CN104760372A - 一种避光保鲜膜 - Google Patents
一种避光保鲜膜 Download PDFInfo
- Publication number
- CN104760372A CN104760372A CN201410832665.9A CN201410832665A CN104760372A CN 104760372 A CN104760372 A CN 104760372A CN 201410832665 A CN201410832665 A CN 201410832665A CN 104760372 A CN104760372 A CN 104760372A
- Authority
- CN
- China
- Prior art keywords
- preservative film
- film
- proof
- light
- theca
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种避光保鲜膜,涉及膜加工领域,所述保鲜膜为内外双层结构,所述保鲜膜有90%内膜层和10%外膜层构成,所述内膜层中按重量百分比,由40-99.6% LLDPE、0-50% MLLDPE和0.2-5% 聚异丁烯混合而成;所述外膜层由40-99.6% LLDPE、0-50% MLLDPE、0.2-5%聚异丁烯和10-20%炭黑与壳聚糖混合液构成,本发明中采用两层膜结构,具有广泛的应用,不仅可以保鲜食物,也可以利用保鲜膜的自发的黏性包裹与玻璃器皿的外层,起到隔绝光源的作用,同时在科学实验中,可以包裹在透明玻璃瓶上代替棕色瓶的使用,避免棕色瓶盛东西时,不能观察其内部实际情况的缺点。
Description
技术领域
本发明涉及膜加工领域,特别是涉及一种避光保鲜膜。
背景技术
PE保鲜膜是食品级包装材料,几乎家庭常备易耗品。PE保鲜膜大多采用LLDPE(线性低密度聚乙烯)制成。PE保鲜膜对包装物起到紧密包装作用,商品包装后阻隔了氧气进入,其中保鲜膜的自发的黏性也被利用到科学实验中,用来隔绝氧气和灰尘,但是却不能解决及时方便的避光问题。
发明内容
为克服现有技术上的不足,本发明目的是提供一种避光保鲜膜。
为实现本发明的目的,本发明的技术方案如下:
一种避光保鲜膜,所述保鲜膜为内外双层结构,所述保鲜膜有90%内膜层和10%外膜层构成,所述内膜层中按重量百分比,由40-99.6%LLDPE、0-50%MLLDPE和0.2-5%聚异丁烯混合而成;所述外膜层由40-99.6%LLDPE、0-50%MLLDPE、0.2-5%聚异丁烯和10-20%炭黑与壳聚糖混合液构成。
上述一种避光保鲜膜,其中,所述炭黑和壳聚糖的混合液的制备方法为将1-5g炭黑加入到100ml壳聚糖溶液中,超声分散均匀制得。
上述一种避光保鲜膜,其中,所述内膜层中加入0.1-1%增塑剂乙酰柠檬酸三丁酯。
上述一种避光保鲜膜,其中,所述内膜层和外膜层中均加入0.1-1%抗静电剂SWJU-1和0.1-0.5%抗氧化剂VC。
上述一种避光保鲜膜的制备方法为,按照所述比例称配料,经塑料粒子混合机将内膜层材料和外膜层材料分别混合均匀后,进入Φ45-65mm的双螺杆挤出吹塑机吹塑,纵横双向拉伸成膜;吹塑成膜的螺杆转速为45r/min,其中四段温度分别为100℃、145℃、165℃、180℃。
本发明的有益效果:本发明中采用两层膜结构,在外膜层中加入用壳聚糖均匀分散的较高浓度的炭黑溶液,经过拉伸后,会形成遮光保鲜层,具有广泛的应用,不仅可以保鲜食物,也可以利用保鲜膜的自发的黏性包裹与玻璃器皿的外层,起到隔绝光源的作用,而且不用二次固定,同时在科学实验中,可以包裹在透明玻璃瓶上代替棕色瓶的使用,避免棕色瓶盛东西时,不能观察其内部实际情况的缺点。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
实施例1:一种避光保鲜膜,所述保鲜膜为内外双层结构,所述保鲜膜有90%内膜层和10%外膜层构成,所述内膜层中按重量百分比,由50%LLDPE、45%MLLDPE、3.9%聚异丁烯、0.1%抗静电剂SWJU-1、0.5%抗氧化剂VC和0.5%增塑剂乙酰柠檬酸三丁酯混合而成;所述外膜层由40%LLDPE、33.5%MLLDPE、5%聚异丁烯、20%炭黑与壳聚糖混合液、0.5%抗氧化剂VC和1%增塑剂乙酰柠檬酸三丁酯构成;
其中,所述炭黑和壳聚糖的混合液的制备方法为将3g炭黑加入到100ml壳聚糖溶液中,超声分散均匀制得。
一种避光保鲜膜制备方法为按照所述比例称配料,经塑料粒子混合机将内膜层材料和外膜层材料分别混合均匀后,进入Φ65mm的双螺杆挤出吹塑机吹塑, 纵横双向拉伸成膜;吹塑成膜的螺杆转速为45r/min,其中四段温度分别为100℃、145℃、165℃、180℃。
实施例2:一种避光保鲜膜,所述保鲜膜为内外双层结构,所述保鲜膜有90%内膜层和10%外膜层构成,所述内膜层中按重量百分比,由49%LLDPE、45%MLLDPE、5%聚异丁烯、0.5%抗静电剂SWJU-1、0.3%抗氧化剂VC和0.2%增塑剂乙酰柠檬酸三丁酯混合而成;所述外膜层由89.6%LLDPE、0.2%聚异丁烯、10%炭黑与壳聚糖混合液、0.1%抗氧化剂VC和0.1%增塑剂乙酰柠檬酸三丁酯构成;
其中,所述炭黑和壳聚糖的混合液的制备方法为将5g炭黑加入到100ml壳聚糖溶液中,超声分散均匀制得。
一种避光保鲜膜制备方法为按照所述比例称配料,经塑料粒子混合机将内膜层材料和外膜层材料分别混合均匀后,进入Φ45mm的双螺杆挤出吹塑机吹塑,纵横双向拉伸成膜;吹塑成膜的螺杆转速为45r/min,其中四段温度分别为100℃、145℃、165℃、180℃。
实施例3:一种避光保鲜膜,所述保鲜膜为内外双层结构,所述保鲜膜有90%内膜层和10%外膜层构成,所述内膜层中按重量百分比,由99.5%LLDPE、0.2%聚异丁烯、0.1%抗静电剂SWJU-1、0.1%抗氧化剂VC和0.1%增塑剂乙酰柠檬酸三丁酯混合而成;所述外膜层由43.1%LLDPE、35%MLLDPE、3%聚异丁烯、18%炭黑与壳聚糖混合液、0.1%抗氧化剂VC和0.8%增塑剂乙酰柠檬酸三丁酯构成;
其中,所述炭黑和壳聚糖的混合液的制备方法为将1g炭黑加入到100ml壳聚糖溶液中,超声分散均匀制得。
一种避光保鲜膜制备方法为按照所述比例称配料,经塑料粒子混合机将内膜层材料和外膜层材料分别混合均匀后,进入Φ50mm的双螺杆挤出吹塑机吹塑,纵横双向拉伸成膜;吹塑成膜的螺杆转速为45r/min,其中四段温度分别为100 ℃、145℃、165℃、180℃。
本发明中采用两层膜结构,在外膜层中加入用壳聚糖均匀分散的较高浓度的炭黑溶液,经过拉伸后,会形成遮光保鲜层,具有广泛的应用,不仅可以保鲜食物,也可以利用保鲜膜的自发的黏性包裹与玻璃器皿的外层,起到隔绝光源的作用,而且不用二次固定,同时在科学实验中,可以包裹在透明玻璃瓶上代替棕色瓶的使用,避免棕色瓶盛东西时,不能观察其内部实际情况的缺点。以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种避光保鲜膜,其特征在于:所述保鲜膜为内外双层结构,所述保鲜膜有90%内膜层和10%外膜层构成,所述内膜层中按重量百分比,由40-99.6% LLDPE、0-50% MLLDPE和0.2-5% 聚异丁烯混合而成;所述外膜层由40-99.6% LLDPE、0-50% MLLDPE、0.2-5%聚异丁烯和10-20%炭黑与壳聚糖混合液构成。
2.根据权利要求1所述的一种避光保鲜膜,其特征在于,其中,所述炭黑和壳聚糖的混合液的制备方法为将1-5g炭黑加入到100ml壳聚糖溶液中,超声分散均匀制得。
3.根据权利要求2所述的一种避光保鲜膜,其特征在于,其中,所述内膜层中加入0.1-1%增塑剂乙酰柠檬酸三丁酯。
4.根据权利要求3所述的一种避光保鲜膜,其特征在于,所述内膜层和外膜层中均加入0.1-1%抗静电剂SWJU-1和0.1-0.5%抗氧化剂VC。
5.根据权利要求1-4所述的一种避光保鲜膜的制备方法,其特征在于,按照所述比例称配料,经塑料粒子混合机将内膜层材料和外膜层材料分别混合均匀后,进入Φ45-65mm的双螺杆挤出吹塑机吹塑,纵横双向拉伸成膜;吹塑成膜的螺杆转速为45r/min,其中四段温度分别为100℃、145℃、165℃、180℃。