CN1060500C - 农膜稀土荧光粉转换剂的制备 - Google Patents
农膜稀土荧光粉转换剂的制备 Download PDFInfo
- Publication number
- CN1060500C CN1060500C CN96123701A CN96123701A CN1060500C CN 1060500 C CN1060500 C CN 1060500C CN 96123701 A CN96123701 A CN 96123701A CN 96123701 A CN96123701 A CN 96123701A CN 1060500 C CN1060500 C CN 1060500C
- Authority
- CN
- China
- Prior art keywords
- changing agent
- fluorescent powder
- agricultural film
- rare
- earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种农膜稀土荧光粉转换剂的制备方法,即选择对稀土离子铕能量传递效率高、光稳定性好的羧酸配体,稀土镧、钇或者铈作为基质,用少量的铕离子作为激活剂合成出新型的农膜荧光粉转换剂,其外观呈白色,激发光谱是宽带240-420nm,最大值位于280nm,发射光谱是窄带580-630nm,最大值位于612nm,其中580-600nm的橙光发射只占总发射强度的3%,因此,它可以吸收太阳辐射中的短波紫外光,发射亮度大、效率高、色纯度好的红光。
Description
本发明属于农膜稀土荧光粉转换剂的制备方法.
农业生产的发展日益依赖于高技术的采用,目前农业部门迫切要求研制性能优良的红光转换剂。因为红光转换剂用在农膜中,可将太阳辐射中对蔬菜有害的紫外光转换成红光,促进蔬菜的生长,从而达到增温、早熟、增产、增收的效果,某些稀土有机配合物具有发光效率高、色纯度好、稳定性强、分散性佳等特点,适合于作红光转换剂,引起科学家们的极大光趣,可以预见高性能的农膜稀土红光转换剂具有广阔的应用前景。
1996年《塑料)》杂志第二十五期报导中国农膜用光转换剂都只能吸收太阳辐射中的部分长波紫外光(340—380nm)转变成可见光红光(600—630nm)。但是,上述农膜荧光转换剂的共同缺点是激发光光谱分布在长波,最大值位于360nm附近,不能有效地吸收短波紫外光因此,量子效率不够高,使用寿命不够长,光稳定性差,而且成本相对都较高。
本发明的目的是提供一种农膜稀土荧光粉转换剂的制备方法,即选择对稀土离子铕能量传递效率高、光稳定性好的羧酸配体,稀土镧、钇或者铈作为基质,用少量的铕离子作为激活剂合成新型高性能的农膜荧光转换剂,荧光转换剂稳定性、相容性及最佳荧光转换剂的筛选是获得高性能转换剂的根本保证,本发明使用通常的化学合成方法得到离效率、高亮度、稳定性好、使用寿命长及成本低有农业开发价值的红光转换剂。
本发明使用的原料由下列组分构成,其通式为LnL4,其中Ln=镧,钇,铈,铕;L=1—羟基—2—萘甲酸,均苯四甲酸,邻苯甲酰苯甲酸。使用的试剂为盐酸、氨水等常见化学试剂,按化学计量比称取稀土氧化物,其中基质La2O3,Y2O3,CeO2的总和占重量比的90%,激活剂Eu2O3,占重量的10%,把基质和激活剂混合溶解于1∶1的稀盐酸中,把配体羧酸溶解在蒸馏水中,两种溶液混合后,调节PH=3—6,采用的工艺流程为溶解→搅拌→沉淀→过滤→烘干→研磨→过筛→成品。
本发明的稀土荧光转换剂粉末外观呈白色其激发光谱是一个宽带240—420nm,最大激发波长位于280nm,发射光谱是一个窄带580—630nm,最大值位于612nm,其中580—600nm的橙光发射只占总发射强度的3%,因此,它可以吸收太阳辐射中的短波紫外光,发射亮度大,效率高、色纯度好的红光。
本发明的荧光转换剂和高亮度的稀土配合物标准荧光粉季铵盐α—噻吩基甲酰三氟丙酮铕相比,在254nm激发下(把标准样品的相对亮度定为100%)其相对亮度约为标准样品的62%,本发明荧光转换剂在空气中,放置18个月,其发射强度和量子效率不变,说明稳定性很高,经过测试,光转换剂使用寿命可达1年半,透光率达国标,分散性好(14μm厚膜1cm2内无>2μm的粒子),膜物理机械性能达到国标,每公斤荧光转换剂可降低成本300元。
本发明的光转换剂制成农膜其膜生产设备,工艺与普通膜相同,在确保光转换功能条件下,制备长寿命的聚乙烯膜。
本发明提供的实施例如下:
实施例1:
按重量比称取基质氧化镧La2O3 90毫克,激活剂氧化铕Eu2O3 10毫克溶于1∶1盐酸中,称取配体1—羟基—2—萘甲酸400毫克溶于蒸馏水中,然后将这两种溶液混合,调节PH值为3—6,搅拌反应半小时,出现白色沉淀,过滤→洗涤→烘干及过筛,得到高性能红光转换剂。在240—380nm特别是250—290nm紫外光激发下,发射明亮的612nm红光。
实施例2:
按重量比称取基质Y2O3 92毫克,激活剂氧化铕Eu2O3 8毫克溶于1∶1盐酸中,称取配体均苯四甲酸400毫克溶于蒸馏水中,然后将这两种溶液混合,调节PH值为3—6,搅拌反应半小时,出现白色沉淀,通过过滤→洗涤→烘干及过筛,得到高性能红光转换剂。在240—380nm特别是250—290nm紫外光激发下,发射明亮的612nm红光。
实施例3:
按重量比称取基质氧化铈CeO2 90毫克,激活剂氧化铕Eu2O3 10毫克溶于1∶1盐酸中,称取邻苯甲酰苯甲酸400毫克溶于蒸馏水中。然后将这两种溶液混合,调节PH值为3—6,搅拌反应半小时,出现白色沉淀,过滤→洗涤→烘干及过筛,得到高性能红光转换剂。在240—380nm特别是250—290nm紫外光激发下,发射明亮的612nm红光。
Claims (1)
1.一种农膜稀土荧光粉转换剂的制备方法,其特征在于选择的原料由下列组分构成,其通式为LnL4,其中Ln=镧,钇,铈,铕;L=1—羟基—2—苯甲酸,均苯四甲酸;邻苯甲酰苯甲酸,使用的试剂为盐酸,氨水,按化学计量比称取稀土氧化物,其中基质La2O3,Y2O3,CeO2的总和占重量比的90%,激活剂Eu2O3占重量的10%,把基质和激活剂混合溶解于1∶1的稀盐酸中,把配体羧酸溶解在蒸馏水中,两种溶液混合后,调节PH=3—6,采用的工艺流程为溶解→搅拌→沉淀→过滤→烘干→研磨→过筛→成品,得到的荧光转换剂外观呈白色其激发光谱是一个宽带240—420nm,最大激发波长位于280nm,发射光谱是一个窄带580—630nm,最大值位于612nm,其中580—600nm的橙光发射只占总发射强度的3%。