JP2015042146A - アルコール含有食品用脱酸素剤 - Google Patents
アルコール含有食品用脱酸素剤 Download PDFInfo
- Publication number
- JP2015042146A JP2015042146A JP2013174455A JP2013174455A JP2015042146A JP 2015042146 A JP2015042146 A JP 2015042146A JP 2013174455 A JP2013174455 A JP 2013174455A JP 2013174455 A JP2013174455 A JP 2013174455A JP 2015042146 A JP2015042146 A JP 2015042146A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- oxygen
- containing food
- alcohol
- food
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】鉄粉が40質量%〜90質量%、アルデヒド吸着体が0.1質量%〜10質量%、ハロゲン化金属が0.4質量%〜5質量%、及びアルカリ性物質が0.1質量%〜2質量%含まれているアルコール含有食品用脱酸素剤である。
【選択図】なし
Description
前記脱酸素剤としては、これまでに様々な種類が知られており、例えば、鉄粉などを含む脱酸素剤が挙げられる。前記脱酸素剤を食品とともに包装することにより、食品包装体内の酸素を除去して、食品の酸化を防止するとともに、有害微生物、カビ等の発生を抑制することができる。
一方、前記アルコール含有食品にこれまでの脱酸素剤を使用すると、アルデヒドガスが生じ、異臭の発生や、変色などが生じる場合があるという問題がある。
そのため、アルコール含有食品向けの脱酸素剤においてもアルデヒド吸着体を用いることが有効とも考えられる。
そのため、従来の技術では、優れた脱酸素性能と、アルデヒドガスの吸着とを両立することができず、新たな技術の開発が求められているのが現状である。
<1> 鉄粉が40質量%〜90質量%、アルデヒド吸着体が0.1質量%〜10質量%、ハロゲン化金属が0.4質量%〜5質量%、及びアルカリ性物質が0.1質量%〜2質量%含まれていることを特徴とするアルコール含有食品用脱酸素剤である。
<2> 前記アルデヒド吸着体が、アミン類及び尿素類から選ばれる少なくともいずれかである前記<1>に記載のアルコール含有食品用脱酸素剤である。
<3> 前記ハロゲン化金属が、アルカリ金属ハロゲン化物である前記<1>から<2>のいずれかに記載のアルコール含有食品用脱酸素剤である。
<4> 前記アルカリ性物質が、アルカリ金属の水酸化物及びアルカリ土類金属の水酸化物から選ばれる少なくともいずれかである前記<1>から<3>のいずれかに記載のアルコール含有食品用脱酸素剤である。
<5> 包材の透気度が、2,000秒/100cc〜7,500秒/100ccである前記<1>から<4>のいずれかに記載のアルコール含有食品用脱酸素剤である。
<6> さらに、水が1質量%〜20質量%、吸着体が1質量%〜15質量%含まれる前記<1>から<5>のいずれかに記載のアルコール含有食品用脱酸素剤である。
本発明のアルコール含有食品用脱酸素剤は、鉄粉と、アルデヒド吸着体と、ハロゲン化金属と、アルカリ性物質とを少なくとも含み、さらに必要に応じてその他の成分を含む。
前記鉄粉は、酸化されることにより、雰囲気中の酸素を吸着及び除去する。
前記鉄粉としては、特に制限はなく、目的に応じて適宜選択することができるが、還元鉄粉、電解鉄粉、アトマイズ鉄粉が好ましい。
前記鉄粉は、純品である必要はなく、種々のきょう雑物が存在していてもよい。
前記鉄粉のアルコール含有食品用脱酸素剤における含有量としては、40質量%〜90質量%であれば、特に制限はなく、目的に応じて適宜選択することができるが、60質量%〜80質量%が好ましく、65質量%〜75質量%がより好ましい。前記含有量が、40質量%未満であると、脱酸素能力が低くなる傾向、又はアルコール含有食品用脱酸素剤の混合粉中で鉄粉が偏析しやすい傾向があり、90質量%を超えると、アルデヒドガス濃度が高くなることがある。
前記アルデヒド吸着体は、食品包装体内のエタノールが酸化して発生するアセトアルデヒドを吸着することにより、アセトアルデヒドに伴う臭気発生、変色などを防止して、食品の品質を保持するものである。
前記アルデヒド吸着体としては、アルデヒドを吸着することができれば、特に制限はなく、目的に応じて適宜選択することができるが、アミン類、尿素類が好ましい。
これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記尿素類の具体例としては、エチレン尿素、尿素などが挙げられる。これらの中でも、アセトアルデヒドの吸着能力が高い点で、エチレン尿素が好ましい。
前記アルデヒド吸着体は、市販品を用いることができる。
前記アルデヒド吸着体のアルコール含有食品用脱酸素剤における含有量としては、0.1質量%〜10質量%であれば、特に制限はなく、目的に応じて適宜選択することができるが、0.2質量%〜5質量%が好ましく、0.3質量%〜2質量%がより好ましい。前記含有量が、0.1質量%未満であると、アセトアルデヒドを吸着しきれないおそれがあり、10質量%を超えると、過剰量となりコスト高やアルコール含有食品用脱酸素剤の容積が大きくなることを招き、又脱酸素反応を阻害するおそれもある。
前記ハロゲン化金属は、前記鉄粉に作用して、前記鉄粉を効果的に酸化させて、雰囲気中の酸素の吸着及び除去機能を促進させるものである。
前記ハロゲン化金属としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、アルカリ金属ハロゲン化物、アルカリ土類金属ハロゲン化物、アルカリ金属及びアルカリ土類金属以外の金属のハロゲン化物などが挙げられる。これらの中でも、前記鉄粉をより効果的に酸化させることができる点で、アルカリ金属ハロゲン化物が好ましい。また、前記ハロゲン化金属のハロゲンとしては、発生するアルデヒドガスの濃度をより低くすることができ、前記アルデヒド吸着体の使用量を低減することができる点で、臭素が好ましい。
これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記ハロゲン化金属のアルコール含有食品用脱酸素剤における含有量としては、0.4質量%〜5質量%であれば、特に制限はなく、目的に応じて適宜選択することができるが、1質量%〜4質量%が好ましく、2質量%〜3質量%がより好ましい。前記含有量が、0.4質量%未満であると、アセトアルデヒドの生成量を十分抑制できないことがあり、5質量%を超えると、脱酸素反応が逆に阻害されることがある。
前記アルカリ性物質は、水素ガスの発生を抑制するものである。
前記アルカリ性物質としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、アルカリ金属又はアルカリ土類金属の水酸化物、炭酸塩、炭酸水素塩、亜硫酸塩、チオ硫酸塩、リン酸塩、有機酸塩などが挙げられる。これらの中でも、アルカリ金属又はアルカリ土類金属の水酸化物が、少ない含有量で効果を示すので、好ましい。
これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記アルカリ性物質のアルコール含有食品用脱酸素剤における含有量としては、0.1質量%〜2質量%であれば、特に制限はなく、目的に応じて適宜選択することができるが、0.2質量%〜1質量%が好ましく、0.3質量%〜0.8質量%がより好ましい。前記含有量が、0.1質量%未満であると、保管中に水素ガスが生成されることがあり、2質量%を超えると、脱酸素反応が阻害されることがある。
前記その他の成分としては、本発明の効果を損なわない限り、特に制限はなく、目的に応じて適宜選択することができ、例えば、水、吸着体などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記その他の成分のアルコール含有食品用脱酸素剤における含有量としては、本発明の効果を損なわない限り、特に制限はなく、目的に応じて適宜選択することができる。
前記水の種類としては、食品に用いることが可能な水であれば特に制限はなく、目的に応じて適宜選択することができる。
前記水のアルコール含有食品用脱酸素剤における含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、1質量%〜20質量%とすることが、脱酸素反応及び容積の点で、好ましい。
また、例えば、前記アルコール含有食品用脱酸素剤が自力反応型の場合には、10質量%〜20質量%とすることが好ましい。
また、前記水を、前記ハロゲン化金属などを溶かすために使用した場合は、1質量%〜20質量%とすることができる。
前記多孔質体としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、シリカ、アルミナ、活性炭、ゼオライトなどが挙げられる。
前記吸着体としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、上述した水などを吸着乃至吸収する多孔質体などが挙げられる。
前記多孔質体としては、例えば、シリカ、アルミナ、活性炭、ゼオライト、珪藻土、タルクなどが挙げられる。これらの中でも、シリカ及びゼオライトが、品質安定性や取り扱い性の点で、好ましい。
これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記アルコール含有食品用脱酸素剤を入れる包材としては、特に制限はなく、公知の包材を適宜選択して用いることができるが、透気度が、2,000秒/100cc〜7,500秒/100ccであることが好ましく、3,500秒/100cc〜7,500秒/100ccであることがより好ましい。前記好ましい範囲とすることにより、発生するアルデヒドガス濃度は低くなり、吸着剤の低減が可能となる点で、有利である。
前記透気度は、ガーレー式透気度(JIS P8117−1998の方法により測定)をいう。
前記透気度は、例えば、包材の種類や開孔の孔径などにより調整することができる。
前記アルコール含有食品としては、アルコールを含有する限り、特に制限はなく、目的に応じて適宜選択することができ、例えば、麺類、惣菜、菓子、パン、ケーキなどが挙げられる。これらの中でも、前記アルコール含有食品用脱酸素剤は、麺類に好適に用いることができる。
前記アルコール含有食品用脱酸素剤を用いて食品を25℃で24時間保管した場合における食品包装体内における酸素濃度としては、5体積%未満が好ましく、1体積%未満がより好ましく、0.1体積%未満が特に好ましい。
前記酸素濃度は、例えば、酸素分析計(LC−700F、東レエンジニアリング株式会社製)にて測定することができる。
前記アルコール含有食品用脱酸素剤を用いて食品を25℃で48時間保管した場合における食品包装体内におけるアルデヒド濃度としては、アセトアルデヒドガスの濃度として、50ppm未満が好ましく、35ppm未満がより好ましく、20ppm未満が特に好ましい。
前記アセトアルデヒドガスの濃度は、例えば、ガスクロマトグラフ(GC−14B、株式会社島津製作所製)にて測定することができる。
前記アルコール含有食品用脱酸素剤は、エタノール蒸気発生体と組み合わせて、複合型の食品品質保持剤として使用してもよい。
前記アルコール含有食品用脱酸素剤の製造方法としては、特に制限はなく、公知の方法を適宜選択することができ、例えば、前記各成分を混合することにより得ることができる。前記混合の条件、順序なども、適宜選択して行うことができる。
また、前記アルコール含有食品用脱酸素剤を前記包材に充填する方法としても、特に制限はなく、公知の手段を適宜選択して行うことができる。
・ 鉄粉 : 粒度150μm以下のアトマイズ鉄粉(純鉄粉270M、株式会社神戸製鋼所製)。
・ アルデヒド吸着体 :
(1) ポリアリルアミン(ニットーボーメディカル株式会社製、以下「PAA」と称することがある)。
(2) エチレン尿素(和光純薬工業株式会社製)。
・ ハロゲン化金属 :
(1) 臭化ナトリウム(和光純薬工業株式会社製、以下「臭化Na」と称することがある)。
(2) 臭化カリウム(和光純薬工業株式会社製、以下「臭化K」と称することがある)。
(3) 塩化ナトリウム(和光純薬工業株式会社製、以下「塩化Na」と称することがある)。
・ アルカリ性物質 : 水酸化カルシウム(和光純薬工業株式会社製、以下「水酸化Ca」と称することがある)。
・ 吸着体 : シリカゲル(重量平均粒径150μmの多孔質シリカ粉体(アドソリダー、フロイント産業株式会社製))。
・ 包材(アルコール含有食品用脱酸素剤用の小袋) :
(1) アルコール含有食品用脱酸素剤と接する側(内側)から外側へ、有孔ポリエチレン、紙、有孔ポリエチレンテレフタレートの順に構成されたフィルム包材を外形40mm×50mmの小袋状になるようヒートシールにより成形したものであり、ガーレー式透気度(JIS P8117−1998の方法により測定)が3,800秒/100cc〜7,500秒/100ccである(以下、「I」と称することがある)。
(2) アルコール含有食品用脱酸素剤と接する側(内側)から外側へ、有孔ポリエチレン、紙、有孔ポリエチレンテレフタレートの順に構成されたフィルム包材を外形40mm×50mmの小袋状になるようヒートシールにより成形したものであり、ガーレー式透気度(JIS P8117−1998の方法により測定)が2,220秒/100cc〜3,050秒/100ccである(以下、「II」と称することがある)。
・ アルコール含有食品 : アルコールを1.5質量%含む生中華麺100g。
・ 食品用包装袋:密封可能な市販の非晶質ナイロンと、ポリエチレンとがこの順で積層されたフィルム包材からなる袋(空気量500mL)。
<アルコール含有食品用脱酸素剤の製造>
表1に示す各成分を、1包あたりにおける含有割合が表1に示す割合となるように以下のようにして混合した。
吸着体に対し、水に溶解させたハロゲン化金属を配合して混合した後、アルデヒド吸着体、鉄粉及びアルカリ性物質を配合して混合した。得られた粉末を、表1に示す1包あたりの量のとおり量りとり、前記包材(I)に充填した後、ヒートシールにより封止して、アルコール含有食品用脱酸素剤を得た。
前記実施例1で得たアルコール含有食品用脱酸素剤を、前記アルコール含有食品を入れた前記食品用包装袋に入れて、ヒートシールにより前記食品包装袋を密封した後、温度25℃で48時間静置保管した。
前記保管開始から24時間後の前記食品用包装袋内の酸素濃度を酸素分析計(LC−700F、東レエンジニアリング株式会社製)にて測定し、以下の評価基準で評価した。結果を表1に示す。
[評価基準]
◎ : 酸素濃度が、0.1体積%未満
○ : 酸素濃度が、0.1体積%以上1体積%未満
△ : 酸素濃度が、1体積%以上5体積%未満
× : 酸素濃度が、5体積%以上
前記保管開始から48時間後の前記食品用包装袋内のアセトアルデヒドガス濃度をガスクロマトグラフ(GC−14B、株式会社島津製作所製)にて測定し、以下の評価基準で評価した。結果を表1に示す。
[評価基準]
◎ : アセトアルデヒドガス濃度が、20ppm未満
○ : アセトアルデヒドガス濃度が、20ppm以上35ppm未満
△ : アセトアルデヒドガス濃度が、35ppm以上50ppm未満
× : アセトアルデヒドガス濃度が、50ppm以上
実施例1において、アルコール含有食品用脱酸素剤に含まれる各成分の組成、1包あたりの量、包材の種類を表1〜4に示すように変更した以外は、実施例1と同様にして、アルコール含有食品用脱酸素剤を作製した。
また、得られた各アルコール含有食品用脱酸素剤について、実施例1と同様にして、脱酸素性能、アセトアルデヒドガス濃度を評価した。結果を表1〜4に示す。
また、実施例1〜7のアルコール含有食品用脱酸素剤の中でも、実施例1及び3が、脱酸素性能及びアセトアルデヒドガス濃度のいずれについても特に優れた評価結果となった。
Claims (6)
- 鉄粉が40質量%〜90質量%、アルデヒド吸着体が0.1質量%〜10質量%、ハロゲン化金属が0.4質量%〜5質量%、及びアルカリ性物質が0.1質量%〜2質量%含まれていることを特徴とするアルコール含有食品用脱酸素剤。
- 前記アルデヒド吸着体が、アミン類及び尿素類から選ばれる少なくともいずれかである請求項1に記載のアルコール含有食品用脱酸素剤。
- 前記ハロゲン化金属が、アルカリ金属ハロゲン化物である請求項1から2のいずれかに記載のアルコール含有食品用脱酸素剤。
- 前記アルカリ性物質が、アルカリ金属の水酸化物及びアルカリ土類金属の水酸化物から選ばれる少なくともいずれかである請求項1から3のいずれかに記載のアルコール含有食品用脱酸素剤。
- 包材の透気度が、2,000秒/100cc〜7,500秒/100ccである請求項1から4のいずれかに記載のアルコール含有食品用脱酸素剤。
- さらに、水が1質量%〜20質量%、吸着体が1質量%〜15質量%含まれる請求項1から5のいずれかに記載のアルコール含有食品用脱酸素剤。