JP2013203886A - 発泡用ポリエチレン系樹脂組成物及びポリエチレン系樹脂発泡シート - Google Patents
発泡用ポリエチレン系樹脂組成物及びポリエチレン系樹脂発泡シート Download PDFInfo
- Publication number
- JP2013203886A JP2013203886A JP2012074701A JP2012074701A JP2013203886A JP 2013203886 A JP2013203886 A JP 2013203886A JP 2012074701 A JP2012074701 A JP 2012074701A JP 2012074701 A JP2012074701 A JP 2012074701A JP 2013203886 A JP2013203886 A JP 2013203886A
- Authority
- JP
- Japan
- Prior art keywords
- polyethylene
- foaming
- resin composition
- melt tension
- polyethylene resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 本発明の発泡用ポリエチレン系樹脂組成物は、密度が0.93〜0.97g/cm3で且つ190℃での溶融張力が4.5cN以上である高溶融張力ポリエチレンと、密度が0.94〜0.97g/cm3で且つ190℃での溶融張力が0.3〜3cNである低溶融張力ポリエチレンとを含み、密度が0.94〜0.97g/cm3であると共にメルトフローレイトが0.2〜3g/10分で且つ190℃での溶融張力が4cN以上であることを特徴とする。
【選択図】 図1
Description
変化率(%)=100×(L−100)/100
第一押出機の先端に第二押出機が接続されてなるタンデム型押出機を用意した。表1に示した所定量の低溶融張力ポリエチレン(A)(Braskem社製 商品名「SGE7252」)、低溶融張力ポリエチレン(B)(Braskem社製 商品名「SHD7255LSL」)、高溶融張力ポリエチレン(A)(東ソー社製 商品名「TOSOH−HMS CK57」)、高溶融張力ポリエチレン(B)(東ソー社製 商品名「TOSOH−HMS CK38」)、高溶融張力ポリエチレン(C)(Braskem社製 商品名「SGF4960」)、低密度ポリエチレン(日本ポリエチレン社製 商品名「LF128」)、及び、重炭酸ナトリウムとクエン酸のマスターバッチ(大日精化社製 商品名「ファインセルマスターPO217K」)を第一押出機に供給して溶融混練して発泡用ポリエチレン系樹脂組成物とする共に、第一押出機にポリエチレンの総量100重量部に対して表1に示した量となるようにブタンを圧入し、発泡用ポリエチレン系樹脂組成物中にブタンを均一に分散させた。
低溶融張力ポリエチレンを用いなかったこと以外は実施例1と同様にしてポリエチレン系樹脂発泡シートを製造した。
ポリエチレン系樹脂発泡シートの連続気泡率は、ASTM D2856−87に準拠して測定された値をいう。具体的には、ポリエチレン系樹脂発泡シートから該ポリエチレン系樹脂発泡シートの厚み方向の全長に亘って切り込むことによって一辺25mmの平面正方形状のシート状試験片を複数枚切り出し、この複数枚の試験片を厚み方向に全体の厚みが25mm程度となるように重ね合わせて積層体を形成した。
連続気泡率(%)
=100×(見掛け体積−空気比較式比重計による積層体の体積)/ 見掛け体積
ポリエチレン系樹脂発泡シートを目視観察して下記基準に基づいて評価した。
○・・・ポリエチレン系樹脂発泡シートの表面に皺は発生していなかった。
×・・・ポリエチレン系樹脂発泡シートの表面に皺が発生していた。
Claims (5)
- 密度が0.93〜0.97g/cm3で且つ190℃での溶融張力が4.5cN以上である高溶融張力ポリエチレンと、密度が0.94〜0.97g/cm3で且つ190℃での溶融張力が0.3〜3cNである低溶融張力ポリエチレンとを含み、密度が0.94〜0.97g/cm3であると共にメルトフローレイトが0.2〜3g/10分で且つ190℃での溶融張力が4cN以上であることを特徴とする発泡用ポリエチレン系樹脂組成物。
- 高溶融張力ポリエチレンの密度が0.94〜0.97g/cm3であることを特徴とする請求項1に記載の発泡用ポリエチレン系樹脂組成物。
- 高溶融張力ポリエチレン100重量部と、低溶融張力ポリエチレン25〜400重量部とを含むことを特徴とする請求項1又は請求項2に記載の発泡用ポリエチレン系樹脂組成物。
- ASTM D6866によって測定された植物度が5%以上であることを特徴とする請求項1乃至請求項3の何れか1項に記載の発泡用ポリエチレン系樹脂組成物。
- 請求項1に記載の発泡用ポリエチレン系樹脂組成物を発泡させてなる発泡シートであって、見掛け密度が0.2〜0.8g/cm3、厚みが0.5〜1.5mm、純曲げ試験における曲げかたさが75〜150gf・cm2/cm、曲げ回復率が15〜35gf・cm/cm、120℃における加熱寸法変化率が−2〜2%であることを特徴とするポリエチレン系樹脂発泡シート。