CN1023698C - 一种用含钛炉渣制备陶瓷釉的配方 - Google Patents

一种用含钛炉渣制备陶瓷釉的配方 Download PDF

Info

Publication number
CN1023698C
CN1023698C CN 91107157 CN91107157A CN1023698C CN 1023698 C CN1023698 C CN 1023698C CN 91107157 CN91107157 CN 91107157 CN 91107157 A CN91107157 A CN 91107157A CN 1023698 C CN1023698 C CN 1023698C
Authority
CN
China
Prior art keywords
glaze
slag
ceramic
titanium slag
sio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 91107157
Other languages
English (en)
Other versions
CN1054410A (zh
Inventor
杨一芹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING SILICATE INST
Original Assignee
CHONGQING SILICATE INST
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING SILICATE INST filed Critical CHONGQING SILICATE INST
Priority to CN 91107157 priority Critical patent/CN1023698C/zh
Publication of CN1054410A publication Critical patent/CN1054410A/zh
Application granted granted Critical
Publication of CN1023698C publication Critical patent/CN1023698C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明是陶瓷釉的制备技术及配方。在含钛炉渣中加入必要的配合料，制备出陶瓷钛渣釉。制备钛渣釉，综合利用了我国的矿产资源，消除了大量排放钛渣造成的环境污染。钛渣釉可取代乳浊釉，成本低；加入色釉后，能得到各种彩色的艺术装饰釉，施于陶瓷制品表面，烧成后能提高陶瓷制品的商品档次。

Description

本发明是陶瓷釉的制备技术及配方。
用低质原料（如页岩、工业废渣、尾矿等）为主要原料生产陶瓷制品，必须使用遮盖力强的乳浊釉或色釉来提高产品的釉面质量。乳浊釉主要有以锡为乳浊剂的锡釉和以锆为乳浊剂的锆釉。近年来，含钛的乳浊釉也已得到生产应用。这些乳浊釉价格昂贵。
国外对利用炉渣制造陶瓷釉进行过大量研究，并已进入实用阶段。但那些研究结果只适用于他们国家的矿产资源及炉渣情况。
我国有含钛量高的铁矿，冶炼后排出的炉渣中百分比成分为：TiO2，22-26;CaO，20-27;SiO2，20-25;Al2O3，5-8;以及其他氧化物。这种含钛炉渣称为钛渣。
为了消除炼铁厂大量排放钛渣所造成的环境污染，综合利用我国的矿产资源，我们发明了一种用含钛炉渣制备陶瓷釉的方法。
所发明的一种用含钛炉渣制备陶瓷釉的方法，根据陶瓷坯体的性质、工艺及质量要求，可以在制备陶瓷釉时加入熔块釉，也可不加熔块釉。表1列出了五种适用熔块釉的化学成分。
表1
编号 SiO2ZrO2Al2O3B2O3CaO MgO ZnO PbO
1    52.92    8.50    5.75    9.00    1.14    3.51    5.80    1.90
2    57.25    9.41    5.21    13.62    1.00    0.13    1.82    -
3    59.82    1.34    5.55    12.02    1.69    1.29    1.46    3.17
4    55.37    9.79    5.92    7.33    4.42    -    8.14    -
5    51.77    9.67    4.81    11.62    5.75    -    7.83    -
续表1
编号 SrO BaO K2O Na2O
1    3.48    0.38    3.43    5.05
2    3.05    2.27    1.87    4.38
3    3.09    -    3.18    6.32
4    -    -    5.23    4.00
5    -    -    4.50    4.08
按上表任一编号的化学成分配成实用原料配比，拌匀，在1350-1450℃温度下熔化，经高温水淬，成为碎块状。即得到熔块釉。
把钛渣、熔块釉及其他原料按下述百分比含量配合：钛渣，10-35;熔块釉，0-80;长石，0-40;粘土，0-10;页岩，0-15;方解石，0-15;石灰石，0-15。
配合好的物料，以料比水为1∶0.55的比例混合球磨，磨至万孔筛筛余量小于0.5%为宜。即得到钛渣陶瓷釉釉浆;或称为钛渣釉釉浆。将钛渣釉釉浆施于陶瓷坯体表面，在适当温度下锻烧，烧成后的釉面呈浅黄色。
要提高钛渣釉釉浆与陶瓷坯体的附着强度，可以在釉浆中加入适量的电解质，如三聚磷酸钠、羧甲基纤维素等。
要得到各种颜色的彩色面釉，可以在上述配合料中加入0-5%的着色剂，一起球磨。这样得到的釉浆，施用烧成后可成为艺术装饰效果好的彩色釉面。
用所发明的方法制备钛渣釉，综合利用了我国的矿产资源，消除了大量排放钛渣造成的环境污染。在低质原料陶瓷制品表面施用，可取代价格昂贵的乳浊釉，降低陶瓷制品的成本。若再加入各种色釉，可获得绚丽多彩的艺术效果，提高陶瓷制品的商品档次。
所发明的一种用含钛炉渣制备陶瓷釉的方法的最好方案是：
熔块釉化学成分采用表1中编号为3的组成。
熔块釉面砖上，效果最好的钛渣釉的百分比配方为：钛渣，20;熔块釉，75;粘土5;烧成温度，1050-1100℃。
施于墙地砖和细陶器表面，效果最好的钛渣釉的百分比配方为：钛渣，35;熔块釉25;长石，25;粘土，5;页岩，10。烧成温度，1120-1135℃。
旋于墙地砖和细陶器表面，不含熔块釉的效果最好的钛渣釉的百分比配方为：钛渣35;长石，40;粘土，5;页岩，10;方解石，10。烧成温度，1120-1200℃。

Claims (1)

1、一种用炉渣中百分比成分为，TiO2，22～26；CaO，20～27；SiO220～25；Al2O3，5～8；以及其他氧化物的含钛渣来制备陶瓷釉的方法，其原料成分百分比含量特征是：钛渣，10～35；长石，0～40；粘土，0～10；页岩，0～15；着色剂，0～5；石灰石，0～15；方解石，0～15；以及各氧化物含量百分比为SiO252.92，ZrO28.50，Al2O35.75，B2O39.00，CaO1.14，MgO3.51，ZnO5.80，PbO1.90，SrO3.48，BaO0.38，K2O，3.43，Na2O5.05；或者为SiO257.25，ZrO29.41，Al2O35.21，B2O313.62，CaO1.00，MgO0.13，ZnO1.82，SrO3.05，BaO2.27，K2O1.87，NaO4.38；或者为SiO259.82，ZrO21.34，Al2O35.55，B2O312.02，CaO1.69，MgO1.29，ZnO1.64，PbO3.17，SrO3.09，K2O3.18，NaO6.32；或者为SiO255.37，ZrO29.79，Al2O35.92，B2O37.33，CaO4.42，ZnO8.14，K2O5.23，Na2O4.00；或者为SiO251.77，ZrO29.67，Al2O34.81，B2O311.62，CaO5.72，ZnO7.83，K2O4.50，Na2O4.08的熔块釉，0～80。
CN 91107157 1991-03-08 1991-03-08 一种用含钛炉渣制备陶瓷釉的配方 Expired - Fee Related CN1023698C (zh)