CN112844344A - 一种甲醛吸收材料的制备方法 - Google Patents
一种甲醛吸收材料的制备方法 Download PDFInfo
- Publication number
- CN112844344A CN112844344A CN202011578892.5A CN202011578892A CN112844344A CN 112844344 A CN112844344 A CN 112844344A CN 202011578892 A CN202011578892 A CN 202011578892A CN 112844344 A CN112844344 A CN 112844344A
- Authority
- CN
- China
- Prior art keywords
- absorbing material
- formaldehyde absorbing
- solution
- formaldehyde
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种甲醛吸收材料的制备方法，涉及甲醛吸收材料制备技术领域，具体为：将石墨烯材料加入至超纯水中，混合后得到均匀溶液；将蓖麻油酸锌加入至所述均匀溶液中，混合后得到混合溶液；在80‑100℃下加热干燥，干燥后得到甲醛吸收材料。本发明以石墨烯材料和蓖麻油酸锌为原料，蓖麻油酸锌进入到石墨烯材料的空隙中或表面附近，一方面，石墨烯碳材料具有良好的吸附气体的能力；另一方面，蓖麻油酸锌在遇水的情况下，可以有效的消除甲醛。因此，以石墨烯材料和蓖麻油酸锌为原料制成的甲醛吸收材料，相比传统的碳材料吸附剂可以更有效率的消除甲醛，且消除的更加彻底。
Description
技术领域
本发明涉及甲醛吸收材料制备技术领域，具体为一种甲醛吸收材料的制备方法。
背景技术
当今，室内由于用到了多种人造材料的装修，因而存在甲醛等有害气体，对人们的健康产生了严重的危害。据统计，室内空气化学污染一般为室外污染的几十倍，特殊情况下可达数百倍，可检测到的有害挥发性有机物有300种之多，其中近20多种具有强致癌致突变作用，据报道我国每年由于室内空气污染引起的死亡人数为十余万人，其中以苯系污染物造成的血液病、白血病、孕妇流产、新生婴儿畸形等案例以及甲醛等污染物造成的人体不适现象最为多见。可见，室内环境空气污染已危及人类健康，其中以甲醛等污染物造成的人体不适现象已广为人知。
目前，对于有限空间空气中低浓度甲醛的处理，主要采用物理吸附、化学方法、催化和低温等离子体氧化等方法处理，其中，常用的物理吸附材料为活性炭。活性炭具有大的比表面积，很容易吸收空气中的有害气体，因此在日常生活中被广泛用于室内空气净化，然而活性炭吸附能力有限，且其寿命短，需要频繁的更换，从而导致更换成本高。不仅如此，活性炭有着易扬尘的缺点，会造成二次污染。
发明内容
本发明专利的目的在于提供一种甲醛吸收材料的制备方法。
为实现上述目的，本发明提供如下技术方案：一种甲醛吸收材料的制备方法，包括将石墨烯材料加入至超纯水中，混合后得到均匀溶液；
将蓖麻油酸锌加入至所述均匀溶液中，混合后得到混合溶液；
在80-100℃下加热干燥，干燥后得到甲醛净化吸附剂。
优选的，所述石墨烯材料按照如下方法制备：将苯胺、含氮聚合物和酸性溶液加入到去离子水中，充分混合均匀，将过硫酸铵溶液逐滴加入到制备的混合溶液中，持续搅拌，将搅拌后的复合物转入到高压水热釜中，加入H2O2溶液，进行反应，水热后的产物经过过滤、多次水洗后，放入真空烘箱中进烘干，将烘干后的样品研磨，在700～1000℃下煅烧，然后冷却到室温后，研磨充分，得到石墨烯材料。
优选的，混合时通过高频振动机高频振动混合或者超声波分散机超声分散进行混合。
优选的，所述石墨烯材料为15-20份，所述蓖麻油酸锌为30-40份，所述超纯水为140-180份。
优选的，所述含氮聚合物为三聚氰胺，所述酸性溶液为次氯酸
与现有技术相比，本发明的有益效果是：
本发明利用上述方法制备的甲醛吸收材料，合成方法简单易行，其结构灵活可控，本发明以石墨烯材料和蓖麻油酸锌为原料，蓖麻油酸锌进入到石墨烯材料的空隙中或表面附近，一方面，石墨烯碳材料具有良好的吸附气体的能力；另一方面，蓖麻油酸锌在遇水的情况下，可以有效的消除甲醛。因此，以石墨烯材料和蓖麻油酸锌为原料制成的甲醛吸收材料，相比传统的碳材料吸附剂可以更有效率的消除甲醛，且消除的更加彻底。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例一：
首先，按照次氯酸：苯胺：三聚氰胺的质量比为1：1：4，称取1份苯胺溶液和4份三聚氰胺，1份次氯酸，将上述物料加入到玻璃器皿中，加入30份的去离子水，超声波分散机超声分散30min，然后持续搅拌4h，得到均匀的混合溶液；
然后称取1.3份的过硫酸铵，加入30份去离子水，得到过硫酸铵溶液，将过硫酸铵溶液逐滴加入到上述混合溶液中，室温反应12h，期间持续搅拌，得到三聚氰胺和聚苯胺的复合物，之后将60份复合物转入到100份的高压水热釜中，加入2份的H2O2溶液，放入烘箱中，在120℃下反应8h，得到水热后的产物；
之后水热后的产物经过过滤、去离子水多次洗涤之后，放入真空烘箱中，在100℃下烘干12h，将烘干后的样品经过研磨2h，得到粉末样品；
将粉末样品转入到石墨坩埚中，石墨坩埚放入到管式炉中，在800℃下煅烧2h，升温速率为2.5℃/min，N2作为保护气体，待冷却到室温后，得到煅烧后的碳材料；将煅烧后的碳材料研磨2h，即可得到石墨烯材料。
之后将15份石墨烯材料加入至150份超纯水中，通过高频振动机高频振动混合后得到均匀溶液，将30份蓖麻油酸锌加入至所述均匀溶液中，混合后得到混合溶液，在100℃下加热干燥，干燥后得到甲醛吸收材料。
在使用时，可以通过将甲醛吸收材料平铺放置在地面，通过喷入适量的水雾，可以将室内壁纸、壁布、地毯、木地板、沙发、窗帘等木质家具中所蕴含的甲醛去除
实施例二：
首先，按照次氯酸：苯胺：三聚氰胺的质量比为1.2：1：4，称取1份苯胺溶液和4份三聚氰胺，1.2份次氯酸，将上述物料加入到玻璃器皿中，加入30份的去离子水，高频振动机高频振动40min，然后持续搅拌5h，得到均匀的混合溶液；
然后称取1.3份的过硫酸铵，加入30份去离子水，得到过硫酸铵溶液，将过硫酸铵溶液逐滴加入到上述混合溶液中，室温反应12h，期间持续搅拌，得到三聚氰胺和聚苯胺的复合物，之后将60份复合物转入到100份的高压水热釜中，加入2份的H2O2溶液，放入烘箱中，在130℃下反应9h，得到水热后的产物；
之后水热后的产物经过过滤、去离子水多次洗涤之后，放入真空烘箱中，在100℃下烘干12h，将烘干后的样品经过研磨2h，得到粉末样品；
将粉末样品转入到石墨坩埚中，石墨坩埚放入到管式炉中，在750℃下煅烧2h，升温速率为2.4℃/min，N2作为保护气体，待冷却到室温后，得到煅烧后的碳材料；将煅烧后的碳材料研磨2h，即可得到石墨烯材料。
之后将18份石墨烯材料加入至160份超纯水中，通过高频振动机高频振动混合后得到均匀溶液，将35份蓖麻油酸锌加入至所述均匀溶液中，混合后得到混合溶液，在90℃下加热干燥，干燥后得到甲醛吸收材料。
在使用时，可以通过将甲醛吸收材料平铺放置在地面，通过喷入适量的水雾，可以将室内壁纸、壁布、地毯、木地板、沙发、窗帘等木质家具中所蕴含的甲醛去除。
实施例三：
首先，按照次氯酸：苯胺：三聚氰胺的质量比为1：1.2：4，称取1.2份苯胺溶液和4份三聚氰胺，1份次氯酸，将上述物料加入到玻璃器皿中，加入30份的去离子水，高频振动机高频振动30min，然后持续搅拌5h，得到均匀的混合溶液；
然后称取1.2份的过硫酸铵，加入30份去离子水，得到过硫酸铵溶液，将过硫酸铵溶液逐滴加入到上述混合溶液中，室温反应12h，期间持续搅拌，得到三聚氰胺和聚苯胺的复合物，之后将60份复合物转入到100份的高压水热釜中，加入2份的H2O2溶液，放入烘箱中，在150℃下反应9h，得到水热后的产物；
之后水热后的产物经过过滤、去离子水多次洗涤之后，放入真空烘箱中，在100℃下烘干12h，将烘干后的样品经过研磨2h，得到粉末样品；
将粉末样品转入到石墨坩埚中，石墨坩埚放入到管式炉中，在750℃下煅烧2h，升温速率为2.7℃/min，N2作为保护气体，待冷却到室温后，得到煅烧后的碳材料；将煅烧后的碳材料研磨2h，即可得到石墨烯材料。
之后将20份石墨烯材料加入至180份超纯水中，通过高频振动机高频振动混合后得到均匀溶液，将40份蓖麻油酸锌加入至所述均匀溶液中，混合后得到混合溶液，在100℃下加热干燥，干燥后得到甲醛吸收材料。
在使用时，可以通过将甲醛吸收材料平铺放置在地面，通过喷入适量的水雾，可以将室内壁纸、壁布、地毯、木地板、沙发、窗帘等木质家具中所蕴含的甲醛去除。
本发明利用上述方法制备的甲醛吸收材料，合成方法简单易行，其结构灵活可控，本发明以石墨烯材料和蓖麻油酸锌为原料，蓖麻油酸锌进入到石墨烯材料的空隙中或表面附近，一方面，石墨烯碳材料具有良好的吸附气体的能力；另一方面，蓖麻油酸锌在遇水的情况下，可以有效的消除甲醛。因此，以石墨烯材料和蓖麻油酸锌为原料制成的甲醛吸收材料，相比传统的碳材料吸附剂可以更有效率的消除甲醛，且消除的更加彻底。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (5)
1.一种甲醛吸收材料的制备方法，其特征在于：将石墨烯材料加入至超纯水中，混合后得到均匀溶液；
将蓖麻油酸锌加入至所述均匀溶液中，混合后得到混合溶液；
在80-100℃下加热干燥，干燥后得到甲醛吸收材料。
2.根据权利要求1所述的一种甲醛吸收材料的制备方法，其特征在于：所述石墨烯材料按照如下方法制备：将苯胺、含氮聚合物和酸性溶液加入到去离子水中，充分混合均匀，将过硫酸铵溶液逐滴加入到制备的混合溶液中，持续搅拌，将搅拌后的复合物转入到高压水热釜中，加入H2O2溶液，进行反应，水热后的产物经过过滤、多次水洗后，放入真空烘箱中进烘干，将烘干后的样品研磨，在700～1000℃下煅烧，然后冷却到室温后，研磨充分，得到石墨烯材料。
3.根据权利要求1所述的一种甲醛吸收材料的制备方法，其特征在于：混合时通过高频振动机高频振动混合或者超声波分散机超声分散进行混合。
4.根据权利要求1所述的一种甲醛吸收材料的制备方法，其特征在于：所述石墨烯材料为15-20份，所述蓖麻油酸锌为30-40份，所述超纯水为140-180份。
5.根据权利要求2所述的一种甲醛吸收材料的制备方法，其特征在于：所述含氮聚合物为三聚氰胺，所述酸性溶液为次氯酸。