CN106977136A - 一种阻燃人造石英石板材及其制备方法 - Google Patents
一种阻燃人造石英石板材及其制备方法 Download PDFInfo
- Publication number
- CN106977136A CN106977136A CN201710358752.9A CN201710358752A CN106977136A CN 106977136 A CN106977136 A CN 106977136A CN 201710358752 A CN201710358752 A CN 201710358752A CN 106977136 A CN106977136 A CN 106977136A
- Authority
- CN
- China
- Prior art keywords
- fire retardant
- quartzite slate
- mixed
- silane
- man
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明所述一种阻燃人造石英石板材及其制备方法,包括如下原料:0.075~5mm颗粒原料、0.005~0.045mm石英粉、有色颜料、硅烷偶联剂、不饱和聚酯树脂、固化剂、阻燃剂,制备方法,包括以下步骤:将称取的石英颗粒、玻璃颗粒、阻燃剂、硅烷偶联剂于双行星式搅拌桶中预混合;进行混合,加入石英粉进行混合;将混合好的物料送入打散机进一步打散,打散后,计量进入布料机内布料;在‑0.1Mpa的真空条件下经压制设备振动压制成型,压力50~200t,振动频率30~55Hz,时间60~600s;经振动压制后,进入固化设备,在80~130℃的温度下固化,固化时间为30~180分钟;常温放置待冷却完全后进入板材定厚机定厚,再经过水磨抛光设备进行抛光,对人造石英石产品阻燃性能有较大增强作用。
Description
技术领域
本发明属于人造石英石板材技术领域,具体地说,涉及一种阻燃人造石英石板材及其制备方法。
背景技术
人造石英石是由90%以上的天然石英和10%左右的色料、树脂和其它调节粘接、固化等的添加剂组成。是经过负压真空、高频振动成型,加温固化(温度高低是根据固化剂的种类而定的生产方法加工而成的板材。其质地坚硬、结构致密具有其他装饰材料无法比拟的耐磨、耐压、耐高温、抗腐蚀、防渗透等特性。
目前石英石产品主要在厨房台面、卫生间台面、吧台、茶几、地面以及内外墙头面等,由于其色彩丰富,产品花色丰富等优点,可以替代天然石材、高档陶瓷、木材、金属类装饰材料。国内绝大多数石英石生产厂商所制作的石英石树脂含量偏高,树脂含量一般都在10%以上,而且生产时间长,提高了产品的生产成本,最终提高了产品的售价。此外,高树脂含量导致石英石成品的热膨胀系数较低,板材耐用性不佳,容易老化,褪色,防火等级低,耐热性能差,大大缩短了板材的使用寿命。
因此,有必要对现有的生产配方进行升级改造或技术改造。
发明内容
本发明克服了现有技术中的缺点,提供了一种阻燃人造石英石板材及其制备方法,其具有阻燃性能好、耐高温、不易老化等优点。
为了解决上述技术问题,本发明是通过以下技术方案实现的:
一种阻燃人造石英石板材,包括如下原料:0.075~5mm颗粒原料、0.005~0.045mm石英粉、有色颜料、硅烷偶联剂、不饱和聚酯树脂、固化剂、阻燃剂。
进一步,按照重量百分比,0.075~5mm颗粒原料55%~65%、0.005~0.045mm石英粉20%~30%;有色颜料0.01%~10%;硅烷偶联剂0.1%~1%;不饱和聚酯树脂7%~14%;固化剂0.8%~1.4%,阻燃剂1%~3.8%;
其中,颗粒原料为石英颗粒或玻璃颗粒,或两种的混合物。
进一步,所述有色颜料为无机颜料或有机颜料或色浆的一种或多种。
进一步,所述无机颜料为无机颜料,所述无机颜料为钛白、中铬黄、铁黄、铁红、铁蓝、镉红、镉黄、炭黑或铁黑。
进一步,所述有机颜料为大红粉、偶氮黄、酞青绿或酞菁蓝有机颜料。
进一步,所述色浆为白浆、黑浆、大红浆、酞青绿浆或酞菁蓝浆。
进一步,所述不饱和聚酯树脂是环氧树脂、酚醛树脂、丙烯酸树脂和聚氨酯树脂中的一种或多种。
进一步,所述固化剂为过氧化(2-乙基己酸)叔丁酯、过氧化甲乙酮、过氧化苯甲酸叔丁酯、过氧化二苯甲酰和脂肪多元胺中的一种或多种。
进一步,所述硅烷偶联剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷、N-β(氨乙基)-γ-氨丙基甲基二甲氧基硅烷、N-(β-氨乙基)-γ-氨丙基三乙氧基硅烷、N-β(氨乙基)-γ-氨丙基三甲氧基硅烷、苯胺甲基三乙氧基硅烷、γ-氨丙基三乙氧基硅烷、乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷和γ-氯丙基三乙氧基硅烷中的一种或多种。
所述阻燃剂为无卤含磷高效阻燃剂,型号FR-U703。
一种阻燃人造石英石板材的制备方法,包括以下步骤:
(1)按照配方称取各组份;
(2)搅拌:将称取的石英颗粒、玻璃颗粒、阻燃剂、硅烷偶联剂于双行星式搅拌桶中预混合;将已混合好的固化剂、装饰有色颜料和不饱和聚酯树脂倒入双行星式搅拌桶中进行混合,然后加入石英粉进行混合,搅拌频率15~55Hz,搅拌时间180~600s;
(3)布料:将步骤(2)混合好的物料送入打散机进一步打散,打散后,经电子计量进入布料机内布料;
(4)压制:布料完成之后,在-0.1Mpa的真空条件下经压制设备振动压制成型,压力50~200t,振动频率30~55Hz,时间60~600s;
(5)热固化:经振动压制后,进入固化设备,在80~130℃的温度下固化,固化时间为30~180分钟;
(6)固化完成后,常温放置待冷却完全后进入板材定厚机定厚,再经过水磨抛光设备进行抛光。
与现有技术相比,本发明的有益效果是:
本发明所述一种阻燃人造石英石板材,包括如下原料:0.075~5mm颗粒原料、0.005~0.045mm石英粉、有色颜料、硅烷偶联剂、不饱和聚酯树脂、固化剂、阻燃剂,对人造石英石产品力学性能有一定增强作用,其具有抗冲击性能好、弯曲强度高,不易开裂、致密性好等优点。
具体实施方式
以下对本发明的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本发明,并不用于限定本发明。
本发明所述一阻燃人造石英石板材,包括如下原料:按照重量百分比,0.075~5mm颗粒原料60%、0.005~0.045mm石英粉23%;有色颜料6.5%;硅烷偶联剂0.5%;不饱和聚酯树脂7.6%;固化剂1%,阻燃剂1.4%,其大小根据板材的规格大小来剪裁。
其中,颗粒原料为石英颗粒或玻璃颗粒,或两种的混合物。
有色颜料为有机颜料或色浆的一种或多种,有机颜料为大红粉,酞青绿和酞菁蓝,色浆为白浆、黑浆、大红浆,酞青绿浆、酞菁蓝浆。
不饱和聚酯树脂也可以是环氧树脂、酚醛树脂、丙烯酸树脂和聚氨酯树脂中的一种或多种。
固化剂为过氧化(2-乙基己酸)叔丁酯、过氧化甲乙酮、过氧化苯甲酸叔丁酯、过氧化二苯甲酰和脂肪多元胺中的一种或多种。
硅烷偶联剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷、N-β(氨乙基)-γ-氨丙基甲基二甲氧基硅烷、N-(β-氨乙基)-γ-氨丙基三乙氧基硅烷、N-β(氨乙基)-γ-氨丙基三甲氧基硅烷、苯胺甲基三乙氧基硅烷、γ-氨丙基三乙氧基硅烷、乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷和γ-氯丙基三乙氧基硅烷中的一种或多种。
所述阻燃剂为无卤含磷高效阻燃剂,型号FR-U703,液态的。
一种阻燃人造石英石板材的制备方法,包括以下步骤:
(1)按照配方称取各组份;
(2)搅拌:将称取的石英颗粒、玻璃颗粒、阻燃剂、硅烷偶联剂于双行星式搅拌桶中预混合;将已混合好的固化剂、装饰有色颜料和不饱和聚酯树脂倒入双行星式搅拌桶中进行混合,然后加入石英粉进行混合。搅拌频率15~55Hz,搅拌时间180~600s;
(3)布料:将步骤(2)混合好的物料送入打散机进一步打散,打散后,经电子计量进入布料机内布料;
(4)压制:布料完成之后,在-0.1Mpa的真空条件下经压制设备振动压制成型,压力50~200t,振动频率30~55Hz,时间60~600s;
(5)热固化:经振动压制后,进入固化设备,在80~130℃的温度下固化,固化时间为30~180分钟;
(6)固化完成后,常温放置待冷却完全后进入板材定厚机定厚,再经过水磨抛光设备进行抛光。
最后应说明的是:以上仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换,但是凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (10)
1.一种阻燃人造石英石板材,其特征在于:包括如下原料:0.075~5mm颗粒原料、0.005~0.045mm石英粉、有色颜料、硅烷偶联剂、不饱和聚酯树脂、固化剂、阻燃剂。
2.根据权利要求1所述一种阻燃人造石英石板材,其特征在于:按照重量百分比,0.075~5mm颗粒原料55%~65%、0.005~0.045mm石英粉20%~30%;有色颜料0.01%~10%;硅烷偶联剂0.1%~1%;不饱和聚酯树脂7%~14%;固化剂0.8%~1.4%,阻燃剂1%~3.8%;
其中,颗粒原料为石英颗粒或玻璃颗粒,或两种的混合物。
3.根据权利要求1所述一种阻燃人造石英石板材,其特征在于:所述有色颜料为无机颜料或有机颜料或色浆的一种或多种。
4.根据权利要求3所述一种阻燃人造石英石板材,其特征在于:所述无机颜料为无机颜料,所述无机颜料为钛白、中铬黄、铁黄、铁红、铁蓝、镉红、镉黄、炭黑或铁黑;所述有机颜料为大红粉、偶氮黄、酞青绿或酞菁蓝有机颜料。
5.根据权利要求3所述一种阻燃人造石英石板材,其特征在于:所述色浆为白浆、黑浆、大红浆、酞青绿浆或酞菁蓝浆。
6.根据权利要求3所述一种阻燃人造石英石板材,其特征在于:所述不饱和聚酯树脂是环氧树脂、酚醛树脂、丙烯酸树脂和聚氨酯树脂中的一种或多种。
7.根据权利要求1所述一种阻燃人造石英石板材,其特征在于:所述固化剂为过氧化(2-乙基己酸)叔丁酯、过氧化甲乙酮、过氧化苯甲酸叔丁酯、过氧化二苯甲酰和脂肪多元胺中的一种或多种。
8.根据权利要求1所述一种阻燃人造石英石板材,其特征在于:所述硅烷偶联剂为γ-甲基丙烯酰氧基丙基三甲氧基硅烷、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷、N-β(氨乙基)-γ-氨丙基甲基二甲氧基硅烷、N-(β-氨乙基)-γ-氨丙基三乙氧基硅烷、N-β(氨乙基)-γ-氨丙基三甲氧基硅烷、苯胺甲基三乙氧基硅烷、γ-氨丙基三乙氧基硅烷、乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷和γ-氯丙基三乙氧基硅烷中的一种或多种。
9.根据权利要求1所述一种阻燃人造石英石板材,其特征在于:所述阻燃剂为无卤含磷高效阻燃剂,型号FR-U703。
10.一种阻燃人造石英石板材的制备方法,其特征在于:包括以下步骤:
(1)按照配方称取各组份;
(2)搅拌:将称取的石英颗粒、玻璃颗粒、阻燃剂、硅烷偶联剂于双行星式搅拌桶中预混合;将已混合好的固化剂、装饰有色颜料和不饱和聚酯树脂倒入双行星式搅拌桶中进行混合,然后加入石英粉进行混合,搅拌频率15~55Hz,搅拌时间180~600s;
(3)布料:将步骤(2)混合好的物料送入打散机进一步打散,打散后,经电子计量进入布料机内布料;
(4)压制:布料完成之后,在-0.1Mpa的真空条件下经压制设备振动压制成型,压力50~200t,振动频率30~55Hz,时间60~600s;
(5)热固化:经振动压制后,进入固化设备,在80~130℃的温度下固化,固化时间为30~180分钟;
(6)固化完成后,常温放置待冷却完全后进入板材定厚机定厚,再经过水磨抛光设备进行抛光。