JP2011129879A - 半導体装置の製造方法、基板処理方法および基板処理装置 - Google Patents
半導体装置の製造方法、基板処理方法および基板処理装置 Download PDFInfo
- Publication number
- JP2011129879A JP2011129879A JP2010223492A JP2010223492A JP2011129879A JP 2011129879 A JP2011129879 A JP 2011129879A JP 2010223492 A JP2010223492 A JP 2010223492A JP 2010223492 A JP2010223492 A JP 2010223492A JP 2011129879 A JP2011129879 A JP 2011129879A
- Authority
- JP
- Japan
- Prior art keywords
- gas
- substrate
- flow rate
- supplying
- hydrogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 基板を収容した処理容器内に原料ガスを供給し排気して所定元素含有層を形成する工程と、加熱された大気圧未満の圧力雰囲気下にある処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して所定元素含有層を酸化層に変化させる工程とを、その間に処理容器内をパージする工程を挟んで交互に繰り返して基板上に酸化膜を形成する工程を有し、所定元素含有層を形成する工程では、原料ガスを基板の側方に設けられたノズルを介して基板に向けて供給し、その際、そのノズルを介して原料ガスと一緒に不活性ガスまたは水素含有ガスを基板に向けて供給することで、基板表面と平行方向に流れる原料ガスの流速を、処理容器内をパージする工程において基板表面と平行方向に流れる不活性ガスの流速よりも大きくする。
【選択図】 図4
Description
基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくする半導体装置の製造方法が提供される。
基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくする基板処理方法が提供される。
基板を収容する処理容器と、
前記処理容器内を加熱するヒータと、
前記処理容器内に所定元素を含む原料ガスを供給する原料ガス供給系と、
前記処理容器内に酸素含有ガスを供給する酸素含有ガス供給系と、
前記処理容器内に水素含有ガスを供給する水素含有ガス供給系と、
前記処理容器内に不活性ガスを供給する不活性ガス供給系と、
前記処理容器内を排気する排気系と、
前記処理容器内の圧力を調整する圧力調整部と、
基板を収容した前記処理容器内に前記原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を行い、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくするように、
前記原料ガス供給系、前記酸素含有ガス供給系、前記水素含有ガス供給系、前記不活性ガス供給系、前記排気系、前記圧力調整部および前記ヒータを制御する制御部と、
を有する基板処理装置が提供される。
不連続に形成される原子層のことを意味している。原料ガスが自己分解する条件下では基板上に所定元素が堆積することで所定元素層が形成される。原料ガスが自己分解しない条件下では、基板上に原料ガスが吸着することで原料ガスの吸着層が形成される。なお、基板上に原料ガスの吸着層を形成するよりも、所定元素層を形成する方が、成膜レートを高くすることができ好ましい。
233aと、第2ガス導入部としての第2ノズル233bとが、反応管203の下部側壁を貫通するように設けられている。第1ノズル233a、第2ノズル233bには、第1ガス供給管232a、第2ガス供給管232bが、それぞれ接続されている。第2ガス供給管232bには第3ガス供給管232cが接続されている。このように、反応管203には2本のノズル233a、233bと、3本のガス供給管232a、232b、232cが設けられており、処理室201内へ複数種類、ここでは3種類のガスを供給することができるように構成されている。
対側の端部に、反応管203の内壁の下部より上部に沿って、ウエハ200の積載方向上方に向かって立ち上がるように設けられている。すなわち、第2ノズル233bは、ウエハ配列領域の側方に設けられている。第2ノズル233bはL字型のロングノズルとして構成されている。第2ノズル233bの側面にはガスを供給するガス供給孔248bが設けられている。ガス供給孔248bはバッファ室237の中心を向くように開口している。このガス供給孔248bは、バッファ室237のガス供給孔248cと同様に、反応管203の下部から上部にわたって複数設けられている。この複数のガス供給孔248bのそれぞれの開口面積は、バッファ室237内と処理室201内の差圧が小さい場合には、上流側(下部)から下流側(上部)まで、それぞれ同一の開口面積で同一の開口ピッチとするとよいが、差圧が大きい場合には上流側から下流側に向かって、それぞれ開口面積を大きくするか、開口ピッチを小さくするとよい。
に、第1不活性ガス供給管232dから、堆積・吸着阻害ガスとしての不活性ガスが、マスフローコントローラ241d、バルブ243dを介して第1ガス供給管232a内に供給される。ここで、堆積・吸着阻害ガスとは、ウエハ200表面上へのシリコンの堆積またはHCDガスの吸着を阻害させるためのガスのことである。第1ガス供給管232a内に供給された堆積・吸着阻害ガスとしての不活性ガスは、第1ノズル233aを介してHCDガスと一緒に処理室201内に供給される。なおこのとき、堆積・吸着阻害ガスとして、不活性ガスの代わりに水素含有ガスを第1ガス供給管232a内に供給するようにしてもよい。この場合、第1不活性ガス供給系を水素含有ガス供給系に置き換えればよい。すなわちこの場合、水素含有ガス供給系は、水素含有ガス供給管232d、マスフローコントローラ241d、バルブ243dにより構成されることとなる。このように、第1不活性ガス供給系は堆積・吸着阻害ガス供給系としても構成され、水素含有ガス供給系に置き換えることも可能となっている。
241b、241c、241d、241e、241f、バルブ243a、243b、243c、243d、243e、243f、圧力センサ245、APCバルブ244、真空ポンプ246、ヒータ207、温度センサ263、ボート回転機構267、ボートエレベータ115、高周波電源273、整合器272等に接続されている。コントローラ121により、マスフローコントローラ241a、241b、241c、241d、241e、241fによる各種ガスの流量調整動作、バルブ243a、243b、243c、243d、243e、243fの開閉動作、APCバルブ244の開閉及び圧力センサ245に基づく圧力調整動作、温度センサ263に基づくヒータ207の温度調整動作、真空ポンプ246の起動・停止、ボート回転機構267の回転速度調節動作、ボートエレベータ115によるボート217の昇降動作等の制御や、高周波電源273の電力供給制御、整合器272によるインピーダンス制御が行われる。
267によりボート217が回転されることでウエハ200が回転される。その後、後述する4つのステップを順次実行する。
第1ガス供給管232aのバルブ243a、第1不活性ガス供給管232dのバルブ243dを開き、第1ガス供給管232aにHCDガス、第1不活性ガス供給管232dに堆積・吸着阻害ガスとしてのN2ガスを流す。N2ガスは、第1不活性ガス供給管232dから流れ、マスフローコントローラ241dにより流量調整される。HCDガスは、第1ガス供給管232aから流れ、マスフローコントローラ241aにより流量調整される。流量調整されたHCDガスは、流量調整されたN2ガスと第1ガス供給管232a内で混合されて、第1ノズル233aのガス供給孔248aから、加熱された減圧状態の処理室201内に供給され、排気管231から排気される(HCDガス+N2ガス供給)。
、基板上にHCDガスの吸着層を形成するよりも、基板上にシリコン層を形成する方が、成膜レートを高くすることができ好ましい。
てのN2ガスをウエハ200表面と平行方向に吹き付けるよりも強く、HCDガスをウエハ200表面と平行方向に吹き付ける。
ウエハ200上にシリコン含有層が形成された後、第1ガス供給管232aのバルブ243aを閉じ、HCDガスの供給を停止する。このとき、排気管231のAPCバルブ244は開いたままとし、真空ポンプ246により処理室201内を真空排気し、残留したHCDガスを処理室201内から排除する。このとき、バルブ243dは開いたままとして、不活性ガスとしてのN2ガスの処理室201内への供給を維持する。N2ガスはパージガスとして作用し、これにより、処理室201内に残留する未反応もしくはシリコン含有層形成に寄与した後のHCDガスを処理室201内から排除する効果を更に高めることができる(残留ガス除去)。
リコン含有層の堆積・吸着抑制効果を得るには、堆積・吸着阻害ガスとしてのN2ガスの体積流量を、パージ効果が十分に得られるだけのN2ガスの体積流量よりも大流量とする必要がある。よって、パージにより処理室201内の残留ガスを除去する際は、マスフローコントローラ241dを制御して、第1不活性ガス供給管232dから供給するN2ガスの供給流量を1〜20slmから0.2〜1slmへと変更し、N2ガスの体積流量を減少させることとなる。なお、パージガスとしては、N2ガスの他、Ar、He、Ne、Xe等の希ガスを用いてもよい。
処理室201内の残留ガスを除去した後、第2ガス供給管232bのバルブ243bを開き、第2ガス供給管232bにO2ガスを流す。O2ガスは第2ガス供給管232bから流れ、マスフローコントローラ241bにより流量調整される。流量調整されたO2ガスは第2ノズル233bのガス供給孔248bから加熱された減圧状態のバッファ室237内に供給される。このとき同時に、第3ガス供給管232cのバルブ243cを開き、第3ガス供給管232cにH2ガスを流す。H2ガスは第3ガス供給管232cから流れ、マスフローコントローラ241cにより流量調整される。流量調整されたH2ガスは第2ガス供給管232bを経由して第2ノズル233bのガス供給孔248bから加熱された減圧状態のバッファ室237内に供給される。なお、H2ガスは第2ガス供給管232bを経由する際に第2ガス供給管232b内でO2ガスと混合される。すなわち、第2ノズル233bからは、O2ガスとH2ガスの混合ガスが供給されることとなる。バッファ室237内に供給されたO2ガスとH2ガスの混合ガスは、バッファ室237のガス供給孔248cから、加熱された減圧状態の処理室201内に供給され、排気管231から排気される(O2ガス及びH2ガス供給)。
ステップ1〜ステップ4(後述)にかけて処理室201内の温度を同様な温度帯に保持するようにヒータ207の温度を設定するのがより好ましい。この場合、ステップ1〜ステップ4(後述)にかけて処理室201内の温度が350〜950℃、好ましくは700〜800℃の範囲内の一定の温度となるようにヒータ207の温度を設定する。なお、減圧雰囲気下でのO2ガスへのH2ガス添加による酸化力向上の効果を得るには、処理室201内の温度を350℃以上とする必要があるが、処理室201内の温度は400℃以上とするのが好ましく、さらには450℃以上とするのが好ましい。処理室201内の温度を400℃以上とすれば、400℃以上の温度で行うO3酸化処理による酸化力を超える酸化力を得ることができ、処理室201内の温度を450℃以上とすれば、450℃以上の温度で行うO2プラズマ酸化処理による酸化力を超える酸化力を得ることができる。
シリコン含有層をシリコン酸化層へと変化させた後、第2ガス供給管232bのバルブ243bを閉じ、O2ガスの供給を停止する。また、第3ガス供給管232cのバルブ243cを閉じ、H2ガスの供給を停止する。このとき、排気管231のAPCバルブ244は開いたままとし、真空ポンプ246により処理室201内を真空排気し、残留したO2ガスやH2ガスを処理室201内から排除する。このとき、バルブ243e,243fを開き、不活性ガスとしてのN2ガスを処理室201内へ供給する。N2ガスはパージガスとして作用し、これにより、処理室201内に残留する未反応もしくはシリコン酸化層形成に寄与した後のO2ガスやH2ガスを処理室201内から排除する効果を更に高めることができる(残留ガス除去)。
。また、本実施形態の成膜シーケンスにより形成したシリコン酸化膜の膜中の不純物濃度は、有機系シリコン原料を用いてCVD法により形成したシリコン酸化膜よりも極めて低くなることを確認した。また、本実施形態の成膜シーケンスによれば、有機系シリコン原料を用いた場合であっても、ウエハ面内における膜厚均一性、膜中の不純物濃度が良好なものとなることを確認した。
、ウエハ200表面と平行方向に流れるHCDガスの流速を高め、ウエハ200上へのシリコンの堆積またはHCDガスの吸着を抑制し、膜厚均一性を向上させることができる。
次に第1実施例について説明する。
堆積・吸着阻害ガスを使用した場合の本実施形態の成膜シーケンス、堆積・吸着阻害ガスを使用しない場合の本実施形態の成膜シーケンスおよび一般的なCVD法によりウエハ上にシリコン酸化膜をそれぞれ形成し、それぞれのシリコン酸化膜のウエハ面内膜厚均一性(WIW Unif)を測定した。なお、一般的なCVD法とは、DCSとN2Oとを同時に供給してCVD法によりシリコン酸化膜(HTO膜)を形成する方法であり、成膜温度は800℃とした。また、本実施形態の成膜シーケンスにおける成膜温度は450〜800℃の間で変化させた。それ以外の成膜条件(各ステップでの処理条件)は、上述の実施形態に記載の条件範囲内の条件とした。
次に第2実施例について説明する。
本実施形態の成膜シーケンスによりウエハ上にシリコン酸化膜を形成し、膜厚(Thickness)およびウエハ面内膜厚均一性(WIW Unif)を測定した。成膜温度(ウエハ温度)は、上述の第1実施例において膜厚均一性の悪化が顕著となることが判明した700〜800℃とした。HCDガスの供給流量は、0.1〜0.5slmの範囲内のある値に固定し、堆積・吸着阻害ガスとしてのN2ガスの供給流量は2〜6slmの間で3通りに変化させた。3通りのN2ガスの供給流量は、最小流量値を基準、すなわち1として比率で表すと、(A)1、(B)1.6、(C)2.0となり、以下、それぞれを流量条件(A)、流量条件(B)、流量条件(C)と称することとする。なお、HCDガスの供給流量に対する堆積・吸着阻害ガスとしてのN2ガスの供給流量の比(N2/HCD流量比)は、10〜30の間で変化させ、パージガスとしてのN2ガスの供給流量に対する堆積・吸着阻害ガスとしてのN2ガスの供給流量の比(N2(パージガス)/N2(堆積・吸着阻害ガス)流量比)は5〜30の間で変化させることとなった。それ以外の成膜条件(各ステップでの処理条件)は、上述の実施形態に記載の処理条件範囲内の条件とした。なお、ウエハとしてはΦ300mmのシリコンウエハを用いた。その結果を図7、図8に示す。
、ウエハ中心における膜厚値を基準、すなわち1とした比率で示している。図7の白丸(○)、黒丸(●)、黒三角(▲)は、それぞれ堆積・吸着阻害ガス(N2)の流量を、流量条件(A)、流量条件(B)、流量条件(C)とした場合の膜厚を示している。
次に第3実施例について説明する。
本実施形態の成膜シーケンスにおけるステップ3のノンプラズマによる酸化処理(以下、O2+H2添加酸化処理)と、プラズマを用いた酸化処理(以下、O2+H2添加プラズマ酸化処理)と、O2プラズマ酸化処理と、O3酸化処理と、O2酸化処理との酸化力を比較した。なお、O2+H2添加プラズマ酸化処理とは、O2にH2を添加したもの(O2とH2との混合ガス)をプラズマで活性化して酸化処理するケースを指す。酸化力は、シリコンに対する酸化量、すなわち、シリコンに対する酸化処理により形成されるシリコン酸化膜の膜厚で判定した。酸化処理温度(ウエハ温度)は30〜600℃の間で変化させた。それ以外の酸化処理条件は、上述の実施形態に記載のステップ3の酸化処理条件範囲内の条件とした。
基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工
程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくする半導体装置の製造方法が提供される。
基板を収容した処理容器内にシリコンを含む原料ガスを供給し排気して、前記基板上にシリコン含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記シリコン含有層をシリコン酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚のシリコン酸化膜を形成する工程を有し、
前記シリコン含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくする半導体装置の製造方法が提供される。
基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、 前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記処理容器内をパージする工程において不活性ガスを前記基板の表面と平行方向に吹き付けるよりも強く、前記原料ガスを前記基板の表面と平行方向に吹き付ける半導体装置の製造方法が提供される。
基板を収容した処理容器内にシリコンを含む原料ガスを供給し排気して、前記基板上にシリコン含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記シリコン含有層をシリコン酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚のシリコン酸化膜を形成する工程を有し、
前記シリコン含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記処理容器内をパージする工程において不活性ガスを前記基板の表面と平行方向に吹き付けるよりも強く、前記原料ガスを前記基板の表面と平行方向に吹き付ける半導体装置の製造方法が提供される。
基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくする基板処理方法が提供される。
基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記処理容器内をパージする工程において不活性ガスを前記基板の表面と平行方向に吹き付けるよりも強く、前記原料ガスを前記基板の表面と平行方向に吹き付ける基板処理方法が提供される。
基板を収容する処理容器と、
前記処理容器内を加熱するヒータと、
前記処理容器内に所定元素を含む原料ガスを供給する原料ガス供給系と、
前記処理容器内に酸素含有ガスを供給する酸素含有ガス供給系と、
前記処理容器内に水素含有ガスを供給する水素含有ガス供給系と、
前記処理容器内に不活性ガスを供給する不活性ガス供給系と、
前記処理容器内を排気する排気系と、
前記処理容器内の圧力を調整する圧力調整部と、
基板を収容した前記処理容器内に前記原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を行い、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくするように、
前記原料ガス供給系、前記酸素含有ガス供給系、前記水素含有ガス供給系、前記不活性ガス供給系、前記排気系、前記圧力調整部および前記ヒータを制御する制御部と、
を有する基板処理装置が提供される。
基板を収容する処理容器と、
前記処理容器内を加熱するヒータと、
前記処理容器内に所定元素を含む原料ガスを供給する原料ガス供給系と、
前記処理容器内に酸素含有ガスを供給する酸素含有ガス供給系と、
前記処理容器内に水素含有ガスを供給する水素含有ガス供給系と、
前記処理容器内に不活性ガスを供給する不活性ガス供給系と、
前記処理容器内を排気する排気系と、
前記処理容器内の圧力を調整する圧力調整部と、
基板を収容した前記処理容器内に前記原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を行い、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記処理容器内をパージする工程において不活性ガスを前記基板の表面と平行方向に吹き付けるよりも強く、前記原料ガスを前記基板の表面と平行方向に吹き付けるように、
前記原料ガス供給系、前記酸素含有ガス供給系、前記水素含有ガス供給系、前記不活性ガス供給系、前記排気系、前記圧力調整部および前記ヒータを制御する制御部と、
を有する基板処理装置が提供される。
200 ウエハ
201 処理室
202 処理炉
203 反応管
207 ヒータ
231 排気管
232a 第1ガス供給管
232b 第2ガス供給管
232c 第3ガス供給管
232d 第1不活性ガス供給管
232e 第2不活性ガス供給管
232f 第3不活性ガス供給管
241a マスフローコントローラ
241b マスフローコントローラ
241c マスフローコントローラ
241d マスフローコントローラ
241e マスフローコントローラ
241f マスフローコントローラ
Claims (3)
- 基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくすることを特徴とする半導体装置の製造方法。 - 基板を収容した処理容器内に所定元素を含む原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を有し、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくすることを特徴とする基板処理方法。 - 基板を収容する処理容器と、
前記処理容器内を加熱するヒータと、
前記処理容器内に所定元素を含む原料ガスを供給する原料ガス供給系と、
前記処理容器内に酸素含有ガスを供給する酸素含有ガス供給系と、
前記処理容器内に水素含有ガスを供給する水素含有ガス供給系と、
前記処理容器内に不活性ガスを供給する不活性ガス供給系と、
前記処理容器内を排気する排気系と、
前記処理容器内の圧力を調整する圧力調整部と、
基板を収容した前記処理容器内に前記原料ガスを供給し排気して、前記基板上に所定元素含有層を形成する工程と、
加熱された大気圧未満の圧力雰囲気下にある前記処理容器内に酸素含有ガスと水素含有ガスとを供給し排気して、前記所定元素含有層を酸化層に変化させる工程とを、
その間に前記処理容器内に不活性ガスを供給し排気して前記処理容器内をパージする工程を挟んで交互に繰り返して、前記基板上に所定膜厚の酸化膜を形成する工程を行い、
前記所定元素含有層を形成する工程では、前記原料ガスを前記基板の側方に設けられたノズルを介して前記基板に向けて供給し、その際、そのノズルを介して前記原料ガスと一緒に不活性ガスまたは水素含有ガスを前記基板に向けて供給することで、前記基板の表面と平行方向に流れる前記原料ガスの流速を、前記処理容器内をパージする工程において前記基板の表面と平行方向に流れる不活性ガスの流速よりも大きくするように、
前記原料ガス供給系、前記酸素含有ガス供給系、前記水素含有ガス供給系、前記不活性ガス供給系、前記排気系、前記圧力調整部および前記ヒータを制御する制御部と、
を有することを特徴とする基板処理装置。