MX335950B - Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma. - Google Patents

Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma.

Info

Publication number
MX335950B
MX335950B MX2011009340A MX2011009340A MX335950B MX 335950 B MX335950 B MX 335950B MX 2011009340 A MX2011009340 A MX 2011009340A MX 2011009340 A MX2011009340 A MX 2011009340A MX 335950 B MX335950 B MX 335950B
Authority
MX
Mexico
Prior art keywords
steel sheet
galvanized steel
excellent formability
manufacturing
martensitic phase
Prior art date
Application number
MX2011009340A
Other languages
English (en)
Other versions
MX2011009340A (es
Inventor
Saiji Matsuoka
Tatsuya Nakagaito
Yoshiyasu Kawasaki
Shinjiro Kaneko
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2011009340A publication Critical patent/MX2011009340A/es
Publication of MX335950B publication Critical patent/MX335950B/es

Abstract

La presente invención se refiere a una lámina de acero galvanizado de alta resistencia que tiene excelente formabilidad que tiene una TS de 780 MPa o más y es excelente en términos de ductilidad, rebordeo por estirado, y doblado; y se proporciona un método para manufacturar la lámina de acero galvanizado de alta resistencia. La lámina de acero galvanizado de alta resistencia que tiene excelente formabilidad tiene una composición de componente que contiene, con base en el porcentaje de masa, 0.05 a 0.2% de C, 0.5 a 2.5% de Si, 1.5 a 3.0% de Mn, 0.001 a 0.05% de P, 0.0001 a 0.01% de S, 0.001 a 0.1% de Al, y 0.0005 a 0.01% de N, el balance es Fe e impurezas incidentales; y la lámina de acero tiene una microestructura que incluye una fase ferrítica y una fase martensítica que incluye una fase martensítica templada, la fase ferrítica tiene una fracción de área de 30% o más con relación a una totalidad de la microestructura, la fase martensítica tiene una fracción de área de 30 a 50% con relación a la totalidad de la microestructura, y la fase martensítica templada tiene una fracción de área de 70% o más con relación una totalidad de la fase martensítica.
MX2011009340A 2009-03-10 2010-02-19 Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma. MX335950B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2009055857A JP5709151B2 (ja) 2009-03-10 2009-03-10 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
PCT/JP2010/053027 WO2010103936A1 (ja) 2009-03-10 2010-02-19 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法

Publications (2)

Publication Number Publication Date
MX2011009340A MX2011009340A (es) 2011-09-27
MX335950B true MX335950B (es) 2016-01-04

Family

ID=42728226

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2011009340A MX335950B (es) 2009-03-10 2010-02-19 Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma.

Country Status (9)

Country Link
US (1) US9157132B2 (es)
EP (1) EP2407568B1 (es)
JP (1) JP5709151B2 (es)
KR (2) KR101380069B1 (es)
CN (1) CN102348821B (es)
CA (1) CA2751414C (es)
MX (1) MX335950B (es)
TW (1) TWI440724B (es)
WO (1) WO2010103936A1 (es)

Families Citing this family (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101410435B1 (ko) * 2010-03-31 2014-06-20 신닛테츠스미킨 카부시키카이샤 성형성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
CN103314120B (zh) * 2010-10-22 2014-11-05 新日铁住金株式会社 热锻压成形体的制造方法及热锻压成形体
US9896736B2 (en) 2010-10-22 2018-02-20 Nippon Steel & Sumitomo Metal Corporation Method for manufacturing hot stamped body having vertical wall and hot stamped body having vertical wall
US9512499B2 (en) 2010-10-22 2016-12-06 Nippon Steel & Sumitomo Metal Corporation Method for manufacturing hot stamped body having vertical wall and hot stamped body having vertical wall
JP5752409B2 (ja) * 2010-12-27 2015-07-22 新日鐵住金株式会社 硬度バラつきの小さいホットスタンプ成形体の製造方法およびその成形体
JP5182386B2 (ja) * 2011-01-31 2013-04-17 Ｊｆｅスチール株式会社 加工性に優れた高降伏比を有する高強度冷延鋼板およびその製造方法
US10100381B2 (en) * 2011-06-07 2018-10-16 Jfe Steel Corporation Steel sheet for hot pressing and process for manufacturing hot pressed member using the steel sheet
CA2850101C (en) * 2011-09-30 2017-01-17 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet and high-strength alloyed hot-dip galvanized steel sheet having excellent plating adhesion, formability, and hole expandability with tensile strength of 980 mpa or more and manufecaturing method therefor
CN103827335B (zh) * 2011-09-30 2015-10-21 新日铁住金株式会社 镀锌钢板及其制造方法
JP5348268B2 (ja) 2012-03-07 2013-11-20 Ｊｆｅスチール株式会社 成形性に優れる高強度冷延鋼板およびその製造方法
JP5870874B2 (ja) * 2012-08-14 2016-03-01 Ｊｆｅスチール株式会社 引張強度が９８０ＭＰａ以上である合金化溶融亜鉛めっき鋼板の製造方法
JP5867435B2 (ja) 2013-03-28 2016-02-24 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
CN105102657B (zh) * 2013-03-29 2017-03-15 杰富意钢铁株式会社 钢材及氢用容器、以及它们的制造方法
EP2980249B1 (en) 2013-03-29 2020-04-29 JFE Steel Corporation Steel plate for thick-walled steel pipe, method for manufacturing the same, and thick-walled high-strength steel pipe
KR101753511B1 (ko) 2013-08-02 2017-07-19 제이에프이 스틸 가부시키가이샤 고강도 고영률 강판 및 그 제조 방법
CN105452509B (zh) 2013-08-02 2017-06-30 杰富意钢铁株式会社 高强度高杨氏模量钢板及其制造方法
CN105899699B (zh) * 2014-01-06 2017-07-28 新日铁住金株式会社 钢材及其制造方法
IN201617022707A (es) 2014-01-06 2016-08-31 Nippon Steel & Sumitomo Metal Corp
JP5967318B1 (ja) 2014-08-28 2016-08-10 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP6052472B2 (ja) * 2015-01-15 2016-12-27 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
MX395053B (es) * 2015-02-13 2025-03-24 Jfe Steel Corp Lámina de acero galvanizada de alta resistencia y método para la fabricación de la misma.
KR102145293B1 (ko) * 2016-05-25 2020-08-18 제이에프이 스틸 가부시키가이샤 도금 강판 및 그의 제조 방법
MX2019001793A (es) 2016-08-30 2019-06-13 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para su fabricacion.
KR102210100B1 (ko) 2016-09-30 2021-01-29 제이에프이 스틸 가부시키가이샤 고강도 도금 강판 및 그의 제조 방법
DE102017130237A1 (de) * 2017-12-15 2019-06-19 Salzgitter Flachstahl Gmbh Hochfestes, warmgewalztes Stahlflachprodukt mit hohem Kantenrisswiderstand und gleichzeitig hohem Bake-Hardening Potential, ein Verfahren zur Herstellung eines solchen Stahlflachprodukts
KR102131538B1 (ko) * 2018-11-30 2020-07-08 주식회사 포스코 냉간가공성 및 ssc 저항성이 우수한 초고강도 강재 및 그 제조방법
CN113366127B (zh) * 2019-03-11 2023-01-17 日本制铁株式会社 热轧钢板
WO2021145442A1 (ja) * 2020-01-16 2021-07-22 日本製鉄株式会社 ホットスタンプ成形体
WO2021145445A1 (ja) 2020-01-16 2021-07-22 日本製鉄株式会社 ホットスタンプ成形体
WO2022004820A1 (ja) * 2020-06-30 2022-01-06 Ｊｆｅスチール株式会社 亜鉛めっき鋼板、部材及びそれらの製造方法
CN113215485B (zh) * 2021-04-15 2022-05-17 首钢集团有限公司 一种780MPa级热基镀层双相钢及其制备方法
CN113403529B (zh) * 2021-05-21 2022-07-19 鞍钢股份有限公司 冷冲压用1470MPa级合金化镀锌钢板及其制备方法
KR20230014121A (ko) * 2021-07-20 2023-01-30 주식회사 포스코 구멍확장성 및 연성이 우수한 고강도 강판 및 이의 제조방법
CN116790986A (zh) * 2023-06-27 2023-09-22 攀钢集团攀枝花钢铁研究院有限公司 一种低成本高扩孔性能780MPa级热镀锌双相钢及其制备方法
CN119162508B (zh) * 2024-09-29 2025-10-31 本钢板材股份有限公司 一种热轧酸洗低合金高强钢及生产方法

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3459500B2 (ja) 1995-06-28 2003-10-20 新日本製鐵株式会社 成型性及びめっき密着性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
JP3527092B2 (ja) 1998-03-27 2004-05-17 新日本製鐵株式会社 加工性の良い高強度合金化溶融亜鉛めっき鋼板とその製造方法
DE19936151A1 (de) * 1999-07-31 2001-02-08 Thyssenkrupp Stahl Ag Höherfestes Stahlband oder -blech und Verfahren zu seiner Herstellung
JP3846206B2 (ja) 2000-02-29 2006-11-15 Ｊｆｅスチール株式会社 歪時効硬化特性に優れた高張力冷延鋼板およびその製造方法
CN1107122C (zh) * 2000-02-29 2003-04-30 济南济钢设计院 奥贝马钢及其制备方法
JP4358418B2 (ja) 2000-09-04 2009-11-04 新日本製鐵株式会社 穴拡げ性に優れた低降伏比高強度冷延鋼板およびめっき鋼板とその製造方法
CA2395901C (en) * 2000-10-31 2006-07-18 Nkk Corporation High strength hot rolled steel sheet and method for manufacturing the same
US7090731B2 (en) * 2001-01-31 2006-08-15 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High strength steel sheet having excellent formability and method for production thereof
JP4188608B2 (ja) * 2001-02-28 2008-11-26 株式会社神戸製鋼所 加工性に優れた高強度鋼板およびその製造方法
JP3898923B2 (ja) 2001-06-06 2007-03-28 新日本製鐵株式会社 高加工時のめっき密着性および延性に優れた高強度溶融Ｚｎめっき鋼板及びその製造方法
EP2017363A3 (en) * 2002-06-14 2009-08-05 JFE Steel Corporation High strength cold-rolled steel sheet and method for manufacturing the same
JP4119758B2 (ja) * 2003-01-16 2008-07-16 株式会社神戸製鋼所 加工性および形状凍結性に優れた高強度鋼板、並びにその製法
JP4649868B2 (ja) * 2003-04-21 2011-03-16 Ｊｆｅスチール株式会社 高強度熱延鋼板およびその製造方法
JP4510488B2 (ja) * 2004-03-11 2010-07-21 新日本製鐵株式会社 成形性および穴拡げ性に優れた溶融亜鉛めっき複合高強度鋼板およびその製造方法
JP4716358B2 (ja) * 2005-03-30 2011-07-06 株式会社神戸製鋼所 強度と加工性のバランスに優れた高強度冷延鋼板およびめっき鋼板
JP4655782B2 (ja) * 2005-06-30 2011-03-23 Ｊｆｅスチール株式会社 高延性で、化成処理性に優れる７８０ＭＰａ以上の引張強度を有する超高強度冷延鋼板の製造方法
JP4503001B2 (ja) * 2006-11-21 2010-07-14 株式会社神戸製鋼所 耐パウダリング性と加工性に優れた高強度合金化溶融亜鉛めっき鋼板
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5194841B2 (ja) * 2008-01-31 2013-05-08 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
JP2010209392A (ja) 2010-09-24
US20110315279A1 (en) 2011-12-29
CA2751414A1 (en) 2010-09-16
CA2751414C (en) 2016-04-12
EP2407568A1 (en) 2012-01-18
TW201038749A (en) 2010-11-01
KR20130091361A (ko) 2013-08-16
MX2011009340A (es) 2011-09-27
US9157132B2 (en) 2015-10-13
KR20110110367A (ko) 2011-10-06
WO2010103936A1 (ja) 2010-09-16
KR101331755B1 (ko) 2013-11-20
JP5709151B2 (ja) 2015-04-30
EP2407568B1 (en) 2019-04-03
KR101380069B1 (ko) 2014-04-01
CN102348821A (zh) 2012-02-08
EP2407568A4 (en) 2017-05-17
TWI440724B (zh) 2014-06-11
CN102348821B (zh) 2017-04-26

Similar Documents

Publication Publication Date Title
MX335950B (es) Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma.
MX385554B (es) Lamina de acero laminada en frio, de alta resistencia, que tiene excelente trabajabilidad y resistencia al impacto, y metodo para manufacturar la misma.
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2016007954A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2015007724A (es) Lamina de acero laminada en frio de alta resistencia con bajo limite de elasticidad y metodo para la fabricacion de la misma.
MX2010008558A (es) Lamina de acero recubierta con zinc por inmersion en caliente, de alta tenacidad, excelente en trabajabilidad y procedimiento para la produccion de la misma.
TW200940717A (en) High strength steel sheet having superior ductility and method for manufacturing the same
WO2008145871A3 (fr) Procede de fabrication de tôles d'acier laminees a froid et recuites a tres haute resistance, et tôles ainsi produites
UA100056C2 (ru) Способ производства холоднокатаного и отожженного листа из двухфазной стали, полученный таким способом лист, способ производства холоднокатаного, отожженного и оцинкованного листа из двухфазной стали (варианты) и использование указанного стального листа
MX2015017874A (es) Lamina de acero enrollada en frio, metodo de fabricacion y vehiculo.
MX374819B (es) Hoja de acero laminada en caliente de alta resistencia, que tiene endurecimiento de recocido y dureza a baja temperatura excelentes, con resistencia a la tension maxima de 980 mpa o mas.
MX2016001723A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX375029B (es) Hoja de acero laminada en caliente y metodo de fabricacion de la misma.
MX335961B (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX374822B (es) Plancha de acero laminada en frio de alta resistencia y proceso para fabricar la misma.
EP2267176A4 (en) HIGH-RESISTANCE HOT-GALVANIZED STEEL PLATE WITH EXCELLENT PROCESSABILITY AND MANUFACTURING METHOD THEREFOR
ATE496150T1 (de) Hochfeste stahlplatte, die eine herausragende formbarkeit aufweist
IN2014DN03212A (es)
MX2015013579A (es) Lamina de acero recocida despues de galvanizada de alta resistencia y metodo para la fabricacion de la misma.
IN2014KN01170A (es)
MX2015013516A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2012008274A (es) Hoja de acero galvanizado de alta resistencia sumergido en caliente que tiene capacidad de formacion y capacidad de soldarse por puntos excelentes y metodo para su fabricacion.
MY176614A (en) Steel sheet for cans and method for manufacturing steel sheet for cans
MY153967A (en) High-strength hot rolled steel sheet having good formability and method for manufacturing the same

Legal Events

Date Code Title Description
HH Correction or change in general