DE2728110B2 - Verfahren zur Herstellung stranggepreßter, keramischer Körper - Google Patents
Verfahren zur Herstellung stranggepreßter, keramischer KörperInfo
- Publication number
- DE2728110B2 DE2728110B2 DE2728110A DE2728110A DE2728110B2 DE 2728110 B2 DE2728110 B2 DE 2728110B2 DE 2728110 A DE2728110 A DE 2728110A DE 2728110 A DE2728110 A DE 2728110A DE 2728110 B2 DE2728110 B2 DE 2728110B2
- Authority
- DE
- Germany
- Prior art keywords
- layer
- production
- ceramic bodies
- evaporation
- extruded ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Die Erfindung bezieht sich auf ein Verfahren zur Herstellung stranggepreßter, keramischer Körper,
insbesondere plattenförmiger Körper, bei denen die Oberfläche nach der Formung behandelt wird.
Bei einem derartigen, aus der DE-PS 1 30 413 bekannten Verfahren wird auf den Tonstrang nach dem
Austritt aus dem Preßmundstück eine flüssige Begußmasse aufgetragen. Bei diesen Begußmassen, wie z. B.
Engoben oder Glasuren, handelt es sich um feinst gemahlene Tonschlämpe, welche mit mineralischen
Farbstoffen versetzt sind und dem Tonstrang chemisch, mineralogisch und physikalisch eng verbunden sind, so
daß sie auch ähnliche Eigenschaften haben. Dies bezieht sich insbesondere auf die Eigenschaften beim Trocknen,
da hier das Schwindverhalten der Begußmasse praktisch identisch sein muß mit dem des Tonstranges, da es sonst
zu Haarrissen auf der aufgebrachten Schicht bzw. zur Ablösung derselben kommt. Ebenso wichtig ist das
praktisch identische Verhalten von Gußmasse und Tonstrang beim Brand, da auch hier das Schwindverhalten
von Begußmasse und Tonstrang in den einzelnen Temperaturbereichen 'sehr genau zusammenpassen
muß. Es ist mit diesen Begußmassen nicht möglich, die unerwünschte Abwärtsbiegung der Ränder plattenförmiger
keramischer Körper und die Aufwölbung des Mittelbereiches durch das Auftragen dieser Begußmasse
zu beeinflussen.
Der Erfindung liegt die Aufgabe zugrunde, bei einem Verfahren der eingangs genannten Gattung die
Formhaltigkeit, insbesondere die Längsbiegung und die Querbiegung von gepreßten keramischen Körpern
ohne zusätzlichen fertigungstechnischen Aufwand wesentlich zu verbessern, insbesondere auch für plattenförmige
Körper unterhalb einer Stärke von ca. 20 bis 25 mm.
Erfindungsgemäß wird diese Aufgabe dadurch gelöst, daß auf eine Oberfläche des Massenstranges, ganz oder
teilweise, zur Behinderung der Verdampfung des Anmachwassers öl. Lack, Fett in reiner oder flüssig
dispergierter Form aufgetragen wird.
Eine derartige Schicht läßt beim Trockenvorgang den Wasserdampf wesentlich langsamer diffundieren als der
Tonstrang selbst bzw. eine flüssige keramische Begußmasse. Hierdurch ist es möglich, die Abwärtsbiegung
der Ränder und die Aufwölbung des Mittelbereiches der
ίο plattenförmigen Körper zu verhindern.
In weiterer Ausgestaltung der Erfindung kann die Dicke der Schicht variiert werden, so daß damit auch die
Stärke der Behinderung der Verdampfung variiert wird. In einer anderen, besonders vorteilhaften Ausführungsform
des erfindungsgemäßen Verfahrens wird die Konzentration des Materials der Schicht variiert, so daß
bei gleichbleibender Dicke der Schicht die Stärke der Behinderung der Verdampfung variierbar ist
Die im folgenden wiedergegebenen Versuchsergebnisse, die durch die Beschichtung von Ziegelplatten von
19 mm Stärke und 300 mm Länge erzielt wurden, zeigen deutlich, daß mit den erwähnten nicht keramischen
Beschichtungen die Austrocknung der keramischen Platte nach oben und damit die Richtung der
Verbiegung der Platte wesentlich beeinflußt werden kann.
Beschichtungmaterial Längsbiegung Verände
rung gegen unbeschich-
tet
1. Unbeschichtet -0,88 mm -
j-, 2. Wasser -0,85 mm +0,03 mm
3. Engobe -0,92 mm -0,04 mm
4. Filzrollenöl = Rüböl -0,40 mm +0,44 mm
S.Vollmilch -0,26 mm +0,62 mm 6. Maschinenöl +0,72 mm +1,60 mm
7. Schmierseife +1,20 mm +2,08 mm
8. Pabix Emulsion 100% + 1,76 mm +2,64 mm
9. Shellack +4,10 mm +4,98 mm
Bei der Pabix-Emulsion handelt es sich um eine wäßrige Emulsion von Naturwachsen und Kunststoffen.
Die Ergebnisse stellen statistische Mittelwerte aus Versuchsreihen dar.
In der Zeichnung ist eine Vorrichtung zur Ausführung des erfindungsgemäßen Verfahrens dargestellt.
Die einzige Figur der Zeichnung zeigt diese Vorrichtung in Seitenansicht. Hinter einem Mundstück
1 ist an einem einstellbaren Halter 2 ein Schwamm 3 befestigt. Der Halter 2 ist derart eingestellt,
daß der Schwamm 3 den aus dem Mundstück 1 kommenden Massestrang möglichst gleichmäßig berührt.
Über einen fein regelbaren Tropfhahn 5 wird der Schwamm 3 mit einer Flüssigkeit 6 aus einem Behälter 7
beaufschlagt.
Hierzu 1 Blatt Zeichnungen
Claims (3)
1. Verfahren zur Herstellung stranggepreßter, keramischer Körper, insbesondere plattenförmiger
Körper, bei denen die Oberfläche nach der Formung behandelt wird, dadurch gekennzeichnet,
daß auf eine Oberfläche des Massestranges, ganz oder teilweise zur Behinderung der Verdampfung
des Anmachwassers öl. Lack, Fett in reiner oder
flüssig däspergierter Form aufgetragen wird.
2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die Schicht in verschiedener Stärke
aufgetragen wird.
3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die Stärke der Behinderung der
Verdampfung bei gleichbleibender Dicke der Schicht durch entsprechende Konzentration des
Materials der Schicht verändert wird.