ウレタンアクリレートオリゴマー(アクリレートを分子中に2つ有する)
(製品名「NKオリゴU−200PA」(新中村化学工業社製))
(B−4)ウレタンアクリレートオリゴマー(アクリレートを分子中に6つ有する)
(製品名「NKオリゴU−6LPA」(新中村化学工業社製))
(B−5)ウレタンアクリレートオリゴマー(アクリレートを分子中に15有する)
(製品名「NKオリゴU−15HA」(新中村化学工業社製))
(C)[光重合開始剤]
(C−1)ジフェニル(2,4,6−トリメチルベンゾイル)ホスフィンオキサイド
(製品名「ジフェニル(2,4,6−トリメチルベンゾイル)ホスフィン=オキシド」(和光純薬工業社製))
(C−2)1−ヒドロキシシクロヘキシルフェニルケトン
(製品名「1−ヒドロキシシクロヘキシル=フェニル=ケトン」(和光純薬工業社製))
表1に示す配合組成で人工爪用組成物を製造した。詳しくは、撹拌機を用いて各構成成分を室温で撹拌して混合することによって、人工爪用組成物(ジェルネイルのベースコート用組成物)を製造した。
配合組成を表2に示すように変更した点以外は、実施例1と同様にして人工爪用組成物(ジェルネイルのトップコート用組成物)を製造した。
配合組成を表3に示すように変更した点以外は、実施例1と同様にして人工爪用組成物を製造した。各原料の詳細は、下記の通りである。
(B)[アニオン性モノマー以外の重合性化合物]
(B−6)フェノキシジエチレングリコールアクリレート
(製品名「AMP−20GY」(新中村化学工業社製))
(B−7)イソボルニルメタクリレート
(製品名「メタクリル酸イソボルニル」(和光純薬工業社製))
(B−8)2−ヒドロキシエチルメタクリレート
(製品名「メタクリル酸2−ヒドロキシエチル」(和光純薬工業社製))
(B−9)親水ノニオン性モノマー 成分名「メトキシポリエチレングリコールメタクリレート」
(製名「M−90G」(新中村化学工業社製))
なお、除去液は、市販のアルカリイオン水を用意するか、または、下記のようにして製造した。
(pH=12.5アルカリ性溶液)
モンモリロナイトなどの結晶性粘度鉱物と水とを少なくとも含む液体を電気分解させることによって製造された、市販のアルカリイオン水(アロンワールド社製)を用いた。
(pH=12.0アルカリ性溶液)
水94質量部に対して無水炭酸カリウム(和光純薬工業社製)6質量部を添加し、pH=12.0のアルカリ性溶液とした。
(pH=11.5アルカリ性溶液)
水98質量部に対して無水炭酸ナトリウム(和光純薬工業社製)2質量部を添加し、pH=11.5のアルカリ性溶液とした。
(pH=11.0アルカリ性溶液)
水99.85質量部に対して無水炭酸ナトリウム(和光純薬工業社製)0.15質量部を添加し、pH=11.0のアルカリ性溶液とした。
(pH=10.5アルカリ性溶液)
水99.98質量部に対して無水炭酸ナトリウム(和光純薬工業社製)0.02質量部を添加し、pH=10.5のアルカリ性溶液とした。
スライドガラスの上に、各人工爪用組成物を、フィルムアプリケーターで、10ミル(mil)のほぼ均一な厚さで塗布し、青色LEDライト(40W)からの青色光を1分間照射して、塗布した組成物を硬化させた。下記の基準に従い、目視により、また、手等で触れて、硬化させた後の状態を判断した。
○ 完全に硬化し、光沢があり、良好。
× 硬化していない、簡単に破けてしまうなど、問題あり。
硬化した人工爪を、上記の各アルカリ性水溶液や水に浸漬して、時間を追って人工爪の除去性を観察した。各時間が経過した後の除去のしやすさを、下記の基準に従って判断した。
◎ 人工爪が十分に膨潤し、浸漬開始から10分後には容易に除去可能であった。
○ 人工爪が膨潤し、浸漬開始から20分後には容易に除去可能であった。
△ 人工爪がやや膨潤し、浸漬開始から30分後には容易に除去可能であった。
× 人工爪が膨潤せず、浸漬開始から30分以上経過しても除去不可能であった。
Claims (7)
- ラジカル反応によって重合するアニオン性モノマーを含む、人工爪用組成物。
- アニオン性モノマーは、リン酸基を含むモノマー、硫酸酸基を含むモノマー、及び、カルボキシ基を含むモノマーからなる群より選択された少なくとも1種である、請求項1に記載の人工爪用組成物。
- ラジカル重合性不飽和二重結合を複数有する前記アニオン性モノマー以外のモノマーをさらに含む、請求項1又は2に記載の人工爪用組成物。
- 前記重合によって形成された人工爪を除去するときに、アルカリ性の水溶液たる除去液によって除去されるための、請求項1〜3のいずれか1項に記載の人工爪用組成物。
- ラジカル反応によって重合したアニオン性モノマー構成単位を有する重合体を含む、人工爪。
- 請求項1〜4のいずれか1項に記載の人工爪用組成物が硬化した人工爪を除去するために用いられ、アルカリ性の水溶液である、除去液。
- 請求項1〜4のいずれか1項に記載の人工爪用組成物と、請求項6に記載の除去液と、を備える、人工爪用キット。