JP2000268821A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2000268821A5 JP2000268821A5 JP1999074482A JP7448299A JP2000268821A5 JP 2000268821 A5 JP2000268821 A5 JP 2000268821A5 JP 1999074482 A JP1999074482 A JP 1999074482A JP 7448299 A JP7448299 A JP 7448299A JP 2000268821 A5 JP2000268821 A5 JP 2000268821A5
- Authority
- JP
- Japan
- Prior art keywords
- lithium
- cobalt
- compound
- positive electrode
- active material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
【００１０】
また、本発明の製造方法においては、コバルト化合物は、酸化コバルト（Ｃｏ３Ｏ４、Ｃｏ２Ｏ３又はこれらの混合物）、水酸化コバルト（Ｃｏ（ＯＨ） ２ ）、オキシ水酸化コバルト（ＣｏＯＯＨ）、及び炭酸コバルト（ＣｏＣＯ３）を含有する化合物からなる群から選ばれる１種以上であることが好ましく、リチウム化合物は、炭酸リチウム及び水酸化リチウムからなる群から選ばれることが好ましい。
また、本発明の製造方法においては、コバルト化合物は、酸化コバルト（Ｃｏ３Ｏ４、Ｃｏ２Ｏ３又はこれらの混合物）、水酸化コバルト（Ｃｏ（ＯＨ） ２ ）、オキシ水酸化コバルト（ＣｏＯＯＨ）、及び炭酸コバルト（ＣｏＣＯ３）を含有する化合物からなる群から選ばれる１種以上であることが好ましく、リチウム化合物は、炭酸リチウム及び水酸化リチウムからなる群から選ばれることが好ましい。
【００１７】
本発明におけるコバルト化合物としては、Ｃｏ３Ｏ４、Ｃｏ２Ｏ３又はこれらの混合物からなる酸化コバルト、水酸化コバルト（Ｃｏ（ＯＨ） ２ ）、オキシ水酸化コバルト（ＣｏＯＯＨ）、炭酸コバルト（ＣｏＣＯ３）を含有する化合物を挙げることができる。また、ｙが０でない場合には、第３成分としてのＭは、酸化物、水酸化物、炭酸塩等として、焼成前のコバルト化合物とリチウム化合物とを含む混合物に添加することが好ましい。また、均一性を高めるためには、予めコバルト化合物と第３成分を含む化合物とを例えば共沈させてコバルトとＭとの均一性の高い固溶体を作成してからリチウム化合物を混合することが好ましい。
本発明におけるコバルト化合物としては、Ｃｏ３Ｏ４、Ｃｏ２Ｏ３又はこれらの混合物からなる酸化コバルト、水酸化コバルト（Ｃｏ（ＯＨ） ２ ）、オキシ水酸化コバルト（ＣｏＯＯＨ）、炭酸コバルト（ＣｏＣＯ３）を含有する化合物を挙げることができる。また、ｙが０でない場合には、第３成分としてのＭは、酸化物、水酸化物、炭酸塩等として、焼成前のコバルト化合物とリチウム化合物とを含む混合物に添加することが好ましい。また、均一性を高めるためには、予めコバルト化合物と第３成分を含む化合物とを例えば共沈させてコバルトとＭとの均一性の高い固溶体を作成してからリチウム化合物を混合することが好ましい。
Claims (5)
- コバルト化合物とリチウム化合物とを含む混合物を、焼成することによって合成される下記式（１）で表されるリチウム２次電池正極活物質用リチウム含有複合酸化物の製造方法において、前記コバルト化合物と前記リチウム化合物との混合時の前記リチウム化合物の含水量が０．１５〜５重量％であることを特徴とするリチウム２次電池正極活物質用リチウム含有複合酸化物の製造方法（式（１）中、ｘは、０．９〜１．１の実数であり、ｙは、０〜０．９の実数であり、Ｍは、Ｎｉ、Ｍｎ、Ｆｅ、Ｖ、Ｃｒ、Ａｌ、Ｍｇ、Ｔｉ、Ｙ、Ｃｅ、Ｎｂ、Ｚｒ、Ｓｉ及びＣａからなる群から選ばれる１種以上の元素を示す。）。
- 前記コバルト化合物は、酸化コバルト（Ｃｏ３Ｏ４、Ｃｏ２Ｏ３又はこれらの混合物）、水酸化コバルト（Ｃｏ（ＯＨ） ２ ）、オキシ水酸化コバルト（ＣｏＯＯＨ）、及び炭酸コバルト（ＣｏＣＯ３）からなる群から選ばれる１種以上であり、リチウム化合物は、炭酸リチウム及び水酸化リチウムからなる群から選ばれる１種以上である請求項１記載のリチウム２次電池正極活物質用リチウム含有複合酸化物の製造方法。
- 前記リチウム化合物の重量平均粒径が１〜１０μｍである請求項１又は２記載のリチウム２次電池正極活物質用リチウム含有複合酸化物の製造方法。
- 前記混合物を、大気中で８５０〜１０００℃にて焼成する請求項１、２又は３記載のリチウム２次電池正極活物質用リチウム含有複合酸化物の製造方法。
- 前記混合物を、１０〜５０時間焼成する請求項１、２、３又は４記載のリチウム２次電池正極活物質用リチウム含有複合酸化物の製造方法。