CN101857463A - 一种陶瓷釉料及其制备方法 - Google Patents

一种陶瓷釉料及其制备方法 Download PDF

Info

Publication number
CN101857463A
CN101857463A CN201010192607A CN201010192607A CN101857463A CN 101857463 A CN101857463 A CN 101857463A CN 201010192607 A CN201010192607 A CN 201010192607A CN 201010192607 A CN201010192607 A CN 201010192607A CN 101857463 A CN101857463 A CN 101857463A
Authority
CN
China
Prior art keywords
percent
ceramic
powder
glaze
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201010192607A
Other languages
English (en)
Other versions
CN101857463B (zh
Inventor
刘权辉
曾学富
刘权耀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Guoci Yongfengyuan Co ltd
Original Assignee
Shenzhen Yong Feng Yuan Industry Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Yong Feng Yuan Industry Co ltd filed Critical Shenzhen Yong Feng Yuan Industry Co ltd
Priority to CN 201010192607 priority Critical patent/CN101857463B/zh
Publication of CN101857463A publication Critical patent/CN101857463A/zh
Application granted granted Critical
Publication of CN101857463B publication Critical patent/CN101857463B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种陶瓷釉料及其制备方法，所述陶瓷釉料包括：SiO2 40～60％，Al2O3 6～12％，CaO 5～10％，MgO 1～3％，P2O5 0～1％，SrO 0.5～2％，ZnO 3～10％，K2O 1～6.5％，Na2O 1～5％，Li2O0.5～4％，B2O3 1～5％，ZrO2 0～4％，Y2O3 0.2～4％，Rb2O 0.1～2％，HfO2 0.1～2％；各组分之和为100％。将本发明的釉料镶嵌在陶瓷坯体中，可以达到装饰产品的艺术效果，可以实现在陶瓷表面进行花色、花面等装饰的效果，可以克服目前陶瓷表面装饰存在的缺陷，同时又能丰富陶瓷的装饰手法。

Description

一种陶瓷釉料及其制备方法
技术领域
本发明属于陶瓷釉料技术领域，尤其是涉及一种可以用于陶瓷玲珑眼的玲珑陶瓷釉料及其制备方法。
背景技术
青花玲珑瓷是景德镇具有明显地方特色、闻名中外的传统品种，玲珑眼多为米粒状，也有水点状、浪花状和兰花瓣状、桃形、菱形等，俗称“芝麻漏”，又称“米花”，日本称“米通”、“萤手”，西方人把玲珑瓷器叫做“嵌玻璃的瓷器”。青花玲珑瓷产生于宋代，宋朝时景德镇制造了一种镂空瓷“香熏炉”，传说有一次由于窑温过高，瓷釉流动而无意地将香熏炉那些原该透烟气的空洞封闭了，形成透明而不透气的效果。在光线照射下，洞眼晶莹透亮，瓷工由此得到启发，于是有意识地在坯体上镂空形成孔眼状，然后填满透明釉入窑烧成。到明代永乐年间，形成有透明釉色的对称长方形的通花洞，因其玲珑剔透，加上以青花料描绘的花卉纹样，宋朝时景德镇制造了一种镂空瓷“香熏炉”，成为最初的青花玲珑。明成化年间，青花玲珑瓷制作达到一定的水平，玲珑眼虽大如黄豆，但极为平整，用手抚摸很难找到玲珑眼的部位，然而对光一照，透明的玲珑便跃然眼前。清代乾隆时，青花玲珑瓷已特别盛行，它是先在坯胎上选择合适的部位描绘青花，再镂雕花纹，使两面洞透，然后内外上釉，使镂空纹样部分透亮，同时在坯胎底部款书“玩玉”两字，“玩玉”两字的意思是青花玲珑瓷既可欣赏又能实用，就像玉色宝贝那样珍贵；青花玲珑瓷的艺术风格很独特，它采纳镂雕艺术的妙法，吸取青花艺术的特长，将两种装饰工艺相结合。在白中泛青的瓷胎上，斑斓透明的玲珑图案与青翠欲滴的青花纹样相映衬托，显得格外精巧细腻，朴素大方，清新明朗。因此，青花玲珑以莹、透、素雅的独特风姿和经久耐磨、不含铅毒、不易导热的优点被人们所赞赏和推崇。
但到目前为止，传统的玲珑陶瓷仍然采用一次高温烧成生产方式，产品表面质量差；玲珑眼的成孔率低，玲珑眼穿或漏不能修补，合格率低；玲珑眼中细小气泡多，造成玲珑眼透明度、通透性差；因产品在没有烧结前采取镂空的原因，造成产品的受力结构发生变化，当产品在高温烧成时易产生变形；生产的产品器型局限性大(多为小件、立体件产品)，对平面或大规格产品根本无法生产等缺陷。
发明内容
本发明的目的之一在于提供一种玲珑瓷用的陶瓷水晶透明釉料，通过特殊的工艺，将本发明的釉料镶嵌在陶瓷坯体中，可以实现装饰产品的艺术效果，其装饰效果可以实现在陶瓷表面进行花色、花面等装饰的效果，可以克服目前陶瓷表面装饰存在的缺陷，同时又能丰富陶瓷的装饰手法。
为实现上述目的，本发明采用如下技术方案：
一种陶瓷釉料，包括如下组分和含量：SiO2 40～60％，Al2O3 6～12％，CaO 5～10％，MgO 1～3％，P2O5 0～1％，SrO 0.5～2％，ZnO 3～10％，K2O 1～6.5％，Na2O 1～5％，Li2O 0.5～4％，B2O3 1～5％，ZrO2 0～4％，Y2O3 0.2～4％，Rb2O 0.1～2％，HfO2 0.1～2％；所述各组分之和为100％。
优选的是：
SiO2 50～55％，Al2O3 6～10％，CaO 6～10％，SrO 1～2％，ZnO 5～8％，K2O 3～6.5％，Na2O 1～3％，Li2O 0.5～2％，B2O3 1～4％，MgO 2～3％，P2O50～0.6％，ZrO2 1～2％，Y2O3 0.2～3％，Rb2O 1～2％，HfO2 0.8～2％；所述各组分之和为100％。
本发明的目的之二在于提供一种玲珑瓷用的陶瓷水晶透明釉料的制备方法，包括如下步骤：
(A1)取325目或者更细的网筛过筛的石英粉20～45％，取325目或者更细的网筛过筛的霞石粉20～40％，取325目或者更细的网筛过筛的高岭土0～18％，，硼砂2～16％，氧化锌2～7％，硅酸锆0～4％，三氧化二钇0.1～3％，碳酸钙6～16％，碳酸镁0～8％，五氧化二磷0～2％，碳酸锶0.5～6％，碳酸锂2～10％，氧化铷0～2.5％，二氧化铪0～3％；
(A2)将上述原料混合均匀后，在1450℃～1550℃熔化，放入冷水中水淬制成熔块；
(A3)将熔块装入球磨机中，加水、高铝球石和325目或者更细的网筛过筛的高岭土0～8％研磨成釉浆，细度控制在万孔筛余小于0.03％，然后经80～100℃烘干，并制成粉末过250目筛或者更细，将制成的干粉加入10～20％(重量分数)水混合搅拌均匀即可使用。
本发明与现有技术相比，具有如下优点和有益效果：
本发明通过优化玲珑眼釉料的配方，引入稀土化合物替代传统玲珑瓷用玲珑眼釉料中的釉果，可以使其具有合理的化学组成和较好的稳定性，达到提高玲珑眼釉料的通透度、高温黏度，拓宽玲珑眼釉料的烧成范围，使其更适合玲珑瓷生产工艺，提高玲珑眼的烧成合格率，同时减少玲珑眼釉料中的气泡，提高玲珑眼的通透度、透明度，使玲珑眼具有水晶通透的艺术效果。
具体实施方式
实施例1玲珑瓷用的陶瓷水晶透明釉料的制备
将石英粉(325目)38份，霞石粉(325目)：25份，硼砂12份，氧化锌3份，硅酸锆2份，三氧化二钇2份，碳酸钙6份，碳酸镁3份，五氧化二磷2份，碳酸锶3份，碳酸锂4份。将上述原料混合均匀后，在1400℃～1520℃熔化，放入冷水中水淬制成熔块。
将熔块装入球磨机中，加水、高铝球石和高岭土(4％)研磨成釉浆，细度控制在万孔筛余小于0.03％，然后经80℃温度条件下烘干，并制成粉末过250目筛，将制成的玲珑眼釉料，在按照料∶水＝10∶1的比例加入水，外加添加剂(CMC羧钾基纤维素0.5％)混合搅拌均匀，即可用于灌玲珑瓷的玲珑眼。
实施例2玲珑瓷用的陶瓷水晶透明釉料的制备
将石英粉(325目)25份，霞石粉(325目)：33份，硼砂8份，氧化锌5份，硅酸锆2份，三氧化二钇2.5份，碳酸钙10份，碳酸镁3.5份，五氧化二磷1份，碳酸锶2份，碳酸锂3份，氧化铷2份，二氧化铪3份。将上述原料混合均匀后，在1480℃熔化，放入冷水中水淬制成熔块。
将熔块装入球磨机中，加水、高铝球石和高岭上(8％)研磨成釉浆，细度控制在万孔筛余小于0.03％，然后经80℃烘干，并制成粉末过250目筛，将制成的玲珑眼釉料，在按照料∶水＝8∶1的比例加入水，外加添加剂(CMC羧钾基纤维素1.0％)混合搅拌均匀，即可用于灌玲珑瓷的玲珑眼。
实施例3玲珑瓷用的陶瓷水晶透明釉料的制备
将石英粉(325目)25份，霞石粉(325目)：25份，高岭土10份，硼砂11份，氧化锌5份，硅酸锆1份，三氧化二钇0.5份，碳酸钙8.5份，五氧化二磷5份，碳酸锶1份，碳酸锂5份，氧化铷2份，二氧化铪1份。将上述原料混合均匀后，在1450℃熔化，放入冷水中水淬制成熔块。
将熔块装入球磨机中，加水、高铝球石和高岭土(2％)研磨成釉浆，细度控制在万孔筛余小于0.03％，然后经80～100℃烘干，并制成粉末过250目筛，将制成的玲珑眼釉料，在按照料∶水＝4∶1的比例加入水，外加添加剂(CMC羧钾基纤维素0.5％)混合搅拌均匀，即可用于灌玲珑瓷的玲珑眼。
实施例4玲珑瓷用的陶瓷水晶透明釉料的制备
将石英粉(325目)25份，霞石粉(325目)：25份，高岭土10份，硼砂12份，氧化锌5份，硅酸锆1份，三氧化二钇0.5份，碳酸钙10.5份，五氧化二磷5份，碳酸锶1份，碳酸锂5份，氧化铷1份，二氧化铪2份。将上述原料混合均匀后，在1480℃熔化，放入冷水中水淬制成熔块。
将熔块装入球磨机中，加水、高铝球石和高岭土(0％)研磨成釉浆，细度控制在万孔筛余小于0.03％，然后经90℃烘干，并制成粉末过250目筛，将制成玲珑眼釉料，在按照料∶水＝6∶1的比例加入水，外加添加剂(CMC羧钾基纤维素1.5％)混合搅拌均匀，即可用于灌玲珑瓷的玲珑眼。
表1实施例中所用的原料的化学成分
Figure BSA00000145613600051
以上内容是结合具体的优选实施方式对本发明所作的进一步详细说明，不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干简单推演或替换，都应当视为属于发明型的保护范围。

Claims (4)

1.一种陶瓷釉料，包括如下组分和含量：SiO2 40～60％，Al2O36～12％，CaO 5～10％，MgO 1～3％，P2O5 0～1％，SrO 0.5～2％，ZnO 3～10％，K2O 1～6.5％，Na2O 1～5％，Li2O 0.5～4％，B2O3 1～5％，ZrO2 0～4％，Y2O3 0.2～4％，Rb2O 0.1～2％，HfO2 0.1～2％；所述各组分之和为100％。
2.如权利要求1所述的陶瓷釉料，其特征是：包括如下组分和含量：
SiO2 50～55％，Al2O3 6～10％，CaO 6～10％，SrO 1～2％，ZnO5～8％，K2O 3～6.5％，Na2O 1～3％，Li2O 0.5～2％，B2O3 1～4％，MgO 2～3％，P2O5 0～0.6％，ZrO2 1～2％，Y2O3 0.2～3％，Rb2O1～2％，HfO2 0.8～2％；所述各组分之和为100％。
3.一种陶瓷釉料的制备方法；包括如下步骤：
(A1)取325目或者更细的网筛过筛的石英粉20～45％，取325目或者更细的网筛过筛的霞石粉20～40％，取325目或者更细的网筛过筛的高岭土0～18％，硼砂2～16％，氧化锌2～7％，硅酸锆0～4％，三氧化二钇0.1～3％，碳酸钙6～16％，碳酸镁0～8％，五氧化二磷0～2％，碳酸锶0.5～6％，碳酸锂2～10％，氧化铷0～2.5％，二氧化铪0～3％；(A2)将上述原料混合均匀后，在1450℃～1550℃熔化，放入冷水中水淬制成熔块；
(A3)将熔块装入球磨机中，加水、高铝球石和325目或者更细的网筛过筛的高岭土0～8％研磨成釉浆，细度控制在万孔筛余小于0.03％，然后经80～100℃烘干，并制成粉末过250目筛或者更细，将制成的干粉加入10～20％(重量分数)水混合搅拌均匀即可使用。
4.权利要求1或者2所述的陶瓷釉料在制备陶瓷玲珑方面的应用。
CN 201010192607 2010-06-04 2010-06-04 一种陶瓷釉料及其制备方法 Active CN101857463B (zh)