CN105237906A - 高回弹性抗菌型医用聚氯乙烯塑料及其制备方法 - Google Patents

高回弹性抗菌型医用聚氯乙烯塑料及其制备方法 Download PDF

Info

Publication number
CN105237906A
CN105237906A CN201510657292.0A CN201510657292A CN105237906A CN 105237906 A CN105237906 A CN 105237906A CN 201510657292 A CN201510657292 A CN 201510657292A CN 105237906 A CN105237906 A CN 105237906A
Authority
CN
China
Prior art keywords
resilience
high resilience
antimicrobial form
form medical
medical polyvinyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510657292.0A
Other languages
English (en)
Inventor
王芹
唐艳芳
吴唯
卞俭俭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XINSHANGHUA HIGH MOLECULAR MATERIAL CO Ltd SHANGHAI
Original Assignee
XINSHANGHUA HIGH MOLECULAR MATERIAL CO Ltd SHANGHAI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XINSHANGHUA HIGH MOLECULAR MATERIAL CO Ltd SHANGHAI filed Critical XINSHANGHUA HIGH MOLECULAR MATERIAL CO Ltd SHANGHAI
Priority to CN201510657292.0A priority Critical patent/CN105237906A/zh
Publication of CN105237906A publication Critical patent/CN105237906A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种高回弹性抗菌型医用聚氯乙烯塑料及其制备方法，高回弹性抗菌型医用聚氯乙烯塑料，包括以下重量份的组分：超高分子量聚氯乙烯树脂100份，增塑剂40～80份，弹性体10～60份，辅助增塑剂5～20份，热稳定剂0.5～5份。本发明物理性能、化学性能和生物性能良好，满足GB15593-1995输血(液)器具用软聚氯乙烯塑料相关要求，回弹性优异、具有抗菌、抑菌作用的医用PVC塑料及其制备方法。所制备的PVC塑料具有抗菌、抑菌、回弹性优异的特性，能够缩短环氧乙烷灭菌周期，提高灭菌效率。

Description

高回弹性抗菌型医用聚氯乙烯塑料及其制备方法
技术领域
本发明涉及一种医用聚氯乙烯材料，具体是一种高回弹性抗菌型医用聚氯乙烯塑料。
背景技术
聚氯乙烯(PVC)因其具有廉价、综合性能好等特点，在各个领域有广泛应用，是目前最广泛使用的塑料之一。目前普遍应用的输血袋、输液袋、医用导管、血液透析管路等，大都采用医用PVC加工制成。医用PVC材料性能优良、价格低廉、使用方便，但也存在着一些问题。首先，目前我国医用器材广泛采用环氧乙烷灭菌，环氧乙烷是一种易燃易爆、疑似致癌的有毒气体，对环境为一定危害，灭菌后需较长时间通风，整个灭菌周期需要约2周时间，存在灭菌效率低下的问题。其次，一些医院管路对所用材料的弹性要求较高，如血液透析管路中的泵管需要材料具有较高的回弹性，目前常规PVC材料并不能满足其弹性需求。第三，PVC器材经灭菌处理后保存期内及使用过程中没有对二次污染进行预防，患者安全性得不到保障。
发明内容
本发明的目的是提供一种高回弹性抗菌型医用聚氯乙烯塑料及其制备方法，以克服现有技术存在的不足。
所述的高回弹性抗菌型医用聚氯乙烯塑料，包括以下重量份的组分：
优选的，所述的一种高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，包括以下重量份的组分：
优选的，还包括抗菌剂1～10份，优选1～5份；
优选的，还包括润滑剂0.1～1份，优选0.3～0.6；
所述的聚氯乙烯树脂为悬浮法聚合的超高分子量聚氯乙烯树脂，聚合度为2000～2500，分子量为10万～18；
所述增塑剂为邻苯二甲酸二辛脂(DOP)、对苯二甲酸二辛酯(DOTP)、邻苯二甲酸二异壬酯(DINP)、乙酰柠檬酸三丁酯(ATBC)、乙酰柠檬酸三辛酯(ATOC)、己二酸二辛脂(DOA)、癸二酸二辛脂(DOS)中的一种或几种的复配。
所述弹性体为苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)、丁腈橡胶(NBR)、聚氨酯(TPU)或乙烯辛烯共聚物(POE)中的一种以上；
优选的，所述弹性体为苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)、丁腈橡胶(NBR)、聚氨酯(TPU)或乙烯辛烯共聚物(POE)的混合物，重量比为：
苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物∶丁腈橡胶∶聚氨酯∶乙烯辛烯共聚弹性体
＝1∶0.2～0.3∶0.3～0.4∶0.2～0.3；
苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物为线型结构，苯乙烯含量为25％～45％，分子量5万～20万；
丁腈橡胶的平均分子量为60万～80万；
聚氨酯采用聚酯型结构，分子量为1万～10万；
乙烯辛烯共聚物中辛烯含量为40％～60％；
所述辅助增塑剂为环氧亚麻籽油(ELO)或环氧大豆油(ESO)。
所述抗菌材料为甲壳素抗菌粉或纳米银抗菌粉。
所述热稳定剂为硬脂酸钙、硬脂酸锌的混合物。
所述润滑剂为硅油、聚乙烯蜡、硬脂酸、氧化聚乙烯蜡或聚酰胺蜡中的一种。
所述高回弹性抗菌型医用聚氯乙烯塑料的制备方法，包括以下步骤：
将聚氯乙烯、增塑剂、辅助增塑剂、弹性体依次加入高速混合机，低速20～40rpm加热搅拌至80℃后加入抗菌材料和热稳定剂，以400～600rpm运转，至温度达120℃后加入润滑剂。持续搅拌至140℃放料至冷却混合机，转速30rpm。待物料温度冷却至45～60℃出料。
将步骤(1)所得物料使用双螺杆挤出机进行造粒。主机螺杆转速40～100rpm，挤出机各段温度：第一段100～120℃，第二段120～150℃，第三段150～170℃，第四段150～170℃，模头温度145～165℃。物料经挤出机塑化风冷造粒，冷却至35～45℃即可进行包装。
本发明所制备的一种高回弹性抗菌型医用聚氯乙烯塑料选用了具有颗粒疏松、加工性能良好、吸油量较高的超高聚合度的PVC树脂，并加入弹性体组分，保证了PVC塑料的弹性，并避免了高聚合度树脂在加工过程中容易出现的熔体黏度过大、产品不易加工等问题。加入了高效抗菌剂甲壳素或纳米银，赋予了PVC材料抗菌、抑菌特性，能够大大缩短环氧乙烷灭菌周期，提高了灭菌效率，降低了环氧乙烷带给环境的危害。本发明解决了目前医用PVC塑料回弹性不足、环氧乙烷灭菌周期长、保存期内无菌效果得不到保障的问题，提供了一种物理性能、化学性能和生物性能良好，满足GB15593-1995输血(液)器具用软聚氯乙烯塑料相关要求，回弹性优异、具有抗菌、抑菌作用的医用PVC塑料及其制备方法。所制备的PVC塑料具有抗菌、抑菌、回弹性优异的特性，能够缩短环氧乙烷灭菌周期，提高灭菌效率。
具体实施方式
实施例中：
拉伸弹性回缩率(％)采用检测的具体方法为：冲切厚度为1.0mm±0.1mm的5型哑铃片三片，在每片试样中央部分标出距离为20mm的标线，把试样放至拉伸试验机的夹具内，进行拉伸，拉伸速度为250mm/min，将标距拉伸至原长的两倍，保持1min，卸去负荷，取下试样，将其放在光滑的台面上1min，测出标线间的距离为L，用以下公式进行计算：D＝L20×100％，D即为拉伸弹性回缩率，取三次试验结果的平均值作为试验的拉伸弹性回缩率。
抑菌率％的检测方法采用以下公式计算：抑菌率(％)＝(阳性对照OD值—试验OD值)/(阳性对照OD值—阴性对照OD值)X100计算抑菌率。
实施例1
组分以及重量份配比：
聚氯乙烯树脂聚合度为2000；
热稳定剂为硬脂酸钙、硬脂酸锌的混合物，重量比为1：1；
制备方法
(1)将聚氯乙烯树脂、增塑剂、辅助增塑剂、弹性体加入高速混合机，30rpm加热搅拌至80℃后，加入抗菌材料和热稳定剂，450rpm运转至温度达120℃后，加入润滑剂。持续搅拌至140℃放料至冷却混合机，转速30rpm。待物料温度冷却至50℃出料。
(2)将步骤(1)所得物料使用双螺杆挤出机进行造粒。主机螺杆转速60rpm，挤出机各段温度：第一段110℃，第二段130℃，第三段160℃，第四段160℃，模头温度160℃。物料经挤出机塑化风冷造粒，冷却至45℃即可进行包装。
实施例2
聚氯乙烯树脂聚合度为2300；
热稳定剂为硬脂酸钙、硬脂酸锌的混合物，重量比为1：1；
制备方法同实施例1。
实施例3
聚氯乙烯树脂聚合度为2500；
弹性体为苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)、丁腈橡胶(NBR)、聚氨酯(TPU)或乙烯辛烯共聚物(POE)的混合物，重量比为：
苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物∶丁腈橡胶∶聚氨酯∶乙烯辛烯共聚弹性体
＝1∶0.2∶0.35∶0.25；
苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物中苯乙烯含量为30％，分子量为7万；
丁腈橡胶的平均分子量为65万；
聚氨酯的平均分子量为3万；
乙烯辛烯共聚物中辛烯含量为40％～60％；
热稳定剂为硬脂酸钙、硬脂酸锌的混合物，重量比为1：1；
制备方法同实施例1。
对比例1
聚氯乙烯树脂聚合度为2000；
热稳定剂为硬脂酸钙、硬脂酸锌的混合物，重量比为1：1；
制备方法同实施例1。：
对比例2
聚氯乙烯树脂聚合度为2000；
热稳定剂为硬脂酸钙、硬脂酸锌的混合物，重量比为1：1；
制备方法同实施例1。
表1实施例及对比例回弹性及抑菌效果测试结果
实施例1 实施例2 实施例3 对比例1 对比例2
拉伸弹性回缩率(％) 125 128 115 150 145
抑菌率(％) 99.2 99.5 99.8 60 99.5

Claims (10)

1.高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，包括以下重量份的组分：
2.高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，优选配方包括以下重量份的组分：
3.根据权利要求1或2所述的高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，还包括抗菌剂1～10份，润滑剂0.1～1份。
4.根据权利要求1或2所述的高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，所述的聚氯乙烯树脂为悬浮法聚合的超高分子量聚氯乙烯树脂，聚合度为2000～2500。
5.根据权利要求1或2所述的高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，所述增塑剂为邻苯二甲酸二辛脂(DOP)、对苯二甲酸二辛酯(DOTP)、邻苯二甲酸二异壬酯(DINP)、乙酰柠檬酸三丁酯(ATBC)、乙酰柠檬酸三辛酯(ATOC)、己二酸二辛脂(DOA)、癸二酸二辛脂(DOS)中的一种或几种的复配。
6.根据权利要求1或2所述的高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，所述弹性体为苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)、丁腈橡胶(NBR)、聚氨酯(TPU)或乙烯辛烯共聚物(POE)中的一种以上。
7.根据权利要求1或2所述的高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，所述弹性体为苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)、丁腈橡胶(NBR)、聚氨酯(TPU)或乙烯辛烯共聚物(POE)的混合物，重量比为：
苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物∶丁腈橡胶∶聚氨酯∶乙烯辛烯共聚弹性体＝1∶0.2～0.3∶0.3～0.4∶0.2～0.3；
苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物为线型结构，苯乙烯含量为25％～45％，分子量5万～20万；
丁腈橡胶的平均分子量为60万～80万；
聚氨酯采用聚酯型结构，分子量为1万～10万；
乙烯辛烯共聚物中辛烯含量为40％～60％。
8.根据权利要求7所述的高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，所述辅助增塑剂为环氧亚麻籽油(ELO)或环氧大豆油(ESO)。
9.根据权利要求3所述的高回弹性抗菌型医用聚氯乙烯塑料，其特征在于，所述抗菌材料为甲壳素抗菌粉或纳米银抗菌粉，所述热稳定剂为硬脂酸钙、硬脂酸锌的混合物。所述润滑剂为硅油、聚乙烯蜡、硬脂酸、氧化聚乙烯蜡或聚酰胺蜡中的一种。
10.根据权利要求1～9任一项所述的高回弹性抗菌型医用聚氯乙烯塑料的制备方法，其特征在于，包括以下步骤：
将聚氯乙烯、增塑剂、辅助增塑剂、弹性体依次加入高速混合机，低速20～40rpm加热搅拌至80℃后加入抗菌材料和热稳定剂，以400～600rpm运转，至温度达120℃后加入润滑剂。持续搅拌至140℃放料至冷却混合机，转速30rpm。待物料温度冷却至45～60℃出料。
将步骤(1)所得物料使用双螺杆挤出机进行造粒。主机螺杆转速40～100rpm，挤出机各段温度：第一段100～120℃，第二段120～150℃，第三段150～170℃，第四段150～170℃，模头温度145～165℃。物料经挤出机塑化风冷造粒，冷却至35～45℃即可进行包装。
CN201510657292.0A 2015-10-12 2015-10-12 高回弹性抗菌型医用聚氯乙烯塑料及其制备方法 Pending CN105237906A (zh)