CN110294780B - 含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂及其制备方法 - Google Patents

含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂及其制备方法 Download PDF

Info

Publication number
CN110294780B
CN110294780B CN201910615470.1A CN201910615470A CN110294780B CN 110294780 B CN110294780 B CN 110294780B CN 201910615470 A CN201910615470 A CN 201910615470A CN 110294780 B CN110294780 B CN 110294780B
Authority
CN
China
Prior art keywords
burning rate
rate catalyst
aromatic amine
triazole group
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201910615470.1A
Other languages
English (en)
Other versions
CN110294780A (zh
Inventor
张国防
程文倩
姜丽萍
石晓玲
张宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi Normal University
Original Assignee
Shaanxi Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi Normal University filed Critical Shaanxi Normal University
Priority to CN201910615470.1A priority Critical patent/CN110294780B/zh
Publication of CN110294780A publication Critical patent/CN110294780A/zh
Application granted granted Critical
Publication of CN110294780B publication Critical patent/CN110294780B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含二茂铁甲基‑1,2,3‑三氮唑基团的芳香胺类燃速催化剂及其制备方法,该燃速催化剂的结构式为
Figure DDA0002123772830000011
其中R1代表‑H或
Figure DDA0002123772830000012
R代表
Figure DDA0002123772830000013
本发明燃速催化剂中引入的氮原子使得分子中易于形成氢键,因此这些化合物在自然条件下不易迁移不易挥发,热稳定性好,富氮基团具有较高的生成热和燃烧热,用于固体推进剂中会提高固体推进剂的能量水平,并且对固体推进剂主组分高氯酸铵及黑索金具有较好的燃烧催化作用。本发明燃速催化剂的制备方法操作简单、合成成本低,克服了现有二茂铁及其衍生物合成工艺复杂、价格昂贵、成本高等缺点。

Description

含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂及 其制备方法
本发明属于固体推进剂技术领域,具体涉及一类含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂,以及该燃速催化剂的制备方法。
背景技术
固体推进剂(固体火药)作为一种复合型的以推进为目的的含能材料逐渐发展起来,它主要为火箭、炮弹、枪炮、导弹提供驱动力,在导弹和航空航天工业发展中起着十分重要的作用,它的性能好坏对武器导弹的作战能力起到了决定性作用,在国防科技事业中占据了重要的位置。为了保证固体火箭发动机弹道性能和发动机工作稳定,大部分战略和战术希望固体推进剂的燃速压力指数较低。而燃速催化剂就能够起到降低推进剂压力指数的作用,它是通过物理或化学作用来调节推进剂燃速的一种添加剂,通过改变燃烧波的结构,从而提高或降低推进剂的燃速,大大减弱了压力指数对燃速的影响,通常加入量为质量分数1%~5%之间。作为固体推进剂配方中一种不可或缺的成分,燃速催化剂的研究是固体推进剂研究的一项重要内容,近几十年来,在国内外已经得到了较大的发展。
二茂铁及其衍生物以其良好的可燃性、分散性、均匀性、相容性等优点而受到广泛关注,如正丁基二茂铁、叔丁基二茂铁和卡托辛是目前已经商品化并广泛运用于复合推进剂中作为燃速催化剂。但是目前应用的二茂铁类燃速催化剂存在易迁移、易挥发等问题,严重影响了我国各类导弹推进剂装药的贮存寿命、使用可靠性及环境适应性,也无形中大幅度增大了国防基础储备的经费支出。所以科研工作者做了大量的研究工作试图研制出力学性能更好、工艺性能更简单和燃烧性能更高的二茂铁类燃速催化剂,为改进二茂铁及其衍生物存在的问题。
1972年Huskins发表的一篇美国专利中提出将烯丙醇结构引入二茂铁中制备了含有双烯丙醇的单核二茂铁,羟基的引入明显的降低了迁移性和挥发性。随后在1974年,Huskins又尝试将异丙氰基团引入二茂铁丁二烯中,通过增长碳链和活性基团氰酸的引入来降低迁移性和挥发性,并获得了较好的催化活性。1989年吴艳钟等人也合成了双-(甲基二茂铁基)-甲烷、2,2-双-(甲基二茂铁基)-丙烷和2,2-双(甲基二茂铁基)-丁烷。1995年德国威巴石油有限公司的布鲁多厂对Catocene进行了改性合成了两种高效燃速催化剂,即2,2-双-(丁基二茂铁)丙烷(BBFPr)和1,1-双-(丁基二茂铁)戊烷(BBFPe)。2001年袁耀峰等人设计并制备了三种双二茂铁高氮衍生物,并测试了所合成化合物的稳定性和燃速催化效果,发现该类化合物对高氯酸铵具有较好的燃烧催化效果,同时具有优良的热稳定性,具有潜在的应用价值。2004年边占喜等人合成了2,2-双-(单烷基二茂铁基)-丙烷和2,2-双(烷基二茂铁基)-丙烷两个系列化合物。2009年李占雄和唐孝明公开发表的专利中制备了一种新型的亚乙撑二茂铁衍生物,该产品合成成本较低,制备流程相对简单,催化作用良好。2011年,张岩等人将二茂铁甲酸与高性能粘合剂环氧化端羟基聚丁二烯(EHTPB)原位接枝制备了一种环氧化端羟基聚丁二烯二茂铁甲酸(EHTPB)燃速催化剂。2012年袁耀锋等人以二茂铁为原料经过甲酰化、缩合、脱水等过程得到丙基桥联双聚二茂铁甲腈和丙基桥联双聚二茂铁四唑,并测试了化合物添加到高氯酸铵中时的燃烧催化性能,显示添加后高氯酸铵的分解峰温提前了50℃左右,但是其合成工艺复杂。2016年,高晓妮等人以二茂铁四氮唑为阴离子,富氮基团和二茂铁类季铵盐为阳离子,合成了高氮含量型和高铁含量型两类化合物。经过测试,两类化合物均对推进剂主组分高氯酸铵具有良好的燃烧催化效果,且迁移性和挥发性较低。
发明内容
本发明的目的是克服商品化二茂铁燃速催化剂存在的易挥发易迁移问题,同时提高固体推进剂的能量水平,提供一种在自然条件下不易迁移和挥发,热稳定性好的含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂,并为该燃速催化剂提供一种操作简单和成本较低的制备方法。
针对上述目的,本发明所采用的含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂的结构式如下:
Figure BDA0002123772810000021
其中R1代表-H或
Figure BDA0002123772810000031
R代表
Figure BDA0002123772810000032
m、n各自独立的取0或1。
本发明燃速催化剂优选下述化合物1~5中任意一种:
Figure BDA0002123772810000033
Figure BDA0002123772810000041
本发明含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂的制备方法为:在N2气氛下,将式I化合物和式II所示叠氮甲基二茂铁加入甲醇中,搅拌均匀,然后加入五水合硫酸铜和抗坏血酸钠,室温搅拌20~24h,过滤得粗产物,将粗产物柱层析分离,得到含二茂铁甲基-1,2,3三氮唑基团的芳香胺类燃速催化剂;
Figure BDA0002123772810000042
Ra代表-H或
Figure BDA0002123772810000051
上述制备方法中,优选式I化合物与叠氮甲基二茂铁、五水硫酸铜、抗坏血酸钠的摩尔比为1:1.5~4.5:0.2~0.4:0.2~0.4。
本发明的有益效果如下:
本发明含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂是一个由二茂铁基团、1,2,3-三氮唑基团和芳香胺基团组成的分子,它不但含有二茂铁类催化剂所要求的二茂铁基团,而且含有1,2,3-三氮唑这种具有正生成焓的高氮杂环基团,其较高的燃烧热和生成热可以在分解时提高推进剂的能量水平。这类化合物铁含量增加,具有比单核二茂铁更优的燃速催化活性。这类化合物的另一个优点是1,2,3-三氮唑基团和芳香胺基团中的氮原子易于形成氢键,通过氢键作用来提高二茂铁类化合物的热稳定性、抗迁移性和挥发性,是一种在自然条件下不易迁移和挥发,热稳定性好且富氮的芳香胺类衍生物,用于固体推进剂中能提高固体推进剂的能量水平。且此类化合物的制备方法操作简单、成本较低。
附图说明
图1是高氯酸铵中添加5%实施例1~5燃速催化剂的差示扫描量热分析曲线。
图2是黑索金中添加5%实施例1~5燃速催化剂的差示扫描量热分析曲线。
图3是实施例1~5燃速催化剂的热重曲线。
图4是实施例1燃速催化剂、二茂铁和卡托辛的迁移距离图。
具体实施方式
下面结合附图和实施例对本发明进一步详细说明,但本发明的保护范围不仅限于这些实施例。
下面实施例中所用N,N′-二-(2-丙炔基)苯胺根据下述方法制备得到:
将0.9995g(10.74mmol)苯胺溶解于10mL DMF中,然后加入3.726g(27mmol)K2CO3,并在60℃下持续搅拌30min,然后滴加2.1mL(27mmol)3-溴丙炔,在60℃下继续搅拌6h,反应完成后,将反应混合物冷却到室温,过滤,将滤液通过旋转蒸发仪蒸去溶剂,得到粗产物,将粗产物进行柱层析分离得到N,N′-二-(2-丙炔基)苯胺,其产率为85%,反应方程式如下:
Figure BDA0002123772810000061
所得N,N′-二-(2-丙炔基)苯胺的结构表征数据为:1H NMR(400MHz,CDCl3):δ7.29(s,2H),6.98(s,3H),4.11(s,4H),2.24(s,2H).
将上述N,N′-二-(2-丙炔基)苯胺制备方法中的苯胺用等摩尔邻苯二胺替换,得到N,N′,N″,N″′-四-(2-丙炔基)邻苯二胺,其产率为83%,反应方程式如下:
Figure BDA0002123772810000062
所得N,N′,N″,N″′-四-(2-丙炔基)邻苯二胺的结构表征数据为:1H NMR(400MHz,CDCl3):δ7.07(s,4H),4.12(s,8H),2.21(s,4H).
将上述N,N′-二-(2-丙炔基)苯胺制备方法中的苯胺用等摩尔间苯二胺替换,得到N,N′,N″,N″′-四-(2-丙炔基)间苯二胺,其产率为87%,反应方程式如下:
Figure BDA0002123772810000063
所得N,N′,N″,N″′-四-(2-丙炔基)间苯二胺的结构表征数据为:1H NMR(400MHz,CDCl3):δ7.19(s,1H),6.58(s,1H),6.51(s,2H),4.12(s,8H),2.25(s,4H).
将上述N,N′-二-(2-丙炔基)苯胺制备方法中的苯胺用等摩尔对苯二胺替换,得到N,N′,N″,N″′-四-(2-丙炔基)对苯二胺,其产率为85%,反应方程式如下:
Figure BDA0002123772810000064
所得N,N′,N″,N″′-四-(2-丙炔基)对苯二胺的结构表征数据为:1H NMR(400MHz,CDCl3):δ6.96(s,4H),4.05(s,8H),2.25(s,4H).
将上述N,N′-二-(2-丙炔基)苯胺制备方法中的苯胺用等摩尔4,4’-联苯二胺替换,得到N,N′,N″,N″′-四-(2-丙炔基)-4,4’-联苯二胺,其产率为82%,反应方程式如下:
Figure BDA0002123772810000065
所得N,N′,N″,N″′-四-(2-丙炔基)-4,4’-联苯二胺的结构表征数据为:1H NMR(400MHz,CDCl3):δ7.50(s,2H),7.48(s,2H),7.02(s,2H),7.00(s,2H),4.16(s,8H),2.27(s,4H).
实施例1
制备结构式如下的双-(二茂铁基甲基-1,2,3-三氮唑基甲基)苯胺
Figure BDA0002123772810000071
向250mL圆底烧瓶中加入0.1691g(1mmol)N,N′-二-(2-丙炔基)苯胺和0.4941g(2.05mmol)叠氮甲基二茂铁,在N2气氛下加入30mL甲醇,搅拌均匀,随后滴加15mL含0.0800g(0.3mmol)五水合硫酸铜的水溶液和15mL含0.0600g(0.3mmol)抗坏血酸钠的水溶液,室温搅拌24h,过滤得粗产物,将粗产物通过柱层析分离,得到双-(二茂铁基甲基-1,2,3-三氮唑基甲基)苯胺,其产率为85%,结构表征数据为:FT-IR(cm-1):3918w,3620w,3316w,3087m,2935w,1681w,1591s,1501vs,1445m,1376m,1314s,1224s,1162m,1106m,1044s,989m,940m,822vs,732s,683m,483vs;1H NMR(400MHz,CDCl3):δ7.28(s,2H),7.18(s,2H),6.86(s,2H),6.72(s,1H),5.19(s,4H),4.61(s,4H),4.19(s,4H),4.18(s,4H),4.13(s,10H).
实施例2
制备结构式如下的N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)邻苯二胺
Figure BDA0002123772810000072
本实施例中,用等摩尔N,N′,N″,N″′-四-(2-丙炔基)邻苯二胺替换实施例1中的N,N′-二-(2-丙炔基)苯胺,其他步骤与实施例1相同,得到N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)邻苯二胺,其产率为82%,结构表征数据为:FT-IR(cm-1):3926w,3641w,3402w,3087m,2935w,2938w,1646w,1487m,1432m,1328s,1217s,1113s,1044vs,919m,822vs,739m,483vs;1H NMR(400MHz,CDCl3):δ7.32(s,4H),6.75(s,4H),5.13(s,8H),4.45(s,8H),4.14(s,17H),4.11(s,19H).
实施例3
制备结构式如下的N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)间苯二胺
Figure BDA0002123772810000081
本实施例中,用等摩尔N,N′,N″,N″′-四-(2-丙炔基)间苯二胺替换实施例1中的N,N′-二-(2-丙炔基)苯胺,其他步骤与实施例1相同,得到N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)间苯二胺,其产率为84%,结构表征数据为:FT-IR(cm-1):3641m,3094m,2928w,1715w,1591s,1494m,1445m,1321s,1217m,1182s,1106m,1037s,926m,808vs,697w,497vs;1H NMR(400MHz,CDCl3):δ7.44(s,4H),6.94(s,2H),6.38(s,1H),6.22(s,2H),5.19(s,8H),4.51(s,8H),4.22(s,8H),4.16(s,8H),4.13(s,20H).
实施例4
制备结构式如下的N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)对苯二胺
Figure BDA0002123772810000091
本实施例中,用等摩尔N,N′,N″,N″′-四-(2-丙炔基)对苯二胺替换实施例1中的N,N′-二-(2-丙炔基)苯胺,其他步骤与实施例1相同,得到N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)对苯二胺,其产率为86%,结构表征数据为:FT-IR(cm-1):3918w,3094m,2921w,2845w,1646m,1522vs,1438m,1363m,1314s,1217s,1113m,1030s,933m,815vs,718m,490vs;1H NMR(400MHz,CDCl3):δ7.27(s,4H),6.76(s,4H),5.19(s,8H),4.42(s,8H),4.20(s,8H),4.18(s,8H),4.13(s,20H).
实施例5
制备结构式如下的N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)-4,4′-联苯二胺
Figure BDA0002123772810000092
本实施例中,用等摩尔N,N′,N″,N″′-四-(2-丙炔基)-4,4′-联苯二胺替换实施例1中的N,N′-二-(2-丙炔基)苯胺,其他步骤与实施例1相同,得到N,N′,N″,N″′-四-(二茂铁基甲基-1,2,3-三氮唑基甲基)-4,4′-联苯二胺,其产率为88%,结构表征数据为:FT-IR(cm-1):3926w,3406m,3073m,2921w,1605s,1508vs,1438m,1376m,1307m,1217s,1099m,1044s,995m,933m,808s,476s;1H NMR(400MHz,CDCl3):δ7.34(s,2H),7.31(s,2H),7.30(s,4H),5.20(s,8H),4.63(s,8H),4.20(s,8H),4.17(s,8H),4.13(s,20H).
为了证明本发明的有益效果,发明人以高氯酸铵(AP)和黑索金(RDX)为例,分别对实施例1~5制备的燃速催化剂的催化性能进行测试,具体实验情况如下:
取燃速催化剂5mg、粉末状的高氯酸铵95mg,研磨混合均匀;取燃速催化剂5mg、粉末状的黑索金95mg,研磨均匀,采用差示扫描量热仪对其催化性能进行测试,结果见图1~2。取燃速催化剂3mg,采用热重分析仪对其热稳定性进行测试,结果见图3。测试了商品化的卡托辛、二茂铁以及实施例1在50℃下1~4周的迁移距离,结果见图4。
由图1可见,AP的热分解可分为三个阶段:第一个过程为AP的相变吸热过程,峰值温度为243.7℃,第二阶段的峰值温度为292.5℃,是AP的低温分解过程,第三阶段的峰值温度为406.6℃,称为高温分解阶段,当AP中分别添加5%实施例1~5燃速催化剂后,AP的晶型转变温度由原来的237.5℃向后移动了5℃左右。同时,AP的高温分解阶段由原来的292.5℃向后移动了50℃左右。变化最大的是原来AP在高温分解阶段时的放热峰,其峰温为406.6℃,加入5%实施例1~5的燃速催化剂后该分解峰温分别提前到355.5℃、350.1℃、347.3℃、352.1℃和349.1℃,且实施例3放出的热量高达1915J/g,与之前研究的含二茂铁-1,2,3-三氮唑基团的苯甲酸脂类化合物催化AP的最大放热量1130J/g相比,增加了69%。可以看出实施例1~5燃速催化剂对AP的热分解有显著的催化作用。由此可见,与纯AP相比,添加本发明燃速催化剂后体系的高温分解阶段呈现集中放热现象,放热峰温均提前,且放出的热量明显增加,说明本发明燃速催化剂对AP的热分解具有良好的燃烧催化作用。
由图2可见,RDX的熔点在202℃,其分解放热峰温在231.2℃,放出的热量为827.9J/g;当RDX中分别添加5%实施例1~5燃速催化剂后,在RDX发生熔化之前有一个峰温分别出现在207.4℃、193.9℃、193.9℃、195.9℃和195.9℃,说明RDX没有熔化之前已经出现了部分分解现象.原来RDX在高温分解阶段的放热峰,其峰温为231.2℃,加入5%的实施例1~5的燃速催化剂后该分解峰温分别为234.5℃、231.3℃、229.9℃、226.0℃和230.9℃,其峰温没有出现大的改变。另外,混合体系的放热量分别为1617.53J/g、1757.33J/g、1614.91J/g、1309.94J/g和1647.71J/g,说明实施例1~5燃速催化剂的加入均使RDX的放热量增加,其中实施例2燃速催化剂使RDX放热量增加幅度最显著,放热量达1757.33J/g,其最大放热量与之前所研究的含二茂铁基团的苯甲酸脂类化合物中催化RDX的最大放热量1429.9J/g相比,增加了23%,说明实施例1~5燃速催化剂对RDX热分解均有明显的催化作用。
由图3可见,本发明燃速催化剂的失重起始温度均在300℃以上,明显高于卡托辛的失重起始温度,显示出了良好的热稳定性能。
由图4可见,本发明燃速催化剂的迁移距离明显低于商品化的卡托辛和二茂铁,具有优良的抗迁移性能。

Claims (4)

1.一种含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂,其特征在于该燃速催化剂的结构式如下:
Figure FDA0003205458260000011
其中R1代表-H或
Figure FDA0003205458260000012
R代表
Figure FDA0003205458260000013
m、n各自独立的取0或1。
2.根据权利要求1所述的含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂,其特征在于该燃速催化剂为下述化合物1~5中任意一种:
Figure FDA0003205458260000014
Figure FDA0003205458260000021
3.一种权利要求1所述的含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂的制备方法,其特征在于:在N2气氛下,将式I化合物和式II所示叠氮甲基二茂铁加入甲醇中,搅拌均匀,然后加入五水合硫酸铜和抗坏血酸钠,室温搅拌20~24h,过滤得粗产物,将粗产物柱层析分离,得到含二茂铁甲基-1,2,3三氮唑基团的芳香胺类燃速催化剂;
Figure FDA0003205458260000022
Ra代表-H或
Figure FDA0003205458260000031
m、n各自独立的取0或1。
4.根据权利要求3所述的含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂的制备方法,其特征在于:所述式I化合物与叠氮甲基二茂铁、五水硫酸铜、抗坏血酸钠的摩尔比为1:1.5~4.5:0.2~0.4:0.2~0.4。
CN201910615470.1A 2019-07-09 2019-07-09 含二茂铁甲基-1,2,3-三氮唑基团的芳香胺类燃速催化剂及其制备方法 Active CN110294780B (zh)