ES2056136T3 - Pelicula de baja emisividad para tratamiento a elevadas temperaturas. - Google Patents

Pelicula de baja emisividad para tratamiento a elevadas temperaturas.

Info

Publication number
ES2056136T3
ES2056136T3 ES89105417T ES89105417T ES2056136T3 ES 2056136 T3 ES2056136 T3 ES 2056136T3 ES 89105417 T ES89105417 T ES 89105417T ES 89105417 T ES89105417 T ES 89105417T ES 2056136 T3 ES2056136 T3 ES 2056136T3
Authority
ES
Spain
Prior art keywords
metal
deposit
spraying
transparent
primer layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES89105417T
Other languages
English (en)
Inventor
James Joseph Finley
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PPG Industries Inc
Original Assignee
PPG Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PPG Industries Inc filed Critical PPG Industries Inc
Application granted granted Critical
Publication of ES2056136T3 publication Critical patent/ES2056136T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Un método para fabricar un producto revestido con capas múltiples de baja emisividad que comprende las etapas de: a. colocar un sustrato no metálico transparente en una cámara de pulverización catódica; b. pulverizar un cátodo metálico en una atmósfera reactiva que comprende oxígeno para depositar una primera película de óxido metálico transparente y antirreflectante sobre una superficie de dicho sustrato; c. depositar una primera capa de imprimación sobre dicha película de óxido metálico transparente que comprende un metal seleccionado entre titanio y circonio; d. pulverizar una superficie de emisión de cátodo metálico en una atmósfera inerte para depositar una película metálica reflectante de rayos infrarrojos sobre dicha primera capa de imprimación; e. depositar una segunda capa de imprimación que contiene metal sobre dicha película metálica reflectante de rayos infrarrojos que comprende un metal seleccionado entre titanio y circonio; f. pulverizar un cátodo metálico en una atmósfera reactiva que comprende oxígeno para depositar una segunda película de óxido metálico transparente y antirreflectante, caracterizado porque la etapa de deposición de la primera capa de imprimación comprende, en primer lugar, pulverizar dicho metal en una atmósfera oxidante para depositar el óxido de dicho metal y luego pulverizar el mismo metal en una atmósfera inerte para depositar dicho metal.
ES89105417T 1988-04-01 1989-03-28 Pelicula de baja emisividad para tratamiento a elevadas temperaturas. Expired - Lifetime ES2056136T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US07/176,511 US4898790A (en) 1986-12-29 1988-04-01 Low emissivity film for high temperature processing

Publications (1)

Publication Number Publication Date
ES2056136T3 true ES2056136T3 (es) 1994-10-01

Family

ID=22644647

Family Applications (1)

Application Number Title Priority Date Filing Date
ES89105417T Expired - Lifetime ES2056136T3 (es) 1988-04-01 1989-03-28 Pelicula de baja emisividad para tratamiento a elevadas temperaturas.

Country Status (8)

Country Link
US (1) US4898790A (es)
EP (1) EP0335309B1 (es)
JP (1) JP2505278B2 (es)
KR (1) KR920005471B1 (es)
BR (1) BR8901510A (es)
CA (1) CA1337483C (es)
DE (1) DE68915042T2 (es)
ES (1) ES2056136T3 (es)

Families Citing this family (156)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5112693A (en) * 1988-10-03 1992-05-12 Ppg Industries, Inc. Low reflectance, highly saturated colored coating for monolithic glazing
US5153062A (en) * 1989-02-13 1992-10-06 Hoechst Aktiengesellschaft Process and device for producing laminated safety glass and laminated safety glass produced thereby
US5215832A (en) * 1990-04-25 1993-06-01 Cardinal Ic Company Lead-free mirrors and environmentally safe manufacture thereof
US5296302A (en) * 1992-03-27 1994-03-22 Cardinal Ig Company Abrasion-resistant overcoat for coated substrates
US5972527A (en) * 1992-12-15 1999-10-26 Idemitsu Kosan Co., Ltd. Transparent electrically conductive layer, electrically conductive transparent substrate and electrically conductive material
EP0657562B1 (en) 1993-11-12 2001-09-12 PPG Industries Ohio, Inc. Durable sputtered metal oxide coating
DE4409934A1 (de) * 1994-03-23 1995-09-28 Ver Glaswerke Gmbh Verfahren und Vorrichtung zum Beschichten einer Glasscheibe mit wenigstens einer Schicht aus Zinndioxid durch reaktive Katodenzerstäubung
CA2161283A1 (en) * 1994-12-27 1996-06-28 Ppg Industries Ohio, Inc. Annealed low emissivity coating
US6086210A (en) * 1995-06-29 2000-07-11 Cardinal Ig Company Bendable mirrors and method of manufacture
US6142642A (en) * 1995-06-29 2000-11-07 Cardinal Ig Company Bendable mirrors and method of manufacture
US5821001A (en) * 1996-04-25 1998-10-13 Ppg Industries, Inc. Coated articles
US7096692B2 (en) * 1997-03-14 2006-08-29 Ppg Industries Ohio, Inc. Visible-light-responsive photoactive coating, coated article, and method of making same
US20020155299A1 (en) 1997-03-14 2002-10-24 Harris Caroline S. Photo-induced hydrophilic article and method of making same
US20030039843A1 (en) * 1997-03-14 2003-02-27 Christopher Johnson Photoactive coating, coated article, and method of making same
US20050096288A1 (en) * 1997-06-13 2005-05-05 Aragene, Inc. Lipoproteins as nucleic acid vectors
CA2319532C (en) 1997-10-31 2004-08-03 Cardinal Ig Company Heat-bendable mirrors
US6833194B1 (en) 1998-05-12 2004-12-21 Ppg Industries Ohio, Inc. Protective layers for sputter coated article
US6899953B1 (en) * 1998-05-08 2005-05-31 Ppg Industries Ohio, Inc. Shippable heat-treatable sputter coated article and zinc cathode sputtering target containing low amounts of tin
US6610410B2 (en) 1998-12-18 2003-08-26 Asahi Glass Company, Limited Glazing panel
HU224414B1 (hu) 1998-12-18 2005-08-29 č< îáęâá< Bevonatos üvegtábla, és eljárás annak előállítására
US6582799B1 (en) 1999-06-02 2003-06-24 Ppg Industries Ohio, Inc. Laminated transparency
US6849328B1 (en) 1999-07-02 2005-02-01 Ppg Industries Ohio, Inc. Light-transmitting and/or coated article with removable protective coating and methods of making the same
US20020136905A1 (en) * 1999-11-24 2002-09-26 Medwick Paul A. Low shading coefficient and low emissivity coatings and coated articles
WO2001038248A1 (en) 1999-11-24 2001-05-31 Ppg Industries Ohio, Inc. Low shading coefficient and low emissivity coatings and coated articles
US20070036989A1 (en) * 1999-11-24 2007-02-15 Ppg Industries Ohio, Inc. Low shading coefficient and low emissivity coatings and coated articles
US6495263B2 (en) 1999-12-06 2002-12-17 Guardian Industries Corp. Low-E matchable coated articles and methods of making same
US6514620B1 (en) 1999-12-06 2003-02-04 Guardian Industries Corp. Matchable low-E I G units and laminates and methods of making same
US6475626B1 (en) * 1999-12-06 2002-11-05 Guardian Industries Corp. Low-E matchable coated articles and methods of making same
US7361404B2 (en) 2000-05-10 2008-04-22 Ppg Industries Ohio, Inc. Coated article with removable protective coating and related methods
US6576349B2 (en) 2000-07-10 2003-06-10 Guardian Industries Corp. Heat treatable low-E coated articles and methods of making same
US6445503B1 (en) 2000-07-10 2002-09-03 Guardian Industries Corp. High durable, low-E, heat treatable layer coating system
US7267879B2 (en) 2001-02-28 2007-09-11 Guardian Industries Corp. Coated article with silicon oxynitride adjacent glass
US6887575B2 (en) * 2001-10-17 2005-05-03 Guardian Industries Corp. Heat treatable coated article with zinc oxide inclusive contact layer(s)
US7462397B2 (en) * 2000-07-10 2008-12-09 Guardian Industries Corp. Coated article with silicon nitride inclusive layer adjacent glass
US7323249B2 (en) * 2000-08-31 2008-01-29 Ppg Industries Ohio, Inc. Methods of obtaining photoactive coatings and/or anatase crystalline phase of titanium oxides and articles made thereby
US6677063B2 (en) 2000-08-31 2004-01-13 Ppg Industries Ohio, Inc. Methods of obtaining photoactive coatings and/or anatase crystalline phase of titanium oxides and articles made thereby
US6869644B2 (en) * 2000-10-24 2005-03-22 Ppg Industries Ohio, Inc. Method of making coated articles and coated articles made thereby
US20020172775A1 (en) * 2000-10-24 2002-11-21 Harry Buhay Method of making coated articles and coated articles made thereby
US7311961B2 (en) * 2000-10-24 2007-12-25 Ppg Industries Ohio, Inc. Method of making coated articles and coated articles made thereby
DE10063180A1 (de) * 2000-12-18 2002-06-27 Bayer Ag Vorrichtung zur Erzeugung von Lichtsignalen
US20020120916A1 (en) * 2001-01-16 2002-08-29 Snider Albert Monroe Head-up display system utilizing fluorescent material
US20030037569A1 (en) * 2001-03-20 2003-02-27 Mehran Arbab Method and apparatus for forming patterned and/or textured glass and glass articles formed thereby
US20030049464A1 (en) * 2001-09-04 2003-03-13 Afg Industries, Inc. Double silver low-emissivity and solar control coatings
US6942923B2 (en) 2001-12-21 2005-09-13 Guardian Industries Corp. Low-e coating with high visible transmission
US7232615B2 (en) * 2001-10-22 2007-06-19 Ppg Industries Ohio, Inc. Coating stack comprising a layer of barrier coating
US6730389B2 (en) 2001-10-25 2004-05-04 Ppg Industries Ohio, Inc. Coated substrate having a frequency selective surface
US6602608B2 (en) * 2001-11-09 2003-08-05 Guardian Industries, Corp. Coated article with improved barrier layer structure and method of making the same
US6830817B2 (en) * 2001-12-21 2004-12-14 Guardian Industries Corp. Low-e coating with high visible transmission
EP1476300B2 (en) * 2002-02-11 2016-07-13 PPG Industries Ohio, Inc. Solar control coating
US20030155065A1 (en) * 2002-02-13 2003-08-21 Thomsen Scott V. Method of making window unit
US6827977B2 (en) * 2002-03-07 2004-12-07 Guardian Industries Corp. Method of making window unit including diamond-like carbon (DLC) coating
US6983104B2 (en) * 2002-03-20 2006-01-03 Guardian Industries Corp. Apparatus and method for bending and/or tempering glass
US7231787B2 (en) * 2002-03-20 2007-06-19 Guardian Industries Corp. Apparatus and method for bending and/or tempering glass
AU2003239167B2 (en) * 2002-04-25 2007-01-18 Ppg Industries Ohio, Inc. Coated articles having a protective coating and cathode targets for making the coated articles
WO2003095383A2 (en) * 2002-04-25 2003-11-20 Ppg Industries Ohio, Inc. Method of making coated articles having an oxygen barrier coating and coated articles made thereby
EP1501768B2 (en) * 2002-05-03 2020-02-12 Vitro, S.A.B. de C.V. Substrate having thermal management coating for an insulating glass unit
US6632491B1 (en) 2002-05-21 2003-10-14 Guardian Industries Corp. IG window unit and method of making the same
US7588829B2 (en) * 2002-05-31 2009-09-15 Ppg Industries Ohio, Inc. Article having an aesthetic coating
US7125462B2 (en) 2002-06-18 2006-10-24 Centre Luxembourgeois De Recherches Pour Le Verre Et Al Ceramique S.A. (C.R.V.C.) Method of making vehicle windshield using coating mask
US7140204B2 (en) * 2002-06-28 2006-11-28 Guardian Industries Corp. Apparatus and method for bending glass using microwaves
US20040112411A1 (en) * 2002-09-10 2004-06-17 Boykin Cheri M. Method and apparatus for cleaning a photoactive and/or hydrophilic surface
CN100339321C (zh) * 2002-09-27 2007-09-26 Ppg工业俄亥俄公司 用于生产具有减少的缺陷密度的浮法玻璃的装置和方法
US7005190B2 (en) * 2002-12-20 2006-02-28 Guardian Industries Corp. Heat treatable coated article with reduced color shift at high viewing angles
US6811884B2 (en) * 2002-12-24 2004-11-02 Ppg Industries Ohio, Inc. Water repellant surface treatment and treated articles
US20040202890A1 (en) 2003-04-08 2004-10-14 Kutilek Luke A. Methods of making crystalline titania coatings
US6967060B2 (en) * 2003-05-09 2005-11-22 Guardian Industries Corp. Coated article with niobium zirconium inclusive layer(s) and method of making same
US7998602B2 (en) * 2003-05-30 2011-08-16 Ppg Industries Ohio, Inc. Appliance with coated transparency
CN101597143B (zh) * 2003-05-30 2011-11-23 Ppg工业俄亥俄公司 具有涂覆透明体的器具
US7087309B2 (en) * 2003-08-22 2006-08-08 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Coated article with tin oxide, silicon nitride and/or zinc oxide under IR reflecting layer and corresponding method
US7153579B2 (en) * 2003-08-22 2006-12-26 Centre Luxembourgeois de Recherches pour le Verre et la Ceramique S.A, (C.R.V.C.) Heat treatable coated article with tin oxide inclusive layer between titanium oxide and silicon nitride
US7060322B2 (en) * 2003-09-02 2006-06-13 Guardian Industries Corp. Method of making heat treatable coated article with diamond-like carbon (DLC) coating
US7507442B2 (en) * 2003-11-04 2009-03-24 Guardian Industries Corp. Heat treatable coated article with diamond-like carbon (DLC) and/or zirconium in coating
US20050208319A1 (en) * 2004-03-22 2005-09-22 Finley James J Methods for forming an electrodeposited coating over a coated substrate and articles made thereby
US20050238923A1 (en) * 2004-04-27 2005-10-27 Thiel James P Hybrid coating stack
US7223940B2 (en) * 2005-02-22 2007-05-29 Ppg Industries Ohio, Inc. Heatable windshield
MX2007014164A (es) * 2005-05-12 2008-02-25 Agc Flat Glass North America Recubrimiento de baja emisividad con bajo coeficiente de ganancia de calor solar, propiedades quimicas y mecanicas mejoradas y metodo para fabricar el mismo.
US7335421B2 (en) * 2005-07-20 2008-02-26 Ppg Industries Ohio, Inc. Heatable windshield
US7342716B2 (en) 2005-10-11 2008-03-11 Cardinal Cg Company Multiple cavity low-emissivity coatings
US7339728B2 (en) * 2005-10-11 2008-03-04 Cardinal Cg Company Low-emissivity coatings having high visible transmission and low solar heat gain coefficient
US7572511B2 (en) * 2005-10-11 2009-08-11 Cardinal Cg Company High infrared reflection coatings
US8025941B2 (en) * 2005-12-01 2011-09-27 Guardian Industries Corp. IG window unit and method of making the same
BRPI0706600A2 (pt) * 2006-01-17 2011-03-29 Ppg Ind Ohio Inc métodos para produção de partìculas, nanopartìculas e para revestir um lìquido iÈnico, composições, filme e aparelho para produção de partìculas
US20070264479A1 (en) * 2006-05-09 2007-11-15 Thiel James P Aesthetic transparency
US7767310B2 (en) * 2006-10-23 2010-08-03 Ppg Industries Ohio, Inc. Primer composition and articles incorporating the primer
CN101058486B (zh) * 2007-04-26 2011-08-17 天津南玻工程玻璃有限公司 可热处理的磁控溅射方法制备的低辐射镀膜玻璃
US8686319B2 (en) * 2007-05-09 2014-04-01 Ppg Industries Ohio, Inc. Vehicle transparency heated with alternating current
US20080280147A1 (en) * 2007-05-09 2008-11-13 Thiel James P Vehicle transparency
US8728634B2 (en) * 2007-06-13 2014-05-20 Ppg Industries Ohio, Inc. Appliance transparency
US8658289B2 (en) * 2007-11-16 2014-02-25 Ppg Industries Ohio, Inc. Electromagnetic radiation shielding device
US7901781B2 (en) * 2007-11-23 2011-03-08 Agc Flat Glass North America, Inc. Low emissivity coating with low solar heat gain coefficient, enhanced chemical and mechanical properties and method of making the same
FR2927897B1 (fr) * 2008-02-27 2011-04-01 Saint Gobain Vitrage antisolaire presentant un coefficient de transmission lumineuse ameliore.
FR2928461B1 (fr) * 2008-03-10 2011-04-01 Saint Gobain Substrat transparent comportant un revetement antireflet
US8445098B2 (en) * 2008-03-11 2013-05-21 Ppg Industries Ohio, Inc. Reflective article having multiple reflective coatings
US8085460B2 (en) * 2008-08-28 2011-12-27 Ppg Industries Ohio, Inc Electrochromic device
US8049949B2 (en) * 2008-08-29 2011-11-01 Ppg Industries Ohio, Inc. Multi-layer electrode for high contrast electrochromic devices
US7907322B2 (en) * 2008-10-23 2011-03-15 Ppg Industries Ohio, Inc. Electrochromic device
DK2429965T3 (da) 2009-05-08 2020-09-28 Vitro Flat Glass Llc Solstyringsbelægning med høj solvarmeindvindingskoefficient
WO2010144709A2 (en) 2009-06-12 2010-12-16 Ppg Industries Ohio, Inc. Aircraft transparency with solar control properties
EP2457413B1 (en) 2009-07-21 2018-03-28 PPG Industries Ohio, Inc. Enhanced bus bar system for aircraft transparencies
US10654747B2 (en) 2010-03-29 2020-05-19 Vitro Flat Glass Llc Solar control coatings with subcritical copper
US10654748B2 (en) 2010-03-29 2020-05-19 Vitro Flat Glass Llc Solar control coatings providing increased absorption or tint
US9932267B2 (en) 2010-03-29 2018-04-03 Vitro, S.A.B. De C.V. Solar control coatings with discontinuous metal layer
US9397240B2 (en) 2010-12-09 2016-07-19 Ppg Industries Ohio, Inc. Corrosion resistant solar mirror
US9758426B2 (en) 2011-06-29 2017-09-12 Vitro, S.A.B. De C.V. Reflective article having a sacrificial cathodic layer
CN103717403B (zh) 2011-08-10 2016-08-31 太阳诱电化学科技株式会社 包含薄底漆膜的结构体和包含薄底漆膜的镂空版印刷版
US9919959B2 (en) 2012-05-31 2018-03-20 Guardian Glass, LLC Window with UV-treated low-E coating and method of making same
US9469565B2 (en) 2012-05-31 2016-10-18 Guardian Industries Corp. Window with selectively writable image(s) and method of making same
US20140113120A1 (en) 2012-10-19 2014-04-24 Ppg Industries Ohio, Inc. Anti-color banding topcoat for coated articles
US10871600B2 (en) 2012-12-17 2020-12-22 Guardian Glass, LLC Window for reducing bird collisions
JP2014167162A (ja) 2013-01-31 2014-09-11 Nitto Denko Corp 赤外線反射フィルムの製造方法
JP2014167163A (ja) 2013-01-31 2014-09-11 Nitto Denko Corp 赤外線反射フィルムの製造方法
US9873633B2 (en) * 2013-11-20 2018-01-23 Guardian Europe S.A.R.L. Heat treatable coated article with low-E coating having zinc stannate based layer between IR reflecting layers and corresponding method
JP6303559B2 (ja) * 2014-02-07 2018-04-04 東レ株式会社 積層フィルムおよびその製造方法
US9650290B2 (en) 2014-05-27 2017-05-16 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique (C.R.V.C.) Sarl IG window unit for preventing bird collisions
JP6423198B2 (ja) 2014-08-05 2018-11-14 日東電工株式会社 赤外線反射フィルム
WO2016171779A1 (en) * 2015-04-20 2016-10-27 3M Innovative Properties Company Durable low emissivity window film constructions
EA034006B1 (ru) * 2015-10-29 2019-12-18 Общество С Ограниченной Ответственностью "Изовак Технологии" Комбинированное оптическое покрытие и способ его изготовления (варианты)
CN113089323B (zh) 2017-02-14 2024-03-22 耐克创新有限合伙公司 防味组合物、具有防味特性的结构、及其制备方法
WO2018181433A1 (ja) * 2017-03-30 2018-10-04 日東電工株式会社 遮熱断熱基板
US12032124B2 (en) 2017-08-04 2024-07-09 Vitro Flat Glass Llc Flash annealing of transparent conductive oxide and semiconductor coatings
US11220455B2 (en) 2017-08-04 2022-01-11 Vitro Flat Glass Llc Flash annealing of silver coatings
US10843961B2 (en) 2017-09-18 2020-11-24 Guardian Glass, LLC IG window unit including laminated substrates for preventing bird collisions
US11609359B2 (en) 2017-09-29 2023-03-21 Nike, Inc. Structurally-colored articles and methods for making and using structurally-colored articles
US11078718B2 (en) 2018-02-05 2021-08-03 Vitro Flat Glass Llc Solar control coatings with quadruple metallic layers
JP2021513950A (ja) 2018-02-15 2021-06-03 ビトロ フラット グラス エルエルシー 窒化ケイ素及び／又は酸窒化ケイ素を含む保護コーティングを有するコーティングされた物品
US10562812B2 (en) 2018-06-12 2020-02-18 Guardian Glass, LLC Coated article having metamaterial-inclusive layer, coating having metamaterial-inclusive layer, and/or method of making the same
US10830933B2 (en) 2018-06-12 2020-11-10 Guardian Glass, LLC Matrix-embedded metamaterial coating, coated article having matrix-embedded metamaterial coating, and/or method of making the same
US11329389B2 (en) * 2018-07-26 2022-05-10 Board Of Regents, The University Of Texas System Method for fabricating a hyperbolic metamaterial having a near-zero refractive index in the optical regime
WO2020035818A1 (en) 2018-08-15 2020-02-20 Guardian Glass, LLC Window unit with patterned coating for reducing bird collisions and method of making same
US12298474B2 (en) 2019-03-28 2025-05-13 Vitro Flat Glass Llc Article having a high visible light reflectance and a neutral color
CN114008493A (zh) 2019-06-26 2022-02-01 耐克创新有限合伙公司 结构着色的物品以及用于制造和使用结构着色的物品的方法
CN114173596A (zh) * 2019-07-26 2022-03-11 耐克创新有限合伙公司 结构着色的物品以及用于制造和使用结构着色的物品的方法
EP3963376A1 (en) 2019-07-26 2022-03-09 Nike Innovate C.V. Structurally-colored articles and methods for making and using structurally-colored articles
WO2021080913A1 (en) 2019-10-21 2021-04-29 Nike, Inc. Structurally-colored articles
EP4103982A1 (en) 2020-02-14 2022-12-21 Vitro Flat Glass LLC Low sheet resistance coating
US11859439B2 (en) 2020-04-15 2024-01-02 Vitro Flat Glass Llc Low thermal conducting spacer assembly for an insulating glazing unit
WO2021243217A1 (en) 2020-05-29 2021-12-02 Nike, Inc. Structurally-colored articles and methods for making and using structurally-colored articles
US11092726B1 (en) 2020-06-19 2021-08-17 Guardian Glass, LLC Window unit having UV reflecting coating with high contrast ratio at large viewing angles for reducing bird collisions
US11129444B1 (en) 2020-08-07 2021-09-28 Nike, Inc. Footwear article having repurposed material with concealing layer
US11241062B1 (en) 2020-08-07 2022-02-08 Nike, Inc. Footwear article having repurposed material with structural-color concealing layer
US11889894B2 (en) 2020-08-07 2024-02-06 Nike, Inc. Footwear article having concealing layer
US12350905B2 (en) 2021-10-11 2025-07-08 Vitro Flat Glass Llc Heat-treatable coating having reduced haze
WO2023064111A1 (en) 2021-10-11 2023-04-20 Vitro Flat Glass Llc Heat-treatable coating having reduced haze
EP4499584A1 (en) 2022-03-31 2025-02-05 Vitro Flat Glass LLC Article coated by a multi-layer coating stack
CN119325568A (zh) 2022-06-07 2025-01-17 维特罗平板玻璃有限责任公司 非对称图案化的反射涂层
WO2024059091A1 (en) 2022-09-14 2024-03-21 Vitro Flat Glass Llc Magnetron sputtering vapor deposition coating composition comprising light absorptive materials
JP2025534232A (ja) 2022-09-14 2025-10-15 ビトロ フラット グラス エルエルシー 反射コーティング
CN120693547A (zh) 2023-02-14 2025-09-23 维特罗平板玻璃有限责任公司 半透明镜子
KR20250157526A (ko) 2023-03-08 2025-11-04 비트로 플랫 글래스 엘엘씨 자동차 적용례용 반사방지 코팅
CN120936582A (zh) 2023-03-13 2025-11-11 维特罗平板玻璃有限责任公司 用于减少鸟类碰撞的窗单元及其制造方法
WO2024220634A1 (en) 2023-04-19 2024-10-24 Vitro Flat Glass Llc Durable coated article having a metal layer
WO2024249073A1 (en) 2023-06-02 2024-12-05 Vitro Flat Glass Llc Glass composition having low iron and low redox
US20250196807A1 (en) 2023-12-19 2025-06-19 Pittsburgh Glass Works, Llc Window Inductive Heating System
WO2025155712A2 (en) 2024-01-16 2025-07-24 Vitro Flat Glass Llc Glass for reducing bird collisions
WO2025240813A1 (en) 2024-05-17 2025-11-20 Vitro Flat Glass Llc Solar control coating with moderate reflectance and improved aesthetics
WO2025255102A1 (en) 2024-06-04 2025-12-11 Vitro Flat Glass Llc Architectural glass for greenhouses

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4094763A (en) * 1970-07-31 1978-06-13 Ppg Industries, Inc. Sputter coating of glass with an oxide of a metal having an atomic number between 48 and 51 and mixtures thereof
US4166018A (en) * 1974-01-31 1979-08-28 Airco, Inc. Sputtering process and apparatus
US4349425A (en) * 1977-09-09 1982-09-14 Hitachi, Ltd. Transparent conductive films and methods of producing same
US4113599A (en) * 1977-09-26 1978-09-12 Ppg Industries, Inc. Sputtering technique for the deposition of indium oxide
US4201649A (en) * 1978-11-29 1980-05-06 Ppg Industries, Inc. Low resistance indium oxide coatings
DE2924833C3 (de) * 1979-06-20 1982-05-19 Bfg Glassgroup, Paris Wärmereflexionsscheibe mit farbneutraler Außenansicht und deren Verwendung als Außenscheibe einer Mehrscheibenanordnung
DE3160998D1 (en) * 1980-03-10 1983-11-03 Teijin Ltd Selectively light-transmitting laminated structure
DE3039821A1 (de) * 1980-10-22 1982-06-03 Robert Bosch Gmbh, 7000 Stuttgart Mehrschichtsystem fuer waermeschutzanwendung
DE3211753C2 (de) * 1982-03-30 1985-03-28 Interpane Entwicklungs- und Beratungsgesellschaft mbH & Co. KG, 3471 Lauenförde Hochtransparenter, in Durch- als auch Außenansicht neutral wirkender und wärmedämmender Belag für ein Substrat aus transparentem Material sowie Verwendung des Belages
JPS5931147A (ja) * 1982-08-17 1984-02-20 株式会社豊田中央研究所 可視光透過性熱線しやへい膜およびその製造方法
NO157212C (no) * 1982-09-21 1988-02-10 Pilkington Brothers Plc Fremgangsmaate for fremstilling av belegg med lav emisjonsevne.
DE3307661A1 (de) * 1983-03-04 1984-09-06 Leybold-Heraeus GmbH, 5000 Köln Verfahren zum herstellen von scheiben mit hohem transmissionsverhalten im sichtbaren spektralbereich und mit hohem reflexionsverhalten fuer waermestrahlung
DE3316548C2 (de) * 1983-03-25 1985-01-17 Flachglas AG, 8510 Fürth Verfahren zur Beschichtung eines transparenten Substrates
US4610771A (en) * 1984-10-29 1986-09-09 Ppg Industries, Inc. Sputtered films of metal alloy oxides and method of preparation thereof
US4716086A (en) * 1984-12-19 1987-12-29 Ppg Industries, Inc. Protective overcoat for low emissivity coated article
DE3543178A1 (de) * 1985-12-06 1987-06-11 Leybold Heraeus Gmbh & Co Kg Verfahren zum herstellen von scheiben mit hohem transmissionsverhalten im sichtbaren spektralbereich und mit hohem reflexionsverhalten fuer waermestrahlung sowie durch das verfahren hergestellte scheiben
CA1331867C (en) * 1986-12-29 1994-09-06 James Joseph Finley Low emissivity film for high temperature processing
US4790922A (en) * 1987-07-13 1988-12-13 Viracon, Inc. Temperable low emissivity and reflective windows
JPS6474806A (en) * 1987-09-17 1989-03-20 Japan Radio Co Ltd Slop array antenna

Also Published As

Publication number Publication date
US4898790A (en) 1990-02-06
KR920005471B1 (ko) 1992-07-04
DE68915042D1 (de) 1994-06-09
JP2505278B2 (ja) 1996-06-05
EP0335309B1 (en) 1994-05-04
BR8901510A (pt) 1989-11-14
DE68915042T2 (de) 1994-11-17
CA1337483C (en) 1995-10-31
KR890015969A (ko) 1989-11-27
EP0335309A1 (en) 1989-10-04
JPH01301537A (ja) 1989-12-05

Similar Documents

Publication Publication Date Title
ES2056136T3 (es) Pelicula de baja emisividad para tratamiento a elevadas temperaturas.
ES548274A0 (es) Un metodo para depositar una pelicula que comprende un oxidode una aleacion metalica
KR890015970A (ko) 자동차의 열부하 감소용 저 발산성 필름
KR890015968A (ko) 시각적으로 드러나지 않는 합금산화물 스퍼터링 필름
CA1269060C (en) SPRAY DEPOSITS OF METAL ALLOY OXIDES (METALLIZATION)
KR880007793A (ko) 높은 투과율과 낮은 복사율의 물품, 내열성 필름의 부착방법 및 다층 저복사율 생성물의 제조방법
AU2003250246A8 (en) Method for production of a glazed piece provided with a multi-layer coating
AU3146399A (en) Organic substrate having optical layers deposited by magnetron sputtering and method for preparing it
ES2192891T3 (es) Mejoras introducidas en el revestimiento de vidrio.
KR900006250A (ko) 반사율이 낮고 색포화도가 높은 일체형 유리 구조물의 피막
ATE191438T1 (de) Durchsichtiges substrat mit einem dünnschichtaufbau mit eigenschaften im infrarotgebiet
GR3023916T3 (en) Process for making thin polymer film by pulsed laser evaporation.
EP0269111A3 (en) Method of forming a thin aluminium film
WO2001042522A3 (en) Sputtering target and methods of making same
KR880011364A (ko) 비스무트/주석 산화물의 스퍼터링된 필름 및, 이런 필름을 포함하는 물품
WO2006041924A3 (en) Thin film coating and temporary protection technology, insulating glazing units, and associated methods
EP0269112A3 (en) Method of forming a thin crystalline metal film
GB2013724A (en) Method for sputtering cadmium stannate films
JPS6138265B2 (es)
GB1309881A (en) Transparent heat ray reflecting glass and process for manufacturing the same
WO2002027057A3 (en) Sputtering target and method of making same
CA2103085A1 (en) Method for Preparing Superconducting Thin Film Formed of High Temperature Superconductor Oxide
JP2577938B2 (ja) 高反射フイルム
JP2532901B2 (ja) 高反射フイルム
JPS569368A (en) Method for decoration by precious metal thin film

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 335309

Country of ref document: ES