JP2001521969A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2001521969A5 JP2001521969A5 JP2000519031A JP2000519031A JP2001521969A5 JP 2001521969 A5 JP2001521969 A5 JP 2001521969A5 JP 2000519031 A JP2000519031 A JP 2000519031A JP 2000519031 A JP2000519031 A JP 2000519031A JP 2001521969 A5 JP2001521969 A5 JP 2001521969A5
- Authority
- JP
- Japan
- Prior art keywords
- weight
- polymer
- polybutylene succinate
- less
- polymers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
【特許請求の範囲】
【請求項1】
a) 0より多く100重量%未満の重量のポリ(乳酸)ポリマー、
b) ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれる、0より多く100重量%未満の重量のポリマー、および
c) 約10〜約40の親水性−親油性平衡比を示し、0より多く約15重量%までの重量の湿潤剤、
から成る熱可塑性組成物であって、すべての重量%は該熱可塑性組成物内に存在するポリ(乳酸)ポリマーと、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーと、湿潤剤の総重量に基づいていること、
を特徴とする熱可塑性組成物。
【請求項2】 ポリ(乳酸)ポリマーは約5重量%〜約95重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約95重量%の重量で存在していること、および湿潤剤は約0.5重量%〜約15重量%の重量で存在していること、
を特徴とする請求項1に記載の熱可塑性組成物。
【請求項3】 ポリ(乳酸)ポリマーは約10重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約10重量%〜約90重量%の重量で存在していること、および湿潤剤は約1重量%〜約13重量%の重量で存在していること、
を特徴とする請求項2に記載の熱可塑性組成物。
【請求項4】 湿潤剤は約10〜約20の親水性−親油性平衡比を示すこと、を特徴とする請求項1に記載の熱可塑性組成物。
【請求項5】 湿潤剤はエトキシレーテッドアルコールであること、
を特徴とする請求項1に記載の熱可塑性組成物。
【請求項6】 ポリ(乳酸)ポリマーは約75重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約20重量%の重量で存在していること、および湿潤剤はエトキソレーテッドアルコールであること、
を特徴とする請求項1に記載の熱可塑性組成物。
【請求項7】 熱可塑性組成物から作られた多成分繊維であって、前記熱可塑性組成物は、
a) 0より多く100重量%未満の重量のポリ(乳酸)ポリマー、
b) ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれる、0より多く100重量%未満の重量のポリマー、および
c) 約10〜約40の親水性−親油性平衡比を示し、0より多く約15重量%までの重量の湿潤剤、
から成り、すべての重量%は前記熱可塑性組成物内に存在するポリ(乳酸)ポリマーと、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーと、湿潤剤の総重量に基づいていること、
前記多成分繊維は約80°未満の前進接触角値と、約60°未満の後退接触角値を示すこと、
を特徴とする多成分繊維。
【請求項8】 ポリ(乳酸)ポリマーは約5重量%〜約95重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約95重量%の重量で存在していること、および湿潤剤は約0.5重量%〜約15重量%の重量で存在していること、
を特徴とする請求項7に記載の多成分繊維。
【請求項9】 湿潤剤は約10〜約20の親水性−親油性平衡比を示すこと、を特徴とする請求項7に記載の多成分繊維。
【請求項10】 湿潤剤はエトキシレーテッドアルコールであること、
を特徴とする請求項7に記載の多成分繊維。
【請求項11】 多成分繊維は約75°未満の前進接触角値と、約55°未満の後退接触角値を示すこと、
を特徴とする請求項7に記載の多成分繊維。
【請求項12】 前進接触角値と後退接触角値との差は約30°未満であること、
を特徴とする請求項7に記載の多成分繊維。
【請求項13】 多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項7に記載の多成分繊維。
【請求項14】 ポリ(乳酸)ポリマーは約75重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約20重量%の重量で存在していること、および湿潤剤はエトキシレーテッドアルコールであること、前進接触角値と後退接触角値との差は約30°未満であること、および多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項7に記載の多成分繊維。
【請求項15】 液体浸透性表面シート、前記表面シートに結合された裏シート、および前記表面シートと前記裏シートの間に置かれた吸収コアから成る使い捨て吸収製品であって、前記液体吸収性表面シートは熱可塑性組成物から作られた多成分繊維から成り、前記熱可塑性組成物は、
a) 0より多く100重量%未満の重量のポリ(乳酸)ポリマー、
b) ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれる、0より多く100重量%未満の重量のポリマー、および
c) 約10〜約40の親水性−親油性平衡比を示し、0より多く約15重量%までの重量の湿潤剤、
から成り、すべての重量%は前記熱可塑性組成物内に存在するポリ(乳酸)ポリマーと、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーと、湿潤剤の総重量に基づいていること、
前記多成分繊維は約80°未満の前進接触角値と約60°未満の後退接触角値を示すこと、
を特徴とする使い捨て吸収製品。
【請求項16】 ポリ(乳酸)ポリマーは約5重量%〜約95重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約95重量%の重量で存在していること、および湿潤剤は約0.5重量%〜約15重量%の重量で存在していること、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項17】 湿潤剤は約10〜約20の親水性−親油性平衡比を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項18】 湿潤剤はエトキシレーテッドアルコールであること、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項19】 多成分繊維は約75°未満の前進接触角値と約55°未満の後退接触角値を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項20】 前進接触角値と後退接触角値との差は約30°未満であること、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項21】 多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項22】 ポリ(乳酸)ポリマーは約75重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約20重量%の重量で存在していること、湿潤剤はエトキシレーテッドアルコールであること、前進接触角値と後退接触角値との差は約30°未満であること、および多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項1】
a) 0より多く100重量%未満の重量のポリ(乳酸)ポリマー、
b) ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれる、0より多く100重量%未満の重量のポリマー、および
c) 約10〜約40の親水性−親油性平衡比を示し、0より多く約15重量%までの重量の湿潤剤、
から成る熱可塑性組成物であって、すべての重量%は該熱可塑性組成物内に存在するポリ(乳酸)ポリマーと、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーと、湿潤剤の総重量に基づいていること、
を特徴とする熱可塑性組成物。
【請求項2】 ポリ(乳酸)ポリマーは約5重量%〜約95重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約95重量%の重量で存在していること、および湿潤剤は約0.5重量%〜約15重量%の重量で存在していること、
を特徴とする請求項1に記載の熱可塑性組成物。
【請求項3】 ポリ(乳酸)ポリマーは約10重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約10重量%〜約90重量%の重量で存在していること、および湿潤剤は約1重量%〜約13重量%の重量で存在していること、
を特徴とする請求項2に記載の熱可塑性組成物。
【請求項4】 湿潤剤は約10〜約20の親水性−親油性平衡比を示すこと、を特徴とする請求項1に記載の熱可塑性組成物。
【請求項5】 湿潤剤はエトキシレーテッドアルコールであること、
を特徴とする請求項1に記載の熱可塑性組成物。
【請求項6】 ポリ(乳酸)ポリマーは約75重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約20重量%の重量で存在していること、および湿潤剤はエトキソレーテッドアルコールであること、
を特徴とする請求項1に記載の熱可塑性組成物。
【請求項7】 熱可塑性組成物から作られた多成分繊維であって、前記熱可塑性組成物は、
a) 0より多く100重量%未満の重量のポリ(乳酸)ポリマー、
b) ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれる、0より多く100重量%未満の重量のポリマー、および
c) 約10〜約40の親水性−親油性平衡比を示し、0より多く約15重量%までの重量の湿潤剤、
から成り、すべての重量%は前記熱可塑性組成物内に存在するポリ(乳酸)ポリマーと、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーと、湿潤剤の総重量に基づいていること、
前記多成分繊維は約80°未満の前進接触角値と、約60°未満の後退接触角値を示すこと、
を特徴とする多成分繊維。
【請求項8】 ポリ(乳酸)ポリマーは約5重量%〜約95重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約95重量%の重量で存在していること、および湿潤剤は約0.5重量%〜約15重量%の重量で存在していること、
を特徴とする請求項7に記載の多成分繊維。
【請求項9】 湿潤剤は約10〜約20の親水性−親油性平衡比を示すこと、を特徴とする請求項7に記載の多成分繊維。
【請求項10】 湿潤剤はエトキシレーテッドアルコールであること、
を特徴とする請求項7に記載の多成分繊維。
【請求項11】 多成分繊維は約75°未満の前進接触角値と、約55°未満の後退接触角値を示すこと、
を特徴とする請求項7に記載の多成分繊維。
【請求項12】 前進接触角値と後退接触角値との差は約30°未満であること、
を特徴とする請求項7に記載の多成分繊維。
【請求項13】 多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項7に記載の多成分繊維。
【請求項14】 ポリ(乳酸)ポリマーは約75重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約20重量%の重量で存在していること、および湿潤剤はエトキシレーテッドアルコールであること、前進接触角値と後退接触角値との差は約30°未満であること、および多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項7に記載の多成分繊維。
【請求項15】 液体浸透性表面シート、前記表面シートに結合された裏シート、および前記表面シートと前記裏シートの間に置かれた吸収コアから成る使い捨て吸収製品であって、前記液体吸収性表面シートは熱可塑性組成物から作られた多成分繊維から成り、前記熱可塑性組成物は、
a) 0より多く100重量%未満の重量のポリ(乳酸)ポリマー、
b) ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれる、0より多く100重量%未満の重量のポリマー、および
c) 約10〜約40の親水性−親油性平衡比を示し、0より多く約15重量%までの重量の湿潤剤、
から成り、すべての重量%は前記熱可塑性組成物内に存在するポリ(乳酸)ポリマーと、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーと、湿潤剤の総重量に基づいていること、
前記多成分繊維は約80°未満の前進接触角値と約60°未満の後退接触角値を示すこと、
を特徴とする使い捨て吸収製品。
【請求項16】 ポリ(乳酸)ポリマーは約5重量%〜約95重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約95重量%の重量で存在していること、および湿潤剤は約0.5重量%〜約15重量%の重量で存在していること、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項17】 湿潤剤は約10〜約20の親水性−親油性平衡比を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項18】 湿潤剤はエトキシレーテッドアルコールであること、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項19】 多成分繊維は約75°未満の前進接触角値と約55°未満の後退接触角値を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項20】 前進接触角値と後退接触角値との差は約30°未満であること、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項21】 多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。
【請求項22】 ポリ(乳酸)ポリマーは約75重量%〜約90重量%の重量で存在していること、ポリブチレンサクシネートポリマー、ポリブチレンサクシネートアジペートポリマー、およびこれらのポリマーの混合物から成る群から選ばれるポリマーは約5重量%〜約20重量%の重量で存在していること、湿潤剤はエトキシレーテッドアルコールであること、前進接触角値と後退接触角値との差は約30°未満であること、および多成分繊維は約15%未満の熱収縮値を示すこと、
を特徴とする請求項15に記載の使い捨て吸収製品。