CN106629650A - 一种单分散酚醛树脂微球以及多孔碳微球的宏量制备方法 - Google Patents
一种单分散酚醛树脂微球以及多孔碳微球的宏量制备方法 Download PDFInfo
- Publication number
- CN106629650A CN106629650A CN201610845783.2A CN201610845783A CN106629650A CN 106629650 A CN106629650 A CN 106629650A CN 201610845783 A CN201610845783 A CN 201610845783A CN 106629650 A CN106629650 A CN 106629650A
- Authority
- CN
- China
- Prior art keywords
- phenolic resin
- porous carbon
- resin microspheres
- microspheres
- carbon microsphere
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (7)