CN104877310A - 一种耐折白塑料薄膜及其制备方法 - Google Patents
一种耐折白塑料薄膜及其制备方法 Download PDFInfo
- Publication number
- CN104877310A CN104877310A CN201510300121.2A CN201510300121A CN104877310A CN 104877310 A CN104877310 A CN 104877310A CN 201510300121 A CN201510300121 A CN 201510300121A CN 104877310 A CN104877310 A CN 104877310A
- Authority
- CN
- China
- Prior art keywords
- weight part
- plastics film
- folding
- white plastics
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐折白塑料薄膜及其制备方法，上述耐折白塑料薄膜，由包含以下重量份的组分制成：双酚S型环氧树脂18-25份、醋酸丁酸纤维素5-11份、双胺丙基聚二甲基硅氧烷1-3份、聚甲基氢硅氧烷0.1-2份、三氟化硼-二甲基苯胺0.02-0.8份、异佛尔酮二胺0.02-0.06份和聚乙二醇的水溶液55-75份。本发明还提供了上述耐折白塑料薄膜的制备方法。
Description
技术领域
本发明属于薄膜材料领域，尤其涉及一种耐折白塑料薄膜及其制备方法。
背景技术
薄膜是一种薄而软的透明薄片，主要通过塑料、胶粘剂、橡胶或其他材料制成。薄膜的制备材料通常为聚合物，主要有聚乙烯薄膜、聚丙烯薄膜、聚氯乙烯薄膜和聚酯薄膜等。主要有包装薄膜、透气薄膜或水溶薄膜和压电性能的薄膜等。
市售的薄膜大多是石油化工材料合成制备的高分子聚合膜，存在着能源消耗、污染环境等诸多问题，因此，研制一种工艺简单，成本低廉的薄膜成为行业发展的新要求。
发明内容
本发明的目的在于为解决上述问题，提供了一种耐折白塑料薄膜及其制备方法。本发明制得的耐折白塑料薄膜具有良好的透光性、表面硬度和耐压折性能。
本发明的目的可以通过下述技术方案来实现：
一种耐折白塑料薄膜，由包含以下重量份的组分制成：
双酚S型环氧树脂 18-25份，
醋酸丁酸纤维素 5-11份,
双胺丙基聚二甲基硅氧烷 1-3份，
聚甲基氢硅氧烷 0.1-2份，
三氟化硼-二甲基苯胺 0.02-0.8份，
异佛尔酮二胺 0.02-0.06份，
聚乙二醇的水溶液 55-75份。
所述组分还包括氧化钴 0-0.5重量份。
所述组分还包括过氧化苯甲酰 0.5-2重量份。
所述聚乙二醇的水溶液中聚乙二醇的质量百分数为15-18％。
所述聚乙二醇的平均相对分子质量为200-400。
一种耐折白塑料薄膜的制备方法，包括以下步骤:
(1)将双酚S型环氧树脂18-25重量份、醋酸丁酸纤维素5-11重量份、双胺丙基聚二甲基硅氧烷1-3重量份、聚甲基氢硅氧烷0.1-2重量份、三氟化硼-二甲基苯胺0.02-0.8重量份、氧化钴0-0.5重量份，搅拌均匀；
(2)加入高压均质机中混合12-18分钟，缓慢加入异佛尔酮二胺0.02-0.06重量份，搅拌均匀；
(3)加入聚乙二醇的水溶液55-75重量份，在85-90℃下搅拌10-15分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
所述高压均质机中压强为19.8-20.5Mpa，温度为55-70℃。
有益效果：
(1)本发明以双酚S型环氧树脂为主要原料，通过加入双胺丙基聚二甲基硅氧烷、聚甲基氢硅氧烷、三氟化硼-二甲基苯胺、异佛尔酮二胺，使制得的薄膜材料具有高透光性、耐高温性和耐折白性能。
(2)本发明的耐折白塑料薄膜是环境友好型材料，原料价格便宜，制备条件简单，易工业化生产。
具体实施方式
实施例1
(1)将双酚S型环氧树脂18kg、醋酸丁酸纤维素5kg、双胺丙基聚二甲基硅氧烷1kg、聚甲基氢硅氧烷0.1kg、三氟化硼-二甲基苯胺0.02kg，搅拌均匀；
(2)加入压强为19.8Mpa、温度为55℃的高压均质机中混合12分钟，缓慢加入异佛尔酮二胺0.02kg，搅拌均匀；
(3)加入15wt％聚乙二醇的水溶液55kg，在85℃下搅拌10分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
其中，所述聚乙二醇的平均相对分子质量为400。
实施例2
(1)将双酚S型环氧树脂18kg、醋酸丁酸纤维素11kg、双胺丙基聚二甲基硅氧烷1kg、聚甲基氢硅氧烷0.1kg、三氟化硼-二甲基苯胺0.02kg、氧化钴0.5kg，搅拌均匀；
(2)加入压强为19.8Mpa、温度为55℃的高压均质机中混合12分钟，缓慢加入异佛尔酮二胺0.02kg，搅拌均匀；
(3)加入15wt％聚乙二醇的水溶液55kg，在85℃下搅拌10分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
其中，所述聚乙二醇的平均相对分子质量为400。
实施例3
(1)将双酚S型环氧树脂25kg、醋酸丁酸纤维素11kg、双胺丙基聚二甲基硅氧烷3kg、聚甲基氢硅氧烷2kg、三氟化硼-二甲基苯胺0.8kg、氧化钴0.5kg，搅拌均匀；
(2)加入压强为20.5Mpa、温度为70℃的高压均质机中混合18分钟，缓慢加入异佛尔酮二胺0.06kg，搅拌均匀；
(3)加入18wt％聚乙二醇的水溶液75kg，在90℃下搅拌15分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
其中，所述聚乙二醇的平均相对分子质量为200。
实施例4
(1)将双酚S型环氧树脂25kg、醋酸丁酸纤维素11kg、双胺丙基聚二甲基硅氧烷3kg、聚甲基氢硅氧烷2kg、三氟化硼-二甲基苯胺0.02kg、氧化钴0.5kg，搅拌均匀；
(2)加入压强为20.5Mpa、温度为70℃的高压均质机中混合18分钟，缓慢加入异佛尔酮二胺0.06kg，搅拌均匀；
(3)加入18wt％聚乙二醇的水溶液75kg，在90℃下搅拌15分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
其中，所述聚乙二醇的平均相对分子质量为200。
实施例5
(1)将双酚S型环氧树脂20kg、醋酸丁酸纤维素8kg、双胺丙基聚二甲基硅氧烷2g、聚甲基氢硅氧烷0.5kg、三氟化硼-二甲基苯胺0.4kg、氧化钴0.2kg，搅拌均匀；
(2)加入压强为20Mpa、温度为60℃的高压均质机中混合16分钟，缓慢加入异佛尔酮二胺0.04kg，搅拌均匀；
(3)加入16wt％聚乙二醇的水溶液65kg，在87℃下搅拌12分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
其中，所述聚乙二醇的平均相对分子质量为200。
对比例
(1)将双酚A型环氧树脂20kg、醋酸纤维素8kg、二氧化硅2g、聚乙烯4kg、氧化钴0.2kg，搅拌均匀；
(2)加入压强为20Mpa、温度为60℃的高压均质机中混合16分钟，缓慢加入乙二胺0.5kg，搅拌均匀；
(3)加入聚乙二醇的水溶液65kg，在87℃下搅拌12分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
本发明实施例1-5和对比例的薄膜的具体性能测试结果如表1所示。
表1
Claims (7)
1.一种耐折白塑料薄膜，其特征在于，由包含以下重量份的组分制成：
2.根据权利要求1所述的耐折白塑料薄膜，其特征在于，所述组分还包括氧化钴0-0.5重量份。
3.根据权利要求1所述的耐折白塑料薄膜，其特征在于，所述组分还包括过氧化苯甲酰 0.5-2重量份。
4.根据权利要求1所述的耐折白塑料薄膜，其特征在于，所述聚乙二醇的水溶液中聚乙二醇的质量百分数为15-18％。
5.根据权利要求4所述的耐折白塑料薄膜，其特征在于，所述聚乙二醇的平均相对分子质量为200-400。
6.一种耐折白塑料薄膜的制备方法，其特征在于，包括以下步骤:
(1)将双酚S型环氧树脂18-25重量份、醋酸丁酸纤维素5-11重量份、双胺丙基聚二甲基硅氧烷1-3重量份、聚甲基氢硅氧烷0.1-2重量份、三氟化硼-二甲基苯胺0.02-0.8重量份、氧化钴0-0.5重量份，搅拌均匀；
(2)加入高压均质机中混合12-18分钟，缓慢加入异佛尔酮二胺0.02-0.06重量份，搅拌均匀；
(3)加入聚乙二醇的水溶液55-75重量份，在85-90℃下搅拌10-15分钟，脱气，倒入平板模具内，烘干，脱模，得到耐折白塑料薄膜。
7.根据权利要求6所述的耐折白塑料薄膜的制备方法，其特征在于，所述高压均质机中压强为19.8-20.5Mpa，温度为55-70℃。