CN108047727A - 一种3d打印硅胶线材及其制备方法 - Google Patents
一种3d打印硅胶线材及其制备方法 Download PDFInfo
- Publication number
- CN108047727A CN108047727A CN201711378857.7A CN201711378857A CN108047727A CN 108047727 A CN108047727 A CN 108047727A CN 201711378857 A CN201711378857 A CN 201711378857A CN 108047727 A CN108047727 A CN 108047727A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- silicone oil
- wire rod
- oil
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
打印性能 | 邵氏硬度 | FDA测试 | |
实施例1 | 挤出稳定,精细度高 | 45A | OK |
实施例2 | 挤出稳定,精细度高 | 89A | OK |
实施例3 | 挤出稳定,精细度高 | 65A | OK |
实施例4 | 挤出稳定,精细度高 | 72A | OK |
实施例5 | 挤出稳定,精细度高 | 68A | OK |
对比例1 | 挤出欠佳,不能打印 | 25A | OK |
对比例2 | 挤出稳定,精细度一般 | 75D,弹性差 | OK |
对比例3 | 挤出欠佳,不能打印 | 85D,弹性差 | OK |
对比例4 | 挤出稳定,精细度高 | 100D,弹性差 | OK |
对比例5 | 光固化打印 | 95D,弹性差 | NG |
Claims (8)