JP2006297838A - 共押出積層発泡体及びその成形体 - Google Patents
共押出積層発泡体及びその成形体 Download PDFInfo
- Publication number
- JP2006297838A JP2006297838A JP2005125731A JP2005125731A JP2006297838A JP 2006297838 A JP2006297838 A JP 2006297838A JP 2005125731 A JP2005125731 A JP 2005125731A JP 2005125731 A JP2005125731 A JP 2005125731A JP 2006297838 A JP2006297838 A JP 2006297838A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- polyolefin resin
- foam
- laminated foam
- resin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
持続性の高い十分な帯電防止効果を有し、耐衝撃性、剛性等機械的物性、緩衝性、熱成形性に優れる発泡体及びその成形体の提供を目的とする。
【解決手段】
見掛け密度が100g/L〜450g/L、連続気泡率が40%以下のポリスチレン系樹脂発泡層の少なくとも片面に帯電防止剤を含むポリオレフィン系樹脂層を有する共押出積層発泡体であって、該発泡層を構成するポリスチレン系樹脂組成物はスチレン系エラストマーを含有するものであり、且つポリスチレン系樹脂組成物中のゴム成分含有量が9〜30重量%であり、該積層発泡体の該ポリオレフィン系樹脂層積層面のエタノール水溶液洗浄後の表面固有抵抗率が1×1013Ω以下であることを特徴とする共押出積層発泡体。
【選択図】 なし
Description
まず500mLの三角フラスコに試料0.2〜0.4gを秤量し、クロロホルム50mLを加えて溶解する。次いで一塩化ヨウ素四塩化炭素溶液25mLを添加して1時間暗所にて放置する。放置後、2.5重量%ヨウ化カリウム溶液75mLを加え、更にチオ硫酸ナトリウム20重量%エタノール溶液によりフラスコ内容物の色が薄くなるまで滴定する。その後、1重量%デンプン指示薬約0.5mLを加え、エタノールでフラスコ内壁を洗浄し、再度無色になるまでチオ硫酸ナトリウム20重量%エタノール溶液で滴定し、次に示す式(1)によりゴム成分の含有量(ゴム成分含有量)(重量%)を算出する。
ゴム成分含有量(重量%)={(c - d)×0.1×f×27/1000}/W×100・・・(1)
ただし、上記式中、c、d、f、Wは次に示すような値である。
c:ブランクの滴定に要した1/10規定のチオ硫酸ナトリウム20重量%アルコール溶
液量(mL)
d:試料の滴定に要した1/10規定のチオ硫酸ナトリウム20重量%アルコール溶液量
(mL)
f:1/10規定のチオ硫酸ナトリウム20重量%アルコール溶液のファクター
W:試料重量(g)
株式会社宍戸商会製のスタティック・オネストメーターTYPE S-5109等の装置を使用して、JIS L 1094(1988)に基づいて測定する。まず縦45mm、横45mmの正方形の試験片を測定面が上になるよう測定装置上の試験片取付枠に取付け、印加部の針電極の先端から試験片上面までの距離を20mm、受電部の電極から試験片までの距離を15mmに各々調整する。次に、ターンテーブルを回転させながら(+)10kvの電圧を印加し、最大帯電圧に達し安定した電圧の値を当該飽和電圧値とする。尚、測定は5回以上行いその平均値を採用する。
坪量(g/m2)=1000×(X/(L×W))・・・(2)
なお、本発明の積層発泡体は複数枚の該発泡体を貼り合わせたものとすることにより厚みを厚くしたものであってかまわない。この場合、厚みの上限は積層枚数を増すことにより任意に大きくすることができる。なお積層発泡体1の厚みは、発泡層2の厚みおよびポリオレフィン系樹脂層3の厚み、更に必要に応じて設けられる重合体層の厚みを合せた積層発泡体1全体の厚み(全厚み)のことである。
S(%)=(Va−Vx)×100/(Va−W/ρ) ・・・(3)
但し、上記式中の、Va、W、ρは以下の通りである。
Va:測定に使用した試験片のみかけ容積(cm3)
W:試験片の重量(g)
ρ:試験片を構成する樹脂の密度(g/cm3)
積層発泡体1のポリオレフィン系樹脂層3の表面固有抵抗率が1.0×1013(Ω)を超える場合は、帯電防止性能が不十分となる虞があり、積層発泡体1の表面には静電荷が蓄積し、埃が付着しやすくなる。この点を考慮すれば、ポリオレフィン系樹脂層3の表面固有抵抗率は、8.0×1012(Ω)以下が好ましく、5.0×1012(Ω)以下がより好ましく、更に1.0×1012(Ω)以下が好ましい。
また積層発泡体1のポリオレフィン系樹脂層3の表面固有抵抗率が1.0×108(Ω)未満の場合は、帯電防止性能として品質過剰となりコスト高に繋がるため、積層発泡体1のポリオレフィン系樹脂層3の表面固有抵抗率は1.0×108(Ω)以上とすることが好ましい。
(a1)のブロックと(b1)のブロックとが繰り返し交互に結合した構造を有するブロックポリマー(A1)であり、一般式(1)で示される繰り返し単位を有するポリマーが含まれる。一般式(1)中、nは2〜50の整数、R1及びR2の一方は水素原子であり他方は水素原子又は炭素数1〜10のアルキル基、yは15〜800の整数、E1はジオール(b0)から水酸基を除いた残基、A1は炭素数2〜4のアルキレン基、m及びm'は1〜300の整数を表し、X及びX'は一般式(2)〜(8)で示される基から選ばれる基及び対応する(2')〜(8')で示される基から選ばれる基、すなわち、Xが一般式(2)で示される基のとき、X'は一般式(2')で示される基であり、一般式(3)〜(8)及び(3')〜(8')についても同様の関係である。
ブロックポリマー(A2)は、ポリオレフィン(a)のブロックと親水性ポリマー(b)のブロックとが(a)-(b)型または(a)-(b)-(a)型に結合されてなるブロックポリマーである。(A2)は、(b2)と一般式(9)〜(11)のいずれかで示されるカルボニル基をポリマーの片末端に有するポリオレフィン(a4)との反応で得ることができる。
ブロックポリマー(A3)は、親水性ポリマー(b)として分子内に非イオン性分子鎖(c1)で隔てられた2〜80個、好ましくは3〜60個のカチオン性基(c2)を分子内に有するカチオン性ポリマー(b3)のブロックを有するものであり、(a)と(b3)とが繰り返し交互に結合した構造を有する。(A3)のMnは、通常2000〜60000、好ましくは5000〜40000、特に好ましくは8000〜30000である。(A3)中のカチオン性基(c2)の含量は、(A3)1分子当り、2〜500個、好ましくは10〜300個、特に好ましくは15〜250個である。カチオン性基(c2)1個当りの(A3)のMnは、通常120〜30000、好ましくは200〜6000、特に好ましくは300〜4000である。
ブロックポリマー(A4)は、(b)として、スルホニル基を有するジカルボン酸(e1)と、ジオール(b0)又はポリエーテル(b1)とを必須構成単位とし、かつ分子内に2〜80個、好ましくは3〜60個のスルホニル基を有するアニオン性ポリマー(b4)のブロックを有するものであり、(a)と(b4)が繰り返し交互に結合した構造を有する。(A4)のMnは、通常2000〜60000、好ましくは5000〜40000、特に好ましくは8000〜30000である。また、(A4)中のスルホニル基の含量は、(A4)1分子当り、2〜500個、好ましくは10〜300個、特に好ましくは15〜250個である。スルホニル基1個当りの(A4)のMnは、通常120〜30000、好ましくは200〜6000、特に好ましくは300〜4000である。
Tb<140℃ ・・・(4)
(但し、式中Tbは高分子型帯電防止剤5の結晶化温度(℃)である。)
(1)HD1:高密度ポリエチレン(密度=964g/L、MFR=8.0g/10min、日本ポリエチレン株式会社製 商品名「HJ566W」)
(2)LL1:直鎖状低密度ポリエチレン(密度=924g/L、MFR=8.0g/10min、日本ポリエチレン株式会社製 商品名「AM630A」)
(3)PP1:ポリプロピレン(密度=900g/L、MFR=14.0g/10min、株式会社プライムポリマー製 商品名「J750HP」)
(4)LD1:分岐状低密度ポリエチレン(密度=917g/L、MFR=4.7g/10min、日本ユニカー株式会社製 商品名「NUC-8008」)
(5)P300:ポリエーテル−ポリプロピレンブロック共重合体を主成分とする高分子型帯電防止剤(密度=990g/L、MFR = 20g/10min、数平均分子量14000、融点136℃、結晶化温度90℃、溶融粘度751Pa・s、三洋化成工業株式会社製 商品名「ペレスタット300」)
ポリスチレン系樹脂発泡層形成用樹脂溶融物を得るための押出機として内径(D)90mm、L/D=32の押出機と内径(D)120mm、L/D=34の押出機との2台の押出機からなるタンデム押出機を使用し、高分子型帯電防止剤を含有するポリオレフィン系樹脂層形成用樹脂溶融物を得るための押出機として内径(D)40mm、L/D=42の押出機を使用した。
得られた積層発泡体について、見掛け密度、連続気泡率、坪量、表面固有抵抗率、飽和電圧を各々前述した方法を用いて測定した。その結果を表2に示す。
得られた積層発泡体について、耐衝撃性、接着強度、成形性について評価した。その結果を表3に示す。
衝撃あなあけ強さは、JIS P8134(1976)に基づく試験で測定され、試験には、厚みが0.9mm、横幅150mm、奥行き150mmのものを試験片として用いた。なお、試験片は、ポリオレフィン系樹脂層を取り除いた発泡層を用いて、発泡層を加熱プレスおよび冷却プレスを用いて脱泡し、厚みを0.9mmに調整したものを用いた。
測定された衝撃あなあけ強さ(kgf・cm)に応じて、次のように評価した。
◎:120 kgf・cm以上
○:40 kgf・cm以上かつ120 kgf・cm未満
×:40 kgf・cm未満
積層発泡体について、JIS Z0237(1991)に準じた90°引き剥がし法により、接着強度を測定した。具体的には、株式会社オリエンテック製のテンシロン万能試験機により、幅25mm、長さ250mmの試験片を用いて、試験速度300mm/minの条件で接着強度を測定した。また、測定は5回以上行ない、得られた測定値のデータから最大値と最小値を除き、残った測定値の平均値を接着性の評価に用いた。なお、ポリオレフィン樹脂層が薄く、測定時に破断してしまう場合には、これに粘着テープなどを貼って補強し、補強したものを用いて接着強度を測定した。
測定された接着強度(gf)に応じて、次のように評価した。
◎:400 gf以上
○:250 gf以上かつ400 gf未満
×:250 gf未満
まず、単発真空成形機(株式会社浅野研究所製:FSK型)と、外寸が340mm×240mm、深さ43mmの部品トレー金型を用いて、金型表面温度を80℃に温調しつつ(但し、ポリオレフィン系樹脂層を構成するポリオレフィン系樹脂がLDの場合(実施例9)は、離型を良くするため40℃に温調)、積層発泡体の表面温度を変化させて成形を行なってトレー形状の成形体を得た。
この際、成形体に、外観上、裂け、デラミ、厚みの偏り、表面ヤケなどを生じていないか評価し、更に、これらの生じていない良好な成形体が得られる積層発泡体の表面温度範囲の幅を測定した。
測定された表面温度の幅に応じて、次に示すように評価した。
◎:良好な成形体が得られる表面温度幅が、10℃以上
○:良好な成形体が得られる表面温度幅が、6℃以上かつ10℃未満
△:良好な成形体が得られる表面温度幅が、3℃以上かつ6℃未満
×:良好な成形体が得られる表面温度幅が、3℃未満
ポリスチレン系樹脂組成物の発泡層形成のために、PSとSBSを表1に示す配合量に変更した以外は実施例1と同様にして積層発泡体を得た。
得られた積層発泡体について、見掛け密度、連続気泡率、坪量、表面固有抵抗率、飽和電圧を各々前述した方法を用いて測定し、また耐衝撃性、接着強度、成形性について評価した。結果を表2、表3に示す。
PS、SBS:200℃、49.03N
HD、LL、高分子型帯電防止剤:190℃、21.18N
PP:230℃、21.18N
また、実施例及び比較例にて用いた気泡調整剤マスターバッチの組成は、スチレン樹脂70重量%とタルク30重量%のものである。
2 ポリスチレン系樹脂組成物発泡層
3 高分子型帯電防止剤を含有してなるポリオレフィン系樹脂層
4 ポリオレフィン系樹脂
5 高分子型帯電防止剤
6 揮発性可塑剤
7 ポリオレフィン系樹脂層形成用樹脂溶融物
8 ポリスチレン系樹脂組成物
9 発泡剤
10 ポリスチレン系樹脂発泡層形成用樹脂溶融物
11 第1の押出機
12 第2の押出機
Claims (7)
- 見掛け密度が100g/L〜450g/L、連続気泡率が40%以下のポリスチレン系樹脂発泡層の少なくとも片面に帯電防止剤を含むポリオレフィン系樹脂層を有する共押出積層発泡体であって、該発泡層を構成するポリスチレン系樹脂組成物はスチレン系エラストマーを含有するものであり、且つポリスチレン系樹脂組成物中のゴム成分含有量が9〜30重量%であり、該積層発泡体の該ポリオレフィン系樹脂層積層面のエタノール水溶液洗浄後の表面固有抵抗率が1×1013Ω以下であることを特徴とする共押出積層発泡体。
- ポリオレフィン系樹脂層の坪量が3〜50g/m2であることを特徴とする請求項1に記載の共押出積層発泡体。
- ポリオレフィン系樹脂層を構成するポリオレフィン系樹脂が融点115℃以上のポリオレフィン系樹脂であることを特徴とする請求項1又は2に記載の共押出積層発泡体。
- ポリオレフィン系樹脂層を構成するポリオレフィン系樹脂がポリエチレン系樹脂およびポリプロピレン系樹脂から選択される1種、或いは2種以上の混合物であることを特徴とする請求項1〜3のいずれかに記載の共押出積層発泡体。
- ポリオレフィン系樹脂層を構成するポリオレフィン系樹脂がポリエチレン系樹脂であり、ポリオレフィン系樹脂層の坪量(g/m2)と共押出積層発泡体の飽和電圧(kV)との積が12kV・g/m2以下であることを特徴とする請求項1〜4のいずれかに記載の共押出積層発泡体。
- ポリオレフィン系樹脂層を構成するポリオレフィン系樹脂がポリプロピレン系樹脂であり、ポリオレフィン系樹脂層の坪量(g/m2)と共押出積層発泡体の飽和電圧(kV)との積が7kV・g/m2以下であることを特徴とする請求項1〜4のいずれかに記載の共押出積層発泡体。
- 請求項1〜6のいずれかに記載の共押出積層発泡体を熱成形してなる成形体。