CN1112394C - 具有聚内酰胺基体的可再热模塑复合材料的制备方法 - Google Patents

具有聚内酰胺基体的可再热模塑复合材料的制备方法 Download PDF

Info

Publication number
CN1112394C
CN1112394C CN97100401A CN97100401A CN1112394C CN 1112394 C CN1112394 C CN 1112394C CN 97100401 A CN97100401 A CN 97100401A CN 97100401 A CN97100401 A CN 97100401A CN 1112394 C CN1112394 C CN 1112394C
Authority
CN
China
Prior art keywords
polymerization
moulding
lactam
poly
activator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN97100401A
Other languages
English (en)
Chinese (zh)
Other versions
CN1161987A (zh
Inventor
爱德华·施密德
罗曼·埃德
乌尔斯·维尔德
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wood Ivanda-Fischer Co.,Ltd.
EMS Patent AG
Original Assignee
EMS Inventa AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EMS Inventa AG filed Critical EMS Inventa AG
Publication of CN1161987A publication Critical patent/CN1161987A/zh
Application granted granted Critical
Publication of CN1112394C publication Critical patent/CN1112394C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/06—Fibrous reinforcements only
    • B29C70/10—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G69/00—Macromolecular compounds obtained by reactions forming a carboxylic amide link in the main chain of the macromolecule
    • C08G69/02—Polyamides derived from amino-carboxylic acids or from polyamines and polycarboxylic acids
    • C08G69/08—Polyamides derived from amino-carboxylic acids or from polyamines and polycarboxylic acids derived from amino-carboxylic acids
    • C08G69/14—Lactams
    • C08G69/16—Preparatory processes
    • C08G69/18—Anionic polymerisation
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G69/00—Macromolecular compounds obtained by reactions forming a carboxylic amide link in the main chain of the macromolecule
    • C08G69/02—Polyamides derived from amino-carboxylic acids or from polyamines and polycarboxylic acids
    • C08G69/08—Polyamides derived from amino-carboxylic acids or from polyamines and polycarboxylic acids derived from amino-carboxylic acids
    • C08G69/14—Lactams
    • C08G69/16—Preparatory processes
    • C08G69/18—Anionic polymerisation
    • C08G69/20—Anionic polymerisation characterised by the catalysts used
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K7/00—Use of ingredients characterised by shape
    • C08K7/02—Fibres or whiskers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2377/00—Characterised by the use of polyamides obtained by reactions forming a carboxylic amide link in the main chain; Derivatives of such polymers
    • C08J2377/02—Polyamides derived from omega-amino carboxylic acids or from lactams thereof
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2201/00—Properties
    • C08L2201/08—Stabilised against heat, light or radiation or oxydation
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L77/00—Compositions of polyamides obtained by reactions forming a carboxylic amide link in the main chain; Compositions of derivatives of such polymers
    • C08L77/02—Polyamides derived from omega-amino carboxylic acids or from lactams thereof
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Mechanical Engineering (AREA)
  • Composite Materials (AREA)
  • Reinforced Plastic Materials (AREA)
  • Moulding By Coating Moulds (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Polyamides (AREA)
  • Casting Or Compression Moulding Of Plastics Or The Like (AREA)
  • Other Resins Obtained By Reactions Not Involving Carbon-To-Carbon Unsaturated Bonds (AREA)
CN97100401A 1996-01-25 1997-01-27 具有聚内酰胺基体的可再热模塑复合材料的制备方法 Expired - Fee Related CN1112394C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19602638.5 1996-01-25
DE1996102638 DE19602638A1 (de) 1996-01-25 1996-01-25 Verfahren zur Herstellung von thermisch nachverformbaren Verbundwerkstoffen mit Polylactam-Matrix

Publications (2)

Publication Number Publication Date
CN1161987A CN1161987A (zh) 1997-10-15
CN1112394C true CN1112394C (zh) 2003-06-25

Family

ID=7783661

Family Applications (1)

Application Number Title Priority Date Filing Date
CN97100401A Expired - Fee Related CN1112394C (zh) 1996-01-25 1997-01-27 具有聚内酰胺基体的可再热模塑复合材料的制备方法

Country Status (9)

Country Link
US (1) US5895808A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
EP (1) EP0791618B1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
JP (1) JP3673354B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
KR (1) KR100473165B1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
CN (1) CN1112394C (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
BR (1) BR9700769A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
DE (2) DE19602638A1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
IN (1) IN191153B (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
TW (1) TW400278B (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103827171A (zh) * 2011-09-08 2014-05-28 莱茵化学莱瑙有限公司 用于生产浇注的聚酰胺的新型组合物

Families Citing this family (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19818046B4 (de) * 1998-04-22 2004-07-08 Johns Manville Europe Gmbh Schlichte und Verwendung der Schlichte
CA2368409A1 (fr) 1999-03-26 2000-10-05 Atofina Procede de polymerisation anionique de lactames
DE19961818C2 (de) * 1999-12-21 2002-12-05 Ems Chemie Ag Flüssiginitiator zur beschleunigten Durchführung der anionischen Lactampolymerisation, Verfahren zu dessen Herstellung und Verwendung
FR2814466B1 (fr) * 2000-09-22 2003-01-10 Atofina Procede de polymerisation anionique de lactames
KR20040071235A (ko) * 2001-12-20 2004-08-11 이엠에스-케미에 아게 열가소성 매트릭스를 이용한 복합 재료의 제조 방법
CN100374487C (zh) * 2002-12-27 2008-03-12 日东纺绩株式会社 纤维增强的热塑性塑料的制造方法和纤维增强的热塑性塑料
KR101013858B1 (ko) * 2008-08-28 2011-02-14 주식회사 엑시아머티리얼스 하이브리드 프론트 엔드 모듈 캐리어용 열가소성 플라스틱 복합체 조성물 및 이의 제조 방법
JP5871620B2 (ja) * 2009-02-11 2016-03-01 ピーピージー・インダストリーズ・オハイオ・インコーポレイテッドＰＰＧ Ｉｎｄｕｓｔｒｉｅｓ Ｏｈｉｏ，Ｉｎｃ． 繊維強化ポリマー複合体およびその作製方法
CN102470559A (zh) 2009-07-08 2012-05-23 巴斯夫欧洲公司 由聚酰胺6以及由聚酰胺6与聚酰胺12制备的共聚酰胺生产纤维增强复合材料的方法
DK2558517T3 (en) * 2010-04-14 2017-01-23 Wingspeed Ag PROCEDURE FOR MANUFACTURING MODIFIED POLYAMIDE 6
EP2439068A1 (de) * 2010-10-08 2012-04-11 Lanxess Deutschland GmbH Mehrschichtiges thermoplastisches Faser-Matrix-Halbzeug
CN102464800B (zh) * 2010-11-18 2013-12-11 合肥杰事杰新材料股份有限公司 一种纤维织物增强尼龙板材及其制备方法
US9085110B2 (en) 2011-03-03 2015-07-21 Basf Se Process for producing fiber-reinforced flat semifinished products with a polyamide matrix
ES2542009T3 (es) 2011-03-03 2015-07-29 Basf Se Procedimiento para la fabricación de productos semiacabados planos reforzados con fibras con matriz de poliamida
TW201303192A (zh) 2011-04-12 2013-01-16 Ticona Llc 用於水下應用之臍管
EP2697800B1 (en) 2011-04-12 2016-11-23 Southwire Company, LLC Electrical transmission cables with composite cores
US9190184B2 (en) 2011-04-12 2015-11-17 Ticona Llc Composite core for electrical transmission cables
JP6045566B2 (ja) 2011-04-12 2016-12-14 ティコナ・エルエルシー 繊維ロービングを含浸するためのダイの含浸区分及び方法
CN103501986B (zh) 2011-04-12 2016-06-01 提克纳有限责任公司 连续纤维增强热塑棒和用于其制造的拉挤方法
CN108407338B (zh) 2011-04-12 2021-05-11 提克纳有限责任公司 用于浸渍纤维粗纱的模具和方法
CA2775442C (en) 2011-04-29 2019-01-08 Ticona Llc Impregnation section with upstream surface and method for impregnating fiber rovings
PL2701886T3 (pl) 2011-04-29 2017-06-30 Ticona Llc Dysza z rozpraszającą strumień bramką przejściową oraz sposób impregnowania włókien niedoprzędów
CA2775445C (en) 2011-04-29 2019-04-09 Ticona Llc Die and method for impregnating fiber rovings
WO2013016121A1 (en) 2011-07-22 2013-01-31 Ticona Llc Extruder and method for producing high fiber density resin structures
CN103987762B (zh) 2011-12-09 2018-03-13 提克纳有限责任公司 不对称纤维增强聚合物带材
WO2013086259A1 (en) 2011-12-09 2013-06-13 Ticona Llc Die and method for impregnating fiber rovings
CN103987514B (zh) 2011-12-09 2016-10-12 提克纳有限责任公司 用于浸渍纤维粗纱的模具的浸渍区段
US9289936B2 (en) 2011-12-09 2016-03-22 Ticona Llc Impregnation section of die for impregnating fiber rovings
US9283708B2 (en) 2011-12-09 2016-03-15 Ticona Llc Impregnation section for impregnating fiber rovings
US9410644B2 (en) 2012-06-15 2016-08-09 Ticona Llc Subsea pipe section with reinforcement layer
US9834885B2 (en) 2012-12-04 2017-12-05 Basf Se Process for the production of a fiber-reinforced composite material
WO2014086757A2 (de) 2012-12-04 2014-06-12 Basf Se Verfahren zur herstellung eines faserverstärkten verbundwerkstoffs
US11548245B2 (en) 2013-11-22 2023-01-10 Johns Manville Fiber-containing prepregs and methods and systems of making
US9186852B2 (en) 2013-11-22 2015-11-17 Johns Manville Fiber-containing prepregs and methods and systems of making
CN103804681A (zh) * 2014-02-12 2014-05-21 扬州赛尔达尼龙制造有限公司 一种尼龙基梯度复合材料传动轮的制造方法
JP2018507953A (ja) 2015-02-23 2018-03-22 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ 繊維強化部品又は半製品の製造方法
WO2016150716A1 (de) 2015-03-24 2016-09-29 Basf Se Verfahren zur herstellung eines thermoplastischen, faserverstärkten halbzeugs
WO2017102310A1 (de) * 2015-12-18 2017-06-22 Lanxess Deutschland Gmbh Herstellung von faserverbundwerkstoffen
AT15930U1 (de) * 2017-02-23 2018-09-15 Engel Austria Gmbh Verfahren zum Herstellen eines Verbundes
US10857744B2 (en) 2018-04-03 2020-12-08 Johns Manville System for producing a fully impregnated thermoplastic prepreg
US10717245B2 (en) 2018-04-03 2020-07-21 Johns Manville System for producing a fully impregnated thermoplastic prepreg
US12220879B2 (en) 2021-02-11 2025-02-11 Johns Manville Lightweight thermoplastic composite products and methods of making same
CN115651395B (zh) * 2022-10-26 2024-02-13 内蒙古蒙能环保科技有限公司 玻璃纤维增强复合材料、制备方法及太阳能电池背板

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CH432828A (de) * 1962-07-17 1967-03-31 Bayer Ag Verfahren zum kontinuierlichen Herstellen faserhaltiger Polyamidgebilde
US3562221A (en) * 1967-01-19 1971-02-09 Basf Ag Accelerating anionic polymerization of lactams
DE4033414A1 (de) * 1990-10-20 1992-04-23 Bayer Ag Verdickte lactamschmelzen erhoehter viskositaet und ihre verwendung
DE4328882A1 (de) * 1993-08-27 1995-03-02 Bayer Ag Verfahren zur Herstellung von gefülltem und/oder verstärktem Gußpolyamid

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3575938A (en) * 1969-01-08 1971-04-20 Monsanto Co Anionic lactam catalyst system
DE2230732C3 (de) * 1972-06-23 1982-03-25 Bayer Ag, 5090 Leverkusen Verfahren zur Herstellung von Polyamiden durch die Polymerisation von Lactamen und Katalysatorlösungen hierfür
DE2801990A1 (de) * 1978-01-18 1979-07-19 Bosch Gmbh Robert Verfahren zur verminderung des schwundes von formteilen aus gusspolyamid
JPS5959427A (ja) * 1982-09-30 1984-04-05 Ube Ind Ltd 反応射出成形方法
US4582879A (en) * 1984-03-22 1986-04-15 Frisch Kurt C Reaction injection molding process and reaction injection molded products
US4694039A (en) * 1986-03-26 1987-09-15 Dsm Rim Nylon V.O.F. Stabilized lactam polymerization solutions
IT1213482B (it) * 1986-08-14 1989-12-20 Canalini Giovanni Processo perfezionato per la polimerizzazione anionica del caprolattame e sua copolimerizzazione con altri lattami.
IT1229220B (it) * 1989-03-31 1991-07-26 Montedipe Spa Processo per la produzione di articoli formati di grandi dimensioni, costituiti da poliammide modificata
JPH05170896A (ja) * 1991-12-20 1993-07-09 Unitika Ltd 変性ポリアミドの製造法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CH432828A (de) * 1962-07-17 1967-03-31 Bayer Ag Verfahren zum kontinuierlichen Herstellen faserhaltiger Polyamidgebilde
US3562221A (en) * 1967-01-19 1971-02-09 Basf Ag Accelerating anionic polymerization of lactams
DE4033414A1 (de) * 1990-10-20 1992-04-23 Bayer Ag Verdickte lactamschmelzen erhoehter viskositaet und ihre verwendung
DE4328882A1 (de) * 1993-08-27 1995-03-02 Bayer Ag Verfahren zur Herstellung von gefülltem und/oder verstärktem Gußpolyamid

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103827171A (zh) * 2011-09-08 2014-05-28 莱茵化学莱瑙有限公司 用于生产浇注的聚酰胺的新型组合物
CN103827171B (zh) * 2011-09-08 2016-10-19 莱茵化学莱瑙有限公司 用于生产浇注的聚酰胺的新型组合物

Also Published As

Publication number Publication date
EP0791618B1 (de) 2001-11-21
EP0791618A2 (de) 1997-08-27
US5895808A (en) 1999-04-20
EP0791618A3 (de) 1998-04-01
KR970059207A (ko) 1997-08-12
DE19602638A1 (de) 1997-08-07
DE59705427D1 (de) 2002-01-03
BR9700769A (pt) 1998-10-06
KR100473165B1 (ko) 2005-07-21
CN1161987A (zh) 1997-10-15
JP3673354B2 (ja) 2005-07-20
JPH09208712A (ja) 1997-08-12
TW400278B (en) 2000-08-01
IN191153B (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 2003-10-11

Similar Documents

Publication Publication Date Title
CN1112394C (zh) 具有聚内酰胺基体的可再热模塑复合材料的制备方法
EP0755966B1 (de) Thermoplastisch verformbare Verbundwerkstoffe
JP6140862B2 (ja) 複合ポリアミド物品
US20110244743A1 (en) Process for producing fiber-reinforced composite materials using polyamides as binders
US20120088048A1 (en) Process for producing fiber-reinforced composite materials
KR20110058852A (ko) 복합 폴리아미드 물품
KR20180092967A (ko) 반응성 프리폴리머 전구체 조성물로부터의 섬유 강화 폴리아미드 매트릭스 복합 재료의 제조 방법
WO2006053071A2 (en) Ring opening polymerization of cyclic amides using n-heterocyclic carbene catalysts
CN103826833A (zh) 制备纤维增强的复合材料的方法
EP1415793A1 (de) Verfahren zur Herstellung von Bauteilen aus Faserverbundkunststoffen
JP7418946B2 (ja) カプロラクタム製剤
JPH11200253A (ja) 繊維複合材料の製造方法、繊維複合材料およびその使用
US20060096699A1 (en) Polymerization of cyclic amides using N-heterocyclic carbene and metal amide and metal alkoxide catalysts
CN100355808C (zh) 连续长纤增强反应型尼龙树脂及其制造方法
CN1386778A (zh) 一种纤维增强热塑性材料的制备方法
KR100270090B1 (ko) 필라멘트 와인딩법에 의한 용액상 폴리아미드이미드계 수지 고분자복합재료 제조방법
Greaney et al. Development of a polyamide copolymer resin transfer molding system for thermoplastic composites
CA2546342C (en) Composite material precursors and composite materials, methods of manufacture and uses thereof
DE102016105228B4 (de) Reduzierung von Sicherungsbrüchen durch partielle Reduktion der Wärmedehnung des Kunststoffgehäuses
Andreopoulos et al. Preparation and study of aramid/epoxy prepregs
JPS6351464B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
HK1098774A (en) Composite material precursors and composite materials, methods of manufacture and uses thereof

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
ASS Succession or assignment of patent right

Owner name: AIMUSI·PATEENTE CO., LTD.

Free format text: FORMER OWNER: UHDE INVENTA-FISCHER CO., LTD.

Effective date: 20070907

C41 Transfer of patent application or patent right or utility model
C56 Change in the name or address of the patentee

Owner name: UHDE INVENTA-FISCHER CO., LTD.

Free format text: FORMER NAME OR ADDRESS: EMS-INVENTA AG

CP03 Change of name, title or address

Address after: Menedorf of Switzerland (8708) koogal Road No. 22

Patentee after: Wood Ivanda-Fischer Co.,Ltd.

Address before: Zurich

Patentee before: EMS-Inventa AG

TR01 Transfer of patent right

Effective date of registration: 20070907

Address after: Swiss Matt / Ames (7013) reichenauer Street

Patentee after: EMS-PATENT AG

Address before: Menedorf of Switzerland (8708) koogal Road No. 22

Patentee before: Wood Ivanda-Fischer Co.,Ltd.

C19 Lapse of patent right due to non-payment of the annual fee
CF01 Termination of patent right due to non-payment of annual fee