DE679594C - Herstellung von Dauermagneten - Google Patents

Herstellung von Dauermagneten

Info

Publication number
DE679594C
DE679594C DEA77677D DEA0077677D DE679594C DE 679594 C DE679594 C DE 679594C DE A77677 D DEA77677 D DE A77677D DE A0077677 D DEA0077677 D DE A0077677D DE 679594 C DE679594 C DE 679594C
Authority
DE
Germany
Prior art keywords
permanent magnets
iron
aluminum
manufacture
nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEA77677D
Other languages
English (en)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AEG AG
Original Assignee
AEG AG
Filing date
Publication date
Application filed by AEG AG filed Critical AEG AG
Application granted granted Critical
Publication of DE679594C publication Critical patent/DE679594C/de
Expired legal-status Critical Current

Description

  • Herstellung von Dauermagneten Dauermagnete aus Aluminium, Nickel und Eisen mit oder ohne Kobaltzusatz hat man bisher aus den einzelnen Bestandteilen der Legierung erschmolzen und das flüssige Metall in Formen gegossen. Danach wurde die erstarrte Legierung einer Wärmebehandlung bei Temperaturen zwischen zooo und ,5 00° C unterworfen, abgekühlt und bei Temperaturen zwischen 7oo und cfOO'C ausgehärtet.
  • Die nach diesem bekannten Verfahren hergestellten Dauermagnete, die aus etwa
    bis 15 % Aluminium,
    2o - 30 % Nickel,
    Rest Eisen
    oder aus
    6 bis 15 % Aluminium,
    12 - 30 % Nickel,
    etwa zo % Kobalt,
    Rest Eisen
    bestehen, besitzen gute magnetische Eigenschaften, sind aber sehr hart und spröde, so daß sie sich nicht für die spanabhebende Bearbeitung eignen und infolgedessen durch Schleifen auf die gewünschte Form gebracht werden müssen. Auch lassen sich nur sehr einfache Formen begrenzter Dicke (etwa 30 mm) eiilwandfrei vergießen. Gegenstand der Erfindung ist die Verwendung von aus Aluminium, Nickel, Eisen und gegebenenfalls Kobalt bestehenden Legierungen, die dadurch erzeugt worden sind, daß durch Erhitzen von Aluminium und Eisen eine Vorlegierung gebildet wird, diese nach Zerkleinerung mit den übrigen Elementen der Endlegierung vermischt und hierauf das Gemisch durch Pressen in die gewünschte Form gebracht und gesintert wurde, für die Herstellung von Dauermagneten. Derartige Magnete können auch bei ziemlich verwickelter Gestalt spanlos geformt werden; sie sind feinkörnig und gleichförmig im Gefüge und haben gute Eigenschaften als Dauermagnete. Bis zu einem gewissen Grade sind die Magnete auch schmiedbar. Wird das Schmieden der Teile zu weit getrieben, so wachsen jedoch die Kristalle stark; und der Stoff wird spröde.
  • Es wurde bereits vorgeschlagen, Aluminium enthaltende Legierungen durch Pressen und Sintern zu gewinnen. Insbesondere wurde vorgeschlagen, Aluminium leicht zerpulverbar zu machen, dadurch, daß eine spröde Vorlegierung mit Eisen hergestellt wird. Diese zerpulverte Legierung wurde dann, gegebenenfalls im Gemisch mit anderen Metallpulvern, zur Verkittung an größeren, kompakten Metallabfällen, angewendet. Über die besonderen Eigenschaften der erhaltenen Erzeugnisse, insbesondere über die magnetischen Eigenschaften, ist nichts bekanntgeworden.
  • Weiterhin wurde auch schon vorgeschlagen, magnetische, Nickel, Eisen und gegebenenfalls auch Aluminium enthaltende Legierungen mit hoher, über einen weiten Bereich gleichbleibender Anfangspermeabilität dadurch herzustellen, daß die Legierungen nicht höher als auf iooo° C erwärmt werden, um Diffusion zu vermeiden; während bei der Herstellung der nach der Erfindung zu verwendenden Legierungen die Sinterung bei so hoher Temperatur erfolgen muß, daß ein den geschmolzenen Legierungen gleicher Kristallaufbau nach Möglichkeit erreicht wird..

Claims (1)

  1. PATENTAN SPRITCFI: Die Verwendung von aus Aluminium, Nickel, Eisen urid gegebenenfalls Kobalt bestehenden Legierungen; die dadurch erzeugt worden sind, daß durch Erhitzen von Aluminium und Eisen eine Vorlegierung gebildet, diese nach Zerkleinerung mit den übrigen gepulverten Elementen der Endlegierung vermischt und hierauf das Gemisch durch Pressei in die gewünschte Form gebracht und gesintert wurde, für die Herstellung von -Dauermagneten.
DEA77677D 1935-11-17 Herstellung von Dauermagneten Expired DE679594C (de)