JP2018101612A - 非水電解質、及び非水電解質蓄電素子 - Google Patents
非水電解質、及び非水電解質蓄電素子 Download PDFInfo
- Publication number
- JP2018101612A JP2018101612A JP2017211854A JP2017211854A JP2018101612A JP 2018101612 A JP2018101612 A JP 2018101612A JP 2017211854 A JP2017211854 A JP 2017211854A JP 2017211854 A JP2017211854 A JP 2017211854A JP 2018101612 A JP2018101612 A JP 2018101612A
- Authority
- JP
- Japan
- Prior art keywords
- nonaqueous electrolyte
- fluorinated
- positive electrode
- negative electrode
- storage element
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明の一態様に係る非水電解質は、リチウムビス(フルオロスルホニル)イミドと、フッ素化カルボン酸エステルを含む非水溶媒とを備える蓄電素子用の非水電解質である。本発明の一態様に係る非水電解質蓄電素子は、上記非水電解質を備える非水電解質蓄電素子である。
【選択図】なし
Description
本発明の一実施形態に係る非水電解質は、電解質塩と非水溶媒とを備える蓄電素子用の非水電解質である。当該非水電解質において、電解質塩は非水溶媒に溶解している。
当該非水電解質は、電解質塩としてLiFSIを含む。上記電解質塩に占めるLiFSIの含有量の下限としては、10モル%が好ましく、30モル%がより好ましく、50モル%がさらに好ましく、60モル%がよりさらに好ましく、70モル%又は80モル%がよりさらに好ましい。電解質塩に占めるLiFSIの含有量を上記下限以上とすることで、蓄電素子における低温での直流抵抗をより低くすることができる。一方、この含有量としては、100モル%であってもよいが、含有量の上限としては、90モル%であってよく、80モル%であってもよく、70モル%であってもよく、60モル%であってもよい。電解質塩に占めるLiFSIの含有量を上記上限以下とすることで、正極基材等としてアルミニウムを用いた場合などにおけるアルミニウムの腐食発生を抑制することなどができる。
上記非水溶媒は、フッ素化カルボン酸エステルを含む。また、上記非水溶媒は、フッ素化環状カーボネートをさらに含むことが好ましい。
上記フッ素化カルボン酸エステルとは、カルボン酸エステルを構成する炭化水素基の水素原子の一部又は全部がフッ素原子に置換された化合物をいう。フッ素化カルボン酸エステルは、1種を単独で又は2種以上を混合して用いることができる。
R1−COO−R2 (1)
式(1)中、R1及びR2は、それぞれ独立して、アルキル基又はフッ素化アルキル基である。但し、R1及びR2の少なくとも一方は、フッ素化アルキル基である。
上記フッ素化環状カーボネートとは、エチレンカーボネート、プロピレンカーボネート、ブチレンカーボネート等の環状カーボネートが有する水素原子の一部又は全部がフッ素原子で置換された化合物をいう。
上記非水溶媒中のフッ素化化合物の含有量の下限としては、90体積%が好ましく、95体積%がより好ましく、99体積%がさらに好ましい。非水溶媒に占めるフッ素化化合物の含有量を上記下限以上とすることで、高電圧における充放電サイクル性能をより改善することができると共に、低温での直流抵抗を低くすることができるという効果を高めることができる。
当該非水電解質は、上記電解質塩及び非水溶媒以外の添加剤を含有していてもよい。上記添加剤としては、スルホン酸エステル等、一般的な蓄電素子用の非水電解質に含有される各種添加剤を挙げることができる。上記スルホン酸エステルとしては、4−メチルスルホニルオキシメチル−2,2−ジオキソ−1,3,2−ジオキサチオラン、4,4’−ビス(2,2−ジオキソ―1,3,2−ジオキサチオラン)、1、3―プロパ−1−エンスルトン等を挙げることができる。
本発明の一実施形態に係る非水電解質蓄電素子は、正極、負極及び非水電解質を有する。以下、非水電解質蓄電素子の一例として、非水電解質二次電池について説明する。上記正極及び負極は、通常、セパレータを介して積層又は巻回により交互に重畳された電極体を形成する。この電極体はケースに収納され、このケース内に非水電解質が充填される。当該非水電解質二次電池においては、非水電解質として、上述した当該非水電解質が用いられている。上記非水電解質は、正極と負極との間に介在する。また、上記ケースとしては、非水電解質二次電池のケースとして通常用いられる公知の金属ケース、樹脂ケース等を用いることができる。
上記正極は、正極基材、及びこの正極基材に直接又は中間層を介して配される正極活物質層を有する。
上記負極は、負極基材、及びこの負極基材に直接又は中間層を介して配される負極活物質層を有する。上記中間層は正極の中間層と同様の構成とすることができる。
上記セパレータの材質としては、例えば織布、不織布、多孔質樹脂フィルム等が用いられる。これらの中でも、強度の観点から多孔質樹脂フィルムが好ましく、非水電解質の保液性の観点から不織布が好ましい。上記セパレータの主成分としては、強度の観点から例えばポリエチレン、ポリプロピレン等のポリオレフィンが好ましく、耐酸化分解性の観点から例えばポリイミドやアラミド等が好ましい。また、これらの樹脂を複合してもよい。
本発明は上記実施形態に限定されるものではなく、上記態様の他、種々の変更、改良を施した態様で実施することができる。例えば、上記正極又は負極において、中間層を設けなくてもよい。
(非水電解質の調製)
フッ素化カルボン酸エステルである3,3,3−トリフルオロプロピオン酸メチル(FMP)と、フッ素化環状カーボネートであるフッ素化エチレンカーボネート(FEC)とを90:10の体積比で混合し、非水溶媒を得た。この非水溶媒に、電解質塩としてLiFSIを0.2mol/L(0.2M)及びLiPF6を1.0mol/L(1.0M)の濃度で溶解させ、実施例1の非水電解質(非水電解液)を得た。
正極活物質として、大粒子及び小粒子を混合してなるLiNi1/3Mn1/3Co1/3O2を用いた。質量比で、正極活物質:ポリフッ化ビニリデン(PVdF):アセチレンブラック(AB)=94:3:3の割合(固形物換算)で含み、N−メチルピロリドンを分散媒とする正極ペーストを作製した。この正極ペーストを正極活物質が単位電極面積あたり19mg/cm2含まれるように、正極基材としての帯状のアルミニウム箔の両面に塗布した。これをローラープレス機により加圧して正極活物質層を成型した後、100℃で14時間減圧乾燥して、極板中の液分を除去した。このようにして正極板を得た。
負極活物質として、黒鉛を用いた。質量比で、負極活物質(黒鉛):スチレンブタジエンゴム(SBR):カルボキシメチルセルロース(CMC)=97:2:1の割合(固形分換算)で含み、水を分散媒とする負極ペーストを作製した。この負極ペーストを、負極活物質が単位電極面積あたり10mg/cm2含まれるように、負極基材としての帯状の銅箔集電体の両面に塗布した。これをローラープレス機により加圧して負極活物質層を成型した後、100℃で12時間減圧乾燥して、極板中の水分を除去した。このようにして負極板を得た。
セパレータとして、無機層が表面に形成されたポリオレフィン製微多孔膜を用いた。このセパレータを介して、上記正極板と上記負極板とを積層することにより電極体を作製した。この電極体を金属樹脂複合フィルム製のケースに収納し、内部に上記非水電解質を注入した後、熱溶着により封口し、実施例1の非水電解質蓄電素子(二次電池)を得た。
用いた非水溶媒及び電解質塩の種類及び量を表1に示すとおりとしたこと以外は、実施例1と同様にして、実施例2〜6及び比較例1〜4の各非水電解質及び非水電解質蓄電素子(二次電池)を得た。なお、比較例4は、LiFSIの代わりにLiTFSIを用いた。また、表1中、「FEA」は、酢酸−2,2,2−トリフルオロエチルを示し、「EMC」は、エチルメチルカーボネートを示し、「LiTFSI」は、リチウムビス(トリフルオロメタンスルホニル)イミドを示す。また、表1中「−」は、相当する成分を用いていないことを示す。
(初期化成)
得られた各二次電池について、以下の条件にて初期化成を行った。1サイクル目は、
25℃で4.3Vまで0.2Cの定電流充電したのちに、4.3Vで定電圧充電した。充電の終了条件は、8時間とした。その後、25℃で2.75Vまで0.2Cの定電流で放電した。2サイクル目は、25℃で4.3Vまで1Cの定電流充電したのちに、4.3Vで定電圧充電した。充電の終了条件は、3時間とした。その後、25℃で2.75Vまで1Cの定電流で放電した。全てのサイクルにおいて、充電後及び放電後に、10分間の休止時間を設定した。
各二次電池を25℃において1Cの定電流で4.3Vまで充電し、さらに4.3Vの定電圧で合計3時間充電した後、1Cの定電流で終止電圧2.75Vまで放電を行うことにより、初期放電容量を測定した。さらに、初期放電容量の確認試験後の各二次電池について、初期容量の50%を充電することで電池の充電状態(SOC)を50%に調整し、−20℃にて5時間保持した後、0.2C(I1)で10秒間放電した時の電圧(E1)、0.5C(I2)で10秒間放電した時の電圧(E2)、及び1C(I3)で10秒間放電した時の電圧(E3)をそれぞれ測定した。これらの測定値(E1、E2、E3)を用いて、直流抵抗を算出した。具体的には、横軸を電流、縦軸を電圧とするグラフ上に、前記測定値E1、E2、E3をプロットし、それら3点を最小二乗法による回帰直線(近似直線)により近似し、その直線の傾きを−20℃でのSOCが50%の直流抵抗(DCR)とした。これを出力抵抗とする。得られた各二次電池における−20℃での初期の直流抵抗(DCR)を表1に示す。また、比較例1の初期の直流抵抗を基準(100%)とした相対値としての直流抵抗の比率もあわせて示す。
用いた非水電解質の組成及び負極活物質を表2に示すとおりとしたこと以外は、実施例1と同様にして、実施例7〜11及び比較例5〜7の各非水電解質蓄電素子(二次電池)を得た。
なお、表2中のGrは、黒鉛を表す。
(低温での充放電サイクル試験)
実施例7〜11及び比較例5〜7の二次電池について、上記と同様に初期化成を行った後、0℃に設定した恒温槽内で充放電サイクル試験を行った。4.3Vまで1.0Cの定電流充電したのちに、4.3Vで定電圧充電した。充電の終了条件は、3時間とした。その後、2.75Vまで1.0Cの定電流で放電した。全てのサイクルにおいて、充電後及び放電後に、10分間の休止時間を設定した。このサイクルを250サイクル実施した。
上記充放電試験後の各二次電池について、上述した「直流抵抗の測定」と同様の方法にて、−10℃における直流抵抗を測定した。得られた各二次電池における−10℃での低温充放電サイクル試験後の直流抵抗(DCR)を表2に示す。
2 電極体
3 電池容器
4 正極端子
4’ 正極リード
5 負極端子
5’ 負極リード
20 蓄電ユニット
30 蓄電装置
Claims (7)
- リチウムビス(フルオロスルホニル)イミドと、
フッ素化カルボン酸エステルを含む非水溶媒と
を備える蓄電素子用の非水電解質。 - 上記非水溶媒が、フッ素化環状カーボネートをさらに含む請求項1の非水電解質。
- 上記リチウムビス(フルオロスルホニル)イミド以外の他のリチウム塩をさらに含む請求項1又は請求項2の非水電解質。
- 上記非水溶媒中のフッ素化化合物の含有量が90体積%以上である請求項1、請求項2又は請求項3の非水電解質。
- 請求項1から請求項4のいずれか1項の非水電解質を備える非水電解質蓄電素子。
- 通常使用時の充電終止電圧における正極電位が、4.4V(vs.Li/Li+)より貴となる請求項5の非水電解質蓄電素子。
- ケイ素を含む負極を備える請求項5又は請求項6の非水電解質蓄電素子。