CN106366232A - 一种微孔pmi泡沫的制备方法及制备得到的pmi泡沫 - Google Patents
一种微孔pmi泡沫的制备方法及制备得到的pmi泡沫 Download PDFInfo
- Publication number
- CN106366232A CN106366232A CN201610830966.7A CN201610830966A CN106366232A CN 106366232 A CN106366232 A CN 106366232A CN 201610830966 A CN201610830966 A CN 201610830966A CN 106366232 A CN106366232 A CN 106366232A
- Authority
- CN
- China
- Prior art keywords
- foam
- ultrasonic
- preparation
- plate body
- pmi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (8)