CN104849959A - 一种无铬型圆网印花用感光胶 - Google Patents

一种无铬型圆网印花用感光胶 Download PDF

Info

Publication number
CN104849959A
CN104849959A CN201510238374.1A CN201510238374A CN104849959A CN 104849959 A CN104849959 A CN 104849959A CN 201510238374 A CN201510238374 A CN 201510238374A CN 104849959 A CN104849959 A CN 104849959A
Authority
CN
China
Prior art keywords
chromium
parts
rotary printing
sensitive resist
printing screen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510238374.1A
Other languages
English (en)
Inventor
陈国荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510238374.1A priority Critical patent/CN104849959A/zh
Publication of CN104849959A publication Critical patent/CN104849959A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种无铬型圆网印花用感光胶，包括如下组分：聚乙烯醇（30%）、明胶、对重氮二苯胺多聚甲醛缩合物、聚异氰酸酯嵌段物、有机硅改性聚氨酯树脂、三羟甲基乙烷、苯乙烯基吡啶硫酸二甲酯盐3-6份、对苯二酚、固化剂、聚乙稀亚胺、乙胺三氟化硼盐、苄基二甲胺、六水合氯化铝、溶剂、活性艳蓝、硅酮消泡剂、维生素E。本发明的高精度印花圆网感光胶与印花圆网的结合力强，有优良的耐化学腐蚀性及耐摩擦性，耐印率高；圆网制版显影清晰、不阻塞网孔，通过添加有机硅改性聚氨酯树脂提高印花圆网在印花过程中的拉伸性能，提高印花圆网的使用寿命。

Description

一种无铬型圆网印花用感光胶
技术领域
本发明涉及一种圆网感光胶，具体是涉及一种无铬型圆网感光胶。
背景技术
圆网印花技术是一项重要的大规模印花技术，是一种可以实现高分辨率、连续、极高耐印率的印花工艺，主要应用于布匹、塑料膜和其他连续纺织品的印花。圆网感光胶是进行圆网印花的重要感光材料，通常由胶体和感光剂组成，其中胶体是一种水性乳液，而感光剂为重铬酸铵的水溶液。使用时将感光剂重铬酸铵溶液加入到胶体中，搅拌均匀，消泡后立即进行涂布，在35-40℃的条件下低温干燥、进行曝光、水洗显影，干燥后，再于180℃烘烤、固化、最终形成圆网印版。现在市售的圆网感光胶几乎全部以重铬酸铵为感光剂，这是因为重铬酸铵具有较高的感光度，曝光后胶膜与镍网的粘结力强，显影性强等优点。但是以重铬酸铵为感光剂也存在明显的缺点：当重铬酸铵与胶体混合后，必须立即使用，否则由于暗反应，胶膜会交联，无法显影；重铬酸铵含有铬元素，而铬元素是一种典型的致癌性重金属，对人体具有极大的毒害性，同时也是导致地下水体重金属污染的来源之一，圆网感光胶曝光后，未见光的胶膜仍然具有水溶性，在显影的过程中被水溶解，从镍网上脱除，同时，胶膜中的铬盐也进入水中，随后被排放到环境中，造成水体的污染。
无铬型圆网感光胶一直是丝网印刷领域多年来希望生产的产品。但是，当不使用重铬酸铵感光剂，而使用重氮盐作为感光剂时，胶膜的湿牢度、显影性和分辨率均达不到工业应用的要求。潘跃进等公开了一种采用N－羟烷基丙烯酸酯改性的PVA－SBQ树脂作为感光剂的圆网感光胶的专利，N－羟烷基丙烯酸酯的引入增加了聚乙烯醇的交联点，在自由基引发剂的存在下，丙烯酰基发生交联，增加了交联强度。但是由于自由基引发剂引发的丙烯酰基的交联反应的反应速率较慢，以及自由基引发的光交联反应对氧比较敏感，氧气对自由基引发剂起到阻聚的作用，所以，以自由基引发剂引发的光交联反应在丝网印刷感光胶的产品中应用还非常少。
发明内容
为了实现上述目的，本发明采用以下技术方案：一种圆网印花用感光胶，由下述重量份的成分组成：
聚乙烯醇（30%）             60-80份
明胶                         15-20份
对重氮二苯胺多聚甲醛缩合物   18-30份
聚异氰酸酯嵌段物             4-10份
有机硅改性聚氨酯树脂         10-15份
三羟甲基乙烷                 15-10份
苯乙烯基吡啶硫酸二甲酯盐      3-6份
对苯二酚                      2-8份
固化剂                       10-12份
聚乙稀亚胺                   1-4份
乙胺三氟化硼盐               7-15份
苄基二甲胺                   3-6份
六水合氯化铝                 8-10份
溶剂                         50-100份
活性艳蓝                     0.2-0.3份
硅酮消泡剂                   2-5份
维生素E                     0.05-1.0份。
优选地，所述固化剂为低分子量聚酰胺树脂、酸酐、三氟化硼及其络合物等。
优选地，所述溶剂为水。
优选地，所述圆网印花用感光胶还可以用于水性油墨的印刷，应用于陶瓷、金属玻璃等的网印制版。
本发明的有益效果是所述的高精度印花圆网感光胶的颗粒粒径在2μm以下，且与印花圆网的结合力强，有优良的耐化学腐蚀性及耐摩擦性，耐印率高；圆网制版显影清晰、不阻塞网孔，通过添加有机硅改性聚氨酯树脂提高印花圆网在印花过程中的拉伸性能，提高印花圆网的使用寿命，通过添加维生素E组分缩短了曝光时间，通过添加苯乙烯基吡啶硫酸二甲酯盐提高了胶层与印花圆网的结合牢度，耐冲洗牢度强，分辨率高；制备过程中无挥发性有机化合物，对环境的污染小，对人体伤害低。
具体实施方式
下面通过实施例来对本发明进行详细说明，应当理解的是，这些实施例仅能用来解释本发明而不能用来解释对本发明的限制。
实施例1：
一种圆网印花用感光胶，由下述重量份的成分组成：
聚乙烯醇（30%）             60份
明胶                        15份
对重氮二苯胺多聚甲醛缩合物  18份
聚异氰酸酯嵌段物             4份
有机硅改性聚氨酯树脂        10份
三羟甲基乙烷                15份
苯乙烯基吡啶硫酸二甲酯盐    3份
对苯二酚                    2份
固化剂                      10份
聚乙稀亚胺                  1份
乙胺三氟化硼盐              7份
苄基二甲胺                  3份
六水合氯化铝                8份
溶剂                        50份
活性艳蓝                    0.2份
硅酮消泡剂                  2份
维生素E                    0.05份。
实施例2：
一种圆网印花用感光胶，由下述重量份的成分组成：
聚乙烯醇（30%）             80份
明胶                         20份
对重氮二苯胺多聚甲醛缩合物   30份
聚异氰酸酯嵌段物             10份
有机硅改性聚氨酯树脂         15份
三羟甲基乙烷                 10份
苯乙烯基吡啶硫酸二甲酯盐     6份
对苯二酚                     8份
固化剂                       12份
聚乙稀亚胺                   4份
乙胺三氟化硼盐               15份
苄基二甲胺                   6份
六水合氯化铝                 10份
溶剂                         100份
活性艳蓝                     0.3份
硅酮消泡剂                   5份
维生素E                     1.0份。
实施例3：
一种圆网印花用感光胶，由下述重量份的成分组成：
聚乙烯醇（30%）             70份
明胶                         18份
对重氮二苯胺多聚甲醛缩合物   22份
聚异氰酸酯嵌段物             7份
有机硅改性聚氨酯树脂         13份
三羟甲基乙烷                 18份
苯乙烯基吡啶硫酸二甲酯盐     4份
对苯二酚                     5份
固化剂                     11份
聚乙稀亚胺                 3份
乙胺三氟化硼盐             10份
苄基二甲胺                 4份
六水合氯化铝               9份
溶剂                       80份
活性艳蓝                   0.25份
硅酮消泡剂                 3份
维生素E                   0.08份。
上述实施例1-3中所述固化剂为低分子量聚酰胺树脂、酸酐、三氟化硼及其络合物等。所述溶剂为水。
本发明得到的圆网印花用感光胶还可以用于水性油墨的印刷，应用于陶瓷、金属玻璃等的网印制版。

Claims (3)

1.一种无铬型圆网印花用感光胶，其特征在于：由下述重量份的成分组成：
聚乙烯醇（30%）             60-80份
明胶                         15-20份
对重氮二苯胺多聚甲醛缩合物   18-30份
聚异氰酸酯嵌段物             4-10份
有机硅改性聚氨酯树脂         10-15份
三羟甲基乙烷                 15-20份
苯乙烯基吡啶硫酸二甲酯盐     3-6份
对苯二酚                     2-8份
固化剂                       10-12份
聚乙稀亚胺                   1-4份
乙胺三氟化硼盐               7-15份
苄基二甲胺                   3-6份
六水合氯化铝                 8-10份
溶剂                         50-100份
活性艳蓝                     0.2-0.3份
硅酮消泡剂                   2-5份
维生素E                     0.05-1.0份。
2.根据权利要求1所述的无铬型圆网印花用感光胶，其特征在于：所述固化剂为低分子量聚酰胺树脂、酸酐、三氟化硼及其络合物等。
3.根据权利要求1所述的无铬型圆网印花用感光胶，其特征在于：所述溶剂为水。
CN201510238374.1A 2015-05-12 2015-05-12 一种无铬型圆网印花用感光胶 Pending CN104849959A (zh)