CN1298844A - 高级日用瓷无铅熔块釉 - Google Patents

高级日用瓷无铅熔块釉 Download PDF

Info

Publication number
CN1298844A
CN1298844A CN 99120405 CN99120405A CN1298844A CN 1298844 A CN1298844 A CN 1298844A CN 99120405 CN99120405 CN 99120405 CN 99120405 A CN99120405 A CN 99120405A CN 1298844 A CN1298844 A CN 1298844A
Authority
CN
China
Prior art keywords
lead
glaze
frit
porcelain
grade
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 99120405
Other languages
English (en)
Other versions
CN1171818C (zh
Inventor
李玉强
王万昌
张学习
朱秀水
王志霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZIBO INDUSTRIAL CERAMIC FACTORY
Original Assignee
ZIBO INDUSTRIAL CERAMIC FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZIBO INDUSTRIAL CERAMIC FACTORY filed Critical ZIBO INDUSTRIAL CERAMIC FACTORY
Priority to CNB991204050A priority Critical patent/CN1171818C/zh
Publication of CN1298844A publication Critical patent/CN1298844A/zh
Application granted granted Critical
Publication of CN1171818C publication Critical patent/CN1171818C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供一种高级日用瓷无铅熔块釉,采用了烧成范围宽、光泽度好的锆、锂熔块釉,组成中加入了较大量的硼砂,不含有毒铅丹组分。本发明高级日用瓷无铅熔块釉,组成科学合理,易于实施,坯釉适应好,适应于多种高级日用瓷坯体,能够满足高级日用瓷的要求。釉面细腻光滑,光亮度高,弹性好,机械强度大,热震稳定性好,铅溶出量为0.000ppm,彻底免除了瓷器中铅釉对人体的毒害问题。

Description

高级日用瓷无铅熔块釉
本发明涉及一种用于高级日用瓷上的无铅熔块釉。
目前，高级日用瓷用熔块釉均为铅熔块釉，由铅丹和硼砂、硅酸盐矿物、其它碱金属氧化物制成低温熔块，由于铅成分的独特特性，使得铅熔块釉具有易熔性、光亮度高、弹性好、机械强度大、热震稳定性好等特点，因此，多少年来，铅熔块釉一直被广泛沿用着。
随着社会的不断发展，人民生活水平的不断提高，铅对人体的危害已引起了人们的高度重视。铅成分持续或经常地侵入人体，会引起多发性神经炎、中毒性脑病等。GB12651-90标准中规定，与食物接触的陶瓷制品的铅、镉溶出量需小于7ppm。因此，开发一种能够满足高级日用瓷要求的无铅熔块釉，是人们迫切需要解决的重大难题，是时代的要求。
本发明的目的在于提供一种高级日用瓷无铅熔块釉，该釉组成科学合理，易于实施，能够满足高级日用瓷的要求，彻底免除了瓷器中铅釉对人体的毒害问题。
本发明所述的高级日用瓷无铅熔块釉，含有SiO2、Al2O3，其其化学组成的重量百分比为：
      SiO2               50～70
      Al2O3              9～14
      B2O3               1～7
      CaO                  1～9
      MgO                  0～4
      SrO                  0～6
      ZnO                  0～5
      K2O                 0～3
      Na2O                0～3
      Li2O                1～3
      P2O5               0～6
      ZrO2                1～4
上述组成的高级日用瓷无铅熔块釉，主要由熔块和粘土配制而成，其中，熔块的配料重量百分组成如下，釉中不足组分由相应的原料调整，如SiO2的量由石英调整等：
石英25.00～30.00 长石12.00～17.00 锆英石5.00～7.00 硼砂13.00～17.00 粘土12.00～16.00 碳酸钙0～8.00 白云石2.00～3.00硼酸0.5～1 碳酸锶7.00～8.00 碳酸锂2.00～4.00 骨灰3.00～5.00氧化锌4.00～6.00。
熔块的最佳配料重量百分组成为：
石英26.00 长石15.00 锆英石6.00 硼砂13.34 龙岩土13.00碳酸钙7.00 白云石3.00 硼酸0.66 碳酸锶7.00 碳酸锂 2.00骨灰3.00 氧化锌4.00。
所述的高级日用瓷无铅熔块釉，其釉料的重量配料比为：熔块80～90％石英0～10％粘土4～10％瓷粉0～16％白云石0～4％碳酸锂0～2％硼酸钙0～6％。
本发明无铅熔块釉采用了烧成范围宽、光泽度好的锆、锂熔块釉，组成中加入了较大量的硼砂，为了改善釉面光泽和高温流动性，外加了少量的强助熔剂。
釉料制备需首先制作熔块，然后再制备釉料。原料的选择、使用与通常的相同，本发明所用原料的组成见表1。
第一步：将熔块原料按要求配比配料，按熔块常规制备工艺制备熔块，熔融温度1200～1300℃。熔块粉碎后备用。
第二步：将熔块粉料和其余生粉料混合，配合减水剂等制备釉料，可以直接在球磨机中粉碎制成备用釉浆，釉浆细度控制在万孔筛余为0.02～0.05％。
本发明釉料按常规的高级日用瓷生产工艺要求和规程使用即可，进行常规的施釉、烧成，得成品。该无铅釉的适宜烧成温度为1160～1200℃。
本发明高级日用瓷无铅熔块釉，组成科学合理，易于实施，坯釉适应好，适应于多种高级日用瓷坯体，如高石英瓷、高长石瓷、骨灰瓷、滑石瓷等等，能够满足高级日用瓷的要求。釉面细腻光滑，光亮度高，透明度好，弹性好，机械强度大，热震稳定性好，铅溶出量为0.00ppm，彻底免除了瓷器中铅釉对人体的毒害问题。
下面结合实施例对本发明作进一步的说明。
实施例用熔块的配料重量百分组成为：
石英26.00 长石15.00 锆英石6.00 硼砂13.34 龙岩土13.00碳酸钙7.00 白云石3.00 硼酸0.66 碳酸锶7.00 碳酸锂2.00 骨灰3.00 氧化锌4.00。
按常规的熔块熔制法用坩埚熔制成熔块，熔融温度1200～1300℃，将熔块粉碎后备用。
实施例1：
釉料重量配比：熔块80％瓷粉16％龙岩土4％
将釉料在球磨机中湿磨制成万孔筛余为0.02～0.05％的釉浆备用：
在高级骨灰瓷坯(重量百分组成为：SiO2 40.32 Al2O3 14.65 Fe2O3 0.21CaO 20.64 MgO 0.94 K2O 1.35 Na2O 0.06 P2O5 18.2 TiO2 0.05余量为常规杂质)上施釉后，在1160～1200℃的温度下烧成，得高级日用骨灰细瓷。产品釉面细腻光亮，经检测，光泽度＞115，白度＞77，硬度＞660Kgf/mm2，铅溶出量为0.00ppm。
实施例2：
釉料重量配比：熔块84％石英4％苏州土5％白云石2％碳酸锂1％硼酸钙4％
将釉料在球磨机中湿磨制成万孔筛余为0.02～0.05％的釉浆备用；
在高长石瓷坯(重量百分组成为：SiO2 59.33 Al2O3 28.40 Fe2O3 0.35CaO 0.55 MgO 0.85 K2O 3.72 Na2O 5.52余量为常规杂质)上施釉后，在1160～1200℃的温度下烧成，得高级日用长石质细瓷。产品釉面光润，经检测，光泽度＞115，硬度＞660Kgf/mm2，铅溶出量为0.00ppm。
实施例的化学组成见表2。
表1：原料化学组成表(重量百分组成)
表2、实施例的化学组成表(重量百分组成)

Claims (4)

1、一种高级日用瓷无铅熔块釉，含有SiO2、Al2O3，其特征在于其化学组成的重量百分比为：
     SiO2          50～70
     Al2O3         9～14
     B2O3           1～7
     CaO              1～9
     MgO              0～4
     SrO              0～6
     ZnO              0～5
     K2O             0～3
     Na2O            0～3
     Li2O            1～3
     P2O5           0～6
     ZrO2            1～4
2、根据权利要求1所述的高级日用瓷无铅熔块釉，其特征在于主要由熔块和粘土配制而成，其中，熔块的配料重量百分组成如下，釉中不足组分由相应的原料调整：
石英25.00～30.00 长石12.00～17.00 锆英石5.00～7.00 硼砂13.00～17.00 粘土12.00～16.00 碳酸钙0～8.00 白云石2.00～3.00 硼酸0.5～1碳酸锶7.00～8.00 碳酸2.00～4.00 骨灰3.00～5.00 氧化锌4.00～6.00。
3、根据权利要求2所述的高级日用瓷无铅熔块釉，其特征在于熔块的配料重量百分组成为：
石英26.00 长石15.00 锆英石6.00 硼砂13.34 龙岩土13.00 碳酸钙7.00 白云石3.00 硼酸0.66 碳酸锶7.00 碳酸锂2.00 骨灰3.00 氧化锌4.00。
4、根据权利要求2或3所述的高级日用瓷无铅熔块釉，其特征在于釉料的重量配料比为：熔块80～90％石英0～10％粘土4～10％瓷粉0～16％白云石0～4％碳酸锂0～2％硼酸钙0～6％。
CNB991204050A 1999-12-03 1999-12-03 高级日用瓷无铅熔块釉 Expired - Fee Related CN1171818C (zh)