DK1685186T4 - Formmasse indeholdende et matteringsmiddel - Google Patents
Formmasse indeholdende et matteringsmiddel Download PDFInfo
- Publication number
- DK1685186T4 DK1685186T4 DK04765213.6T DK04765213T DK1685186T4 DK 1685186 T4 DK1685186 T4 DK 1685186T4 DK 04765213 T DK04765213 T DK 04765213T DK 1685186 T4 DK1685186 T4 DK 1685186T4
- Authority
- DK
- Denmark
- Prior art keywords
- weight
- matrix
- matting agent
- ethylenically unsaturated
- acrylate
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L51/00—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
- C08L51/003—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers grafted on to macromolecular compounds obtained by reactions only involving unsaturated carbon-to-carbon bonds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F265/00—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F265/00—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00
- C08F265/04—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00 on to polymers of esters
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F265/00—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00
- C08F265/04—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00 on to polymers of esters
- C08F265/06—Polymerisation of acrylate or methacrylate esters on to polymers thereof
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F279/00—Macromolecular compounds obtained by polymerising monomers on to polymers of monomers having two or more carbon-to-carbon double bonds as defined in group C08F36/00
- C08F279/02—Macromolecular compounds obtained by polymerising monomers on to polymers of monomers having two or more carbon-to-carbon double bonds as defined in group C08F36/00 on to polymers of conjugated dienes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L101/00—Compositions of unspecified macromolecular compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
- C08L33/04—Homopolymers or copolymers of esters
- C08L33/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical
- C08L33/10—Homopolymers or copolymers of methacrylic acid esters
- C08L33/12—Homopolymers or copolymers of methyl methacrylate
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L35/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical, and containing at least one other carboxyl radical in the molecule, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
- C08L35/06—Copolymers with vinyl aromatic monomers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L51/00—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L55/00—Compositions of homopolymers or copolymers, obtained by polymerisation reactions only involving carbon-to-carbon unsaturated bonds, not provided for in groups C08L23/00 - C08L53/00
- C08L55/02—ABS [Acrylonitrile-Butadiene-Styrene] polymers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2205/00—Polymer mixtures characterised by other features
- C08L2205/22—Mixtures comprising a continuous polymer matrix in which are dispersed crosslinked particles of another polymer
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Graft Or Block Polymers (AREA)
- Macromonomer-Based Addition Polymer (AREA)
- Manufacture Of Macromolecular Shaped Articles (AREA)
- Dry Formation Of Fiberboard And The Like (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Moulds For Moulding Plastics Or The Like (AREA)
Claims (11)
1. Formmasse indeholdende a) 50 bis 99,9 vægt-% af en matrix af et termoplastisk kunststof, og b) 0,1 til 50 vægt-% af et i matrixen fordelt matteringsmiddel i form af en (meth)acrylatcopolymer, kendetegnet ved, at matteringsmidlet er en (meth)acrylatcopolymer, som er fremstillet ud fra de følgende monomerer: bl) 50 til 95 vægt-% methylmethacrylat b2) 5 til 50 vægt-% C%- til C6-alkylacrylater b3) 0,01 til mindre end 0,5 vægt-% af en tværbindende monomer og/eller podningstværbindende midler med to eller flere ethylenisk umættede radikalisk polymeriserbare grupper, b4) 0 til 20 vægt-% af en eller flere yderligere ikke- tværbindende ethylenisk umættede radikalisk polymeriserbare monomerer, hvorved bestanddelene bl) og b2) samt eventuelt b3) og/eller b4) adderer op til 100 vægt-%, og at matteringsmidlet har en glasovergangstemperatur Tmg på mindst 20 °C, og hvorved matteringsmidlet b) blev fremstillet ved emulsionspolymerisation og før indarbejdning i matrixen har en middelpartikelradius i området på 100 nm til 10 pm.
2. Formmasse ifølge krav 1, kendetegnet ved, at matrixen a) kan bestå af et polymethylmethacrylat, et slagsejt modificeret polymethylmethacrylat, et polycarbonat, en polystyren, en acrylsyreester/styren/acrylnitril-propcopolymer (ASA), en styren-acryl-nitril (SAN), en polyester, et polyethylenterephthalat (PET), et glycolmodificeret polyethylenterephthalat (PETG), et polybutylenterephthalat-kunststof (PBT), et polyvinylchlorid-kunststof (PVC), et polyolefin-kunststof, en cycloolefincopolymer (COC), en acrylnitril-butadien-styren (ABS) eller blandinger (blends) af forskellige termoplastiske kunststoffer.
3. Formmasse ifølge krav 1 eller 2, kendetegnet ved, at matrixen a) er et slagsejhedsmodificeret polymethylmethacrylat, som indeholder et to- eller trelags opbygget slagsejhedsmodificeringsmiddel.
4. Formmasse ifølge et eller flere af kravene 1 til 3, kendetegnet ved, at matrixen a) er et slagsejhedsmodificeret polymerisat bestående af: al) 10 til 95 vægt-% af en sammenhængende hård fase med en glasovergangstemperatur Tmg over 70 °C, opbygget af all) 80 til 100 vægt-% (baseret på al) methylmethacrylat, og al2) 0 til 20 vægt-% af en eller flere ethylenisk umættede radikalisk polymeriserbare monomerer, og a2) 90 til 5 vægt-% af en i den hårde fase fordelt sej fase med en glasovergangstemperatur Tmg under -10 °C, opbygget af a21) 50 til 99,5 vægt-% af et Ci-Cio-alkylacrylat (baseret på a2) a22) 0,5 til 5 vægt-% af en tværbindende monomer med to eller flere ethylenisk umættede radikalisk polymeriserbare grupper, og a23) eventuelt flere ethylenisk umættede radikalisk polymeriserbare monomerer, hvorved mindst 15 vægt-% af den hårde fase al) er covalent bundet til den seje fase a2).
5. Formmasse ifølge et eller flere af kravene 1 til 4, kendetegnet ved, at matteringsmidlet b) er et copolymerisat af 50 til 90 vægt-% methylmethacrylat 10 til 50 vægt-% ethylacrylat og/eller butylacrylat 0,01 til mindre end 0,5 vægt-% af en tværbindende monomer og/eller podningstværbindingsmiddel med to eller flere ethylenisk umættede radikalisk polymeriserbare grupper.
6. Formmasse ifølge et eller flere af kravene 1 til 4, kendetegnet ved, at man som tværbindende monomer anvender ethylenglycoldimethacrylat.
7. Formmasse ifølge et eller flere af kravene 1 til 6, kendetegnet ved, at et derudfra fremstillet prøvelegeme har ruhedsstørrelser ifølge DIN 4768 i området på Ra = 0,1 til 0,5 pm, Rz = 0,5 til 5,0 pm, og Rmax =0,5 til 5,0 pm.
8. Fremgangsmåde til fremstilling af en formmasse ifølge et eller flere af kravene 1 til 7 på i og for sig kendt måde ved blanding af matrixen og matteringsmidlet i smeltetilstand i en ekstruder, udføring og afkøling af ekstrudatet og efterfølgende granulering.
9. Formlegeme, der kan fremstilles på i og for sig kendt måde ved hjælp af ekstrudering eller sprøjtestøbning ud fra en formmasse ifølge et eller flere af kravene 1 til 7.
10. Formlegeme ifølge krav 9, kendetegnet ved, at det drejer sig om en folie, en flad plade, en bølgeplade, en mellemf lerlagsplade, et rør, en stav eller en hvilken som helst formet sprøjtestøbningsdel.
11. Anvendelse af en folie fremstillet ud fra formmassen ifølge et eller flere af kravene 1 til 7, til co-laminering med et yderligere, foliemateriale eventuelt med tryk, til eftersprøjtning med et kunststofmateriale, til efterskumning med et kunststofskum, til ekstruderingskachering eller til kachering af hvilke som helst substrater.