JP2014534152A - 固体懸濁物用分散剤 - Google Patents
固体懸濁物用分散剤 Download PDFInfo
- Publication number
- JP2014534152A JP2014534152A JP2014533857A JP2014533857A JP2014534152A JP 2014534152 A JP2014534152 A JP 2014534152A JP 2014533857 A JP2014533857 A JP 2014533857A JP 2014533857 A JP2014533857 A JP 2014533857A JP 2014534152 A JP2014534152 A JP 2014534152A
- Authority
- JP
- Japan
- Prior art keywords
- poly
- methyl
- oxyalkylene
- carbon atoms
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
また、たとえ長期間保存しても、特にその水性形態で、添加剤の有効性を維持することも望ましい。
固体懸濁物のための易分散作用及び可塑化作用も有利であり、これは、特に固体懸濁物がミネラルバインダーである時、処理時間の最適かつ実用的な制御を可能にする。
驚くべきことに、請求項1でのように、粉末物質用の分散剤として、式(XIV)を有するポリマーを使用することが、この目的を達成することがわかった。
公知の添加剤と比較して、分散剤として式(XIV)を有する本発明のポリマーの使用は、顕著に高い分散力を与える。
本発明のさらなる形態は、さらなる独立請求項の主題である。本発明の特に好適な態様は、従属請求項の主題である。
R2、R3、及びR4は、互いに独立に、H、CH3、COOH,又はCH2−COOHである。本文脈において、COOH又はCH2−COOHがまた、アルカリ金属イオン、アルカリ土類金属イオン、2価若しくは3価金属イオン、又はアンモニウムイオンを有する塩、例えばCOO−Na+又はCH2−COO−Na+であることは、当業者には明らかである。
R5は、−CH2−CH2−又は−CH2−CH(CH3)−であり、
R6は、O又はNである。
R7は、少なくとも1種のモノマーMを重合状態で含むポリマーであり、ここでR7は、500〜200,000g/mol、好ましくは2,000〜50,000g/molの分子量を有する。
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びモノエチレン系不飽和(C3〜C6)ジカルボン酸、並びにそれらのC1〜C20アルキルエステル、及び(メチル−)ポリ(オキシアルキレン)エステル、これらのアミド、ニトリル、及び無水物、
− (C1〜C20)(メタ)アルキルアクリレート、(C1〜C20)(メタ)アルキルアクリルアミド、(C1〜C20)(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル及びアリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、(メチル−)ポリ(オキシアルキレン)ビニルエーテル、
− 2〜10個の炭素原子及び1又は2個のオレフィン系2重結合を有する脂肪族炭化水素、環状及び非環状(open chain)N−ビニルアミド、
− 及び、これらのモノマーの混合物、
からなる群から選択される。
重合状態のモノマーMは、ラジカル重合反応後のポリマーの形態で存在するMを意味すると理解される。
下付き文字xは、好ましくは2〜50、特に好ましくは3〜15であり、その合計y+z=0である。
本明細書において用語「ポリマー」は、一方では、化学的に規定されるが、重合度、モル質量、及び鎖長の点で異なる高分子のプールであり、ポリマー化反応(polyreaction)(重合、重付加、重縮合)により製造されているプールを含む。他方では、この用語はまた、重反応からのかかる高分子プールの誘導体、すなわち、例えば、所定の高分子上の官能基の付加又は置換などの反応により得られる化合物を含み、これは化学的に規定されてもされなくてもよい。
本明細書においてX、W、Y、Y’、P、Mなどの太字の記載は、読解と特定を良好にするためにのみ提供される。
Xが、200g/mol以下の分子量を有する有機基である場合、これは、好ましくは200g/mol以下の分子量を有するC1〜C20アルキル基又はアルキレンオキシドを含む基である。
式(VII)のW、
式(III)のY、
R1=H又はCH3、
R2=R3=R4=H,を含み
ここで、指数が、x=14〜15で、y=z=0である、化合物;
式(VII)のW、
式(III)のY、
R1=H又はCH3、
R2=R3=R4=H,を含み
ここで、指数が、x=13〜14で、y=z=1である、化合物;
式(VIII)のW、
式(III)のY、
R1=H又はCH3、
R2=R3=R4=H,を含み
ここで、指数が、x=2〜8で、y=z=0である、化合物;
式(VIII)のW、
式(III)のY、
R1=H又はCH3、
R2=R3=R4=H,を含み
ここで、指数が、x=3〜10で、y=z=0である、化合物;
式(VIII)のW、
式(III)のY、
R1=H又はCH3、
R2=R3=R4=H,を含み
ここで、指数が、x=9〜11で、y=z=0である、化合物;
式(VIII)のW、
式(III)のY、
R1=H又はCH3、
R2=R3=R4=H,を含み
ここで、指数が、x+y=20で、z=0である、化合物;又は
式(IX)のW、
式(III)のY、
R1=H又はCH3、
R2=H、R3=H又はCH3、R4=COOH若しくはCOO−Na+,を含み
ここで、指数が、x=2〜8で、y=z=0である、化合物。
本発明の分子量制御物質は、他の反応成分と同時に加えることができるが、異なる時に加えてもよい。分子量制御物質の添加は、好ましくは重合反応中連続して、又は反応器に投入することにより行われる。
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びジカルボン酸、及びそのC1〜C20アルキルエステル、及び(メチル−)ポリ(オキシアルキレン)エステル、これらのアミド、ニトリル、及び無水物、
− (C1〜C20)(メタ)アルキルアクリレート、(C1〜C20)(メタ)アルキルアクリルアミド、(C1〜C20)(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル及びアリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、(メチル−)ポリ(オキシアルキレン)ビニルエーテル、
− 2〜10個の炭素原子及び1又は2個のオレフィン系2重結合を有する脂肪族炭化水素、環状及び非環状N−ビニルアミド、及び
− これらのモノマーの混合物、
からなる群から選択される。
(C1〜C10)ヒドロキシアルキルアクリレート及びメタクリレート、例えばヒドロキシエチルアクリレート、ヒドロキシプロピルアクリレート、ヒドロキシブチルアクリレート、ヒドロキシエチルメタクリレート、ヒドロキシプロピルメタクリレート、及びヒドロキシイソブチルメタクリレートである。
好適なビニル芳香族化合物は、o−及びp−メチルスチレン、ビニルトルエン、特に好ましくはスチレンである。
言及すべき好適なビニルエーテルは、例えば、メチルビニルエーテル、エチルビニルエーテル、ブチルビニルエーテル、4−ヒドロキシブチルビニルエーテル、イソプロピルビニルエーテル、プロピルビニルエーテル、ビニルイソブチルエーテル、及びドデシルビニルエーテルである。
しかし、非環状N−ビニルアミド化合物、例えばN−ビニルホルムアミド、N−ビニル−N−メチルホルムアミド、N−ビニルアセトアミド、及びN−ビニル−N−メチルアセトアミドを使用することも可能である。
さらに、その重合がラジカル開始機構に従って進行するすべてのさらなるエチレン系不飽和モノマーが可能である。
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びジカルボン酸、及びこれらのC1〜C20アルキルエステル、及び(メチル−)ポリ(オキシアルキレン)エステル、これらのアミド、ニトリル、及び無水物、
− (C1〜C20)(メタ)アルキルアクリレート、(C1〜C20)(メタ)アルキルアクリルアミド、(C1〜C20)(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル及びアリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、(メチル−)ポリ(オキシアルキレン)ビニルエーテル。
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びジカルボン酸、及びこれらのC1〜C20アルキルエステル、及び(メチル−)ポリ(オキシアルキレン)エステル、これらのアミド、ニトリル、及び無水物、
− (C1〜C20)(メタ)アルキルアクリレート、(C1〜C20)(メタ)アルキルアクリルアミド、(C1〜C20)(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル及びアリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、(メチル−)ポリ(オキシアルキレン)ビニルエーテル。
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びジカルボン酸、及びこれらのC1〜C20アルキルエステル、及び(メチル−)ポリ(オキシアルキレン)エステル、これらのアミド、ニトリル、及び無水物、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル及びアリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、(メチル−)ポリ(オキシアルキレン)ビニルエーテル。
ラジカル重合は、当該分野で公知の方法で、典型的には攪拌器、複数の供給容器及びライン、還流冷却器、加熱及び冷却装置を具備しており、不活性ガス雰囲気下で及び陽圧又は陰圧下での運転に適した重合反応器で行うことができる。
ペルオキソ二硫酸塩、例えば、ペルオキソ二硫酸ナトリウム、カリウム又はアンモニウム;
2,2’−アゾビスイソブチロニトリル;及び
過酸化水素、t−ブチルヒドロペルオキシド、及びクメンヒドロペルオキシドなどのヒドロペルオキシド系の酸化還元システム(これらは、単独で、又は亜硫酸水素ナトリウム、亜硫酸ナトリウム、アスコルビン酸、イソアスコルビン酸、及びホルムアルデヒドスルホキシル酸ナトリウムなどの酸化還元開始剤とともに使用される。
ラジカル重合で使用されるモノ置換ホスフィン酸又はその塩とモノマーMとのmol%比は、ラジカル重合で使用されるモノ置換ホスフィン酸とモノマーMの総モル量に基づいて、好ましくは0.1〜20、好ましくは1〜5である。
ラジカル開始剤は、モノマーMの総重量に基づいて、0.001〜10wt%、好ましくは0.05〜5wt%、特に好ましくは0.1〜2wt%の比で使用される。
粉末物質は、好ましくは固体懸濁物、特にその水性スラリーである。
粉末物質は、好ましくはミネラルバインダーである。
水硬性バインダーは、好ましくはセメントである。
公知の添加剤と比較して、式(XIV)を有するポリマーは、顕著に大きな分散力を示す。
粉末物質は、好ましくはミネラルバインダーである。
本発明はさらに、上記したように、水硬性バインダーと式(XIV)を有するポリマーとを含む混合物に関する。
さらに本発明は、上記したように、式(XIV)を有するポリマーを含む水硬性バインダーに基づく建築材料に関する。
粘度は、タイプRM180のMettler Toledo製の回転粘度計(測定システム11、シリンダ1、密度1.1、間隔100、回転100rpm)で測定した。
クロマトグラフィー測定は、ELS及びPDA検出器を用いてWaters社製ACQUITY UPLC(登録商標)を用いて、ならびにBEH300 C18、2.1×100mmの1.7μmカラムを使用し、移動相Aとして水中の0.15%HCOOHと移動相Bとしてアセトニトリルを用いて、行なった。
制御物質1
3−[メチル−ポリ(オキシエチレン)−オキシ−]プロピルホスフィン酸ナトリウム(アルコキシル化度:2〜8EO、Mwが300〜500g/mol)
212gの水に溶解した212g(2mol)の次亜リン酸ナトリウム一水和物を、機械攪拌器、温度計、及び滴下ロートを含むガラス反応器に投入し、70℃に加熱した。次に、同時に、350g(約2mol)の(ポリ(オキシエチレン)アリルメチルエーテル(アルコキシル化度:3〜8EO)と300gの水からなる溶液と、100gの水中の10gの過硫酸ナトリウムの溶液との両方を、75〜80℃で180分以内にこの溶液に滴下した。
次に、アリルメチルエーテルがもはや液体クロマトグラフィーにより検出されなくなるまで、反応を70℃でさらに30分間継続した。
3−[メチル−ポリ(オキシエチレン)−オキシ−]プロピルホスフィン酸ナトリウム(アルコキシル化度:3〜10EO、Mwが400〜600g/mol)
制御物質2の製造は、制御物質1の製造と同様に行ったが、違いは、500g(約2mol)の(ポリ(オキシエチレン)アリルメチルエーテル(アルコキシル化度:3〜10EO)と300gの水からなる溶液が、アルコキシル化度2〜8EOを有する(ポリ(オキシエチレン)アリルメチルエーテルの代わりに使用されたことである。
実施例1(P1)
制御物質1を分子量制御物質として使用するアクリル酸からのポリマーの製造
初期容量:
60g(約0.1mol)の制御物質1(水中57.5%)
350gの水
原料1:
576g(8mol)のアクリル酸
110gの水
原料2:
60g(約0.1mol)の制御物質1(水中57.5%)
100gの水
原料3:
24gのペルオキソ二硫酸ナトリウム
100gの水
制御物質1を分子量制御物質として使用するメタクリル酸からのポリマーの製造
初期容量:
350gの水
原料1:
860g(10mol)のメタクリル酸
500gの水
原料2:
690g(約0.9mol)の制御物質1(水中50%)
210gの水
原料3:
25gのペルオキソ二硫酸ナトリウム
180gの水
次に、加熱還流し攪拌しながら、180分以内に原料1を計量し、原料2と原料3を同時に開始し、原料1の添加が完了する約5分前に原料2が加えられるようにした。
制御物質2を分子量制御物質として使用するアクリル酸、ヒドロキシエチルアクリレート、及びビニルエーテルからのコポリマーの製造
初期容量:
300gの水
200gのメチル−ポリ(オキシエチレン)ビニルエーテル(アルコキシル化度:約100EO)(約0.05mol)
2gの水酸化ナトリウム(水中50%)
11.5g(約0.02mol)の制御物質2(水中77%)
原料1:
7.2g(10mol)のアクリル酸
23.4gのヒドロキシエチルアクリレート
50gの水
原料2:
1.2gのRongalit C
10gの水
原料3:
2.2gの過酸化水素(水中35%)
10gの水
制御物質1を分子量制御物質として使用するメタクリル酸から作製し、以後のエステル化したポリマーの製造
制御物質1を用いて製造された水性ポリメタクリル酸の約580g(約2molのCOOH)を、機械攪拌器と、温度追跡装置と、加熱マントルと、及び真空ポンプとを具備した1500mlの反応容器に投入した。この混合液に約500gのメチルポリエチレングリコールを加え、攪拌しながら、約5gの37%硫酸を加えた。反応混合物を175℃に加熱し、ここで水を蒸留した。この温度で30分間攪拌後、この反応混合物に、6.47gのJeffamine M2070と6.47gの50%水酸化ナトリウムからなる混合物を注意深く加えた。反応混合物が再度175℃に達したら直ぐ、所望の収率が達成されるまで、80mbarの陰圧で反応を行ない、こうして約95%のMPEGがエステル化された(UPLCにより測定した)。溶融物を冷却し、水で希釈して固形分含有量を50%とした。
制御物質1を分子量制御物質として使用するマレイン酸、アリルエーテル、及びビニルエーテルからのポリマーの製造
200gの水、46.4gのマレイン酸(0.4mol)、330gのアリルポリグリコールエーテル(0.3mol,Mw=1000〜2000g/mol)、8.6gの酢酸ビニル(0.1mol)及び35gの制御物質1(水中50%)を、攪拌器と、温度計と、及び還流冷却器とを有する1000mlの反応容器に投入した。次に、0.1gの硫酸鉄(II)7水和物を加え、攪拌した。
次に、温度を25℃にした。次に、135gの水と14.4gのアクリル酸(0.2mol)からなる溶液Aを作製した。さらに、38gの水と12gの35%過酸化水素からなる溶液Bを作製した。さらに、45gの水と5gのRongalit Cからなる溶液Cを作製した。80分間かけて、溶液A、B、及びCを、攪拌しながら、同時に滴下して初期容量まで加えた。この間、温度は30〜45℃に維持された。添加後、攪拌を30分間続けた。固形分含有量48%を有する無色のわずかに粘性の溶液が得られた。
制御物質1を分子量制御物質として使用するメタクリル酸とメチル−ポリ(オキシエチレン)メタクリレートからのコポリマーの製造
初期容量1:
450gの水
原料1:
775gのポリグリコールMA 1000(Clariant)、水中70%(0.5mol)
129gのメタクリル酸
100gの水
0.1gの硫酸鉄(II)7水和物
原料2:
10gの過硫酸ナトリウム
100gの水
原料3:
114gの制御物質1(50%)
50gの水
すべての添加後、過酸化物が検出されなくなるまで30分間、混合物を攪拌し続けた。混合物を50℃まで冷却した後、固形分含有量42%を有する透明のポリマー溶液が得られた。
比較例VP1〜VP6
比較例VP1〜VP6は、等モルの亜リン酸ナトリウムが、分子量制御物質である制御物質1と制御物質2の代わりに使用された以外は、実施例P1〜P6と同様に製造された。
比較例VP1〜VP6を5℃で3ヶ月以上保存中、比較例が沈着物/沈殿物を生成することが見出された。実施例P1〜P6では、対応する保存でそのような沈着物/沈殿物は観察されなかった。
セメント中の分散力の測定
30gの水に正確に秤量した100gのセメント CEMI 42.5を、第2のビーカーに正確に秤量し、0.5gの40%ポリマー溶液(200mgの固形物質)と混合した。次に、この混合物をセメントに加え、木べらを使用して2分間よく混合した。その後、ペーストをコーン(コーンの寸法:高さ58mm、内側の幅38mm、内側の上の幅19mm、内容量38ml)に充填し、15秒後、コーンをゆっくりと上げた。流出した塊は、次に縦横方向を測定し、2つの測定値の平均値を求めた。値を表1に示す。
100gのNekafill 15(Kalkfabrik Netstal製CaCO3)をビーカー中に秤量した。20g又は30gの水を第2のビーカーに秤量し、0.5gの40%ポリマー溶液(200mgの固形物)と混合した。次にこの混合物を炭酸カルシウムに加え、木べらを使用して2分間よく混合した。その後、ペーストをコーン(コーンの寸法:高さ58mm、内側の幅38mm、内側の上の幅19mm、内容量38ml)に充填し、15秒後、コーンをゆっくりと上げた。流出した塊は縦横方向を測定し、2つの測定値の平均値を求めた。値を表2に示す。
驚くべきことに、下記〈1〉でのように、粉末物質用の分散剤として、式(XIV)を有するポリマーを使用することが、この目的を達成することがわかった。
公知の添加剤と比較して、分散剤として式(XIV)を有する本発明のポリマーの使用は、顕著に高い分散力を与える。
本発明のさらなる形態は、さらなる下記の独立的態様の主題である。本発明の特に好適な態様は、下記の従属的態様の主題である。
本発明の態様としては、以下を挙げることができる:
〈1〉
粉末物質用の分散剤としての、以下の式(XIV)を有するポリマーの使用:
Xは、H + 、アルカリ金属イオン、アルカリ土類金属イオン、2価若しくは3価金属イオン、アンモニウムイオン、有機アンモニウム基、又は200g/mol以下の分子量を有する有機基であり、特にXはNa + 又はK + であり;
Yは、以下の式(II)〜(VI)の1つであり:
R 1 は、H、アルキル基、好ましくは1〜20個の炭素原子を有するアルキル基、アルキルアリール基、好ましくは7〜20個の炭素原子を有するアルキルアリール基、又は以下の式(XI)であり:
R 2 、R 3 、及びR 4 は、互いに独立に、H、CH 3 、COOH,又はCH 2 −COOHであり、
R 5 は、−CH 2 −CH 2 −又は−CH 2 −CH(CH 3 )−であり、かつ
R 6 は、O又はNである);
R 7 は、少なくとも1種のモノマーMを重合状態で含むポリマーであり、ここでR 7 は、500〜200,000g/mol、好ましくは2,000〜50,000g/molの分子量を有し;
前記モノマーMは、次からなる群より選択される:
− モノエチレン系不飽和(C 3 〜C 6 )モノカルボン酸及びモノエチレン系不飽和(C 3 〜C 6 )ジカルボン酸、並びにそれらのC1〜C20アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− (C 1 〜C 20 )(メタ)アルキルアクリレート、(C 1 〜C 20 )(メタ)アルキルアクリルアミド、(C 1 〜C 20 )(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル及びアリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、並びに(メチル−)ポリ(オキシアルキレン)ビニルエーテル、
− 2〜10個の炭素原子及び1個又は2個のオレフィン系2重結合を有する脂肪族炭化水素、環状及び非環状N−ビニルアミド、
−これらのモノマーの混合物]。
〈2〉
前記粉末物質が、粘土、磁器スリップ、ケイ酸粉末、チョーク、カーボンブラック、岩粉、顔料、タルク、プラスチック粉末、及びミネラルバインダーからなる群から選択されることを特徴とする、〈1〉に記載の使用。
〈3〉
前記粉末物質が、ミネラルバインダーであることを特徴とする、〈2〉に記載の使用。
〈4〉
前記粉末物質が、ミネラルバインダーであることを特徴とする、〈3〉に記載の使用。
〈5〉
前記粉末物質が、固体懸濁物、特に水性スラリーであることを特徴とする、〈1〉〜〈4〉のいずれか一項に記載の使用。
〈6〉
前記モノマーMが、次からなる群より選択されることを特徴とする、〈1〉〜〈5〉のいずれか一項に記載の使用:
− モノエチレン系不飽和(C 3 〜C 6 )モノカルボン酸及びモノエチレン系不飽和(C 3 〜C 6 )ジカルボン酸、並びにそれらのC 1 〜C 20 アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− (C 1 〜C 20 )(メタ)アルキルアクリレート、(C 1 〜C 20 )(メタ)アルキルアクリルアミド、(C 1 〜C 20 )(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル、アリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、及び(メチル−)ポリ(オキシアルキレン)ビニルエーテル。
〈7〉
前記モノマーMが、以下のモノマー分類の混合物であることを特徴とする、〈1〉〜〈5〉のいずれか一項に記載の使用:
− モノエチレン系不飽和(C 3 〜C 6 )モノカルボン酸及びモノエチレン系不飽和(C 3 〜C 6 )モノカルボン酸ジカルボン酸、並びにそれらのC 1 〜C 20 アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− (C 1 〜C 20 )(メタ)アルキルアクリレート、(C 1 〜C 20 )(メタ)アルキルアクリルアミド、(C 1 〜C 20 )(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル、アリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、及び(メチル−)ポリ(オキシアルキレン)ビニルエーテル。
〈8〉
前記モノマーMが、以下のモノマー分類の混合物であることを特徴とする、〈1〉〜〈5〉のいずれか一項に記載の使用:
− モノエチレン系不飽和(C 3 〜C 6 )モノカルボン酸及びモノエチレン系不飽和(C 3 〜C 6 )ジカルボン酸、並びにこれらのC1〜C20アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル、アリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、及び(メチル−)ポリ(オキシアルキレン)ビニルエーテル。
〈9〉
〈1〉〜〈8〉のいずれか一項に記載の式(XIV)を有するポリマーが、粉末物質に加えられることを特徴とする、粉末物質の流れ特性を改善する方法。
〈10〉
前記粉末物質はミネラルバインダーであることを特徴とする、〈9〉に記載の方法。
〈11〉
〈1〉〜〈8〉のいずれか一項に記載の式(XIV)を有するポリマーと、粉末物質とを含む、混合物。
〈12〉
〈1〉〜〈8〉のいずれか一項に記載の式(XIV)を有するポリマーと、水硬性バインダーとを含む、バインダー混合物。
〈13〉
〈1〉〜〈8〉のいずれか一項に記載の式(XIV)を有するポリマーを含む、水硬性バインダーに基づく建築資材。
Claims (13)
- 粉末物質用の分散剤としての、以下の式(XIV)を有するポリマーの使用:
Xは、H+、アルカリ金属イオン、アルカリ土類金属イオン、2価若しくは3価金属イオン、アンモニウムイオン、有機アンモニウム基、又は200g/mol以下の分子量を有する有機基であり、特にXはNa+又はK+であり;
Yは、以下の式(II)〜(VI)の1つであり:
R2、R3、及びR4は、互いに独立に、H、CH3、COOH、又はCH2−COOHであり、
R5は、−CH2−CH2−又は−CH2−CH(CH3)−であり、かつ
R6は、O又はNである);
R7は、少なくとも1種のモノマーMを重合状態で含むポリマーであり、ここでR7は、500〜200,000g/mol、好ましくは2,000〜50,000g/molの分子量を有し;
前記モノマーMは、次からなる群より選択される:
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びモノエチレン系不飽和(C3〜C6)ジカルボン酸、並びにそれらのC1〜C20アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− (C1〜C20)(メタ)アルキルアクリレート、(C1〜C20)(メタ)アルキルアクリルアミド、(C1〜C20)(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル及びアリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、並びに(メチル−)ポリ(オキシアルキレン)ビニルエーテル、
− 2〜10個の炭素原子及び1個又は2個のオレフィン系2重結合を有する脂肪族炭化水素、環状及び非環状N−ビニルアミド、
−これらのモノマーの混合物]。 - 前記粉末物質が、粘土、磁器スリップ、ケイ酸粉末、チョーク、カーボンブラック、岩粉、顔料、タルク、プラスチック粉末、及びミネラルバインダーからなる群から選択されることを特徴とする、請求項1に記載の使用。
- 前記粉末物質が、ミネラルバインダーであることを特徴とする、請求項2に記載の使用。
- 前記粉末物質が、ミネラルバインダーであることを特徴とする、請求項3に記載の使用。
- 前記粉末物質が、固体懸濁物、特に水性スラリーであることを特徴とする、請求項1〜4のいずれか一項に記載の使用。
- 前記モノマーMが、次からなる群より選択されることを特徴とする、請求項1〜5のいずれか一項に記載の使用:
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びモノエチレン系不飽和(C3〜C6)ジカルボン酸、並びにそれらのC1〜C20アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− (C1〜C20)(メタ)アルキルアクリレート、(C1〜C20)(メタ)アルキルアクリルアミド、(C1〜C20)(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル、アリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、及び(メチル−)ポリ(オキシアルキレン)ビニルエーテル。 - 前記モノマーMが、以下のモノマー分類の混合物であることを特徴とする、請求項1〜5のいずれか一項に記載の使用:
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びモノエチレン系不飽和(C3〜C6)モノカルボン酸ジカルボン酸、並びにそれらのC1〜C20アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− (C1〜C20)(メタ)アルキルアクリレート、(C1〜C20)(メタ)アルキルアクリルアミド、(C1〜C20)(メタ)アルキルアクリロニトリル、及び(メチル−)ポリ(オキシアルキレン)(メタ)アクリレート、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル、アリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、及び(メチル−)ポリ(オキシアルキレン)ビニルエーテル。 - 前記モノマーMが、以下のモノマー分類の混合物であることを特徴とする、請求項1〜5のいずれか一項に記載の使用:
− モノエチレン系不飽和(C3〜C6)モノカルボン酸及びモノエチレン系不飽和(C3〜C6)ジカルボン酸、並びにこれらのC1〜C20アルキルエステル、(メチル−)ポリ(オキシアルキレン)エステル、アミド、ニトリル、及び無水物、
− 最大20個の炭素原子を有するカルボン酸のビニルエステル、最大20個の炭素原子を有するビニル芳香族化合物、
− 1〜12個の炭素原子を有するアルコールのビニルエーテル、アリルエーテル、(メチル−)ポリ(オキシアルキレン)アリルエーテル、及び(メチル−)ポリ(オキシアルキレン)ビニルエーテル。 - 請求項1〜8のいずれか一項に記載の式(XIV)を有するポリマーが、粉末物質に加えられることを特徴とする、粉末物質の流れ特性を改善する方法。
- 前記粉末物質はミネラルバインダーであることを特徴とする、請求項9に記載の方法。
- 請求項1〜8のいずれか一項に記載の式(XIV)を有するポリマーと、粉末物質とを含む、混合物。
- 請求項1〜8のいずれか一項に記載の式(XIV)を有するポリマーと、水硬性バインダーとを含む、バインダー混合物。
- 請求項1〜8のいずれか一項に記載の式(XIV)を有するポリマーを含む、水硬性バインダーに基づく建築資材。