CN105014998A - 一种木塑板材的生产工艺 - Google Patents

一种木塑板材的生产工艺 Download PDF

Info

Publication number
CN105014998A
CN105014998A CN201510384220.3A CN201510384220A CN105014998A CN 105014998 A CN105014998 A CN 105014998A CN 201510384220 A CN201510384220 A CN 201510384220A CN 105014998 A CN105014998 A CN 105014998A
Authority
CN
China
Prior art keywords
wood
production technology
raw material
extruder
plastic plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510384220.3A
Other languages
English (en)
Inventor
汪漭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGCHENG HONESTY WPC TECHNOLOGY MATERIAL Co Ltd
Original Assignee
TONGCHENG HONESTY WPC TECHNOLOGY MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGCHENG HONESTY WPC TECHNOLOGY MATERIAL Co Ltd filed Critical TONGCHENG HONESTY WPC TECHNOLOGY MATERIAL Co Ltd
Priority to CN201510384220.3A priority Critical patent/CN105014998A/zh
Publication of CN105014998A publication Critical patent/CN105014998A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种木塑板材的生产工艺，其主要步骤包括混合配料-挤出-冷却定型-牵引切割，本生产工艺过程简单易操作，生产出的木塑板材强度好、硬度高、防滑、耐磨、不开裂、不虫蛀，吸水性小、耐老化，有木材的自然外观、质感，比木材尺寸稳定性好，无木材节疤，不会产生裂纹、翘曲、变形，产品可制成多种颜色，可长久保新不退色。

Description

一种木塑板材的生产工艺
技术领域
    本发明涉及木塑制品生产工艺，特别是涉及一种木塑板材的生产工艺。
背景技术
木塑复合板材是一种主要由木材为基础材料与热塑性高分子材料和加工助剂等，混合均匀后再经模具设备加热挤出成型而制成的高科技绿色环保材料，兼有木材和塑料的性能与特征，能替代木材和塑料的新型环保高科技材料，木塑地板是用木塑复合材料制成的地板，拥有和木材一样的加工特性，使用普通的工具即可锯切、钻孔、上钉，非常方便，可以像普通木材一样使用。同时具有木材的木质感和塑料的耐水防腐特性，使得它成为一种性能优良并十分耐用的室外防水防腐建材，木塑复合材料是来才出现的新型环保建材，在国外也是刚刚起步。木塑产品所用的原料可用废旧塑料及废弃的木料、农林桔杆等植物纤维作基材，不含任何外加有害成分。而且可回收再次利用，称得上真正意义上的环保、节能、资源再生利用的新颖产品。
发明内容
本发明提供一种木塑板材的生产工艺。为实现本发明的目的，本发明的技术方案如下：
    一种木塑板材的生产工艺，其特征在于，其具体步骤为：
（1）混合配料
将PVC颗粒、稳定剂、润滑剂、发泡剂、发泡调节剂、和木粉按照15:1:3:1:5:23的比例在高速混合机中混匀，混合机的转速为5500-6000r/min，混合时间为15-25min；
（2）挤出
将混合均匀的原料喂入挤出机中，在挤出机中加热熔融被挤出，挤出温度为190-200℃，挤出压力为6.5-9.5MPa，挤出速度为0.35-0.55m3/min；
（3）冷却定型
熔融原料从挤出机中挤出到模具中，使用冷却水对原料进行冷却定型，冷却水的水温为5-8℃,；
（4）牵引切割
对定型木塑板进行牵引切割，牵引压力为0.088-0.125MPa，牵引速度为1.14-1.24m/min，切割完成的即为成品；
优选的，步骤（1）中原料中添加1.5%的加工助剂。
优选的，步骤（2）中在喂入挤出机之前先对原料进行冷却，冷却至35℃。
有益效果：本发明提供一种木塑板材的生产工艺，其主要步骤包括混合配料-挤出-冷却定型-牵引切割，本生产工艺过程简单易操作，生产出的木塑板材强度好、硬度高、防滑、耐磨、不开裂、不虫蛀，吸水性小、耐老化，有木材的自然外观、质感，比木材尺寸稳定性好，无木材节疤，不会产生裂纹、翘曲、变形，产品可制成多种颜色，可长久保新不退色。
具体实施方式
      为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
    一种木塑板材的生产工艺，其特征在于，其具体步骤为：
（1）混合配料
将PVC颗粒、稳定剂、润滑剂、发泡剂、发泡调节剂、和木粉按照15:1:3:1:5:23的比例在高速混合机中混匀，混合机的转速为5500r/min，混合时间为25min；
（2）挤出
将混合均匀的原料喂入挤出机中，在挤出机中加热熔融被挤出，挤出温度为200℃，挤出压力为8.5MPa，挤出速度为0.55m3/min；
（3）冷却定型
熔融原料从挤出机中挤出到模具中，使用冷却水对原料进行冷却定型，冷却水的水温为8℃,；
（4）牵引切割
对定型木塑板进行牵引切割，牵引压力为0.125MPa，牵引速度为1.14m/min，切割完成的即为成品；
其中，步骤（1）中原料中添加1.5%的加工助剂，步骤（2）中在喂入挤出机之前先对原料进行冷却，冷却至35℃。
本发明提供一种木塑板材的生产工艺，其主要步骤包括混合配料-挤出-冷却定型-牵引切割，本生产工艺过程简单易操作，生产出的木塑板材强度好、硬度高、防滑、耐磨、不开裂、不虫蛀，吸水性小、耐老化，有木材的自然外观、质感，比木材尺寸稳定性好，无木材节疤，不会产生裂纹、翘曲、变形，产品可制成多种颜色，可长久保新不退色。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (3)

1.一种木塑板材的生产工艺，其特征在于，其具体步骤为：
（1）混合配料
将PVC颗粒、稳定剂、润滑剂、发泡剂、发泡调节剂、和木粉按照15:1:3:1:5:23的比例在高速混合机中混匀，混合机的转速为5500-6000r/min，混合时间为15-25min；
（2）挤出
将混合均匀的原料喂入挤出机中，在挤出机中加热熔融被挤出，挤出温度为190-200℃，挤出压力为6.5-9.5MPa，挤出速度为0.35-0.55m3/min；
（3）冷却定型
熔融原料从挤出机中挤出到模具中，使用冷却水对原料进行冷却定型，冷却水的水温为5-8℃；
（4）牵引切割
对定型木塑板进行牵引切割，牵引压力为0.088-0.125MPa，牵引速度为1.14-1.24m/min，切割完成的即为成品。
2.根据权利要求1所述的一种木塑板材的生产工艺，其特征在于，步骤（1）中原料中添加1.5%的加工助剂。
3.根据权利要求1所述的一种木塑板材的生产工艺，其特征在于，步骤（2）中在喂入挤出机之前先对原料进行冷却，冷却至35℃。
CN201510384220.3A 2015-06-30 2015-06-30 一种木塑板材的生产工艺 Pending CN105014998A (zh)