CN1305791C - 低羟基含量圆柱形石英玻璃体的制造方法 - Google Patents

低羟基含量圆柱形石英玻璃体的制造方法 Download PDF

Info

Publication number
CN1305791C
CN1305791C CNB038094622A CN03809462A CN1305791C CN 1305791 C CN1305791 C CN 1305791C CN B038094622 A CNB038094622 A CN B038094622A CN 03809462 A CN03809462 A CN 03809462A CN 1305791 C CN1305791 C CN 1305791C
Authority
CN
China
Prior art keywords
soot body
vitrification
soot
pretreatment
furnace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CNB038094622A
Other languages
English (en)
Chinese (zh)
Other versions
CN1649797A (zh
Inventor
S·施密德特
K·罗泽利布
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Heraeus Quarzglas GmbH and Co KG
Original Assignee
Heraeus Tenevo GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heraeus Tenevo GmbH filed Critical Heraeus Tenevo GmbH
Publication of CN1649797A publication Critical patent/CN1649797A/zh
Application granted granted Critical
Publication of CN1305791C publication Critical patent/CN1305791C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B19/00—Other methods of shaping glass
    • C03B19/14—Other methods of shaping glass by gas- or vapour- phase reaction processes
    • C03B19/1453—Thermal after-treatment of the shaped article, e.g. dehydrating, consolidating, sintering
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B37/00—Manufacture or treatment of flakes, fibres, or filaments from softened glass, minerals, or slags
    • C03B37/01—Manufacture of glass fibres or filaments
    • C03B37/012—Manufacture of preforms for drawing fibres or filaments
    • C03B37/014—Manufacture of preforms for drawing fibres or filaments made entirely or partially by chemical means, e.g. vapour phase deposition of bulk porous glass either by outside vapour deposition [OVD], or by outside vapour phase oxidation [OVPO] or by vapour axial deposition [VAD]
    • C03B37/01446—Thermal after-treatment of preforms, e.g. dehydrating, consolidating, sintering
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B37/00—Manufacture or treatment of flakes, fibres, or filaments from softened glass, minerals, or slags
    • C03B37/01—Manufacture of glass fibres or filaments
    • C03B37/012—Manufacture of preforms for drawing fibres or filaments
    • C03B37/014—Manufacture of preforms for drawing fibres or filaments made entirely or partially by chemical means, e.g. vapour phase deposition of bulk porous glass either by outside vapour deposition [OVD], or by outside vapour phase oxidation [OVPO] or by vapour axial deposition [VAD]
    • C03B37/01446—Thermal after-treatment of preforms, e.g. dehydrating, consolidating, sintering
    • C03B37/0146—Furnaces therefor, e.g. muffle tubes, furnace linings
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2201/00—Type of glass produced
    • C03B2201/02—Pure silica glass, e.g. pure fused quartz
    • C03B2201/03—Impurity concentration specified
    • C03B2201/04—Hydroxyl ion (OH)
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P40/00—Technologies relating to the processing of minerals
    • Y02P40/50—Glass production, e.g. reusing waste heat during processing or shaping
    • Y02P40/57—Improving the yield, e-g- reduction of reject rates

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Thermal Sciences (AREA)
  • Manufacturing & Machinery (AREA)
  • Physics & Mathematics (AREA)
  • Organic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Glass Melting And Manufacturing (AREA)
  • Manufacture, Treatment Of Glass Fibers (AREA)
CNB038094622A 2002-04-26 2003-04-28 低羟基含量圆柱形石英玻璃体的制造方法 Expired - Lifetime CN1305791C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE10218864A DE10218864C1 (de) 2002-04-26 2002-04-26 Verfahren zur Herstellung eines zylinderförmigen Quarzglaskörpers mit geringem OH-Gehalt
DE10218864.5 2002-04-26

Publications (2)

Publication Number Publication Date
CN1649797A CN1649797A (zh) 2005-08-03
CN1305791C true CN1305791C (zh) 2007-03-21

Family

ID=28458955

Family Applications (1)

Application Number Title Priority Date Filing Date
CNB038094622A Expired - Lifetime CN1305791C (zh) 2002-04-26 2003-04-28 低羟基含量圆柱形石英玻璃体的制造方法

Country Status (6)

Country Link
US (1) US20050172676A1 (enExample)
JP (1) JP4443234B2 (enExample)
CN (1) CN1305791C (enExample)
AU (1) AU2003236840A1 (enExample)
DE (1) DE10218864C1 (enExample)
WO (1) WO2003091171A2 (enExample)

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7486862B2 (en) * 2003-05-19 2009-02-03 Sumitomo Electric Industries, Ltd. Optical fiber and manufacturing method thereof
WO2005099357A1 (en) * 2004-04-13 2005-10-27 Sebit Co., Ltd Method for manufacturing high heat-resistant quartz glass
JP5066784B2 (ja) * 2005-02-04 2012-11-07 旭硝子株式会社 合成石英ガラスの製造方法
DE102005059290A1 (de) * 2005-12-09 2007-06-14 Heraeus Tenevo Gmbh Verfahren und Vorrichtung zur Herstellung eines Formkörpers aus Quarzglas
DE102006059779B4 (de) * 2006-12-15 2010-06-24 Heraeus Quarzglas Gmbh & Co. Kg Verfahren für die Herstellung eines Hohlzylinders aus synthetischem Quarzglas, nach dem Verfahren erhaltener dickwandiger Hohlzylinder und Verfahren zur Herstellung einer Vorform für optische Fasern
CN101323501B (zh) * 2007-01-02 2015-10-07 德雷卡通信技术公司 用于石英玻璃沉积管的连续焙烧方法
US8062986B2 (en) * 2007-07-27 2011-11-22 Corning Incorporated Fused silica having low OH, OD levels and method of making
US20100122558A1 (en) * 2008-11-19 2010-05-20 John Michael Jewell Apparatus and Method of Sintering an Optical Fiber Preform
EP2977359B1 (de) 2014-07-21 2016-10-19 Heraeus Quarzglas GmbH & Co. KG Verfahren zur herstellung von mit fluor dotiertem quarzglas
CN114031274A (zh) * 2021-12-09 2022-02-11 中天科技精密材料有限公司 连续式低羟基高均匀性石英玻璃的制备方法

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0692648A (ja) * 1992-09-07 1994-04-05 Shin Etsu Chem Co Ltd 合成石英ガラス部材の製造方法
JPH0891867A (ja) * 1994-09-21 1996-04-09 Sumitomo Metal Ind Ltd 紫外光透過用合成石英ガラスおよびその製造方法
CN1131646A (zh) * 1995-03-17 1996-09-25 中国建筑材料科学研究院 紫外激光传能光纤预制棒制造方法
JPH09309735A (ja) * 1996-05-21 1997-12-02 Shinetsu Quartz Prod Co Ltd 石英ガラスの製造方法
US5713979A (en) * 1992-05-14 1998-02-03 Tsl Group Plc Heat treatment facility for synthetic vitreous silica bodies
JPH111331A (ja) * 1998-04-03 1999-01-06 Asahi Glass Co Ltd 石英ガラス光学部材の製造方法
CN1252778A (zh) * 1997-12-19 2000-05-10 纤维管有限公司 采用等离子外部汽相沉积法制造用于光纤生产的管状件的方法
WO2002014231A2 (en) * 2000-08-10 2002-02-21 Yazaki Corporation Process for making glass bodies having refractive index gradients

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6136129A (ja) * 1984-07-30 1986-02-20 Sumitomo Electric Ind Ltd 光フアイバ用ガラス母材の製造方法
US4969941A (en) * 1987-02-16 1990-11-13 Sumitomo Electric Industries, Ltd. Furnace for heating glass preform for optical fiber and method for producing glass preform
AU626362B2 (en) * 1988-12-29 1992-07-30 Sumitomo Electric Industries, Ltd. Furnace for producing high purity quartz glass preform
AU653411B2 (en) * 1991-07-19 1994-09-29 Sumitomo Electric Industries, Ltd. Method for producing glass preform for optical fiber
DE19649935C2 (de) * 1996-12-02 1999-09-16 Heraeus Quarzglas Verfahren zur Herstellung von Quarzglaskörpern
EP1101741B1 (de) * 1999-11-15 2005-07-13 Heraeus Quarzglas GmbH & Co. KG Quarzglaskörper für ein optisches Bauteil und Verfahren zu seiner Herstellung
WO2002026645A1 (en) * 2000-09-27 2002-04-04 Corning Incorporated Process for drying porous glass preforms
JP2003183042A (ja) * 2001-12-14 2003-07-03 Shin Etsu Chem Co Ltd 光ファイバ用母材の製造方法及びその製造方法で製造した光ファイバ用母材

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5713979A (en) * 1992-05-14 1998-02-03 Tsl Group Plc Heat treatment facility for synthetic vitreous silica bodies
JPH0692648A (ja) * 1992-09-07 1994-04-05 Shin Etsu Chem Co Ltd 合成石英ガラス部材の製造方法
JPH0891867A (ja) * 1994-09-21 1996-04-09 Sumitomo Metal Ind Ltd 紫外光透過用合成石英ガラスおよびその製造方法
CN1131646A (zh) * 1995-03-17 1996-09-25 中国建筑材料科学研究院 紫外激光传能光纤预制棒制造方法
JPH09309735A (ja) * 1996-05-21 1997-12-02 Shinetsu Quartz Prod Co Ltd 石英ガラスの製造方法
CN1252778A (zh) * 1997-12-19 2000-05-10 纤维管有限公司 采用等离子外部汽相沉积法制造用于光纤生产的管状件的方法
JPH111331A (ja) * 1998-04-03 1999-01-06 Asahi Glass Co Ltd 石英ガラス光学部材の製造方法
WO2002014231A2 (en) * 2000-08-10 2002-02-21 Yazaki Corporation Process for making glass bodies having refractive index gradients

Also Published As

Publication number Publication date
JP4443234B2 (ja) 2010-03-31
WO2003091171A2 (de) 2003-11-06
DE10218864C1 (de) 2003-10-23
AU2003236840A1 (en) 2003-11-10
JP2005523863A (ja) 2005-08-11
US20050172676A1 (en) 2005-08-11
CN1649797A (zh) 2005-08-03
WO2003091171A3 (de) 2004-10-14
AU2003236840A8 (en) 2003-11-10

Similar Documents

Publication Publication Date Title
CN1305791C (zh) 低羟基含量圆柱形石英玻璃体的制造方法
JPH07507034A (ja) 合成ガラス質シリカ成形体の熱処理設備
CN1275887C (zh) 石英玻璃管的制造方法
KR101725359B1 (ko) 석영 유리 실린더의 제조 방법 및 그 제조 방법을 수행하기 위한 지지체
CN104245610B (zh) 由含氟的合成石英玻璃制备圆柱形组件的方法
CN1282619C (zh) 由人造石英玻璃制造的套管和由该套管制造的光纤
JP6068571B2 (ja) ドープ石英ガラスの製造方法
US8393179B2 (en) Method for producing a semifinished product from synthetic quartz glass
CN100335430C (zh) 借助保持装置生产用合成石英玻璃制成的中空筒的方法和实施所述方法的保持装置
US7975507B2 (en) Process for producing synthetic quartz glass and synthetic quartz glass for optical member
JP2808857B2 (ja) 光ファイバ用ガラス母材の加熱炉および製法
CN1262501C (zh) 在mcvd法中使用双喷灯制备光纤预制棒的方法和设备
CN100351192C (zh) 用于生产预制体的合成二氧化硅玻璃管、用垂直拉丝工艺生产它的方法和所述管的用途
CN1266061C (zh) 预形体制造方法及预形体
TW200422270A (en) Fluorine-doped quartz glass article and manufacturing method thereof
US8245542B2 (en) Method for producing a cylinder from synthetic quartz glass
CN1362938A (zh) 玻璃预制坯的生产方法与由其预制坯得到的光纤
WO2004101457A1 (ja) 光ファイバ用ガラス母材の製造方法
US20040007026A1 (en) Glass base material and method of manufacturing glass base material
JP2003192357A (ja) 多孔質ガラス母材の熱処理方法及び装置
CN1213955C (zh) 石英玻璃体和石英玻璃支持部件的制造方法
JPS63291832A (ja) 光ファイバ母材の製造方法及び装置
HK1061011B (en) Preform body manufacturing method and preform body

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
C56 Change in the name or address of the patentee

Owner name: HEROEASY QUARTZ GLASS CO. KG

Free format text: FORMER NAME OR ADDRESS: HERAEUS TENEVO AG

CP01 Change in the name or title of a patent holder

Address after: Hanau

Patentee after: HERAEUS QUARZGLAS GmbH & Co.KG

Address before: Hanau

Patentee before: HERAEUS TENEVO GmbH

CX01 Expiry of patent term
CX01 Expiry of patent term

Granted publication date: 20070321