CN107572588B - 一种环保型钨酸钠制备工艺及其应用 - Google Patents

一种环保型钨酸钠制备工艺及其应用 Download PDF

Info

Publication number
CN107572588B
CN107572588B CN201710802876.1A CN201710802876A CN107572588B CN 107572588 B CN107572588 B CN 107572588B CN 201710802876 A CN201710802876 A CN 201710802876A CN 107572588 B CN107572588 B CN 107572588B
Authority
CN
China
Prior art keywords
sodium tungstate
environment
friendly type
preparation process
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710802876.1A
Other languages
English (en)
Other versions
CN107572588A (zh
Inventor
丁明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710802876.1A priority Critical patent/CN107572588B/zh
Publication of CN107572588A publication Critical patent/CN107572588A/zh
Application granted granted Critical
Publication of CN107572588B publication Critical patent/CN107572588B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保型钨酸钠制备工艺及其应用，通过含钨废料提取、制备钨酸钠溶液、钨料去杂、钨酸钠溶液浓缩及钨酸钠烘干等步骤从含钨废料提取钨酸钠，本发明一种环保型钨酸钠制备工艺及其应用，工艺简单，绿色环保的生产过程，产品纯度高，广泛适合在颜料行业及医疗行业使用。

Description

一种环保型钨酸钠制备工艺及其应用
技术领域
本发明属于冶金技术领域，更加具体地说，是涉及一种环保型钨酸钠制备工艺及其应用。
背景技术
钨酸钠为无色结晶或白色斜方结晶，白色具有光泽的片状结晶或结晶粉末，溶于水呈微碱性(PH8.5-9),不溶于乙醇，微溶于氨。在空中风化。加热到100℃失去结晶水而成无水物。与强酸(氢氟酸除外)反应生成不溶于水的黄色钨酸,与磷酸或磷酸盐反应生成磷钨杂多酸络合物,与酒石酸、柠檬酸、草酸等有机酸反应生成相应有机酸络合物。
钨酸钠主要用于制取仲钨酸铵及深度加工制取三氧化钨、金属钨、碳化钨、硬质合金、钨条、钨丝等,制偏钨酸铵、钨酸及其它钨化合物用于石油化工、电镀、纺织、阻燃剂、水处理、染料、颜料、油墨等方面。
发明内容
发明目的：本发明的目的是针对现有技术不足和缺陷，提供一种环保型钨酸钠制备工艺及其应用，按照本发明所提供的技术方案制成的钨酸钠具有良好的环保性能及应用价值。
技术方案：为了实现上述目的，本发明所采用的技术方案为：一种环保型钨酸钠制备工艺：
步骤A、含钨废料提取首先将含钨废料进行粉碎，粉碎后的含钨废料通过传送带传送至碾磨机，碾磨机将含钨废料碾磨至2000－2500目，将碾磨好的含钨废料倒入搅拌桶中，搅拌桶以1000rad/min的转速搅拌5min，加入浓H2SO4，搅拌桶以1500rad/min的转速搅拌30min，静置60min，过滤出不溶杂质，保留滤液；
步骤B、制备钨酸钠溶液将步骤A中滤液转移至反应釜中进行碱煮，即加入碱液，设置压力温度，时间为120min，所得为粗钨酸钠溶液，将粗钨酸钠溶液移至另一个干净的容器中，加入萃取剂，静置60min，过滤出不溶杂质，保留滤液；
步骤C、钨料去杂将步骤B中粗钨酸钠溶液移至另一个干净的搅拌桶中，加入氧化剂，搅拌桶以2000rad/min的转速搅拌90min，静置30min，所得溶液即为钨酸钠溶液；
步骤D、钨酸钠溶液浓缩首先将步骤C中得到的钨酸钠溶液进行提纯处理，再将提纯后的钨酸钠溶液进行浓缩处理，得到湿的高纯度钨酸钠；
步骤E、钨酸钠烘干将步骤D中得到的湿的高纯度钨酸钠加入烘箱烘干，烘干时间为120min，得到干的钨酸钠。
所述步骤B中的杂质为Co、TiC、TaC、Fe2+/Fe3+、Ni及Cu中的一种或几种。
所述步骤C中的氧化剂为NaOH、NaNO3或KNO3中的一种或几种，其中优选的为NaNO3。
所述提纯处理是对步骤D中的钨酸钠溶液进行离子交换长距离，所述离子交换处理为多级离子交换。
所述浓缩处理是对步骤D中的钨酸钠溶液进行蒸发结晶处理。
一种环保型钨酸钠在医药上的应用：
将所述步骤E所得的干的钨酸钠溶解后加入酒精进行溶解，溶解后溶液过滤出不溶性物质后，重复步骤D及步骤E，得到高纯度的干的钨酸钠。
一种环保型钨酸钠在颜料中的应用：
将所述步骤E所得的干的钨酸钠溶解后加入酒精进行溶解稀释，所述酒精质量为钨酸钠总量的2％，然后将酒精及钨酸钠混合物搅拌3－5min，静置2min，再加入所需颜料进行混合。
有益效果：本发明与现有技术相比，其有益效果是：
本发明一种环保型钨酸钠制备工艺及其应用，工艺简单，绿色环保的生产过程，产品纯度高，广泛适合在颜料行业及医疗行业使用。
具体实施方式
下面结合具体实施方式，进一步说明本发明。
一种环保型钨酸钠制备工艺及其应用：
步骤A、含钨废料提取首先将含钨废料进行粉碎，粉碎后的含钨废料通过传送带传送至碾磨机，碾磨机将含钨废料碾磨至2000－2500目，将碾磨好的含钨废料倒入搅拌桶中，搅拌桶以1000rad/min的转速搅拌5min，加入浓H2SO4，搅拌桶以1500rad/min的转速搅拌30min，静置60min，过滤出不溶杂质，保留滤液；
步骤B、制备钨酸钠溶液将步骤A中滤液转移至反应釜中进行碱煮，即加入碱液，设置压力温度，时间为120min，所得为粗钨酸钠溶液，将粗钨酸钠溶液移至另一个干净的容器中，加入萃取剂，静置60min，过滤出不溶杂质，保留滤液；
步骤C、钨料去杂将步骤B中粗钨酸钠溶液移至另一个干净的搅拌桶中，加入氧化剂，搅拌桶以2000rad/min的转速搅拌90min，静置30min，所得溶液即为钨酸钠溶液；
步骤D、钨酸钠溶液浓缩首先将步骤C中得到的钨酸钠溶液进行提纯处理，再将提纯后的钨酸钠溶液进行浓缩处理，得到湿的高纯度钨酸钠；
步骤E、钨酸钠烘干将步骤D中得到的湿的高纯度钨酸钠加入烘箱烘干，烘干时间为120min。
所述步骤C中的氧化剂为NaOH、NaNO3或KNO3中的一种或几种，其中优选的为NaNO3。
一种环保型钨酸钠在医药上的应用：
将所述步骤E所得的干的钨酸钠溶解后加入酒精进行溶解，溶解后溶液过滤出不溶性物质后，重复步骤D及步骤E，得到高纯度的干的钨酸钠。
一种环保型钨酸钠在颜料中的应用：
将所述步骤E所得的干的钨酸钠100g溶解后加入2g酒精进行溶解稀释，然后将酒精及钨酸钠混合物搅拌3－5min，静置2min，再加入所需颜料进行混合。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (5)

1.一种环保型钨酸钠的制备工艺，其特征在于：
步骤A、含钨废料提取：首先将含钨废料进行粉碎，粉碎后的含钨废料通过传送带传送至碾磨机，碾磨机将含钨废料碾磨至2000－2500目，将碾磨好的含钨废料倒入搅拌桶中，搅拌桶以1000rad/min的转速搅拌5min，加入浓H2SO4，搅拌桶以1500rad/min的转速搅拌30min，静置60min，过滤出不溶杂质，保留滤液；
步骤B、制备钨酸钠溶液：将步骤A中滤液转移至反应釜中进行碱煮，即加入碱液，设置压力温度，时间为120min，所得为粗钨酸钠溶液，将粗钨酸钠溶液移至另一个干净的容器中，加入萃取剂，静置60min，过滤出不溶杂质，保留滤液；
步骤C、钨料去杂：将步骤B中粗钨酸钠溶液移至另一个干净的搅拌桶中，加入氧化剂，搅拌桶以2000rad/min的转速搅拌90min，静置30min，所得溶液即为钨酸钠溶液；
步骤D、钨酸钠溶液浓缩：首先将步骤C中得到的钨酸钠溶液进行提纯处理，再将提纯后的钨酸钠溶液进行浓缩处理，得到湿的高纯度钨酸钠；
步骤E、钨酸钠烘干将步骤D中得到的湿的高纯度钨酸钠加入烘箱烘干，烘干时间为120min。
2.根据权利要求1所述的一种环保型钨酸钠的制备工艺，其特征在于：所述步骤B中的杂质为Co、TiC、TaC、Ni及Cu中的一种或几种。
3.根据权利要求1所述的一种环保型钨酸钠的制备工艺，其特征在于：所述步骤C中的氧化剂为NaNO3或KNO3中的一种或几种。
4.根据权利要求1所述的一种环保型钨酸钠的制备工艺，其特征在于：所述提纯处理是对步骤D中的钨酸钠溶液进行离子交换处理，所述离子交换处理为多级离子交换。
5.根据权利要求1所述的一种环保型钨酸钠的制备工艺，其特征在于：所述浓缩处理是对步骤D中的钨酸钠溶液进行蒸发结晶处理。
CN201710802876.1A 2017-09-08 2017-09-08 一种环保型钨酸钠制备工艺及其应用 Active CN107572588B (zh)