CN114784380A - 一种电解液及其电化学装置和电子装置 - Google Patents

一种电解液及其电化学装置和电子装置 Download PDF

Info

Publication number
CN114784380A
CN114784380A CN202210593780.XA CN202210593780A CN114784380A CN 114784380 A CN114784380 A CN 114784380A CN 202210593780 A CN202210593780 A CN 202210593780A CN 114784380 A CN114784380 A CN 114784380A
Authority
CN
China
Prior art keywords
electrolyte
substituted
unsubstituted
lithium
active material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202210593780.XA
Other languages
English (en)
Inventor
王仁和
王子沅
余乐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Envision Power Technology Jiangsu Co Ltd
Envision Ruitai Power Technology Shanghai Co Ltd
Original Assignee
Envision Power Technology Jiangsu Co Ltd
Envision Ruitai Power Technology Shanghai Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Envision Power Technology Jiangsu Co Ltd, Envision Ruitai Power Technology Shanghai Co Ltd filed Critical Envision Power Technology Jiangsu Co Ltd
Publication of CN114784380A publication Critical patent/CN114784380A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种电解液及其电化学装置和电子装置。一种电解液，包含二氟磷酸锂和式(I)所示的化合物，基于所述电解液的质量，所述二氟磷酸锂的质量含量为A％，所述式(I)所示的化合物的质量含量为B％，A+B的取值范围为0.5至7.5，A/B的取值范围为0.07至20。本发明的电解液可以改善电化学装置的高温、室温循环性能，同时降低电化学装置的内阻。

Description

一种电解液及其电化学装置和电子装置
本申请要求申请号为202110592885.9专利申请的优先权(在先申请的申请日为2021年5月28日，发明名称为一种锂电池用非水电解液及其制备方法和锂离子电池，申请人为远景动力技术(江苏)有限公司)。
技术领域
本发明涉及电解液技术领域，尤其涉及一种电解液及其电化学装置和电子装置。
背景技术
由于锂离子电池具有高电压、高容量的重要优点，且循环寿命长、安全性能好，使其在便携式电子设备、电动汽车、空间技术、国防工业等多方面具有广阔的应用前景。
电解液为锂电池的“血液”，是锂电池四大关键原材料之一，是电池中离子传输的载体，在正负极之间起到传导锂离子的作用，对锂电池的能量密度、比容量、工作温度范围、循环寿命、安全性能等均有重要影响。
为了研发出合适的高性能电解液，往往会在电解液中添加合适的电解液添加剂，常用的电解液添加剂包括含硼添加剂、有机磷类添加剂、碳酸酯类添加剂、羧酸酯类添加剂、含硫添加剂离子液体添加剂等。
但是，常用的VC等负极成膜添加剂在产生保护效果的同时具有高内阻的特点，因此难以兼顾高温和室温循环性能以及低电阻的特点。
当前，锂离子电池非水电解液中主要使用的锂盐和锂盐添加剂包括六氟磷酸锂(LiPF6)、二氟磷酸锂(LiPO2F2)、二氟双草酸磷酸锂、四氟硼酸锂、二氟草酸硼酸锂、双草酸硼酸锂、双(三氟甲基磺酰)亚胺锂和双氟磺酰亚胺锂中的一种或多种。但是，目前采用这些锂盐较难实际参与到负极成膜过程中，导致降阻抗效果大打折扣。
发明内容
针对现有技术的不足，本发明的目的在于提供一种电解液及其电化学装置和电子装置，本发明的电解液可以改善电化学装置的高温、室温循环性能，同时降低电化学装置的内阻。本发明的目的之一在于提供一种电解液，为达此目的，本发明采用以下技术方案：
一种电解液，包含二氟磷酸锂和式(I)所示的化合物：：
Figure BDA0003666771350000021
其中，R1、R3、R4各自独立地选自氢、氰基、取代或未取代的C1-12的烃基、取代或未取代的C1-12的碳氧基、取代或未取代的C6-26的芳基、取代或未取代的C2-12的酰胺基、取代或未取代的C0-12的磷酸酯基、取代或未取代的C0-12的磺酰基、取代或未取代的C0-12的硅氧基或取代或未取代的C0-12的硼酸酯基，经取代时，取代基包括卤素原子；
基于所述电解液的质量，所述二氟磷酸锂的质量含量为A％，A的取值范围为0.1至2，所述式(I)所示的化合物的质量含量为B％，B的取值范围为0.1至7，A+B的取值范围为0.5至7.5，A/B的取值范围为0.07至20。
本发明的电解液，通过式(I)所示的化合物和二氟磷酸锂配合使用，并通过调整二者的用量配比，可以改善电化学装置的高温、室温循环性能，同时降低电化学装置的内阻。
A的取值范围为0.1至2，例如为0.1、0.2、0.3、0.4、0.5、0.6、0.7、0.8、0.9、1、1.1、1.2、1.3、1.4、1.5、1.6、1.7、1.8、1.9、2等。如果A太小，会使降阻抗效果不明显，如果A太大，会使导致结晶析出，影响电池性能；
B的取值范围为0.1至7，例如为0.1、0.2、0.3、0.4、0.5、0.6、0.7、0.8、0.9、1、1.1、1.2、1.3、1.4、1.5、1.6、1.7、1.8、1.9、2、2.1、2.2、2.3、2.4、2.5、2.6、2.7、2.8、2.9、3、3.1、3.2、3.3、3.4、3.5、3.6、3.7、3.8、3.9、4、4.1、4.2、4.3、4.4、4.5、4.6、4.7、4.8、4.9、5、5.1、5.2、5.3、5.4、5.5、5.6、5.7、5.8、5.9、6、6.1、6.2、6.3、6.4、6.5、6.6、6.7、6.8、6.9或7等。如果式(I)所示的化合物的用量太少，少于0.1％，会使成膜效果不明显；如果式(I)所示的化合物的用量太多，多于7％，会使阻抗剧增。
A+B的取值范围为0.5至7.5，例如为0.5、0.6、0.7、0.8、0.9、1、1.1、1.2、1.3、1.4、1.5、1.6、1.7、1.8、1.9、2、2.1、2.2、2.3、2.4、2.5、2.6、2.7、2.8、2.9、3、3.1、3.2、3.3、3.4、3.5、3.6、3.7、3.8、3.9、4、4.1、4.2、4.3、4.4、4.5、4.6、4.7、4.8、4.9、5、5.1、5.2、5.3、5.4、5.5、5.6、5.7、5.8、5.9、6、6.1、6.2、6.3、6.4、6.5、6.6、6.7、6.8、6.9、7、7.1、7.2、7.3、7.4或7.5等。如果A+B太小，会使改善效果不显著，如果A+B太大，会使化合物结晶析出，对电池改进效果变差；
A/B的取值范围为0.07至20，例如为0.02、0.03、0.04、0.05、0.06、0.07、0.08、0.09、0.1、0.5、1、2、3、4、5、6、7、8、9、10、15、20等。如果A/B太小，会使锂盐添加相对过少，降阻抗效果不理想，如果A/B太大，会使成膜添加剂相对过少，成膜效果差，电池稳定性受影响；
本发明中，作为优选方案，A+B的取值范围为1至5.5，A/B的取值范围为0.1至1.5。
所述的电解液中，R1、R3、R4各自独立地选自氢、取代或未取代的C1-12的烃基；R2选自C1-12的取代或未取代的烃基，经取代时，取代基为卤素原子。
其中，作为说明，C1-12的烃基，是指含有碳原子数为1至12的烃基。
所述式(I)所示的化合物为富马酸二甲酯
Figure BDA0003666771350000041
甲基丙烯酸甲酯
Figure BDA0003666771350000042
顺丁烯二酸二甲酯
Figure BDA0003666771350000043
甲基丙烯酸1,1,1,3,3,3-六氟异丙酯
Figure BDA0003666771350000044
甲基丙烯酸乙烯酯
Figure BDA0003666771350000045
中的任意一种或两种以上的混合物。所述混合物典型但非限制的组合为两种、三种、四种或5种的混合物，例如为富马酸二甲酯、甲基丙烯酸甲酯的混合物，富马酸二甲酯、顺丁烯二酸二甲酯的混合物，富马酸二甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯的混合物，富马酸二甲酯、甲基丙烯酸乙烯酯的混合物，富马酸二甲酯、甲基丙烯酸甲酯、顺丁烯二酸二甲酯的混合物，富马酸二甲酯、甲基丙烯酸甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯的混合物，富马酸二甲酯、甲基丙烯酸甲酯、甲基丙烯酸乙烯酯的混合物，甲基丙烯酸甲酯、顺丁烯二酸二甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯的混合物，甲基丙烯酸甲酯、顺丁烯二酸二甲酯、甲基丙烯酸乙烯酯的混合物，顺丁烯二酸二甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯、甲基丙烯酸乙烯酯的混合物，富马酸二甲酯、甲基丙烯酸甲酯、顺丁烯二酸二甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯的混合物，富马酸二甲酯、甲基丙烯酸甲酯、顺丁烯二酸二甲酯、甲基丙烯酸乙烯酯的混合物，甲基丙烯酸甲酯、顺丁烯二酸二甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯、甲基丙烯酸乙烯酯的混合物，富马酸二甲酯、甲基丙烯酸甲酯、顺丁烯二酸二甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯、甲基丙烯酸乙烯酯的混合物。
本发明的目的之二在于提供一种电化学装置，包括负极、正极和目的之一所述的电解液。
本申请的电化学装置包括发生电化学反应的任何装置，它的具体实例包括所有种类的一次电池、二次电池、燃料电池、太阳能电池或电容。特别地，该电化学装置是锂二次电池，包括锂金属二次电池、锂离子二次电池、锂聚合物二次电池或锂离子聚合物二次电池。
在一些实施例中，本申请的电化学装置是具备具有能够吸留、放出金属离子的正极活性物质的正极以及具有能够吸留、放出金属离子的负极活性材料的负极的电化学装置。
所述正极包含正极活性材料，所述正极活性材料选自磷酸铁锂、锂镍过渡金属复合氧化物、具有尖晶石结构的锂镍锰复合氧化物的任意一种或两种以上的混合物。
所述负极包括负极活性材料和集流体，所述负极活性材料包括石墨。
所述硅碳负极活性材料选自硅、硅氧化合物和硅基合金中的任意一种或两种以上的混合物。
所述负极还包括碳材料，所述碳材料选自乙炔黑、导电炭黑、碳纤维、碳纳米管和科琴黑中的任意一种或两种以上的混合物。
本发明的目的之三在于提供一种电子装置，所述电子装置包括目的之二所述的电化学装置。
所述电子装置包括但不限于如下类型，例如笔记本电脑、笔输入型计算机、移动电脑、电子书播放器、便携式电话、便携式传真机、便携式复印机、便携式打印机、头戴式立体声耳机、录像机、液晶电视、手提式清洁器、便携CD机、迷你光盘、收发机、电子记事本、计算器、存储卡、便携式录音机、收音机、备用电源、电机、汽车、摩托车、助力自行车、自行车、照明器具、玩具、游戏机、钟表、电动工具、闪光灯、照相机、家庭用大型蓄电池或锂离子电容器等。
与现有技术相比，本发明的有益效果为：
本发明的电解液，通过添加式(I)所示的化合物，并与二氟磷酸锂配合使用，通过调整用量，可使负极表面成膜得到改善，优化内阻，使得电化学装置具有更好的高温、室温循环性能、高温存储性能，实现更低的内阻。
具体实施方式
下面并通过具体实施方式来进一步说明本发明的技术方案。
如无具体说明，本发明的各种原料均可市售购得，或根据本领域的常规方法制备得到。
本发明的电解液，包含二氟磷酸锂和式(I)所示的化合物：
Figure BDA0003666771350000061
其中，R1、R3、R4各自独立地选自氢、氰基、取代或未取代的C1-12的烃基、取代或未取代的C1-12的碳氧基、取代或未取代的C6-26的芳基、取代或未取代的C2-12的酰胺基、取代或未取代的C0-12的磷酸酯基、取代或未取代的C0-12的磺酰基、取代或未取代的C0-12的硅氧基或取代或未取代的C0-12的硼酸酯基，经取代时，取代基包括卤素原子；基于所述电解液的质量，二氟磷酸锂的质量含量为A％，A的取值范围为0.1至2，式(I)所示的化合物的质量含量为B％，B的取值范围为0.1至7，A+B的取值范围为0.5至7.5，A/B的取值范围为0.07至20。
本发明中，电化学装置为锂离子电池，锂离子电池为一次锂电池或二次锂电池，包括：正极、负极、位于正极和负极之间的隔膜以及电解液。
本发明的二次锂电池的制备方法如下：
(1)LFP(LiFePO4)正极的制备：
将正极活性材料(LiFePO4)、作为粘结剂的聚偏氟乙烯以及作为导电剂的Super P按照重量比97:2:1进行混合后，加入N-甲基吡咯烷酮(NMP)，在真空搅拌机作用下搅拌至体系呈均一透明状，获得正极浆料；将正极浆料均匀涂覆于铝箔上；将铝箔在室温晾干后转移至烘箱干燥，然后经过冷压、分切得到正极(极片)；
(2)石墨负极的制备：
将人造石墨作为负极活性材料、Super P作为导电剂、羧甲基纤维素钠(CMC-Na)作为增稠剂、丁苯橡胶(SBR)作为粘结剂，按质量比96:1:1:2进行混合，加入去离子水，在真空搅拌机作用下获得负极浆料；将负极浆料均匀涂覆在负极集流体铜箔上；将铜箔在室温晾干后转移至烘箱干燥，然后经过冷压、分切得到负极(极片)；
(3)电解液的制备：
在含水量<10ppm的氩气气氛手套箱中，将电池级碳酸乙烯酯(EC)与碳酸甲乙酯(EMC)按照配比进行混合，形成有机溶剂。按照后述表格所述电解液组成定量加入其他成分，混合均匀，得到电解液。表中各成分含量为基于电解液的总重量计算得到的重量百分数；下文中表示电解液成分的“FEC”为氟代碳酸乙烯酯，“VC”为碳酸亚乙烯酯。
(4)隔离膜的制备：
以聚丙烯膜作为隔离膜；
(5)二次电池的制备：
以厚度12μm的聚丙烯薄膜(PP)作为隔离膜，将上述制得的正极、隔离膜、负极依次进行叠片，使隔离膜处于正、负极中间起到隔离的作用。然后外包铝塑膜，转移至真空烘箱中120℃干燥，注入上述制得的电解液3.0g/Ah之后封口，进行电解液化成，最终制备得容量为1Ah的软包电池(即锂离子电池)。
本发明制得的锂离子电池，负极克容量为350mAh/g，注液系数为3g/Ah，电芯容量为1Ah，负极质量为3g，电解液质量为3g。
电解液在本发明涉及的铁锂电芯中的化成条件如下所述。
所述电解液在铁锂电芯的化成步骤具体为：将电解液进行注液后，保持0.1MPa的热压环境，以静置状态在45℃下以0.02C充电17min，静置5min后再以0.02C充到0.3Ah，之后割去气袋并真空封装，常温静置48h，从而使电解液完成化成。
其中，本发明的示例中，式(I)所示的化合物采用以下五种，化合物1为甲基丙烯酸甲酯，化合物2为富马酸二甲酯，化合物3为顺丁烯二酸二甲酯，化合物4为甲基丙烯酸1,1,1,3,3,3-六氟异丙酯，化合物5为甲基丙烯酸乙烯酯。
本发明的二次电池可以通过如下方法进行测试：
(1)二次电池循环测试
在指定温度(室温25℃或高温45℃)的烘箱内，以1C的电流在指定电位区间内进行循环充放电，记录每一圈的放电容量，当电池容量到达首圈容量80％时结束测试。
(2)二次电池直流电阻(DCR)测试
在指定温度下，将电池以1C电流放电至50％SOC(荷电状态，反映电池的剩余容量)时，将电流调高至4C，并保持30s，检测更新的稳定电压与原平台电压的差，其数值与3C电流值的比值即为电池的直流电阻。电池首次满充后进行的DCR测试结果为电池的初始DCR。
(3)二次电池高温存储容量保持率测试
将二次电池充满电后放置在60℃的恒温箱中，30天后取出，待冷却到室温后以0.33C倍率放电至截止电压，对照其容量相对于初始放电容量的百分比。
其中，充放电的截止电压具体如下：
LFP-石墨是2.5V至3.65V。
(4)隔膜HF(氢氟酸)吸附能力的测试
在氩气气氛下，在包含0.1～6.0mol/L的LiPF6的环状和/或链状碳酸酯混合液中添加蒸馏水，从而制备HF浓度为10～10000ppm的非水电解液，在23℃下保存2周，从而制备包含800ppm的HF的非水电解质。将该非水电解质100质量份以及隔膜无机颗粒8质量份投入聚丙烯制密闭容器中，在23℃下振动搅拌5分钟。之后，用孔径0.2微米的PTFE制膜过滤器进行过滤。通过离子色谱分析对该滤液中的氟化物离子浓度进行定量，并计算HF浓度。HF浓度低于720ppm的记为HF吸附能力：“有”，720ppm以上的记为HF吸附能力：“无”。
本发明的实施例1至11，对比例1、对比例2的电解液组成如表1-1所示，采用上述制备方法制备锂离子电池，对其性能进行测试，测试结果如表1-2所示。
表1-1
Figure BDA0003666771350000091
Figure BDA0003666771350000101
注：“-”代表未添加，下同。
表1-2
Figure BDA0003666771350000102
Figure BDA0003666771350000111
由表1-2的数据可以看出，相对于对比例1、对比例2的式(I)所示的化合物不与LiPO2F2配合使用，本发明实施例1-11由于式(I)所示的化合物与LiPO2F2配合使用，制得的电池的高温、室温循环性能、高温存储性能更好，电阻更低，实施例1至实施例11的室温循环80％圈数为1416至1739，高温循环80％圈数为1131至1404，初始DCR为95至101mOhm(毫欧姆)，60℃存储30天容量保持率为88至95％，该各项测试结果都不同程度的优于对比例1、对比例2；特别是式(I)所示的化合物与LiPO2F2配合使用，两者用量之和(A+B)为0.5至7.5时，式(I)所示的化合物与LiPO2F2的用量比(A/B)为0.1至1.5时，效果更好。
实施例12至实施例15
实施例12至实施例15的电解液组成与实施例3的区别在于式(I)所示的化合物种类不同，实施例3采用化合物1，实施例12采用化合物2，实施例13采用化合物3，实施例14采用化合物4，实施例15采用化合物5，其他的与实施例3的均相同。
采用上述制备方法制备锂离子电池，对其性能进行测试，测试结果如表2所示。
表2
Figure BDA0003666771350000112
Figure BDA0003666771350000121
由表2数据可以看出，相对于对比例1不加式(I)所示的化合物，实施例3、实施例12至实施例15，式(I)所示的化合物采用不同种类，均能使电池的高温、室温循环性能、高温存储性能更好，电阻更低。
实施例16
本实施例与实施例3的区别之处在于，所用隔膜不具有HF(氢氟酸)吸附能力，而实施例3所用隔膜具有HF吸附能力。
表3
Figure BDA0003666771350000122
由于LiPF6和LiPO2F2参与负极成膜添加剂反应的过程中会产生HF，因此有必要使用具备HF吸附能力的隔膜，保障电池性能，避免HF对正负极的腐蚀。
本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程，但本发明并不局限于上述详细工艺设备和工艺流程，即不意味着本发明必须依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。
以上详细描述了本发明的优选实施方式，但是，本发明并不限于上述实施方式中的具体细节，在本发明的技术构思范围内，可以对本发明的技术方案进行多种简单变型，这些简单变型均属于本发明的保护范围。
另外需要说明的是，在上述具体实施方式中所描述的各个具体技术特征，在不矛盾的情况下，可以通过任何合适的方式进行组合，为了避免不必要的重复，本发明对各种可能的组合方式不再另行说明。
此外，本发明的各种不同的实施方式之间也可以进行任意组合，只要其不违背本发明的思想，其同样应当视为本发明所公开的内容。

Claims (10)

1.一种电解液，其特征在于，包含二氟磷酸锂和式(I)所示的化合物：
Figure FDA0003666771340000011
其中，R1、R3、R4各自独立地选自氢、氰基、取代或未取代的C1-12的烃基、取代或未取代的C1-12的碳氧基、取代或未取代的C6-26的芳基、取代或未取代的C2-12的酰胺基、取代或未取代的C0-12的磷酸酯基、取代或未取代的C0-12的磺酰基、取代或未取代的C0-12的硅氧基或取代或未取代的C0-12的硼酸酯基，经取代时，取代基包括卤素原子；
基于所述电解液的质量，所述二氟磷酸锂的质量含量为A％，所述式(I)所示的化合物的质量含量为B％，A+B的取值范围为0.5至7.5，A/B的取值范围为0.07至20。
2.根据权利要求1所述的电解液，其特征在于，A+B的取值范围为1至5.5。
3.根据权利要求1所述的电解液，其特征在于，A/B的取值范围为0.1至1.5。
4.根据权利要求1所述的电解液，其特征在于，A的取值范围为0.1至0.5。
5.根据权利要求1所述的电解液，其特征在于，B的取值范围为0.5至3。
6.根据权利要求1所述的电解液，其特征在于，R1、R3、R4各自独立地选自氢、取代或未取代的C1-12的烃基；R2选自C1-12的取代或未取代的烃基，经取代时，取代基为卤素原子。
7.根据权利要求1所述的电解液，其特征在于，所述式(I)所示的化合物为富马酸二甲酯、甲基丙烯酸甲酯、顺丁烯二酸二甲酯、甲基丙烯酸1,1,1,3,3,3-六氟异丙酯、甲基丙烯酸乙烯酯中的任意一种或两种以上的混合物。
8.一种电化学装置，其特征在于，包含负极、正极和权利要求1至7的任一项所述的电解液。
9.根据权利要求8所述的电化学装置，其特征在于，所述负极包括负极活性材料和集流体，所述负极活性材料包括石墨；
所述硅碳负极活性材料选自硅、硅氧化合物和硅基合金中的任意一种或两种以上的混合物；
所述正极包含正极活性材料；所述正极活性材料选自磷酸铁锂、锂镍过渡金属复合氧化物、具有尖晶石结构的锂镍锰复合氧化物的任意一种或两种以上的混合物；
所述隔膜对HF具有吸附能力。
10.一种电子装置，其特征在于，包含权利要求8或9所述的电化学装置。
CN202210593780.XA 2021-05-28 2022-05-27 一种电解液及其电化学装置和电子装置 Pending CN114784380A (zh)