IN2014DN03212A - - Google Patents

Info

Publication number
IN2014DN03212A
IN2014DN03212A IN3212DEN2014A IN2014DN03212A IN 2014DN03212 A IN2014DN03212 A IN 2014DN03212A IN 3212DEN2014 A IN3212DEN2014 A IN 3212DEN2014A IN 2014DN03212 A IN2014DN03212 A IN 2014DN03212A
Authority
IN
India
Prior art keywords
steel sheet
less
volume
hot dipped
martensite
Prior art date
Application number
Other languages
English (en)
Inventor
Chisato Wakabayashi
Masafumi Azuma
Nobuhiro Fujita
Kohichi Sano
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of IN2014DN03212A publication Critical patent/IN2014DN03212A/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
    • C21D8/0426—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
    • C21D8/0436—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0478—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/009—Pearlite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
IN3212DEN2014 2011-09-30 2012-09-28 IN2014DN03212A (hu)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011216967 2011-09-30
PCT/JP2012/075230 WO2013047830A1 (ja) 2011-09-30 2012-09-28 引張強度980MPa以上有するめっき密着性、成形性と穴広げ性に優れた高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板とその製造方法

Publications (1)

Publication Number Publication Date
IN2014DN03212A true IN2014DN03212A (hu) 2015-05-22

Family

ID=47995853

Family Applications (1)

Application Number Title Priority Date Filing Date
IN3212DEN2014 IN2014DN03212A (hu) 2011-09-30 2012-09-28

Country Status (15)

Country Link
US (2) US9783878B2 (hu)
EP (1) EP2762592B1 (hu)
JP (1) JP5403185B2 (hu)
KR (1) KR101607786B1 (hu)
CN (1) CN103827336B (hu)
BR (1) BR112014007496B1 (hu)
CA (1) CA2850101C (hu)
ES (1) ES2670893T3 (hu)
IN (1) IN2014DN03212A (hu)
MX (1) MX2014003712A (hu)
PL (1) PL2762592T3 (hu)
RU (1) RU2586386C2 (hu)
TW (1) TWI523975B (hu)
WO (1) WO2013047830A1 (hu)
ZA (1) ZA201402970B (hu)

Families Citing this family (55)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
MX2014003712A (es) * 2011-09-30 2014-07-09 Nippon Steel & Sumitomo Metal Corp Lamina de acero galvanizada por inmersion en caliente, de alta resistencia, y lamina de acero galvanizada por inmersion en caliente, aleada, de alta resistencia, que tiene excelente adhesion de enchapado, formabilidad, y capacidad de expansion de agujero con resistencia a la traccion de 980 mpa o mas y metodo de fabricacion de las mismas.
JP5953693B2 (ja) * 2011-09-30 2016-07-20 新日鐵住金株式会社 めっき密着性と成形性に優れた高強度溶融亜鉛めっき鋼板とその製造方法
JP6168144B2 (ja) 2013-05-01 2017-07-26 新日鐵住金株式会社 亜鉛めっき鋼板及びその製造方法
PL2993245T3 (pl) 2013-05-01 2018-12-31 Nippon Steel & Sumitomo Metal Corp Blacha stalowa cienka o dużej wytrzymałości i niskim ciężarze właściwym mająca doskonałą spawalność punktową
JP6007882B2 (ja) * 2013-10-15 2016-10-19 新日鐵住金株式会社 引張最大強度７８０ＭＰａを有する衝突特性に優れた高強度鋼板、高強度溶融亜鉛めっき鋼板、並びに、高強度合金化溶融亜鉛めっき鋼板
JP6007881B2 (ja) * 2013-10-15 2016-10-12 新日鐵住金株式会社 引張最大強度７８０ＭＰａ以上を有する衝突特性に優れた高強度鋼板、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板
WO2015080242A1 (ja) * 2013-11-29 2015-06-04 新日鐵住金株式会社 熱間成形鋼板部材およびその製造方法ならびに熱間成形用鋼板
JP6314520B2 (ja) * 2014-02-13 2018-04-25 新日鐵住金株式会社 引張最大強度１３００ＭＰａ以上を有する成形性に優れた高強度鋼板、高強度溶融亜鉛めっき鋼板、及び、高強度合金化溶融亜鉛めっき鋼板とそれらの製造方法
CA2953741C (en) 2014-07-03 2021-08-10 Arcelormittal Method for producing an ultra high strength coated or not coated steel sheet and obtained sheet
CN104213040B (zh) * 2014-08-27 2016-02-17 南京创贝高速传动机械有限公司 一种高强度轴承的专用钢材及其加工工艺
JP6179674B2 (ja) * 2014-10-30 2017-08-16 Ｊｆｅスチール株式会社 高強度鋼板、高強度溶融亜鉛めっき鋼板、高強度溶融アルミニウムめっき鋼板および高強度電気亜鉛めっき鋼板、ならびに、それらの製造方法
TWI606123B (zh) * 2015-05-07 2017-11-21 Nippon Steel & Sumitomo Metal Corp High-strength steel plate and its manufacturing method
BR112017025389A2 (pt) * 2015-06-11 2018-08-07 Nippon Steel & Sumitomo Metal Corporation chapa de aço galvanizada e método para fabricar a mesma
US10808293B2 (en) * 2015-07-15 2020-10-20 Ak Steel Properties, Inc. High formability dual phase steel
EP3342893A4 (en) * 2015-08-24 2019-01-16 Nippon Steel & Sumitomo Metal Corporation ALLOY-FILLED ZINC PLATED STEEL SHEET AND METHOD FOR MANUFACTURING SAME
CN105112914A (zh) * 2015-08-31 2015-12-02 中国钢研科技集团有限公司 连续热镀锌装置和连续热镀锌方法
EP3378958B1 (en) 2015-09-22 2021-08-04 Hyundai Steel Company Plated steel plate and manufacturing method thereof
CA3006405A1 (en) 2015-12-15 2017-06-22 Tata Steel Ijmuiden B.V. High strength hot dip galvanised steel strip
WO2017109538A1 (en) * 2015-12-21 2017-06-29 Arcelormittal Method for producing a steel sheet having improved strength, ductility and formability
WO2017109540A1 (en) * 2015-12-21 2017-06-29 Arcelormittal Method for producing a high strength steel sheet having improved ductility and formability, and obtained steel sheet
CA3009294C (en) 2015-12-29 2022-06-21 Arcelormittal Method for producing a ultra high strength galvannealed steel sheet and obtained galvannealed steel sheet
KR102119333B1 (ko) * 2016-02-10 2020-06-04 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
US11993823B2 (en) 2016-05-10 2024-05-28 United States Steel Corporation High strength annealed steel products and annealing processes for making the same
EP3455068A1 (en) 2016-05-10 2019-03-20 United States Steel Corporation High strength steel products and annealing processes for making the same
US11560606B2 (en) 2016-05-10 2023-01-24 United States Steel Corporation Methods of producing continuously cast hot rolled high strength steel sheet products
TWI618799B (zh) * 2016-09-21 2018-03-21 新日鐵住金股份有限公司 鋼板
WO2018055425A1 (en) 2016-09-22 2018-03-29 Arcelormittal High strength and high formability steel sheet and manufacturing method
TWI602956B (zh) * 2016-10-04 2017-10-21 中國鋼鐵股份有限公司 提高鋼材顯微組織鑑別度之分析方法
WO2018085672A1 (en) 2016-11-04 2018-05-11 Nucor Corporation Multiphase, cold-rolled ultra-high strength steel
US11021776B2 (en) 2016-11-04 2021-06-01 Nucor Corporation Method of manufacture of multiphase, hot-rolled ultra-high strength steel
KR102252841B1 (ko) 2016-12-27 2021-05-14 제이에프이 스틸 가부시키가이샤 고강도 아연 도금 강판 및 그 제조 방법
US11326234B2 (en) 2017-03-31 2022-05-10 Nippon Steel Corporation Cold-rolled steel sheet and hot-dip galvanized cold-rolled steel sheet
MX2019011709A (es) * 2017-03-31 2019-11-21 Nippon Steel Corp Lamina de acero laminada en caliente, pieza forjada de acero y metodo de produccion para la misma.
WO2018193032A1 (en) * 2017-04-20 2018-10-25 Tata Steel Nederland Technology B.V. High strength steel sheet having excellent ductility and stretch flangeability
WO2018203097A1 (en) * 2017-05-05 2018-11-08 Arcelormittal A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet
WO2019092483A1 (en) 2017-11-10 2019-05-16 Arcelormittal Cold rolled and heat treated steel sheet and a method of manufacturing thereof
KR102020411B1 (ko) 2017-12-22 2019-09-10 주식회사 포스코 가공성이 우수한 고강도 강판 및 이의 제조방법
KR102075216B1 (ko) * 2017-12-24 2020-02-07 주식회사 포스코 고 항복비형 고 강도 강판 및 그 제조방법
TWI650435B (zh) * 2018-03-30 2019-02-11 日商新日鐵住金股份有限公司 鋼板及其製造方法
KR102109261B1 (ko) 2018-08-07 2020-05-11 주식회사 포스코 강도 및 도금성이 우수한 저비중 클래드 강판 및 그 제조방법
KR102285523B1 (ko) * 2019-11-20 2021-08-03 현대제철 주식회사 고강도 및 고성형성을 가지는 강판 및 그 제조방법
KR102250333B1 (ko) * 2019-12-09 2021-05-10 현대제철 주식회사 초고강도 냉연강판 및 이의 제조방법
CN111334720B (zh) * 2020-03-30 2022-03-25 邯郸钢铁集团有限责任公司 具有良好冷成型性能的高Al耐磨钢带及其生产方法
KR102504647B1 (ko) * 2020-09-16 2023-03-03 현대제철 주식회사 초고강도 냉연강판 및 그 제조방법
KR102496311B1 (ko) * 2020-09-25 2023-02-07 현대제철 주식회사 고강도 및 고성형성 강판 및 그 제조방법
KR102497567B1 (ko) * 2020-12-08 2023-02-10 현대제철 주식회사 고강도 및 고성형성 강판 및 그 제조방법
CN114807737B (zh) * 2021-01-21 2023-06-13 宝山钢铁股份有限公司 一种热镀锌钢及其制造方法
KR102459164B1 (ko) 2021-06-23 2022-10-25 울산과학기술원 강재의 신장 플랜지 성형성 평가방법
KR102504097B1 (ko) * 2021-06-29 2023-02-28 현대제철 주식회사 도금 강판 및 그 제조방법
CN113817961B (zh) * 2021-08-26 2022-06-21 马鞍山钢铁股份有限公司 彩涂基料用热浸镀锌钢板及其制造方法
WO2023162522A1 (ja) * 2022-02-24 2023-08-31 Ｊｆｅスチール株式会社 鋼板およびその製造方法
CN114737037B (zh) * 2022-03-30 2023-06-27 马鞍山钢铁股份有限公司 一种基于CSP工艺的550MPa级高塑韧性热镀锌钢板及其生产方法
KR20240045835A (ko) * 2022-09-30 2024-04-08 현대제철 주식회사 초고강도 강판 및 그 제조방법
KR20240106695A (ko) * 2022-12-29 2024-07-08 현대제철 주식회사 고강도 냉연강판 및 그 제조방법
CN116043118B (zh) * 2023-01-19 2023-10-27 鞍钢股份有限公司 一种超高扩孔性能980MPa级热镀锌复相钢及制备方法

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59219473A (ja) 1983-05-26 1984-12-10 Nippon Steel Corp カラ−エツチング液及びエツチング方法
JPS61217529A (ja) 1985-03-22 1986-09-27 Nippon Steel Corp 延性のすぐれた高強度鋼板の製造方法
JP2526320B2 (ja) 1991-05-07 1996-08-21 新日本製鐵株式会社 高張力合金化溶融亜鉛めっき鋼板の製造方法
JP2526322B2 (ja) 1991-05-23 1996-08-21 新日本製鐵株式会社 高張力溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
JP2601581B2 (ja) 1991-09-03 1997-04-16 新日本製鐵株式会社 加工性に優れた高強度複合組織冷延鋼板の製造方法
US20030015263A1 (en) * 2000-05-26 2003-01-23 Chikara Kami Cold rolled steel sheet and galvanized steel sheet having strain aging hardening property and method for producing the same
JP3631710B2 (ja) * 2001-10-01 2005-03-23 新日本製鐵株式会社 耐食性と延性に優れたＳｉ含有高強度溶融亜鉛めっき鋼板及びその製造方法
ES2347435T3 (es) * 2003-03-31 2010-10-29 Nippon Steel Corporation Chapa de acero recubierta en caliente con cinc aleado y metodo para su produccion.
JP4192051B2 (ja) * 2003-08-19 2008-12-03 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
TWI302572B (en) * 2003-09-30 2008-11-01 Nippon Steel Corp High yield ratio, high strength steel sheet, high yield ratio, high strength hot dip galvanized steel sheet and high yield ratio, high strength alloyed hot dip galvanized steel sheet and process for producing same
JP4486336B2 (ja) 2003-09-30 2010-06-23 新日本製鐵株式会社 溶接性と延性に優れた高降伏比高強度冷延鋼板および高降伏比高強度溶融亜鉛めっき鋼板、並びに、高降伏比高強度合金化溶融亜鉛めっき鋼板とその製造方法
JP4445365B2 (ja) * 2004-10-06 2010-04-07 新日本製鐵株式会社 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法
JP4528184B2 (ja) 2005-03-31 2010-08-18 新日本製鐵株式会社 加工性の良好な合金化溶融亜鉛メッキ高強度鋼板の製造方法
JP2007270176A (ja) 2006-03-30 2007-10-18 Nippon Steel Corp 表面外観及びめっき密着性に優れた合金化溶融亜鉛めっき鋼板
JP5194811B2 (ja) * 2007-03-30 2013-05-08 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板
JP5251208B2 (ja) 2008-03-28 2013-07-31 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
JP2010065272A (ja) 2008-09-10 2010-03-25 Jfe Steel Corp 高強度鋼板およびその製造方法
CN101348885B (zh) * 2008-09-11 2010-06-02 北京科技大学 一种1000MPa级冷轧热镀锌双相钢及其制造方法
JP5709151B2 (ja) 2009-03-10 2015-04-30 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5374193B2 (ja) 2009-03-11 2013-12-25 株式会社神戸製鋼所 曲げ加工性および疲労強度に優れた溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板
JP5499663B2 (ja) * 2009-11-30 2014-05-21 新日鐵住金株式会社 機械切断特性に優れた引張最大強度９００ＭＰａ以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法
MX360965B (es) * 2009-11-30 2018-11-23 Nippon Steel & Sumitomo Metal Corp Placa de acero de alta resistencia con resistencia a la tracción final de 900 mpa o mas, excelente en resistencia a la fragilizacion por hidrógeno y método de producción de la misma.
JP5651964B2 (ja) * 2010-02-16 2015-01-14 新日鐵住金株式会社 延性及び穴広げ性並びに耐食性に優れた合金化溶融亜鉛めっき鋼板及びその製造方法
MX2014003712A (es) * 2011-09-30 2014-07-09 Nippon Steel & Sumitomo Metal Corp Lamina de acero galvanizada por inmersion en caliente, de alta resistencia, y lamina de acero galvanizada por inmersion en caliente, aleada, de alta resistencia, que tiene excelente adhesion de enchapado, formabilidad, y capacidad de expansion de agujero con resistencia a la traccion de 980 mpa o mas y metodo de fabricacion de las mismas.

Also Published As

Publication number Publication date
MX2014003712A (es) 2014-07-09
RU2586386C2 (ru) 2016-06-10
WO2013047830A1 (ja) 2013-04-04
CA2850101A1 (en) 2013-04-04
EP2762592A4 (en) 2015-07-08
JPWO2013047830A1 (ja) 2015-03-30
RU2014116634A (ru) 2015-11-10
KR101607786B1 (ko) 2016-03-30
EP2762592B1 (en) 2018-04-25
PL2762592T3 (pl) 2018-08-31
US10465272B2 (en) 2019-11-05
US20170369979A1 (en) 2017-12-28
ZA201402970B (en) 2015-04-29
BR112014007496B1 (pt) 2019-02-12
US20140342183A1 (en) 2014-11-20
TW201323655A (zh) 2013-06-16
CA2850101C (en) 2017-01-17
KR20140068222A (ko) 2014-06-05
EP2762592A1 (en) 2014-08-06
TWI523975B (zh) 2016-03-01
CN103827336B (zh) 2016-01-06
ES2670893T3 (es) 2018-06-01
JP5403185B2 (ja) 2014-01-29
CN103827336A (zh) 2014-05-28
BR112014007496A2 (pt) 2017-04-04
US9783878B2 (en) 2017-10-10

Similar Documents

Publication Publication Date Title
IN2014DN03212A (hu)
IN2014DN03211A (hu)
MX2016007954A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
IN2014DN11262A (hu)
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2010008558A (es) Lamina de acero recubierta con zinc por inmersion en caliente, de alta tenacidad, excelente en trabajabilidad y procedimiento para la produccion de la misma.
MX2015017874A (es) Lamina de acero enrollada en frio, metodo de fabricacion y vehiculo.
GB201210376D0 (en) High Strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
MX339219B (es) Lamina de acero de alta resistencia y lamina de acero revestida con zinc de alta resistencia que tiene excelente ductilidad y capacidad de embridado por estiramiento y metodo de fabricacion de las mismas.
MX2010008404A (es) Chapa de acero de alta resistencia y metodo para elaboracion de la misma.
MX2020010051A (es) Articulo moldeado por estampado en caliente, lamina de acero enrollada en frio, y metodo para manufacturar el articulo moldeado por estampado en caliente.
MX2013001456A (es) Lamina de acero laminada en frio, de alta resistencia, que tiene excelente trabajabilidad y resistencia al impacto, y metodo para manufacturar la misma.
MX2010010116A (es) Chapa de acero galvanizado de alta resistencia, chapa galvanizada en baño caliente, aleada, de alta resistencia y chapa de acero laminada en frio de alta resistencia las cuales tienen propiedades superiores en moldeabilidad y soldabilidad, y metodo d
MX360965B (es) Placa de acero de alta resistencia con resistencia a la tracción final de 900 mpa o mas, excelente en resistencia a la fragilizacion por hidrógeno y método de producción de la misma.
EP2267176A4 (en) HIGH-RESISTANCE HOT-GALVANIZED STEEL PLATE WITH EXCELLENT PROCESSABILITY AND MANUFACTURING METHOD THEREFOR
IN2014KN01673A (hu)
UA118036C2 (uk) Високоміцна сталь та спосіб виготовлення
IN2014KN01170A (hu)
MX350016B (es) Lámina de acero con altas propiedades de resistencia mecánica, ductilidad y de formación, método de producción de la misma y uso de dichas láminas.
MX2010008227A (es) Lamina de acero de alta resistencia y metodo para su fabricacion.
MX335950B (es) Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma.
MX2016011356A (es) Chapa de acero galvanofusionado por inmersion en caliente de alta resistencia que tiene una excelente propiedad de endurecimiento por horneado y capacidad de flexion.
MX2014003713A (es) Placa de acero galvanizado, y metodo para fabricarla.
MX2009001762A (es) Lamina de acero de alta tenacidad con ductilidad superior y metodo para su fabricacion.
MX2016014963A (es) Tira de acero que tiene alta resistencia y alta plasticidad, la tira de acero tiene un recubrimiento a base de zinc en caliente.