JP2012218257A - 繊維強化樹脂成形品の製造方法、および繊維強化樹脂成形品 - Google Patents
繊維強化樹脂成形品の製造方法、および繊維強化樹脂成形品 Download PDFInfo
- Publication number
- JP2012218257A JP2012218257A JP2011084980A JP2011084980A JP2012218257A JP 2012218257 A JP2012218257 A JP 2012218257A JP 2011084980 A JP2011084980 A JP 2011084980A JP 2011084980 A JP2011084980 A JP 2011084980A JP 2012218257 A JP2012218257 A JP 2012218257A
- Authority
- JP
- Japan
- Prior art keywords
- resin molded
- reinforced resin
- fiber
- release
- molded product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】繊維強化樹脂成形品の製造方法は、配置工程と、加熱成形工程と、剥離工程とからなり、離型フィルム100は離型層110を有する。離型層110は、主にポリメチルペンテン系樹脂、シンジオタクチックポリスチレン系樹脂、またはポリブチレンテレフタレート系樹脂からなる。配置工程では、離型フィルム100を金型200上に配置する。このとき、離型フィルム100は、金型200と接する側と反対側に離型層110が位置するようにして配置する。加熱成形工程で、樹脂前駆体が含浸される布帛300を金型200によって加熱成形して繊維強化樹脂成形品を作製した後、繊維強化樹脂成形品から離型フィルム100を剥離する。
【選択図】図1
Description
本発明に係る繊維強化樹脂成形品の製造方法は、配置工程と、加熱成形工程と、剥離工程とを備える。離型フィルムは、離型層を有する。この離型フィルムは、離型層のみからなる単層構造のフィルムであってもよいし、複数の層からなる多層構造のフィルムであってもよい。離型層は、主に、ポリメチルペンテン系樹脂(以下、「PMP系樹脂」という)、シンジオタクチックポリスチレン系樹脂(以下、「SPS系樹脂」という)、またはポリブチレンテレフタレート系樹脂(以下、「PBT系樹脂」という)からなる。配置工程では、離型フィルムを金型上に配置する。このとき、離型フィルムは、金型と接する側と反対側に離型層が位置するようにして配置される。加熱成形工程では、樹脂前駆体が含浸される布帛を、金型によって加熱成形して繊維強化樹脂成形品を作製する。剥離工程では、繊維強化樹脂成形品から離型フィルムを剥がす。
上述(1)の繊維強化樹脂成形品の製造方法では、離型フィルムは、クッション層をさらに備えることが好ましい。
上述(1)または(2)の繊維強化樹脂成形品の製造方法では、離型層の熱収縮率は、2.0%以下であることが好ましい。
上述(1)〜(3)のいずれかの繊維強化樹脂成形品の製造方法では、離型層の表面粗さRz(JIS B0601に準じて測定)は、1.0μm以上15.0μm以下であることが好ましい。
本発明に係る繊維強化樹脂成形品は、上述(1)〜(4)のいずれかの繊維強化樹脂成形品の製造方法で製造される。
図1に示されるように、配置工程では、先ず、離型フィルム100が金型200上に配置される。次いで、離型フィルム100が配置された金型200間に、樹脂前駆体が含浸される布帛(以下、「プリプレグ」という)300を配置する。なお、配置工程では、あらかじめプリプレグ300の表面に貼り付けられた状態の離型フィルム100が、金型200間に配置されてもよい。
図2に示されるように、加熱成形工程では、金型200を移動させて金型200でプリプレグ300を挟み込む。その後、金型200によってプリプレグ300を加熱成形して繊維強化樹脂成形品310を作製する。なお、加熱成形工程では、上記のような、プリプレグ300を金型200に配置して加熱成形を行う方法(例えば、ハンドレイアップ成形)以外の公知の成形法が用いられてもよい。例えば、樹脂前駆体を含浸させていない布帛を金型200内に配置した状態で、圧力を加えて樹脂前駆体を金型200中に流し込むことで、布帛に樹脂前駆体を含浸させるレジントランスファーモールディングなどの方法が用いられる。
図3に示されるように、剥離工程では、金型200を移動させて繊維強化樹脂成形品310から離型フィルム100が剥がされ、任意の形状に成形された繊維強化樹脂成形品310が得られる。
(A)
図4に示されるように、離型フィルム100aは、単層構造のフィルムに代えて、複数の層からなる多層構造のフィルムであってもよい。
110 離型層
110a 第1離型層(離型層)
120 クッション層
130 第2離型層
200 金型
300 プリプレグ(樹脂前駆体が含浸される布帛)
310 繊維強化樹脂成形品
Claims (5)
- 主に、ポリメチルペンテン系樹脂、シンジオタクチックポリスチレン系樹脂、またはポリブチレンテレフタレート系樹脂からなる離型層を有する離型フィルムを、金型上に、前記離型フィルムの前記金型と接する側と反対側に前記離型層が位置するようにして配置する配置工程と、
樹脂前駆体が含浸される布帛を前記金型によって加熱成形して繊維強化樹脂成形品を作製する加熱成形工程と、
前記繊維強化樹脂成形品から前記離型フィルムを剥がす剥離工程とを備える繊維強化樹脂成形品の製造方法。 - 前記離型フィルムは、クッション層をさらに備える請求項1に記載の繊維強化樹脂成形品の製造方法。
- 前記離型層の熱収縮率は、2.0%以下である請求項1または2に記載の繊維強化樹脂成形品の製造方法。
- 前記離型層の表面粗さRz(JIS B0601に準じて測定)は、1.0μm以上15.0μm以下である請求項1〜3のいずれか1項に記載の繊維強化樹脂成形品の製造方法。
- 請求項1〜4のいずれか1項に記載の繊維強化樹脂成形品の製造方法で製造された繊維強化樹脂成形品。