JP2008156802A - 高強力ロープ - Google Patents
高強力ロープ Download PDFInfo
- Publication number
- JP2008156802A JP2008156802A JP2006349387A JP2006349387A JP2008156802A JP 2008156802 A JP2008156802 A JP 2008156802A JP 2006349387 A JP2006349387 A JP 2006349387A JP 2006349387 A JP2006349387 A JP 2006349387A JP 2008156802 A JP2008156802 A JP 2008156802A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- rope
- aromatic polyamide
- fine powder
- inorganic fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】平均粒径が約20μm以下の微細な無機微粉末が、繊維表面に1.5〜14mg/m2付着された全芳香族ポリアミド繊維、特に、コポリパラフェニレン3,4’−オキシジフェニレン・テレフタルアミド繊維、でロープを構成する。
【選択図】なし
Description
全芳香族ポリアミド繊維を用いたロープは従来知られており、例えば特開平11−286830号公報(特許文献1)等、数多くの提案がなされている。しかし、従来の全芳香族ポリアミド繊維は機械的強度に優れるものの、耐摩耗性が悪く、容易に毛羽立ち易いために、これをロープにして繰り返し使用すると強度が低下するという問題点があった。また、金属ワイヤーロープでは、自重が重いために取扱いが困難であるという問題点があった。
このため、軽量で、柔軟で、取扱い性に優れ、かつ耐摩耗性に優れた高強力ロープの登場が望まれていた。
(1)全芳香族ポリアミド繊維の繊維表面に無機微粉末を0.4〜15mg/m2の割合で付着させてなる繊維から構成されている高強力ロープ。
(2)繊維表面に付着している無機微粉末の平均粒径が20μm以下である上記(1)の高強力ロープ。
(3)繊維表面に付着している無機微粉末が無水珪酸アルミニウム及び/又はアルミノ珪酸ナトリウムの微粉末である上記(1)又は(2)の高強力ロープ。
(4)全芳香族ポリアミド繊維がコポリパラフェニレン・3,4’−オキシジフェニレン・テレフタルアミド繊維である上記(1)〜(3)のいずれかの高強力ロープ。
(5)上記全芳香族ポリアミド繊維が引張り強度が20cN/dtex以上で、かつ初期モジュラスが500cN/dtex以上の繊維である上記(1)〜(4)のいずれかの高強力ロープ。
特に、本発明においてコポリパラフェニレン・3,4’−オキシジフェニレン・テレフタルアミド繊維からなるロープは、上記の諸特性に加え、引張り強度、化学的安定性等にも優れており、また、使用中にフィブリル化が生じるおそれもないので、過酷な条件でも十分長期間使用できるという利点がある。従って、従来の全芳香族ポリアミド繊維製ロープでは使用できなかった大型船舶の係留用ロープ、ザイル、アンカーロープ、底曳漁業用ロープ等の用途にも有効に利用することが可能となる。
反応条件は特別な制限を必要としない。酸クロライドとジアミンとの反応は、一般に急速であり、反応温度は例えば−25℃〜100℃、好ましくは−10℃〜80℃である。
予め仕上げオイルを付与しない試料を約3gサンプリングする。次いで120℃で1時間乾燥した後に重量a(g)を精秤する。次いで、この試料を800℃の焼却炉中で完全に灰化させ、灰化後の灰分重量b(g)を測定し、次式で算出した。
繊度、切断強度、弾性率をJIS L1013に準拠して測定した。
耐摩耗性は、JIS L1095のうち磨耗強さを測定するB法の準拠した磨耗試験により、破断までの摩擦回数で評価した。
JIS L 2707の方法により引張り試験を行い、測定した。
コポリパラフェニレン・3,4’−オキシジフェニレン・テレフタルアミド(共重合モル比が1:1の芳香族コポリアミド)の濃度6重量%のNMP溶液を紡糸ドープに用い、該ドープを孔数667ホールの紡糸口金から吐出し、エアーギャップ約10mmを介してNMP濃度30重量%の水溶液中に紡出して凝固させた(半乾半湿式紡糸法)。その後、凝固糸条を水洗し、絞りローラに通して表面付着水を除去し、無水珪酸アルミニウムとアルミノ珪酸ナトリウムの重量比率が1対1である無機微粉末(無水珪酸アルミニウムの平均粒径1.1μm、アルミノ珪酸ナトリウムの平均粒径2.1μm)の濃度2.0重量%の水性分散浴に約1秒間浸漬し、次いで、絞りローラに通し、無機微粉末液の付着した糸条を得た。引き続いて、該糸条を表面温度が200℃の乾燥ローラを用いて完全に乾燥させた後、温度500℃下で10倍に延伸した後、表面を水シャワーで洗浄した後、巻き取ることにより繊維表面に無機微粉末が良好に分散したパラ型芳香族ポリアミド繊維マルチフィラメント糸条を得た。
巻き取り工程前の洗浄での条件を変更して、繊維表面の無機微粉末の付着量が多いこと以外は実施例1と同様にして、無機微粉末付着原糸を作成し、その原糸及びロープの特性を表1に示す。
巻き取り工程前の洗浄を行わず、繊維表面の無機微粉末の付着量が多いこと以外は実施例1と同様にして、無機微粉末付着原糸を作成し、その原糸及びロープの特性を表1に示す。
Claims (5)
- 全芳香族ポリアミド繊維の繊維表面に無機微粉末を0.4〜15mg/m2の割合で付着させてなる繊維から構成されていることを特徴とする高強力ロープ。
- 繊維表面に付着している無機微粉末の平均粒径が、20μm以下であることを特徴とする請求項1記載の高強力ロープ。
- 繊維表面に付着している無機微粉末が、無水珪酸アルミニウム及び/又はアルミノ珪酸ナトリウムの微粉末であることを特徴とする請求項1又は請求項2記載の高強力ロープ。
- 全芳香族ポリアミド繊維が、コポリパラフェニレン3,4’−オキシジフェニレン・テレフタルアミド繊維であることを特徴とする請求項1〜請求項3のいずれかに記載の高強力ロープ。
- 全芳香族ポリアミド繊維が、引張り強度が20cN/dtex以上であって、かつ初期モジュラスが500cN/dtex以上、の繊維であることを特徴とする請求項1〜請求項4のいずれかに記載の高強力ロープ。