CN114721229B - 一种新型非对称性紫外曝光方法 - Google Patents
一种新型非对称性紫外曝光方法 Download PDFInfo
- Publication number
- CN114721229B CN114721229B CN202210271740.3A CN202210271740A CN114721229B CN 114721229 B CN114721229 B CN 114721229B CN 202210271740 A CN202210271740 A CN 202210271740A CN 114721229 B CN114721229 B CN 114721229B
- Authority
- CN
- China
- Prior art keywords
- curable material
- asymmetric
- exposure method
- absorber
- wavelength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种非对称性紫外曝光方法及其中使用的紫外可固化材料，以及使用它制造的金属网格传感器，所述方法包括将第一紫外可固化材料施加在光学透明基材的一侧上，将第二紫外可固化材料施加在所述光学透明基材的另一侧上，并且将所述光学透明基材的两侧同时分别曝光于紫外光，其中，所述第一紫外可固化材料的紫外吸收峰低于所述第二紫外可固化材料的紫外吸收峰，所述紫外光分别具有与对应侧的紫外可固化材料的紫外吸收峰相对应的波长，并且所述第二紫外可固化材料包含紫外吸收剂。本发明的方法可以进一步降低非对称性紫外曝光方法中两侧不同的紫外光对另一侧的涂层带来的影响。
Description
技术领域
本发明属于金属网格触控传感器领域，更具体地，涉及一种可以应用于光学透明基材(不管是否有紫外阻隔功能)的非对称性紫外曝光方法。
背景技术
基于柔性基材的金属网格触控传感器因具备优越的柔性、优异的光学性能和较低的制造成本等优点而广受关注。目前主流的GF2(触控网格在同一基材的上下两侧分布)结构要求在基材的每一侧形成独特的微图案，并且相互不存在干涉，这需要材料及工艺的技术支撑。通常的实现方式一是通过两个或者多个重复的曝光、显影制程后再进行蚀刻或者湿法镀金属工艺；二是通过双面同时曝光工艺制程后再进行显影及湿法镀金属工艺，但该工艺要求光学透明基材具有紫外阻隔功能(例如某个紫外波段的阻隔率大于90％)，以保证来自一侧的紫外光不会穿透基材干涉另一侧的图案。
但是上述的技术方案中，要么存在工艺复杂，产品良率低，生产成本高等问题；要么基板的可用选项非常有限，不仅需要基材供应商配合开发，并且通常会牺牲基板的光学性能，例如较低的透光率和较高的雾度，这对于拓展金属网格触控传感器更广泛的应用是不利的。
本申请人在之前的一篇专利(PCT申请号为PCT/CN2021/100610)中公开了一种非对称性紫外曝光方法，其包括将紫外可固化涂层#1(以下简称涂层#1)施加在光学透明基板的一侧上，并将紫外可固化涂层#2(以下简称涂层#2)施加在所述光学透明基板的另一侧上，并且将所述光学透明基板的两侧同时曝光于紫外光，其中所述涂层#1与所述涂层#2在不同的波长处具有紫外吸收峰。优选地，涂层#2使用365nm或者以上更高波长的紫外光固化，而涂层#1使用314nm固化。
但经过申请人的进一步研究，一般的高波长固化用光引发剂在低波长的波长处也可能存在一定程度的吸收，所以低波长涂层在较低的曝光能量下也可能使高波长涂层发生一定的固化，因此为了避免影响，通常可以通过降低低波长光阻的曝光能量及减少高波长光阻配方中光引发剂量或调整高波长光阻配方中光引发种类来实施非对称曝光。然而，降低低波长涂层的曝光能量或降低高波长中光引发剂的量可能导致固化不足，使得光阻涂层固化后在基材表面粘附力降低，从而带来新的问题，因此对非对称性紫外曝光工艺的进一步开发及改进仍存在挑战。
发明内容
本发明的目的在于克服现有技术的上述缺陷，对非对称性紫外曝光方法进行进一步改进，从而进一步降低非对称性紫外曝光方法中两侧不同的紫外光对另一侧的涂层带来的影响。
为了实现上述目的，在一方面，本发明提供了一种非对称性紫外曝光方法，其包括将第一紫外可固化材料施加在光学透明基材的一侧上，将第二紫外可固化材料施加在所述光学透明基材的另一侧上，并且将所述光学透明基材的两侧同时分别曝光于紫外光，其中，所述第一紫外可固化材料的紫外吸收峰低于所述第二紫外可固化材料的紫外吸收峰，所述紫外光分别具有与对应侧的紫外可固化材料的紫外吸收峰相对应的波长，并且所述第二紫外可固化材料包含紫外吸收剂。
除非另有定义，本文使用的所有术语(包括技术和科学术语)具有与本发明所属领域的普通技术人员通常理解的相同的含义。还应当理解，诸如在通常使用的字典中定义的那些术语应该被解释为具有与它们在相关技术的上下文中的含义一致的含义，并且不会以理想化或过度形式化的含义来解释，除非在此明确地定义。
应当理解，尽管术语“第一”，“第二”等在本文中可以用于描述各种元件，但是这些元件不应受这些术语限制。这些术语仅用于将一个元件与另一个元件区分开。例如，在不脱离本发明范围的情况下，第一元件可以被称为第二元件，并且类似地，第二元件可以被称为第一元件。
具体地，在本发明中，虽然限定了所述第一紫外可固化材料的紫外吸收峰低于所述第二紫外可固化材料的紫外吸收峰，但这仅用于区分两种不同的紫外可固化材料，当两者的编号进行互换时，即为所述第二紫外可固化材料的紫外吸收峰低于所述第一紫外可固化材料的紫外吸收峰。
根据本发明，为了使得所述第一紫外可固化材料于所述第二紫外可固化材料在紫外吸收峰上尽可能地区分开，在一个优选的实施方式中，所述第一紫外可固化材料与所述第二紫外可固化材料的紫外吸收峰之间的波长差异可以为至少10nm，例如20nm、30nm、40nm、50nm、60nm、80nm或100nm等。
根据本发明，对所述紫外可固化材料的种类没有特别限制，并且可以为本领域中常见的光刻胶。在一个实施方式中，所述第一紫外可固化材料和所述第二紫外可固化材料各自独立地选自由正性光刻胶和负性光刻胶组成的组。换句话说，所述第一紫外可固化材料和所述第二紫外可固化材料两者可以均为正性光刻胶；所述第一紫外可固化材料和所述第二紫外可固化材料两者可以均为负性光刻胶；或者所述第一紫外可固化材料和所述第二紫外可固化材料中的一者为正性光刻胶，且另一者为负性光刻胶。
此外，所述光刻胶的类型可以根据实际需要进一步选择。在一个实施方式中，所述正性光刻胶可以优选地包含曝光后可溶于显影液的树脂材料，并且所述负光刻胶可以优选地包含曝光后不溶于显影液的树脂材料。所述显影液通常是含有碱性化合物和表面活性剂的水溶液，碱性化合物可以是无机或有机碱性化合物，这些无机和有机碱性化合物可以单独使用或两种以上组合使用；而作为表面活性剂，可以使用选自由非离子表面活性剂、阴离子表面活性剂和阳离子表面活性剂所组成的组中的至少一种，这些表面活性剂可以单独使用，也可以两种以上组合使用。
根据本发明，所述第一紫外可固化材料和所述第二紫外可固化材料各自包含光引发剂(也称为敏化剂或感光剂等)，以便允许所述第一紫外可固化材料和所述第二紫外可固化材料在不同的波长处具有紫外吸收峰。在一个实施方式中，所述第一紫外可固化材料与所述第二紫外可固化材料的紫外吸收峰之间的波长差异可以通过使用在不同的波长下具有紫外吸收峰的两种不同的光引发剂来实现。因此，本发明的所述第一紫外可固化材料和所述第二紫外可固化材料通常包含不同的光引发剂。
进一步地，对本发明的光引发剂的种类没有特别限制，并且可以为本领域中常见的光引发剂。在一个优选的实施方式中，所述第一紫外可固化材料和所述第二紫外可固化材料的光引发剂各自独立地为选自由苯乙酮类化合物、二苯甲酮类化合物、三嗪类化合物、噻吨酮类化合物和肟酯类化合物组成的组中的至少一种。苯乙酮类化合物的具体实例可以包括2-羟基-2-甲基-1-苯基丙-1-酮、二乙氧基苯乙酮和2-(4-甲基苄基)-2-(二甲基氨基)-1-(4-吗啉代苯基)丁-1-酮等。二苯甲酮类化合物的具体实例可以包括二苯甲酮、邻苯甲酰基苯甲酸甲酯、4-苯甲酰基-4'-甲基二苯基硫醚和2,4,6-三甲基二苯甲酮等。三嗪类化合物的具体实例可以包括2,4-双(三氯甲基)-6-(4-甲氧基苯基)-1,3,5-三嗪、2,4-双(三氯甲基)-6-(4-甲氧基萘基)-1,3,5-三嗪、2,4-双(三氯甲基)-6-[2-(3,4-二甲氧基苯基)乙烯基]-1,3,5-三嗪和2,4-双(三氯甲基)-6-2-(4-二乙基氨基-2-甲基苯基)乙烯基]-1,3,5-三嗪等。噻吨酮类化合物的具体实例可以包括2-异丙基噻吨酮、2,4-二乙基噻吨酮、2,4-二氯噻吨酮和1-氯-4-丙氧基噻吨酮等。肟酯类化合物的具体实例可以包括邻乙氧基羰基-α-氧基亚氨基-1-苯基丙-1-酮、1,2-辛二酮、1-(4-苯硫基)苯基和2-(邻苯甲酰肟)等。
根据本发明，为了进一步降低非对称性紫外曝光方法中两侧不同的紫外光对另一侧的涂层带来的影响，本发明的方法包括在所述第二紫外可固化材料中加入紫外吸收剂，也就是在紫外吸收峰高的紫外可固化材料中加入紫外吸收剂。通常地，紫外吸收剂根据种类的不同能够吸收紫外光谱中的一部分波段。
根据本发明需要，为了降低第一紫外可固化材料一侧的低波长光对第二紫外可固化材料的影响，紫外吸收剂应当能够将所述低波长光进行吸收。因此，在一个优选的实施方式中，所述紫外吸收剂能够吸收具有所述第一紫外可固化材料的紫外吸收峰+10nm的波长以下的波段，或者能够吸收具有所述第二紫外可固化材料的紫外吸收峰-10nm的波长以下的波段。
根据本发明，对所述紫外吸收剂的种类和用量没有特别限制，只要能够达到吸收来自第一紫外可固化材料一侧的低波长光的效果即可。因此，在一个实施方式中，所述紫外吸收剂可以为水杨酸酯类、二苯甲酮类、苯并三唑类、取代丙烯腈类或三嗪类紫外吸收剂。在另一个实施方式中，基于所述第二紫外可固化材料的总重量，所述紫外吸收剂的含量可以为0.5-5重量％(例如1重量％、2重量％、3重量％或4重量％等)。
根据本发明，所述透明光学薄膜可以为具有优异的透明性、机械强度、热稳定性的基板，并且作为具体示例，所述光学透明基板可以由选自以下中的至少一种制成：聚酯类树脂例如聚对苯二甲酸乙二醇酯(PET)、聚萘二甲酸乙二醇酯和聚对苯二甲酸丁二醇酯等；纤维素类树脂例如二乙酰基纤维素和三乙酸纤维素等；丙烯酸类树脂例如聚(甲基)丙烯酸甲酯和聚(甲基)丙烯酸乙酯等；苯乙烯类树脂例如聚苯乙烯和丙烯腈苯乙烯共聚物等；聚烯烃类树脂例如聚乙烯、聚丙烯、环基或降冰片烯-聚烯烃和乙烯-聚丙烯共聚物等；氯乙烯类树脂；酰胺类树脂例如尼龙和芳族聚酰胺等；聚醚醚酮类树脂；聚苯硫醚类树脂；乙烯醇类树脂；聚偏二氯乙烯类树脂；乙烯醇缩丁醛类树脂；环氧类树脂，或一些其他新兴材料、例如环烯烃聚合物(COP)和透明聚酰亚胺(CPI)等。在一个优选的实施方式中，所述光学透明基板由PET、COP、CPI、或者其他柔性或刚性材料制成。
根据本发明的非对称性紫外曝光方法的优点，光学透明基板的紫外阻隔功能不是必需的，以允许所述光学透明基板的更多选择。因此，在一个优选的实施方式中，所述光学透明基板可以为不具有紫外阻隔功能的基板，例如，所述光学透明基材的紫外透过率高于90％(例如99％等)。
在另一方面，本发明还提供了一种用于根据上述的非对称性紫外曝光方法中的紫外可固化材料，其包含紫外吸收剂。
与上述的非对称性紫外曝光方法相对应的，其中所使用的紫外可固化材料，特别是具有高紫外吸收峰的第二紫外可固化材料中应当包含紫外吸收剂，从而达到本发明所声称的技术效果。
与上述的非对称性紫外曝光方法类似的，对所述紫外吸收剂的种类和用量没有特别限制，只要能够达到吸收来自第一紫外可固化材料一侧的低波长光的效果即可。因此，在一个实施方式中，所述紫外吸收剂可以为水杨酸酯类、二苯甲酮类、苯并三唑类、取代丙烯腈类或三嗪类紫外吸收剂。在另一个实施方式中，基于所述第二紫外可固化材料的总重量，所述紫外吸收剂的含量可以为0.5-5重量％(例如1重量％、2重量％、3重量％或4重量％等)。
更具体地，根据本领域对紫外可固化材料中的一些常规组分的配制方法，相应地，本发明的紫外可固化材料的配方可以例如具体地包括：溶剂、光引发剂、流平剂、树脂、单体和紫外吸收剂，以及任选地，例如塑化剂，阻聚剂等，但不限于此。
在另一方面，本发明还提供了一种金属网格触控传感器，其通过根据上述非对称性紫外曝光方法制造。
本发明的技术方案的优点至少在于：(1)在光学透明基材中不需要紫外阻隔功能；(2)允许光学透明基材的更多选择；(3)既适用于正性紫外可固化光刻胶，又适用于负性紫外可固化光刻胶；(4)使用其制造的产品诸如柔性设备具有改善的光学性能；以及(5)相比于先前的双面紫外曝光方法进一步降低了两侧不同的紫外光对另一侧的涂层，特别是低紫外吸收峰一侧的紫外光对另一侧的具有光紫外吸收峰的材料带来的影响。
附图说明
附图是用来提供对本发明的进一步理解，并且构成说明书的一部分，与下面的具体实施方式一起用于解释本发明，但并不构成对本发明的限制。在附图中：
图1示出了测试例1中得到的光阻涂层图案的检测结果；
图2示出了测试例1中得到的铜生长情况的检测结果；
图3示出了测试例2中得到的光阻涂层图案的检测结果；以及
图4示出了测试例2中得到的铜生长情况的检测结果。
具体实施方式
以下对本发明的实施例进行详细说明。应当理解的是，此处所描述的具体实施例仅用于说明和解释本发明，并不用于限制本发明。
在本文中所披露的范围的端点和任何值都不限于该精确的范围或值，这些范围或值应当理解为包含接近这些范围或值的值。对于数值范围来说，各个范围的端点值之间、各个范围的端点值和单独的点值之间，以及单独的点值之间可以彼此组合而得到一个或多个新的数值范围，这些数值范围应被视为在本文中具体公开。
实施例
实施例1
紫外可固化材料1(紫外吸收峰为314nm，无紫外吸收剂)如下配制：在不锈钢或者塑料容器中称取65.5份的乳酸乙酯，然后再添加20份聚酯丙烯酸酯齐聚物(沙多玛CN293)和10份二季戊四醇六丙烯酸酯(DPHA)至上述溶剂中，开启高剪切搅拌机至转速6000rpm，称取2份2-甲基-1-(4-甲硫基苯基)-2-吗啉-1-丙酮(907)，1份邻苯二甲酸二(2-乙基己基)酯，0.01份对羟基苯甲醚(MEHQ)至上一步溶液中，保持6000rpm转速搅拌1小时，称取1.49份毕克BYK-333至上一步溶液中，继续搅拌10分钟。使用1μm滤芯过滤溶液，保存在遮光瓶中，避光、低温保存。
实施例2
紫外可固化材料2(紫外吸收波段为365-405nm，无紫外吸收剂)如下配制：在不锈钢或者塑料容器中称取65.5份的乳酸乙酯，然后再添加19.5份聚酯丙烯酸酯齐聚物(沙多玛CN293)和9.5份二季戊四醇六丙烯酸酯(DPHA)至上述溶剂中，开启高剪切搅拌机至转速6000rpm，称取2份2-异丙基硫杂蒽酮，0.5份4-二甲氨基苯甲酸乙酯(EDAB)，1份邻苯二甲酸二(2-乙基己基)酯，0.01份对羟基苯甲醚(MEHQ)至上一步溶液中，保持6000rpm转速搅拌1小时，称取称取1.49份毕克BYK-333至上一步溶液中，继续搅拌10分钟。使用1μm滤芯过滤溶液，保存在遮光瓶中，避光、低温保存。
实施例3
紫外可固化材料3(紫外吸收波段为365-405nm，含紫外吸收剂)如下配制：在不锈钢或者塑料容器中称取65.5份的乳酸乙酯，然后再添加19份聚酯丙烯酸酯齐聚物(沙多玛CN293)和9份二季戊四醇六丙烯酸酯(DPHA)至上述溶剂中，开启高剪切搅拌机至转速6000rpm，称取2.0份2-异丙基硫杂蒽酮，0.5份4-二甲氨基苯甲酸乙酯(EDAB)，1份上海联志化工紫外吸收剂164，1份邻苯二甲酸二(2-乙基己基)酯，0.01份对羟基苯甲醚(MEHQ)至上一步溶液中，保持6000rpm转速搅拌1小时，称取1.49份毕克BYK-333至上一步溶液中，继续搅拌10分钟。使用1μm滤芯过滤溶液，保存在遮光瓶中，避光、低温保存。
实施例4
紫外可固化材料4(紫外吸收波段为365-405nm，无紫外吸收剂)如下配制：在不锈钢或者塑料容器中称取65.5份的乳酸乙酯，然后再添加18.25份聚酯丙烯酸酯齐聚物(沙多玛CN293)和8.25份二季戊四醇六丙烯酸酯(DPHA)至上述溶剂中，开启高剪切搅拌机至转速600rpm，称取4份2-异丙基硫杂蒽酮，1份4-二甲氨基苯甲酸乙酯(EDAB)，1份邻苯二甲酸二(2-乙基己基)酯，0.01份对羟基苯甲醚(MEHQ)至上一步溶液中，保持6000RPM转速搅拌1小时，称取1.49份毕克BYK-333至上一步溶液中，继续搅拌10分钟。使用1μm滤芯过滤溶液，保存在遮光瓶中，避光、低温保存。
实施例5
紫外可固化材料5(紫外吸收波段为365-405nm，含紫外吸收剂)如下配制：在不锈钢或者塑料容器中称取65.5份的溶剂，然后再添加17.75份聚酯丙烯酸酯齐聚物(沙多玛CN293)和7.75份二季戊四醇六丙烯酸酯(DPHA)17.75份树脂至上述溶剂中，开启高剪切搅拌机至转速6000rpm，称取4份2-异丙基硫杂蒽酮，1份4-二甲氨基苯甲酸乙酯(EDAB)，1份上海联志化工紫外吸收剂3638，1份邻苯二甲酸二(2-乙基己基)酯，0.01份对羟基苯甲醚(MEHQ)至上一步溶液中，保持6000rpm转速搅拌1小时，称取1.49份毕克BYK-333至上一步溶液中，继续搅拌10分钟。使用1μm滤芯过滤溶液，保存在遮光瓶中，避光、低温保存。
在以下测试例中，通过以下方法得到光阻涂层图案及金属网格：使用微凹涂布线棒在柔性基材的一个表面上涂覆紫外可固化材料以形成光阻涂层，然后在烘箱中于65℃的温度下干燥100s，以得到厚度为700nm的涂层；在光刻胶膜的顶部涂覆一层钯纳米颗粒催化剂涂层，75℃烘烤30s；然后再涂一层隔绝水氧的功能保护涂层，于80℃烘箱中烘烤30s；之后使用与光阻匹配波长的紫外光及设计线宽2um的光罩进行接触式曝光。曝光后，在使用碱性显影液冲洗基材30s，以去除水溶性保护涂层及未固化的光阻涂层，显微镜下观察所得显影后光阻涂层图案。所得样品浸入化学镀铜液中96s以生长铜网格，在显微镜下观察铜网格的生长情况。
测试例1在不同波长及曝光能量下对是否含紫外吸收剂的影响
将紫外可固化材料1、2、3分别涂覆于基材表面，并通过上述方法分别在四组条件下制备光阻涂层图案及金属网格，其中所述四组条件分别为在曝光机下314nm低波长下曝光能量5mj、7mj、11mj，以及365nm高波长下曝光能量11mj，所述光阻涂层图案及金属网格的结果如图1和图2所示。
参照图1，A1与B1结果对比可见，低波长曝光能量较低时，低波长紫外光并没有对高波长用光阻产生影响；B1与B2、B3结果对比可见，随着低波长曝光能量升高，高波长光阻开始产生图案，说明高波长用光阻中未加紫外吸收剂时，低波长可选用的曝光能量范围较窄；
B2与C2、C3结果对比可见，高波长用光阻中增加紫外吸收剂后，有效消除来自对面透过的低波长紫外光的影响，并且低波长可选的曝光能量范围变宽，即在低波长曝光能量较高的情况下，也可以实现双面非对称曝光。
A4、B4、C4对比结果可见，高波长用光阻中添加紫外吸收剂，未对光阻本身固化产生不良影响，并且在高波长光阻能量可以固化的能量下，不会对低波长用光阻产生影响。
参照图2，A3和C4在镀铜后线条上铜良好，即紫外吸收剂的加入并不干涉网格上铜情况。
测试例2在不同波长及光引发剂用量下对是否含紫外吸收剂的影响
将紫外可固化材料2、4、5分别涂覆于基材表面，并通过上述方法分别在三组条件下制备光阻涂层图案及金属网格，其中所述三组条件分别为在曝光机下365nm低波长下曝光能量11mj，以及405nm高波长下曝光能量50mj、100mj，所述光阻涂层图案及金属网格的结果如图3和图4所示。
参照图3，A1、B1、C1结果对比可见，低波长紫外光在较低能量下也可对对面高波长用光阻产生影响；高波长用光阻光引发剂增加后，低波长紫外光对其影响效果更为明显；但是在增加了光引发剂用量的高波长用光阻中添加紫外吸收剂后，可以有效消除低波长紫外光对高波长用光阻的影响；并且随着低波长曝光能量的增加，高波长光阻也不会产生图案。
A3、A2、B2结果对比可见，同样的光阻引发剂配方下，存在高波长紫外光对低波长产生影响的现象，降低高波长的曝光能量同样能减轻对低波长光阻的影响，但是会导致高波长光阻自身固化不足；增加高波长用光阻中光引发剂用量可以实现较低能量固化良好，也不会对低波长用光阻产生影响，但是存在上述B1中高波长用光阻光引发剂增加后，低波长紫外光对其影响效果更为明显的问题；
C2与B2、C3与B3对比，添加了紫外吸收剂的高曝光用光阻在低能量和较高能量下均能固化完全。
参照图4，A1和C2在镀铜后线条上铜良好，即紫外吸收剂的加入并不干涉网格上铜情况。
综上，在高波长用光阻中添加紫外吸收剂可以有效消除低波长紫外光对高波长用光阻的影响，并且可以扩宽高波长光阻的光引发剂用量及种类。
以上详细描述了本发明的优选实施方式，但是，本发明并不限于上述实施方式中的具体细节，在本发明的技术构思范围内，可以对本发明的技术方案进行多种简单变型，这些简单变型均属于本发明的保护范围。
另外需要说明的是，在上述具体实施方式中所描述的各个具体技术特征，在不矛盾的情况下，可以通过任何合适的方式进行组合，为了避免不必要的重复，本发明对各种可能的组合方式不再另行说明。
此外，本发明的各种不同的实施方式之间也可以进行任意组合，只要其不违背本发明的思想，其同样应当视为本发明所公开的内容。
Claims (15)
1.一种非对称性紫外曝光方法，其包括：将第一紫外可固化材料施加在光学透明基材的一侧上，将第二紫外可固化材料施加在所述光学透明基材的另一侧上，并且将所述光学透明基材的两侧同时分别曝光于紫外光，其中，所述第一紫外可固化材料的紫外吸收峰低于所述第二紫外可固化材料的紫外吸收峰，所述紫外光分别具有与对应侧的紫外可固化材料的紫外吸收峰相对应的波长，并且所述第二紫外可固化材料包含紫外吸收剂，所述紫外吸收剂能够吸收来自第一紫外可固化材料一侧的低波长光。
2.根据权利要求1所述的非对称性紫外曝光方法，其中，所述第一紫外可固化材料与所述第二紫外可固化材料的紫外吸收峰之间的波长差异为至少10nm。
3.根据权利要求1或2所述的非对称性紫外曝光方法，其中，所述紫外吸收剂能够吸收具有所述第一紫外可固化材料的紫外吸收峰+10nm的波长以下的波段，或者能够吸收具有所述第二紫外可固化材料的紫外吸收峰-10nm的波长以下的波段。
4.根据权利要求1所述的非对称性紫外曝光方法，其中，所述紫外吸收剂为水杨酸酯类、二苯甲酮类、苯并三唑类、取代丙烯腈类或三嗪类紫外吸收剂。
5.根据权利要求1所述的非对称性紫外曝光方法，其中，基于所述第二紫外可固化材料的总重量，所述紫外吸收剂的含量为0.5-5重量％。
6.根据权利要求1所述的非对称性紫外曝光方法，其中，所述第一紫外可固化材料和所述第二紫外可固化材料各自独立地选自正性光刻胶和负性光刻胶。
7.根据权利要求1所述的非对称性紫外曝光方法，其中，所述第一紫外可固化材料和所述第二紫外可固化材料各自包含光引发剂。
8.根据权利要求7所述的非对称性紫外曝光方法，其中，所述第一紫外可固化材料和所述第二紫外可固化材料的光引发剂各自独立地为选自由苯乙酮类化合物、二苯甲酮类化合物、三嗪类化合物、噻吨酮类化合物和肟酯类化合物组成的组中的至少一种。
9.根据权利要求7或8所述的非对称性紫外曝光方法，其中，通过使用在不同的波长下具有紫外吸收峰的两种不同的光引发剂来实现所述第一紫外可固化材料与所述第二紫外可固化材料的紫外吸收峰之间的波长差异。
10.根据权利要求1所述的非对称性紫外曝光方法，其中，所述光学透明基材由PET、COP、CPI、或者其他柔性或刚性材料制成。
11.根据权利要求1或10所述的非对称性紫外曝光方法，其中，所述光学透明基材的紫外透过率高于90％。
12.一种用于根据权利要求1-11中任一项所述的非对称性紫外曝光方法中的紫外可固化材料，其包含紫外吸收剂。
13.根据权利要求12所述的紫外可固化材料，其中，所述紫外吸收剂为水杨酸酯类、二苯甲酮类、苯并三唑类、取代丙烯腈类或三嗪类紫外吸收剂。
14.根据权利要求12所述的紫外可固化材料，其中，基于所述紫外可固化材料的总重量，所述紫外吸收剂的含量为0.5-5重量％。
15.一种金属网格触控传感器，其通过根据权利要求1-11中任一项所述的非对称性紫外曝光方法制造。