CN106008913A - 一种耐水解聚氨酯树脂及其在耐水解镜面革中的应用 - Google Patents

一种耐水解聚氨酯树脂及其在耐水解镜面革中的应用 Download PDF

Info

Publication number
CN106008913A
CN106008913A CN201610388055.3A CN201610388055A CN106008913A CN 106008913 A CN106008913 A CN 106008913A CN 201610388055 A CN201610388055 A CN 201610388055A CN 106008913 A CN106008913 A CN 106008913A
Authority
CN
China
Prior art keywords
parts
polyurethane resin
hydrolysis
resistant polyurethane
hydrolysis resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610388055.3A
Other languages
English (en)
Inventor
张勇
文远海
齐佳圭
何俭辉
韩方平
朱沂
陈伟波
杨旭东
李毅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAIZHOU HEXIN POLYMER NEW MATERIAL Co Ltd
Original Assignee
TAIZHOU HEXIN POLYMER NEW MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAIZHOU HEXIN POLYMER NEW MATERIAL Co Ltd filed Critical TAIZHOU HEXIN POLYMER NEW MATERIAL Co Ltd
Priority to CN201610388055.3A priority Critical patent/CN106008913A/zh
Publication of CN106008913A publication Critical patent/CN106008913A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐水解聚氨酯树脂，包括如下重量份数的组分：二苯基甲烷‑4,4’‑二异氰酸酯10.5份‑13.0份、多元醇组合物12份‑15份、小分子扩链剂2.5份‑4.5份、N,N‑二甲基甲酰胺溶剂68份‑72份、封端剂0.03份‑0.1份和助剂1份‑2份，该聚氨酯树脂无泡孔或细小泡孔结构、凝固速度适中、水洗速度快，耐水解性能达到12小时耐碱后剥离保持率在80%以上，并且利用该聚氨酯树脂制造耐水解镜面革。

Description

一种耐水解聚氨酯树脂及其在耐水解镜面革中的应用
技术领域
本发明涉及聚氨酯树脂领域，特别涉及一种耐水解聚氨酯树脂及其在耐水解镜面革中的应用。
背景技术
PU合成革广泛应用于衣食住行等各个领域，随着合成革行业的不断发展与进步，作为合成革行业的上游企业，也需要不断的跟紧发展的步伐，不断提高产品性能以满足客户需求。聚氨酯树脂对合成革产品的性能起到了决定性作用，尤其是对耐水解、耐黄变，耐磨等性能。镜面PU合成革也是PU合成革中应用范围比较广，需求量比较大的产品，但由于普通合成革在长期水气侵袭后会发生水解、变质，在寒冷地区会因长期受低温变硬、易折断，剥离强度降低，同时，随着合成革市场的发展，普通镜面PU合成革已经无法满足人们正常生活水平的需要，镜面革已经由普通镜面革向耐水解镜面革升级。
发明内容
本发明的第一发明目的是提供一种耐水解的聚氨酯树脂。
本发明的上述技术目的是通过以下技术方案得以实现的：一种耐水解聚氨酯树脂，其中：包括如下重量份数的组分：
二苯基甲烷-4，4’-二异氰酸酯(MDI)具有对称的化学结构，可以形成结构规整且有序的相区，相应聚氨酯的强度、硬度和结晶度等都比较大，且具有很好的耐磨性。
作为优选方案，所述多元醇聚合物包括聚酯多元醇和聚醚多元醇，其中聚醚多元醇与聚酯多元醇的质量比为9∶1-7∶3之间。
聚酯多元醇制备的聚氨酯产品强度和硬度较大，因为如聚酯型聚氨酯分子内部一般含有强极性的酯基基团，内聚强度大，而且酯基易与N-H生成氢键，使分子链段的运动受到限制；而由聚醚多元醇制备的聚氨酯一般具有良好的弹性和延伸率，因为醚键的旋转比较容易，且其能使聚氨酯具有较好的耐低温性、疏水性和耐水解性，采用不同分子量大小的多元醇调整泡孔结构，采用70％以上的聚醚多元醇以提高耐水解性能，采用聚醚多元醇和聚酯多元醇共聚的方法以提高产品的水洗速度，同时也降低反应结晶性。另外，结晶性的降低，对泡孔结构也有影响，使泡孔结构更细小，满足镜面革用聚氨酯树脂的无泡孔或细小泡孔结构的要求。
作为优选方案，所述聚酯多元醇的分子量在2000-4000之间，聚醚多元醇的分子量在1000-3000之间。
作为优选方案，所述小分子扩链剂为乙二醇、二乙二醇、1，4-丁二醇、2，2-二甲基-1，3-丙二醇中的任意两种。
为了调整凝固和水洗速度，使得凝固速度适中，水洗速度加快，选择混合扩链剂，通过调整混合扩链剂各组分的质量比，缓解树脂表面凝固速度。
作为优选方案，所述聚酯多元醇为己二酸与二元醇反应得到的二醇系化合物。
作为优选方案，所述聚酯多元醇的制备中与己二酸反应的二元醇是乙二醇、二乙二醇、1，4-丁二醇中的一种或者两种混合物。
作为优选方案，所述聚醚多元醇化合物为环氧丙烷缩合物和聚四亚甲基醚二醇中的一种或多种。
作为优选方案，所述封端剂为甲醇和异丙醇中的一种或两种。
甲醇和异丁醇具有稳定的甲基和异丁基，醇基与反应链的端部反应将甲基和异丁基添加到相应位置，从而消除封端处的活性，终止分子链段的继续增长。
作为优选方案，所述助剂为氨基改性硅油和环氧基改性硅油中的一种或两种。
氨基硅油是侧链或端基中含有氨基的聚二甲基硅氧烷，将硅引入聚氨酯树脂中，提高聚氨酯树脂的耐水性，并且在制成皮革时具有更好的手感，以及提高水洗速度。
环氧基硅油是聚二甲基硅氧烷的侧链或端基中含有环氧基的一类硅油，可以提高聚氨酯树脂的弹性，增强耐水性，与氨基硅油调配使用可以使聚氨酯树脂制成的合成革具有更好的柔软性，提高手感。
本技术方案生产出的聚氨酯树脂无泡孔或细小泡孔结构、凝固速度适中、水洗速度快，耐水解性能达到12小时耐碱后剥离保持率在80％以上。
本发明的第二发明目的在于提供一种耐水解的镜面革。
本发明的上述技术目的是通过以下技术方案实现的：一种耐水解的镜面革，采用上述技术方案中制得的聚氨酯树脂加工而成。
具体实施方式
实施例一：
一种耐水解聚氨酯树脂，包括如下质量的组分(Kg)：
其中聚酯多元醇的分子量为：2000
环氧丙烷缩合物的分子量为：1500。
实施例二：
一种耐水解聚氨酯树脂，包括如下质量的组分(Kg)：
其中聚酯多元醇的分子量为：3000
聚四亚甲基醚二醇的分子量为：1000。
实施例三：
一种耐水解聚氨酯树脂，包括如下质量的组分(Kg)：
其中聚酯多元醇的分子量为：4000
聚四亚甲基醚二醇：2500
环氧丙烷缩合物的分子量为：2500。
实施例四：
一种耐水解聚氨酯树脂，包括如下质量的组分(Kg)：
其中聚酯多元醇的分子量为：2500
聚四亚甲基醚二醇的分子量为：2000。
实施例五：
一种耐水解聚氨酯树脂，包括如下质量的组分(Kg)：
其中聚酯多元醇的分子量为：3500
环氧丙烷缩合物的分子量为：3000。
对比例一：
一种耐水解聚氨酯树脂，包括如下质量的组分(Kg)：
其中聚酯多元醇的分子量为：3500
环氧丙烷缩合物的分子量为：3000。
上述实施例与对比例都采用如下方法制备：
步骤一：将多元醇组合物与部分异氰酸酯在溶剂DMF中进行预聚反应；
步骤二：将小分子扩链剂和溶剂DMF与步骤一所得的预聚物充分反应，再加入剩余异氰酸酯，并在反应过程中加入溶剂，调整树脂粘度在0.1～30000Mpa·s/25℃；
步骤三：加入封端剂终止反应，再加入助剂和少量溶剂DMF充分搅拌均匀。
为了验证本发明的聚氨酯树脂具有能优异的耐水解性能，对上述实施例的产品进行分别实验，具体实验步骤如下：
将上述实施例和对比例的产品按照合成革加工配方制作成Base样并分别裁取宽度30mm长度80mm的长条片状样品各三片，放置在10％的氢氧化钠水溶液中，在室温下放置12小时后，用清水洗净至PH为中性后80℃烘干，测试剥离强度；记录各个样品在放置10％的氢氧化钠水溶液中12小时前后的剥离强度，测试结果见表1。
表1剥离强度测试结果
从上述实验数据看出，本发明的聚氨酯树脂的耐水解性能大大增强，满足设计的耐碱后剥离保持率在80％以上的要求。
进一步的，再测试本发明产品的泡孔结构：将普通镜面革用聚氨酯树脂和本实施例和对比例中的产品按照合成革加工配方制作成Base样后用锋利的刀片切开，观察横切面泡孔结构，观察结果见下表2。
表2泡孔结构观察结果
样品 是否具有泡孔结构
普通镜面革用聚氨酯树脂 具有较大泡孔
实施例1样品 无泡孔
实施例2样品 均匀细小泡孔
实施例3样品 无泡孔
实施例4样品 均匀细小泡孔
实施例5样品 均匀细小泡孔
对比例1样品 均匀细小泡孔
进一步再测试本发明样品的凝固速度和水洗速度，即DMF从聚氨酯溶液中萃取出来的速度。
将普通镜面革用聚氨酯树脂和本实施例中的产品按照合成革加工配方搅拌均匀后刮涂在革基布上，每隔一分钟观察凝固速度。待完全凝固后放入清水中浸泡，并每隔一分钟裁剪一条长约80mm，宽约15mm的样品测试其水洗情况，测试结果见如下表3。
表3水洗速度测试结果
样品 凝固速度(min) 水洗速度(mm)
普通镜面革用聚氨酯树脂 7 7
实施例1样品 7 3
实施例2样品 7 4
实施例3样品 6 4
实施例4样品 6 3
实施例5样品 8 3
对比例1样品 7 3
从表2和表3可以看出本发明制备的聚氨酯树脂具有无泡孔或细小泡孔结构、12小时耐碱后耐剥离保持率在90％以上，水洗速度快。
应当指出：对于本行业的技术人员来说，在不脱离本发明原理的前提下，还可以做出各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等同物界定。

Claims (10)

1.一种耐水解聚氨酯树脂，其特征在于：包括如下重量份数的组分：
二苯基甲烷-4,4’-二异氰酸酯 10.5份-13.0份
多元醇组合物 12份-15份
小分子扩链剂 2.5份-4.5份
N,N-二甲基甲酰胺溶剂 68份-72份
封端剂 0.03份-0.1份
助剂 1份-2份。
2.根据权利要求1所述的一种耐水解聚氨酯树脂，其特征在于：所述多元醇组合物包括聚醚多元醇和聚酯多元醇，其中聚醚多元醇与聚酯多元醇的质量比为9:1-7:3之间。
3.根据权利要求1所述的一种耐水解聚氨酯树脂，其特征在于：聚酯多元醇的分子量在2000-4000之间，聚醚多元醇的分子量在1000-3000之间。
4.根据权利要求1所述的一种耐水解聚氨酯树脂，其特征在于：所述小分子扩链剂为乙二醇、二乙二醇、1,4-丁二醇、2,2-二甲基-1,3-丙二醇中的任意两种。
5.根据权利要求1所述的一种耐水解聚氨酯树脂，其特征在于：所述聚酯多元醇为己二酸与二元醇反应得到的二醇系化合物，其中与己二酸反应的二元醇是乙二醇、二乙二醇、1,4-丁二醇中的一种或者两种混合物。
6.根据权利要求1所述的一种耐水解聚氨酯树脂，其特征在于：所述聚醚多元醇化合物为环氧丙烷缩合物和聚四亚甲基醚二醇中的一种或两种。
7.根据权利要求1所述的一种耐水解聚氨酯树脂，其特征在于：所述封端剂为甲醇、异丙醇中的一种或两种。
8.根据权利要求1所述的一种耐水解聚氨酯树脂，其特征在于：所述助剂为硅油类助剂。
9.根据权利要求8所述的一种耐水解聚氨酯树脂，其特征在于：所述硅油类助剂为氨基改性硅油和环氧基改性硅油中的一种或两种。
10.权利要求1至9任一所述的一种耐水解聚氨酯树脂在制造耐水解镜面革中的应用。
CN201610388055.3A 2016-06-02 2016-06-02 一种耐水解聚氨酯树脂及其在耐水解镜面革中的应用 Pending CN106008913A (zh)