DE3713601A1 - Verfahren zur herstellung eines stark wasserabsorbierenden polymerisats - Google Patents
Verfahren zur herstellung eines stark wasserabsorbierenden polymerisatsInfo
- Publication number
- DE3713601A1 DE3713601A1 DE19873713601 DE3713601A DE3713601A1 DE 3713601 A1 DE3713601 A1 DE 3713601A1 DE 19873713601 DE19873713601 DE 19873713601 DE 3713601 A DE3713601 A DE 3713601A DE 3713601 A1 DE3713601 A1 DE 3713601A1
- Authority
- DE
- Germany
- Prior art keywords
- water
- meth
- carboxyl
- acrylate
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Die Erfindung betrifft ein Verfahren zur Herstellung
eines stark wasserabsorbierenden Polymerisates, das
nur noch einen geringen Anteil an extrahierbaren
Oligomeren aufweist.
Als Absorptionsmittel für Flüssigkeiten, insbesondere
physiologische Flüssigkeiten im Hygienebereich, sind
synthetische Polymere auf der Basis anionischer Mono
merer bekannt. Diese auch als Superabsorber bezeichne
ten Stoffe sind in der Lage, die Flüssigkeit rasch
und in großen Mengen, bezogen auf eingesetztes Poly
mer, aufzunehmen. Die Superabsorber sind wasserunlös
lich und quellen stark im Kontakt mit den Flüssigkei
ten, was die Vernetzung der Polymeren erfordert,
aus denen der Superabsorber aufgebaut ist.
Aus der DE-OS 33 31 644 wird ein Verfahren zur Her
stellung von stark wasserabsorbierenden Polymerisaten
beschrieben, die hochresistent gegen Salzlösungen
sind. Um Resistenz gegen Salzlösungen bei gleichzei
tig guter Wasseraufnahmekapazität zu erhalten, wird
ein hydrophiles Polymer (z. B. Polyacrylsäure) bei
einem bestimmten Wassergehalt des Polymerisats von
10 bis 40 Gew.-% mit einem wenigstens zweifunktionelle
Gruppen aufweisenden Vernetzungsmittel vernetzt.
Das Vernetzungsmittel muß im Stande sein, mit einer
Carboxylgruppe und einer Carboxylatgruppe des Polyme
risats zu reagieren.
Als Vernetzungsmittel werden Polyglycidylether
genannt. Abgesehen davon, daß der Einsatzbereich
dieses Verfahrens auf die Verwendung von Vernetzern
beschränkt ist, die mindestens zwei mit Carboxylgrup
pen reagierende funktionelle Gruppen aufweisen müs
sen, sind die Polymerisate vor der Umsetzung mit
den wenigstens bifunktionellen, mit der Carboxylgruppe
reagierenden Vernetzungsmittel unvernetzt.
In der DE-OS 34 29 379 wird ein Verfahren zur Herstel
lung eines hochreaktiven wasserabsorbierenden Harzes
beschrieben, in dem das wasserabsorbierende Harz,
welches Carboxyl- oder Carboxylatgruppen enthält
und einen Wassergehalt von 50 Gew.-% oder weniger
aufweist, mit einem hydrophilen Polymer mit einer
reaktiven Gruppe oder einem hydrophilen Monomer mit
einer reaktiven Gruppe imprägniert und das Monomer
polymerisiert wird. Das hydrophile Polymer kann nach
oder während seiner Polymerisation vernetzt werden.
Als Vernetzer für das hydrophile Polymer bzw. das
hydrophile Monomer werden Verbindungen mit wenigstens
zwei funktionellen Gruppen, z. B. Polyglycidylether
wie Ethylenglycoldiglycidylether, erwähnt. Bei diesem
Verfahren werden jedoch große Mengen an hydrophilen
Monomeren bzw. Polymeren (ab 10% bezogen auf das
Monomere der vorhergegangenen Polymerisation) benö
tigt, um die gewünschten Absorptionseigenschaften
zu erzielen. Die Beschränkung auf hydrophile Monomere
und hydrophile Polymere beeinträchtigt außerdem die
Auswahl an verwertbaren Substanzen, insbesondere,
wenn das wasserabsorbierende Harz nach dem Umkehrsus
pensionspolymerisationsverfahren hergestellt wird.
In der DE-OS 35 23 617 werden wasserabsorbierende
Mittel beschrieben, die durch Umsetzung eines wasser
absorbierenden Harzes, z. B. von teilneutralisierter
Polyacrylsäure, die auch vernetzt sein kann, mit
0,001 bis 10 Gew.-Teilen eines mehrwertigen Alkohols,
z. B. Glycerin, in Gegenwart von Wasser und hydrophi
len Lösungsmitteln und anschließendem Erwärmen erhal
ten werden. Durch die Umsetzung mit dem mehrwertigen
Alkohol wird das wasserabsorbierende Harz oberfläch
lich vernetzt. Eine solche Arbeitsweise ist aber
besonders bei den durch Umkehrsuspensionspolymerisation
hergestellten Produkten wegen nachträglich erfol
gender weiterer Arbeitsgänge unwirtschaftlich.
Aufgabe der Erfindung ist es, ein einfaches und wirt
schaftliches Verfahren für die Herstellung solcher
vorstehend als Superabsorber bezeichneten Absorptions
mittel für Flüssigkeiten, insbesondere physiologische
Flüssigkeiten, im Hygienebereich bereitzustellen,
die nur noch einen geringen Anteil Oligomeren enthal
ten, welche durch Wasser oder physiologische Kochsalz
lösung extrahierbar sind. Es hat sich nämlich ge
zeigt, daß die Wirksamkeit der Vernetzung eines
solchen Absorptionsmittels, die für die Wasserunlös
lichkeit und das herausragende Quellvermögen entschei
dend ist, deutlich an dem Anteil Oligomerer ein
schließlich Monomerer erkennbar ist, der aus dem
dem Superabsorber zugrundeliegenden carboxylgruppen
haltigen Polymerisat durch Wasser oder physiologische
Kochsalzlösung extrahiert werden kann. Dieser auch
für die Verwendung des wasserabsorbierenden Harzes
im Hygienebereich wichtige Aspekt ist bisher nicht
berücksichtigt worden.
Diese Aufgabe wird erfindungsgemäß durch die Merkmale
des Kennzeichens von Patentanspruch 1 gelöst.
Überraschenderweise reichen geringe Mengen einer
hydrophoben ungesättigten Glycidylverbindung, wahlweise
unter Zusatz eines mindestens bifunktionell unge
sättigten Vernetzers aus, um ein Absorptionsmittel
zu erhalten, das weniger als 20, vorzugsweise weniger
als 10 Gew.-% an mit Wasser oder physiologischer
Kochsalzlösung extrahierbaren Oligomeren einschließ
lich Monomeren enthält.
Als hydrophobe ungesättigte Glycidylverbindung werden
bevorzugt solche mit einer maximalen Anzahl von 10
Kohlenstoffatomen eingesetzt, vorzugsweise Glycidyl
ester ungesättigter Carbonsäuren wie Glycidylacrylat
und Glycidylmethacrylat sowie ungesättigte Glycidyl
ether wie Glycidyllylether oder ein Gemisch dieser
Verbindungen. Die Menge an hydrophober ungesättigter
Glycidylverbindung (im weiteren auch als hydrophobes
Monomer bezeichnet), die eine ausreichende Modifizie
rung des carboxylgruppenhaltigen Harzes bewirkt,
ist gering und liegt im allgemeinen bei 0,01-5,0
Gew.-%, vorzugsweise bei 0,02-2%, besonders bevor
zugt bei 0,2-0,4%, bezogen auf das carboxyl(at)
gruppenhaltige Monomere.
Die hydrophobe ungesättigte Glycidylverbindung kann
zusammen mit einem mindestens bifunktionell ungesät
tigten Vernetzungsmittel eingesetzt werden. Geeignet
hierfür sind z. B. (meth)acryl- und allylgruppenhaltige
Stoffe. Vorzugsweise werden Triallylmethylammonium
chlorid, Trimethylolpropantriacrylat, Tetraallylam
moniumchlorid, Alkylenbisacrylamid, Glycerinpropoxy
triacrylat eingesetzt. Die Zugabe des Vernetzungs
mittels hat den Zweck, die Vernetzungsreaktion zu
beschleunigen und zu vervollständigen. Die Vernet
zungsreaktion findet dann parallel zur Polymerisation
des hydrophoben Monomers statt. Das Vernetzungsmittel
kann gleichzeitig mit dem hydrophoben Monomer oder
anschließend an dessen Zugabe dem carboxylgruppen
haltigen Polymerisat zugeführt werden.
Die Menge des verwendeten Vernetzungsmittels liegt
im allgemeinen bei 0,01 bis 5 Gew.-%.
Die Verfahren, stark wasserabsorbierende Harze durch
Polymerisation carboxyl- oder carboxylatgruppenhaltiger
hydrophiler Monomerer herzustellen, sind an sich
bekannt, so z. B. Lösungspolymerisation, adiabatische
Polymerisation und Polymerisation in umgekehrter
Suspension. Das letztere, die Umkehrphasensuspensions
polymerisation, erweist sich für die Ausführung
der Erfindung als besonders geeignet und wird bevor
zugt. Die Umsetzung des Polymerisates mit dem hydro
phoben Monomer allein oder auch in Kombination mit
dem oben erwähnten Vernetzungsmittel ist hierbei
besonders leicht in situ ausführbar, und es wird
außerdem ein gut rieselfähiges, staubfreies Produkt
enger Korngrößenverteilung gewonnen. In aller Regel
wird bei dieser Umkehrphasensuspensionspolymerisation
das carboxyl- oder carboxylatgruppenhaltige hydrophile
Monomer in einer wäßrigen Lösung in Gegenwart
eines wasserlöslichen Initiators und ggf. eines Ver
netzers in einem Dispersionsmedium, bestehend aus
einem hydrophoben organischen Lösungsmittel oder
einem Gemisch hydrophober organischer Lösungsmittel
und einem öllöslichen Schutzkolloid, suspendiert
und polymerisiert.
Geeignete carboxyl- oder carboxylatgruppenhaltige
Monomeren sind Acrylsäure und ihre Salze und Meth
acrylsäure und ihre Salze, die aber auch in Kombination
mit weiteren hydrophilen Monomeren als Comonomeren
wie z. B. Maleinsäure, Itaconsäure, Acrylamid, 2-Acryl
amido-2-methylpropansulfonsäure, 2-Hydroxyethyl
(meth)acrylat, Hydroxypropyl(meth)acrylat, Dimethyl
aminopropylacrylamid eingesetzt werden können. Vor
zugsweise werden Acrylsäure und ihre Alkali- und
Ammoniumsalze verwendet.
Die Polymerisation der hydrophilen Monomeren wird
in Gegenwart wasserlöslicher Initiatoren wie Persul
faten, Hydroperoxiden oder Azoverbindungen für sich
oder in Kombination durchgeführt.
Zur Erzielung guter Absorptionseigenschaften ist
es vorteilhaft, in der Polymerisationsstufe der hydro
philen Monomeren eine mehrfach funktionelle Verbin
dung als Vernetzer einzusetzen. Diese vernetzende
Verbindung ist in ihrer Funktionalität nicht auf
die Gruppe der mehrfach ungesättigten Verbindungen
beschränkt, sondern es können auch sogenannte Polygly
cidylverbindungen verwendet werden. Zu diesen mehr
fach funktionellen Verbindungen sind demnach einer
seits die Acryl- und Methacrylester mehrwertiger
Alkohole, Alkylenbis(meth)acrylamide, Polyallylamine,
Polyallylammoniumverbindungen, Addukte von Diallyl
amin an Epichlorhydrin oder an 1,3-Dichlorpropanol-2,
im Amidteil ungesättigte (Meth)acrylamide, anderer
seits Glycidylether mehrwertiger Alkohole zu rechnen.
Auch in diesem Sinne gemischt funktionelle Verbin
dungen sind für die Vernetzung in der Polymeri
sationsstufe der hydrophilen Monomeren einsetzbar.
Bevorzugt verwendet werden Pentaerythrittriacrylat,
Glycerintriglycidylether.
Als hydrophobes organisches Lösungsmittel kann jedes
nichtpolare Lösungsmittel wie z. B. ein üblicher ali
phatischer oder cycloaliphatischer Kohlenwasserstoff
eingesetzt werden. Bevorzugt verwendet wird Cyclohexan.
Geeignete Dispergiermittel, die öllösliche
Schutzkolloide bilden, sind z. B. Sorbitanfettsäure
ester, Celluloseether und Celluloseester. Vorteilhaft
ist es, Celluloseether zu verwenden, da sie die Sus
pension gut stabilisieren und die Anbackungen der
Innenwand des Polymerisationsgefäßes minimal sind.
Vorzugsweise wird Ethylcellulose verwendet.
Die Umsetzung des carboxyl(at)gruppenhaltigen Polymeri
sats mit der ungesättigten Glycidylverbindung,
wahlweise unter gleichzeitiger Anwesenheit eines
mindestens bifunktionell ungesättigten Vernetzungsmit
tels oder anschließender Zugabe oder Abwesenheit
des Vernetzungsmittels, erfolgt nach der Herstellung
des hydrophilen Carboxyl- und/oder Carboxylgruppen
enthaltenden Polymerisats. Die geringe Menge an hydro
phobem Monomer ist erfindugnsgemäß und entscheidend,
weil sie den Anteil an mit Wasser oder physiologi
scher Kochsalzlösung aus dem fertigen Polymerisat
extrahierbarer Oligomerer einschließlich Monomerer
auf unter 20 Gew.-%, vorzugsweise auf unter 10
Gew.-%, herabsetzt und derart ein hochwirksam vernetz
tes Produkt mit stark wasserabsorbierenden Eigenschaf
ten erzielt wird. Das hydrophobe Monomer und wahlweise
der Vernetzer werden in einem hydrophoben Lösungs
mittel aufgenommen, vorzugsweise in dem schon während
der Polymerisation des hydrophilen Monomeren ver
wendeten hydrophoben Lösungsmittel. Die Polymerisa
tion der ungesättigten Glycidylverbindung und des
Vernetzungsmittels wird in Gegenwart öllöslicher
Initiatoren durchgeführt. Das Endprodukt wird durch
Filtration isoliert und unter vermindertem Druck
bei 120°C 2 Stunden getrocknet.
Als physiologische Lösung zur Ermittlung der Absorptions
kapazität wurde Modellurin verwendet. Die Absorption
wurde ohne und mit Druckbelastung, wie in der
EP 00 68 189 beschrieben, ermittelt und ist in Tabelle 3
in g Modellurin/g Polymerisat angegeben.
Die Menge der durch Wasser oder physiologische Koch
salzlösung extrahierbaren Oligomeren und Monomeren
ist erfindungsgemäß gering und wurde wie folgt ermit
telt:
200 mg des Polymerisats wurden in 100 ml 0,9% Koch
salzlösung aufgenommen und 12 Stunden gerührt. Danach
wurde durch Weißband- und Membranfilter filtriert,
die Menge des Filtrats festgestellt und mit Natron
lauge vollständig neutralisiert. Der Gehalt an Car
boxylgruppen wurde dann verdrängungstritrimetrisch
bestimmt und mit dem mittleren Molekulargewicht des
teilneutralisierten Monomeren verrechnet.
180,1 g Acrylsäure wurde unter Kühlung mit 327,2 g
30% Kalilauge neutralisiert und anschließend mit
400 mg Pentaerythrittriacrylat, 62 mg Kaliumpersulfat
und 250 mg ABAH (2,2′Azobis-(2-amidinopropan)dihydro
chlorid) versetzt. Getrennt hiervon wurden in einem
2-l-Kolben mit Rückflußkühler, Rührer, Tropftrichter
und Innenthermometer 800 g Cyclohexan und 10 g Ethyl
cellulose vorgelegt. Nach Erwärmen auf 55°C wurde
ein geringer Unterdruck zur Austreibung des Sauer
stoffs angelegt, der bis zum Polymerisationsende
aufrecht erhalten wurde. Die Monomerlösung wurde
innerhalb 1 Stunde zugetropft, anschließend zur Ver
vollständigung der Polymerisation 3 Stunden unter
allmählichem Abbau des Unterdrucks und Erwärmen auf
70°C nachgerührt. Das Polymerisat wurde durch Fil
tration isoliert und bei 120°C 2 Stunden unter ver
ringertem Druck getrocknet. Der Anteil an extra
hierbaren Oligomeren einschließlich Monomeren, im
folgenden kurz als extrahierbarer Anteil bezeichnet,
betrug 16,1 Gew.-%.
Die Erfindung wird durch die nachfolgenden Beispiele
erläutert: In Beispiel 1 wurde zu Vergleichszwecken
auf die nachträgliche Zugabe des hydrophoben Mono
meren verzichtet.
180,1 g Acrylsäure wurde unter Kühlung mit 327,2 g
30% Kalilauge neutralisiert und anschließend mit
400 mg Pentaerythrittriacrylat, 62 mg Kaliumpersulfat
und 250 mg ABAH versetzt. Getrennt hiervon wurden
in einem 2-l-Kolben mit Rückflußkühler, Rührer,
Tropftrichter und Innenthermometer 800 g Cyclohexan
und 10 g Ethylcellulose vorgelegt. Nach Erwärmen
auf 55°C wurde ein geringer Unterdruck zur Austrei
bung des Sauerstoffs angelegt, der bis zum Polymerisa
tionsende aufrechterhalten wurde. Die Monomerlösung
wurde innerhalb 1 Stunde zugetropft, anschließend
zur Vervollständigung der Polymerisation 3 Stunden
unter allmählichem Abbau des Unterdrucks auf Erwärmen
auf 70°C nachgerührt. Anschließend wurde eine Lösung
von 1 g Glycidylacrylat, 25 mg t-Butylhydroperoxid
und 50 mg Azobisisobutyronitril in 10 ml Cyclohexan
dazugegeben. Nach weiteren 2 Stunden Nachrühren bei
70°C wurde das Polymerisat durch Filtration isoliert
und bei 120°C 2 Stunden unter verringertem Druck
getrocknet. Der extrahierbaren Anteil betrug 5,3
Gew.-%.
In den Beispielen 2-9 (s. nachstehende Tabelle 1)
sind gegenüber Bsp. 2 lediglich die Vernetzermen
gen für die teilneutralisierte Acrylsäure (Spalte 2)
und die Menge an hydrophobem Monomer - wahlweise
mit Vernetzer - (Spalte 3) abgeändert. Die extrahier
baren Anteile in Gew.-% sind Spalte 4 zu entnehmen.
Die Versuche zu den Beispielen 2 bis 9 wurden im
übrigen, wie in Beispiel 1 beschrieben, ausgeführt.
Hier wurden 180,1 g Acrylsäure mit einer Lösung von
138,4 g Ammoniumhydrogencarbonat in 108,5 g Wasser
neutralisiert. Es wurden in der Acrylsäurelösung
50 mg PETA und als hydrophobes Monomer 500 mg GA
verwendet. Im übrigen wurde wie in Beispiel 1 verfah
ren. Der extrahierbare Anteil betrug 3,0 Gew,-%.
Claims (15)
1. Verfahren zur Herstellung eines stark wasserabsor
bierenden Polymerisats mit niedrigem Gehalt an mit
Wasser oder physiologischer Kochsalzlösung extrahier
baren Oligomeren, dadurch gekennzeichnet, daß man
ein vernetztes Carboxyl- und/oder Carboxylatgruppen
enthaltendes Polymer mit wenigstens einer ungesättig
ten hydrophoben Glycidylverbindung umsetzt und danach
polymerisiert.
2. Verfahren nach Anspruch 1, dadurch gekennzeichnet,
daß man mit einer Glycidylverbindung umsetzt, die
maximal 10 Kohlenstoffatome aufweist.
3. Verfahren nach einem der Ansprüche 1 bis 2, da
durch gekennzeichnet, daß man mit einer Monoglyci
dylverbindung umsetzt.
4. Verfahren nach Anspruch 3, dadurch gekennzeichnet,
daß man als ungesättigte hydrophobe Glycidalverbin
dung Glycidyl(meth)acrylat und/oder Glycidylallyl
ether einsetzt.
5. Verfahren nach einem der Ansprüche 1 bis 4,
dadurch gekennzeichnet, daß die Umsetzung mit der
Glycidylverbindung und/oder die darauffolgende Poly
merisation in Gegenwart einer mindestens bifunktio
nell ungesättigten Verbindung als Vernetzungsmittel
vorgenommen wird.
6. Verfahren nach Anspruch 5, dadurch gekennzeich
net, daß als mehrfach ungesättigte Verbindung Tri
allylmethylammoniumchlorid, Trimethylolpropantri
acrylat, Glycerinpropoxytriacrylat und/oder Tetra
allylammoniumchlorid verwendet werden.
7. Verfahren nach einem der Ansprüche 1 bis 6, da
durch gekennzeichnet, daß als Carboxyl- und/oder
Carboxylatgruppen enthaltende Polymere Polyacrylsäure,
Polymethacrylsäure, die Alkali- und Ammoniumpoly-
(meth)acrylate und/oder die Copolymeren von (Meth)-
acrylsäure mit ihren Alkali- und/oder Ammoniumsalzen
und/oder die Copolymerisate von (Meth)acrylsäure
mit anderen hydrophilen Monomeren verwendet werden.
8. Verfahren nach Anspruch 7, dadurch gekennzeich
net, daß Carboxyl- und/oder Carboxylatgruppen enthal
tende Polymerisate eingesetzt werden, die als weitere
hydrophile Monomere Maleinsäure, Itaconsäure, Acryl
amid, 2-Acrylamido-2-methylpropansulfonsäure, 2-Hy
droxyethyl(meth)acrylat, Hydroxypropyl(meth)acrylat,
Hydroxypropyl(meth)acrylat und/oder Dimethylamino
propylacrylamid enthalten.
9. Verfahren nach einem der Ansprüche 1 bis 8, da
durch gekennzeichnet, daß das vernetzte carboxyl
gruppenhaltige Polymer durch Umkehrphasensuspensions
polymerisation erhalten wird.
10. Verfahren nach Anspruch 9, dadurch gekennzeich
net, daß das vernetzte carboxylgruppenhaltige Poly
mer durch Umkehrphasensuspensionspolymerisation einer
wäßrigen Acrylsäurelösung oder einer wäßrigen teil
neutralisierten Acrylsäurelösung in Gegenwart einer
mehrfach funktionellen Verbindung als Vernetzer unter
Verwendung eines wasserlöslichen Initiators herge
stellt wird.
11. Verfahren nach einem der Ansprüche 1 bis 10,
dadurch gekennzeichnet, daß die Polymerisation nach
Umsetzung mit der Glycidylverbindung unter Verwendung
öllöslicher Initiatoren durchgeführt wird.
12. Verfahren nach einem der Ansprüche 1 bis 12,
dadurch gekennzeichnet, daß die Glycidylverbindung
in einer Menge von 0,01 bis 5 Gew.-%, bezogen auf
das carboxyl- und/oder carboxylatgruppenhaltige Poly
merisat eingesetzt wird.
13. Verfahren nach Anspruch 5, dadurch gekennzeich
net, daß das mindestens bifunktionell ungesättigte
Vernetzungsmittel in Mengen von 0,01-5 Gew.-%,
bezogen auf Carboxyl und/oder carboxylatgruppen
haltige Polymerisat, eingesetzt wird.
14. Stark wasserabsorbierendes Mittel mit niedrigem
Gehalt an mit Wasser oder physiologischer Kochsalzlö
sung extrahierbarer Oligomerer, erhältlich nach einem
der Ansprüche 1 bis 13.
15. Verwendung der wasserabsorbierenden Polymerisate
nach Ansprüchen 1 bis 11 zur Absorption von Körper
flüssigkeiten im Hygienebereich.