JP2011089112A - 着氷霜抑制性に優れた樹脂組成物、および着氷霜抑制層が形成された積層金属板 - Google Patents
着氷霜抑制性に優れた樹脂組成物、および着氷霜抑制層が形成された積層金属板 Download PDFInfo
- Publication number
- JP2011089112A JP2011089112A JP2010207233A JP2010207233A JP2011089112A JP 2011089112 A JP2011089112 A JP 2011089112A JP 2010207233 A JP2010207233 A JP 2010207233A JP 2010207233 A JP2010207233 A JP 2010207233A JP 2011089112 A JP2011089112 A JP 2011089112A
- Authority
- JP
- Japan
- Prior art keywords
- group
- metal plate
- compound
- groups
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A群)ビニルポリマー、ビニリデンポリマー、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つ、カルボキシル基、スルホ基、リン酸基、およびホウ酸基よりなる群から選ばれるアニオン性基を少なくとも1種含有しているアニオン性化合物。(B群)ビニルポリマー、ビニリデンポリマー、ポリアルキレンイミン、ポリアミン、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つアミノ基、イミノ基、アミジン基、ピリジル基、イミダゾリン基、および核酸塩基よりなる群から選ばれるカチオン性基を少なくとも1種含有しているカチオン性化合物、から構成されている着氷霜抑制性に優れた樹脂組成物。
【選択図】なし
Description
(A群)
ビニルポリマー、ビニリデンポリマー、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つカルボキシル基、スルホ基、リン酸基、およびホウ酸基よりなる群から選ばれるアニオン性基を少なくとも1種含有しているアニオン性化合物。
(B群)
ビニルポリマー、ビニリデンポリマー、ポリアルキレンイミン、ポリアミン、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つアミノ基、イミノ基、アミジン基、ピリジル基、イミダゾリン基、および核酸塩基よりなる群から選ばれるカチオン性基を少なくとも1種含有しているカチオン性化合物。
(C群)
ビニルポリマー、ビニリデンポリマー、糖鎖高分子、ポリアミノ酸、ポリペプチド、ポリエチレングリコール、およびアルギン酸よりなる群から選ばれる少なくとも1種の化合物であり、且つアミド基、イミド基、水酸基、エーテル基、両性イオン構造の置換基、および糖鎖よりなる群から選ばれる水素結合性基を少なくとも1種含有している水素結合性化合物。
(a)無機酸化物または有機−無機複合化合物からなる耐食性化成処理皮膜層や、
(b)ポリエステル系樹脂、ポリオレフィン系樹脂、エポキシ系樹脂、アクリル系樹脂、およびウレタン系樹脂よりなる群から選ばれる少なくとも1種の樹脂からなる耐食性皮膜層、
を備えていることが好ましい。
(A群)
ビニルポリマー(例えば、1,2−ジ置換ビニルポリマーなど)、ビニリデンポリマー、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つカルボキシル基、スルホ基、リン酸基、およびホウ酸基よりなる群から選ばれるアニオン性基を少なくとも1種含有しているアニオン性化合物。
(B群)
ビニルポリマー(例えば、1,2−ジ置換ビニルポリマーなど)、ビニリデンポリマー、ポリアルキレンイミン(例えば、ポリエチレンイミンなど)、ポリアミン、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つアミノ基、イミノ基、アミジン基、ピリジル基、イミダゾリン基、および核酸塩基よりなる群から選ばれるカチオン性基を少なくとも1種含有しているカチオン性化合物。
文献:J.Macromol.Sci.A Pure Appl.Chem.,Vol.44,No.1/3 Page.113−118(2007)
なお、上記A群から選ばれるアニオン性化合物を2種以上用いる場合はその合計量、上記B群から選ばれるカチオン性化合物を2種以上用いる場合はその合計量に基づいて、上記質量基準の固形分比を算出すればよい。
(C群)
ビニルポリマー(例えば、1,2−ジ置換ビニルポリマーなど)、ビニリデンポリマー、糖鎖高分子、ポリアミノ酸、ポリペプチド、ポリエチレングリコール、およびアルギン酸よりなる群から選ばれる少なくとも1種の化合物であり、且つアミド基、イミド基、水酸基、エーテル基、両性イオン構造の置換基、および糖鎖よりなる群から選ばれる水素結合性基を少なくとも1種含有している水素結合性化合物。なお、C群は、アニオン性およびカチオン性を示すものを除く。
上記着氷霜抑制層の形成方法は、上記ロールコート装置等を用いた塗装法のほか、プラズマ処理−ポストグラフト重合法などを適用しても良い。
(a)無機酸化物または有機−無機複合化合物からなる耐食性化成処理皮膜層や、
(b)ポリエステル系樹脂、ポリオレフィン系樹脂、エポキシ系樹脂、アクリル系樹脂、およびウレタン系樹脂よりなる群から選ばれる少なくとも1種の樹脂からなる耐食性皮膜層、
などが挙げられる。
耐食性化成処理皮膜層は、無機系の皮膜層であり、無機酸化物または有機−無機複合化合物で構成されている。
耐食性皮膜層は、有機系の皮膜層であり、公知の塗料用樹脂が使用できる。例えば、ポリエステル系樹脂、ポリオレフィン系樹脂、エポキシ系樹脂、アクリル系樹脂、およびウレタン系樹脂よりなる群から選ばれる少なくとも1種の樹脂で構成されている。これらの樹脂は架橋剤によって架橋させてもよい。例えば、ポリエステル系樹脂の場合は、ヒドロキシ基と架橋可能なメラミン系架橋剤で架橋できる。
従来公知の製造方法により、純アルミニウム系のA1200(JIS H4000)からなるアルミニウム板(板厚0.10mm)を製造した。即ち、純アルミニウムの鋳塊を作製し、この鋳塊に均質化熱処理を施した後、熱間圧延し、続いて焼鈍処理した後、冷間圧延してアルミニウム板を製造した。得られたアルミニウム板の両面を、アルカリ性薬剤(日本ペイント社製「サーフクリーナー(登録商標)360」)で脱脂した後、リン酸クロメート処理を行って耐食性化成処理皮膜層を形成した。リン酸クロメート皮膜(耐食性化成処理皮膜層)の付着量は、Cr換算で10mg/m2とした。
下記表1に記載の着氷霜抑制層用化合物を純水で適宜希釈して化合物を完全に溶解するか、均質に分散するまで攪拌して着氷霜抑制層用樹脂組成物を調製した。表1に示したA群、B群、C群は、夫々上記で説明した各分類に対応している。表1に示した「他」とは、上記A群〜C群に分類されなかった化合物を示している。
耐食性皮膜層用塗料は5種類(塗料α〜ε)調製した。
・塗料αとしては、水系ポリエステル樹脂エマルジョン(「バイロナール(登録商標)MD−1200」:東洋紡績製)と、メラミン系架橋剤(「スミマール(登録商標)M−50W」:住友化学製)を、固形分の質量比で樹脂:架橋剤が83:17となるように混合したものを用いた。
・塗料βとしては、水系ポリエチレン樹脂エマルジョン(「HYTEC S−3121」:東邦化学工業製)を用いた。
・塗料γとしては、水系エポキシ樹脂エマルジョン(「アデカレジン(登録商標)EM−0436F」:アデカ製)を用いた。
・塗料δとしては、水系アクリル樹脂エマルジョン(「アルマテックス(登録商標)E208」:三井化学製)を用いた。
・塗料εとしては、水系ウレタン樹脂エマルジョン(「スーパーフレックス(登録商標)150」:第一工業製薬製)を用いた。
調製した着氷霜抑制層用樹脂組成物と、耐食性皮膜層用塗料α〜εを用いて、下記表2〜表4に示した皮膜構成となるように、上記リン酸クロメート処理後のアルミニウム板に塗工し、加熱乾燥し、アルミニウム製フィン材(積層金属板)を製造した。着氷霜抑制層は、下記表2〜表4に示すように、2層に分けて形成するか、1層(単層)として形成した。
上記で得られたアルミニウム製フィン材の性能を下記のように評価した。評価結果を下記表2〜表4に併記した。
アルミニウム製フィン材の着氷霜抑制性は、長さ方向に冷却液の流路となる貫通穴(φ4.0mm)を設けたアルミニウム製ブロック(幅25mm×長さ100mm×厚み20mm)の表面に、上記アルミニウム製フィン材(幅25mm×長さ100mm)を、着氷霜抑制層が外側(取り付け面とは逆側)となるように取り付けた供試材を用いて評価した。評価手順は次の通りである。なお、アルミニウム製ブロックには熱電対を取り付けてあり、データロガーでブロック温度の経時変化を記録できるようにした。
まず、上記供試材を恒温恒湿槽に入れ、温度2℃、湿度85%に保持した。温度と湿度が安定したことを確認した後、供試材に設けられている貫通穴に−10℃の冷却液を流して冷却を開始し、着氷霜抑制層表面における着氷霜の状況をビデオカメラで撮影して観察すると共に、着氷霜抑制層の表面全体に霜が付着したときの着霜温度を測定した。次に、冷却液の供給を止めて供試材を徐々に昇温し、着氷霜抑制層の表面に付着した霜が溶けていく様子をビデオカメラで撮影して観察した。冷却と解凍を複数回繰り返し、着霜温度の平均値を算出した。
(評価基準)
◎(特に良好):着霜温度の差が1.5℃以上
○(良好) :着霜温度の差が0.5℃以上、1.5℃未満
△(概ね良好):着霜温度の差が0.1℃以上、0.5℃未満
×(不良) :着霜温度の差が0.1℃未満
アルミニウム製フィン材の表面に約0.5μlの純水を滴下し、接触角測定器(協和界面科学社製:CA−05型)を用いて純水との接触角(初期接触角)を測定してフィン材表面の親水性を評価した。接触角の測定は室温で行った。
(評価基準)
◎(特に良好):接触角が20°未満
○(良好) :接触角が20°以上、40°未満
△(概ね良好):接触角が40°以上、60°未満
×(不良) :接触角が60°以上
フィン成形用のプレス成形機で、アルミニウム製フィン材をフィンの形状に成形し、カラーの内面の焼き付きの有無を目視で評価した。評価基準は以下の通りである。なお、プレス成形する際は、アルミニウム製フィン材の間隔を維持するために、フィン材に立ち上がり部分を設けるための銅管を通す穴を開けるが、上記「カラーの内面」とは、フィン材のうち銅管と接する面を指す。
(評価基準)
○(良好) :カラーの内面に焼き付きが全く見られない
△(概ね良好):カラーの内面に軽微な焼き付きが見られる
×(不良) :カラーの内面の全面で焼き付きが見られる
Claims (10)
- 下記A群から選ばれるアニオン性化合物と、
下記B群から選ばれるカチオン性化合物から構成されていることを特徴とする着氷霜抑制性に優れた樹脂組成物。
(A群)
ビニルポリマー、ビニリデンポリマー、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つ
カルボキシル基、スルホ基、リン酸基、およびホウ酸基よりなる群から選ばれるアニオン性基を少なくとも1種含有しているアニオン性化合物。
(B群)
ビニルポリマー、ビニリデンポリマー、ポリアルキレンイミン、ポリアミン、糖鎖高分子、ポリアミノ酸、およびポリペプチドよりなる群から選ばれる少なくとも1種の化合物であり、且つ
アミノ基、イミノ基、アミジン基、ピリジル基、イミダゾリン基、および核酸塩基よりなる群から選ばれるカチオン性基を少なくとも1種含有しているカチオン性化合物。 - 更に下記C群から選ばれる水素結合性化合物を含有するものである請求項1に記載の樹脂組成物。
(C群)
ビニルポリマー、ビニリデンポリマー、糖鎖高分子、ポリアミノ酸、ポリペプチド、ポリエチレングリコール、およびアルギン酸よりなる群から選ばれる少なくとも1種の化合物であり、且つ
アミド基、イミド基、水酸基、エーテル基、両性イオン構造の置換基、および糖鎖よりなる群から選ばれる水素結合性基を少なくとも1種含有している水素結合性化合物。 - 金属板の表面に、請求項1または2に記載の樹脂組成物から得られた着氷霜抑制層が形成されていることを特徴とする積層金属板。
- 前記着氷霜抑制層と金属板との間に、無機酸化物または有機−無機複合化合物からなる耐食性化成処理皮膜層を備えている請求項3に記載の積層金属板。
- 前記着氷霜抑制層と金属板との間に、ポリエステル系樹脂、ポリオレフィン系樹脂、エポキシ系樹脂、アクリル系樹脂、およびウレタン系樹脂よりなる群から選ばれる少なくとも1種の樹脂からなる耐食性皮膜層を備えている請求項3に記載の積層金属板。
- 前記耐食性皮膜層と金属板との間に、無機酸化物または有機−無機複合化合物からなる耐食性化成処理皮膜層を備えている請求項5に記載の積層金属板。
- 前記金属板が、アルミニウム板またはアルミニウム合金板である請求項3〜6のいずれかに記載の積層金属板。
- 請求項3〜7のいずれかに記載の積層金属板からなる熱交換器用フィン材。
- 請求項8に記載の熱交換器用フィン材を用いた熱交換器。
- 請求項9に記載の熱交換器を備えた空調機。