JP2018035352A - 回収アスファルトの再生 - Google Patents
回収アスファルトの再生 Download PDFInfo
- Publication number
- JP2018035352A JP2018035352A JP2017162942A JP2017162942A JP2018035352A JP 2018035352 A JP2018035352 A JP 2018035352A JP 2017162942 A JP2017162942 A JP 2017162942A JP 2017162942 A JP2017162942 A JP 2017162942A JP 2018035352 A JP2018035352 A JP 2018035352A
- Authority
- JP
- Japan
- Prior art keywords
- binder
- asphalt
- regenerant
- composition
- aged
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】回収アスファルトと、トールオイル由来のエステル官能性再生剤とを含むアスファルト組成物、及び再生結合剤組成物により未使用のアスファルトの望ましい特性を回収アスファルトに復活させ、ガラス転移開始温度の低減及びクリープ剛性の改善により、アスファルトの耐低温クラック性の改善がもたらし、良好な耐疲労クラック性および耐わだち掘れ性を有する組成物。再生剤がトリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラート及びグリセリンモノメラーから選択される、組成物。再生剤が、アスファルト組成物を圧密又は混合に必要な温度を低減し、エネルギーが節約され、コストが低減され建設業が未使用で再生不可能な材料に依存する程度を低減する方法。
【選択図】なし
Description
、この結合剤は、具体的に、再生用として教示されていない。植物油は、老化結合剤の望ましい軟化を提供することができるが、再生アスファルトから漏出しやすい。
来し、アスファルトを混合し敷設するのに通常使用される高められた温度で良好な熱安定性を有し、結合剤に当初の性能グレードを復活させることができると思われる。
られた温度における性能を有することを示す。わだち掘れ(Rutting)は、アスファルト
道路面、特に頻繁な交通量または高重量の交通のあるアスファルト道路面では普通の破損モードである。
ストマー、非瀝青結合剤、接着促進剤、軟化剤、追加の再生剤(本発明以外の)、または他の適切な添加剤が挙げられる。有用なエラストマーとして、例えば、エチレン−ビニルアセテートコポリマー、ポリブタジエン、エチレン−プロピレンコポリマー、エチレン−プロピレン−ジエンターポリマー、ブタジエン−スチレンブロックコポリマー、スチレン−ブタジエン−スチレン(SBS)ブロックターポリマー、イソプレン−スチレンブロックコポリマーおよびスチレン−イソプレン−スチレン(SIS)ブロックターポリマーなどが挙げられる。老化エラストマー添加剤は、粉砕タイヤゴム材料を含むことができる。
一態様では、本発明は、回収アスファルトと一緒に使用するのに適した再生結合剤組成物に関する。結合剤組成物は、老化結合剤とトールオイル由来のエステル官能性再生剤の組合せを含む。
別の態様では、本発明は、アスファルト組成物に関する。アスファルト組成物は、回収アスファルトとトールオイル由来のエステル官能性再生剤とを含む。回収アスファルトは、骨材と老化結合剤とを含む。本発明の組成物中の回収アスファルト、骨材および老化結合剤は、上で定義したのと同様である。適切な再生剤は、以下で議論される。
本発明のアスファルトおよび結合剤組成物では、再生剤は、老化結合剤と再生剤を合わせた量に対して0.1〜20重量%、好ましくは、0.5〜10重量%の範囲内の量で存在する。
トール、スクロースなどおよびその混合物が挙げられる。本明細書で「熱安定性改善アルコール」としても特定される特に好ましいアルコールは、任意のそのヒドロキシル基の酸素に対してβ位に位置する第四級炭素を有する。例として、トリメチロールプロパン、ネオペンチルグリコール、トリメチロールエタン、ペンタエリスリトール、ジペンタエリスリトール、ベンジリックアルコール(benzylic alcohols)などが挙げられる。
−エチルヘキシルタラート、ポリエチレングリコールタラート、トールオイルピッチエステル、エチレングリコールモノメラート、グリセリンモノメラート、トリメチロールプロパンモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラート、エチレングリコールジメラート、2−エチルヘキシルジメラート、2−エチルヘキシルトリメラートなどが挙げられる。特に好ましい再生剤は、タラートおよびモノメラート、特にトリメチロールプロパンタラート、エチレングリコールモノメラート、およびグリセリンモノメラートである。
イルであるツダレン(Tudalen)(登録商標)65は、10%添加剤水準でTg開始を所望の5℃低減しないことに留意されたい。別の市販の再生剤(ベントラコ ケミー
ビーブイ(Ventraco Chemie、B.V.)の製品であるレオファルト(RheoFalt)(登録商標)HP−EM)の有効成分であるカルダノールは、Tg開始温度を有効に低減するが、カルダノールは、フェノールの長鎖不飽和アルキラートであり、エステル官能基を持たない。
常、2〜8重量%、より通常には、3〜6重量%の老化アスファルト結合剤を含む。したがって、再生剤の有効量は、アスファルト源によって変動してよい。一般に、再生剤は、好ましくは、老化アスファルト結合剤の量に対して0.1〜15重量%、より好ましくは、0.5〜10重量%、さらにより好ましくは、2〜8重量%、最も好ましくは、3〜6重量%で使用される。
to rutting)などの高められた温度の特性を犠牲にすることによってのみ得られること
があまりにも頻発する。しかし、表3に示されるように、70℃で測定されたG*/sinδの低い値(対照に対して)は、トールオイル由来のエステル官能性再生剤を含む結合剤もまた高められた温度で良好に働くことが期待されることを示す。試験の結果は、特定の結合剤の使用によって期待されるわだち掘れ(rut)の形成量を推測するのに使用され
る。表3の結果は、再生剤による結合剤の軟化が、究極のアスファルト組成物におけるわだち掘れ(rutting)問題を、暑い夏の日でも創出しないことを示唆する。
明者らは、エステル成分の少なくとも一部分が、熱安定性改善アルコールに由来する再生剤が、望ましくは低い曇り点(好ましくは、−20℃未満)、低い流動点(好ましくは、−30℃未満)、および良好から優良までの低温特性(以下の表4を参照されたい)を有する再生剤をもたらすことを見出した。
剤は、200mPa・s以下の粘度で混合するのに必要な温度を少なくとも5℃、好ましくは、少なくとも10℃低減する。200mPa・sの粘度に到達するのに高温が必要である場合、その工程は、あまりにも多くのエネルギーを消費するのでコスト効率が悪くなる恐れがある。したがって、混合するための妥当な粘度に到達するために必要な温度を少しでも低減することは貴重である。別の態様では、再生剤は、3000mPa・s以下の粘度で圧密するのに必要な温度を少なくとも5℃、好ましくは、少なくとも10℃低減する。3000mPa・sの粘度に到達するのに高温が必要である場合、その工程は、あまりにも多くのエネルギーを消費するのでコスト効率が悪くなる恐れがある。したがって、圧密するための妥当な粘度に到達するために必要な温度を少しでも低減することは貴重である。表6に示されるように、トールオイル由来のエステル官能性再生剤は、混合と圧密の両方に必要な最低温度を低減するのに有効である。
再生剤を用いてRAP結合剤を調製するための方法
RAPを18.1kg(40ポンド)袋で受け取る。材料を袋から取り出し、眼に見える水分が残らずなくなるまで空気乾燥させる。複数の針金ゲージを備えた篩台を利用して材料を異なる大きさ:大、中、微細に分ける。
ガイドラインとして固体含量を使用して、濃縮材料を目標2gで50mL丸底フラスコに装入する。評価すべき添加剤をトルエンで最小50%まで稀釈し、全添加量0.2gを目標に同じ丸底に装入する。次いで150℃の油浴を使用して溶液を0.5時間真空下で揮散させる。冷却するまで濃縮生成物を窒素パージ下に保持する。
示差走査熱量測定分析を、以下の条件:試料重量:4〜6mgのRAP;試料容器:ティーエー社(TA Inc.)製標準アルミニウム皿および蓋(ティーエー社(TA Inc.)の部品番号900786.901および900779.901);装置のパージ:窒素、50mL/分を使用してサーマル アナリシス社(Thermal Analysis Inc.)モデルQ2000装置で実施する。
データに適用する:(1)試料採取間隔0.60sec/pt;(2)0.0℃におけるゼロ熱流;(3)165.00℃において平衡化させる;(4)データの保存オフ;(5)5.00分間等温;(6)サイクル1のエンドマーク;(7)データの保存オン;(8)−45.00℃まで5.00℃/分の傾斜;(9)データの保存オフ;(10)5.00分間等温;(11)サイクル2のエンドマーク;(12)データの保存オン;(13)165.00℃まで10.00℃/分の傾斜;(14)データの保存オフ;(15)5.00分間等温;(16)サイクル3のエンドマーク;(17)データの保存オン;(18)−85.00℃まで5.00℃/分の傾斜;(19)データの保存オフ;(20)5.00分間等温;(21)サイクル4のエンドマーク;(22)データの保存オン;(23)165.00℃まで10.00℃/分の傾斜;(24)サイクル5のエンドマーク;(25)方法の終了。
上記のように調製した10重量%の再生剤A〜Gを含むRAP結合剤の試料を、動的せん断粘弾性測定(DSR)を使用して低、中、および高温性能を評価するために独立の実験室に提出した。試料Eを除いて試料はそれぞれ、再生剤によって顕著に軟化することが判明する。レオロジー特性を使用してRAPに富む熱いおよび暖かいミックスアスファルトで使用するための再生生成物を評価する。
低温特性を4mm板粘弾性測定法を用いて測定する。曲げビーム粘弾性測定計(BBR)によるm−値およびクリープ剛性(S(t))をSuiらが開発した相関関係(「A New Low−temperature Performance Grading Method using 4−mm Parallel Plates on a DSR」、Transportation Research Record 2207 (2011)43〜48.)によって評価する。
RTFO/PAV老化アスファルト結合剤の耐疲労クラック性は、通常、G*sinδ(疲労因子)を使用して評価する。G*は、結合剤の複素せん断弾性率を表し、δは、位相角を表す。G*は、剛性を近似し、δは、結合剤の粘弾性応答を近似する。結合剤購入規格では、通常、その因子が5MPa未満であることが必要である。因子は、疲労損傷に関係するエネルギー消散の評価基準であるとみなされる。疲労損傷に対する臨界温度範囲は、最高使用温度と最低使用温度の間の中間温度に近い。試験温度25℃が使用される。試験用試料A〜Gの結果は、表3にある。
高温機械特性はパラメーターG*/sinδによって評価される。この因子は、結合剤の耐わだち掘れ性(resistance to rutting)の指標である。結合剤購入規格では、通常
、この因子がRTFOの老化アスファルトについて2.2kPa超、RTFO老化前では
1kPa超であることが必要である。試験試料の全てにおいて、G*/sinδは、再生剤の添加で顕著に減少する。
曇り点は、混ざりもののない溶融試料を徐々に冷却し、清澄な試料がちょうど曇る温度を観察することによって分る。流動点は、液体試料が注げる状態にある最低温度である。
エリスリトールなど)由来の脂肪酸エステルを含む再生剤が特に注目すべきであり、これらは、例外的に低い曇り点(−25℃未満)および流動点(−50℃未満)を有する。こうした添加剤は、結合剤の用途における温度範囲内で相変化を受けず、一般に再生結合剤に優れた低および高温性能をもたらす。
数種のトールオイル由来のエステル官能性再生剤、特にエチレングリコール(EG)モノメレート、およびトリメチロールプロパン(TMP)タラートをさらに評価する。これらを、それぞれ約40および55℃の環球式軟化点を有するアリゾナ ケミカル(Arizona Chemical)の製品であるシルバタック(Sylvatac)(登録商標)ロジンエステルRE40およびRE55と比較する。
温度条件にわたり期待される舗装道路面特性と相関する結合剤のレオロジー特性を特定するためにアスファルト工業によって基準が確立された。
)。老化結合剤は、この特性では、未使用結合剤と劇的に異なっておらず、低温基準は、EGモノメラートまたはTMPタラートの1重量%で満足される(しかし、シルバタック(Sylvatac)(登録商標)RE55による結果を参照されたい、これは、10重量%でもこのパラメーターを改善しない)。
以下であり、これは、未使用結合剤を使用して得られた結果と一致する。したがって、再生剤を使用する場合、質量損失に対する有害な影響は存在しない。
本発明の具体的態様は以下のとおりである。
[1]
回収アスファルトと、トールオイル由来のエステル官能性再生剤とを含み、ここで、回収アスファルトが、骨材と老化アスファルト結合剤とを含み、ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で存在するアスファルト組成物。
[2]
未使用アスファルトをさらに含み、前記未使用アスファルトが未使用結合剤と未使用骨材とを含み、未使用アスファルト、回収アスファルトおよび再生剤を合わせた量に対して1〜99重量%の未使用骨材を含む、[1]に記載の組成物。
[3]
老化アスファルト結合剤および再生剤を合わせた量に対して0.1〜20重量%の再生剤を含む、[1]に記載の組成物。
[4]
再生剤が、老化アスファルト結合剤のガラス転移開始温度を少なくとも10℃低減するのに有効な量で存在する、[1]に記載の組成物。
[5]
再生剤が、再生剤を含まない場合のガラス転移温度の広がりに比較して老化アスファルト結合剤のガラス転移温度の広がりを少なくとも5℃狭くするのに有効な量で存在する、[1]に記載の組成物。
[6]
再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、[1]に記載の組成物。
[7]
再生剤が、トールオイル脂肪酸、モノマー酸、およびダイマー酸由来のエステルである、[1]に記載の組成物。
[8]
(a)老化アスファルト結合剤;及び
(b)老化アスファルト結合剤と再生剤を合わせた量に対して0.1〜20重量%のトールオイル由来のエステル官能性再生剤;を含み、
再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で存在する、
回収アスファルトと一緒に使用するのに適した再生結合剤。
[9]
未使用結合剤と老化アスファルト結合剤を合わせた量に対して1〜99重量%の未使用結合剤をさらに含む、[8]に記載の結合剤。
[10]
0.5〜10重量%の再生剤を含む、[8]に記載の結合剤。
[11]
回収アスファルトをトールオイル由来のエステル官能性再生剤と合わせるステップを含み、ここで、回収アスファルトが、骨材と老化アスファルト結合剤とを含み、ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で使用される方法。
[12]
回収アスファルト、再生剤またはその混合物が、未使用アスファルトと合わせられ、前記未使用アスファルトが、未使用結合剤と未使用骨材とを含み、得られたアスファルト組成物が、回収アスファルト、未使用アスファルトおよび再生剤を合わせた量に対して1〜99重量%の回収アスファルトを含む、[11]に記載の方法。
[13]
得られたアスファルト組成物が、回収アスファルト、未使用アスファルトおよび再生剤を合わせた量に対して30〜70重量%の回収アスファルトを含む、[12]に記載の方法。
[14]
老化アスファルト結合剤と再生剤を合わせた量に対して0.1〜20重量%の再生剤が使用される、[11]に記載の方法。
[15]
再生剤が、老化アスファルト結合剤のガラス転移開始温度を少なくとも10℃低減するのに有効な量で使用される、[11]に記載の方法。
[16]
再生剤が、老化アスファルト結合剤のガラス転移温度の広がりを少なくとも5℃狭くするのに有効な量で使用される、[11]に記載の方法。
[17]
再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、[11]に記載の方法。
[18]
老化アスファルト結合剤を含む結合剤組成物をトールオイル由来のエステル官能性再生剤と合わせるステップを含み、再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で使用される方法。
[19]
(a)老化結合剤を含む少なくとも15重量%の回収アスファルト;及び
(b)トールオイル由来のエステル官能性再生剤;を含み、
ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、老化結合剤と再生剤を合わせた量に対して0.1〜20重量%の範囲内の量で存在し、
ここで、再生剤および老化結合剤が、再生結合剤を形成し、再生結合剤が、再生剤を含まない老化結合剤より少なくとも5℃低いEN1427による環球式軟化点を有し、再生剤を含まない老化結合剤の少なくとも2倍のEN1426による25℃における針入値を有する、
アスファルト組成物。
[20]
追加の骨材および/または結合剤をさらに含む、[19]に記載の組成物。
[21]
再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、[19]に記載の組成物。
[22]
再生剤が、200mPa・s以下の粘度で混合するのに必要な温度を少なくとも5℃低減する、[19]に記載の組成物。
[23]
再生剤が、3000mPa・s以下の粘度で圧密するのに必要な温度を少なくとも5℃低減する、[19]に記載の組成物。
[24]
(a)老化結合剤を含む少なくとも15重量%の回収アスファルト;及び
(b)トールオイル由来のエステル官能性再生剤;を含み、
ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、老化結合剤と再生剤を合わせた量に対して0.1〜20重量%の範囲内の量で存在し、
ここで、再生剤および老化結合剤が、再生結合剤を形成し、再生結合剤が、再生剤を含まない老化結合剤より少なくとも1グレード低いPGグレードを有する、
アスファルト組成物。
[25]
(a)老化結合剤;及び
(b)トールオイル由来のエステル官能性再生剤;を含み、
ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、老化結合剤と再生剤を合わせた量に対して0.1〜20重量%の範囲内の量で存在し、
ここで、再生結合剤が、再生剤を含まない老化結合剤より少なくとも5℃低いEN1427による環球式軟化点を有し、再生剤を含まない老化結合剤の少なくとも2倍のEN1426による25℃における針入値を有する、
再生結合剤。
[26]
AASHTO T−300によって測定された場合、強制延性が、15℃〜25℃の範囲内の温度で1.0J/cm2である、[25]に記載の結合剤。
[27]
再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、[25]に記載の結合剤。
[28]
EN12607−1による回転薄膜オーブン試験による短期の老化、およびEN14769による圧力老化ベッセル試験による長期の老化を受けた場合に安定性を実際に示す、[25]に記載の結合剤。
[29]
回収アスファルトとトールオイル由来のエステル官能性再生剤とを含み、回収アスファルトが骨材と老化アスファルト結合剤とを含み、再生剤が、熱安定性改善アルコールに由来する、アスファルト組成物。
[30]
アルコールが、トリメチロールエタン、トリメチロールプロパン、ネオペンチルグリコール、ペンタエリスリトール、ジペンタエリスリトール、ベンジリックアルコールおよびその混合物からなる群から選択される、[29]に記載の組成物。
[31]
−20℃未満の曇り点、および−30℃未満の流動点を有する、[29]に記載の組成物。
[32]
[1]に記載のアスファルト組成物を含む舗装面。
[33]
[19]に記載のアスファルト組成物を含む舗装面。
[34]
[29]に記載のアスファルト組成物を含む舗装面。
Claims (34)
- 回収アスファルトと、トールオイル由来のエステル官能性再生剤とを含み、ここで、回収アスファルトが、骨材と老化アスファルト結合剤とを含み、ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で存在するアスファルト組成物。
- 未使用アスファルトをさらに含み、前記未使用アスファルトが未使用結合剤と未使用骨材とを含み、未使用アスファルト、回収アスファルトおよび再生剤を合わせた量に対して1〜99重量%の未使用骨材を含む、請求項1に記載の組成物。
- 老化アスファルト結合剤および再生剤を合わせた量に対して0.1〜20重量%の再生剤を含む、請求項1に記載の組成物。
- 再生剤が、老化アスファルト結合剤のガラス転移開始温度を少なくとも10℃低減するのに有効な量で存在する、請求項1に記載の組成物。
- 再生剤が、再生剤を含まない場合のガラス転移温度の広がりに比較して老化アスファルト結合剤のガラス転移温度の広がりを少なくとも5℃狭くするのに有効な量で存在する、請求項1に記載の組成物。
- 再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、請求項1に記載の組成物。
- 再生剤が、トールオイル脂肪酸、モノマー酸、およびダイマー酸由来のエステルである、請求項1に記載の組成物。
- (a)老化アスファルト結合剤;及び
(b)老化アスファルト結合剤と再生剤を合わせた量に対して0.1〜20重量%のトールオイル由来のエステル官能性再生剤;を含み、
再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で存在する、
回収アスファルトと一緒に使用するのに適した再生結合剤。 - 未使用結合剤と老化アスファルト結合剤を合わせた量に対して1〜99重量%の未使用結合剤をさらに含む、請求項8に記載の結合剤。
- 0.5〜10重量%の再生剤を含む、請求項8に記載の結合剤。
- 回収アスファルトをトールオイル由来のエステル官能性再生剤と合わせるステップを含み、ここで、回収アスファルトが、骨材と老化アスファルト結合剤とを含み、ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で使用される方法。
- 回収アスファルト、再生剤またはその混合物が、未使用アスファルトと合わせられ、前記未使用アスファルトが、未使用結合剤と未使用骨材とを含み、得られたアスファルト組
成物が、回収アスファルト、未使用アスファルトおよび再生剤を合わせた量に対して1〜99重量%の回収アスファルトを含む、請求項11に記載の方法。 - 得られたアスファルト組成物が、回収アスファルト、未使用アスファルトおよび再生剤を合わせた量に対して30〜70重量%の回収アスファルトを含む、請求項12に記載の方法。
- 老化アスファルト結合剤と再生剤を合わせた量に対して0.1〜20重量%の再生剤が使用される、請求項11に記載の方法。
- 再生剤が、老化アスファルト結合剤のガラス転移開始温度を少なくとも10℃低減するのに有効な量で使用される、請求項11に記載の方法。
- 再生剤が、老化アスファルト結合剤のガラス転移温度の広がりを少なくとも5℃狭くするのに有効な量で使用される、請求項11に記載の方法。
- 再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、請求項11に記載の方法。
- 老化アスファルト結合剤を含む結合剤組成物をトールオイル由来のエステル官能性再生剤と合わせるステップを含み、再生剤が、ASTM D1982による30℃未満のタイターを有し、再生剤を含まない老化アスファルト結合剤のガラス転移開始温度に比較して老化アスファルト結合剤のガラス転移開始温度を少なくとも5℃低減するのに有効な量で使用される方法。
- (a)老化結合剤を含む少なくとも15重量%の回収アスファルト;及び
(b)トールオイル由来のエステル官能性再生剤;を含み、
ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、老化結合剤と再生剤を合わせた量に対して0.1〜20重量%の範囲内の量で存在し、
ここで、再生剤および老化結合剤が、再生結合剤を形成し、再生結合剤が、再生剤を含まない老化結合剤より少なくとも5℃低いEN1427による環球式軟化点を有し、再生剤を含まない老化結合剤の少なくとも2倍のEN1426による25℃における針入値を有する、
アスファルト組成物。 - 追加の骨材および/または結合剤をさらに含む、請求項19に記載の組成物。
- 再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、請求項19に記載の組成物。
- 再生剤が、200mPa・s以下の粘度で混合するのに必要な温度を少なくとも5℃低減する、請求項19に記載の組成物。
- 再生剤が、3000mPa・s以下の粘度で圧密するのに必要な温度を少なくとも5℃低減する、請求項19に記載の組成物。
- (a)老化結合剤を含む少なくとも15重量%の回収アスファルト;及び
(b)トールオイル由来のエステル官能性再生剤;を含み、
ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、老化結合剤と再生剤を合わせた量に対して0.1〜20重量%の範囲内の量で存在し、
ここで、再生剤および老化結合剤が、再生結合剤を形成し、再生結合剤が、再生剤を含まない老化結合剤より少なくとも1グレード低いPGグレードを有する、
アスファルト組成物。 - (a)老化結合剤;及び
(b)トールオイル由来のエステル官能性再生剤;を含み、
ここで、再生剤が、ASTM D1982による30℃未満のタイターを有し、老化結合剤と再生剤を合わせた量に対して0.1〜20重量%の範囲内の量で存在し、
ここで、再生結合剤が、再生剤を含まない老化結合剤より少なくとも5℃低いEN1427による環球式軟化点を有し、再生剤を含まない老化結合剤の少なくとも2倍のEN1426による25℃における針入値を有する、
再生結合剤。 - AASHTO T−300によって測定された場合、強制延性が、15℃〜25℃の範囲内の温度で1.0J/cm2である、請求項25に記載の結合剤。
- 再生剤が、トリメチロールプロパンタラート、エチレングリコールモノメラート、ネオペンチルグリコールモノメラート、2−エチルヘキシルモノメラートおよびグリセリンモノメラートからなる群から選択される、請求項25に記載の結合剤。
- EN12607−1による回転薄膜オーブン試験による短期の老化、およびEN14769による圧力老化ベッセル試験による長期の老化を受けた場合に安定性を実際に示す、請求項25に記載の結合剤。
- 回収アスファルトとトールオイル由来のエステル官能性再生剤とを含み、回収アスファルトが骨材と老化アスファルト結合剤とを含み、再生剤が、熱安定性改善アルコールに由来する、アスファルト組成物。
- アルコールが、トリメチロールエタン、トリメチロールプロパン、ネオペンチルグリコール、ペンタエリスリトール、ジペンタエリスリトール、ベンジリックアルコールおよびその混合物からなる群から選択される、請求項29に記載の組成物。
- −20℃未満の曇り点、および−30℃未満の流動点を有する、請求項29に記載の組成物。
- 請求項1に記載のアスファルト組成物を含む舗装面。
- 請求項19に記載のアスファルト組成物を含む舗装面。
- 請求項29に記載のアスファルト組成物を含む舗装面。