CN103467940A - 一种抗菌微孔pha保鲜膜及其制备方法 - Google Patents

一种抗菌微孔pha保鲜膜及其制备方法 Download PDF

Info

Publication number
CN103467940A
CN103467940A CN201310351928XA CN201310351928A CN103467940A CN 103467940 A CN103467940 A CN 103467940A CN 201310351928X A CN201310351928X A CN 201310351928XA CN 201310351928 A CN201310351928 A CN 201310351928A CN 103467940 A CN103467940 A CN 103467940A
Authority
CN
China
Prior art keywords
parts
pha
preservative film
micropore
antibiotic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310351928XA
Other languages
English (en)
Other versions
CN103467940B (zh
Inventor
倪迪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Original Assignee
WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd filed Critical WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Priority to CN201310351928.XA priority Critical patent/CN103467940B/zh
Publication of CN103467940A publication Critical patent/CN103467940A/zh
Application granted granted Critical
Publication of CN103467940B publication Critical patent/CN103467940B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种抗菌微孔PHA保鲜膜及其制备方法,属于高分子材料技术领域。该保鲜膜包括按照重量份数计的如下原料:PHA树脂100~120份、乙酰柠檬酸三乙酯8~15份、碳酸钙6~8份、改性凹凸棒土8~12份、抗氧剂0.5~2份、硬脂酸正丁酯0.5~2份、钛酸酯偶联剂1~3份、壳聚糖4~7份。本发明制备方法简单,制得的抗菌微孔PHA保鲜膜产品结构稳定,透气性好,且可生物降解,避免了以乙烯母料为原材料的保鲜膜对环境的污染。

Description

一种抗菌微孔PHA保鲜膜及其制备方法
技术领域
本发明属于高分子材料技术领域,具体涉及一种抗菌微孔PHA保鲜膜及其制备方法。
背景技术
保鲜膜是人们常用的一类保鲜食品的塑料包装制品,现在有很多家庭都离不开它们,如微波炉食物加热、冰箱里存放食物等都需要保鲜膜。
目前保鲜膜功能较为单一,大部分保鲜膜不具有抗菌功能,且无法做到O2和CO2的双向调节,贮藏时容易在保鲜膜内结露。同时,市场上大部分保鲜膜以乙烯母料为原材料,废弃后无法降解,污染环境,破坏生态平衡。因此如何克服现有技术的不足是目前高分子技术领域亟需解决的问题。
发明内容
本发明的目的是为了解决现有技术的不足,提供一种抗菌微孔PHA保鲜膜及其制备方法,该方法简单易行,制得的保鲜膜透气性好,能够生物降解,且具有一定的抗菌性。
本发明采用的技术方案如下:
一种抗菌微孔PHA保鲜膜,包括按照重量份数计的如下原料:PHA树脂100~120份、乙酰柠檬酸三乙酯8~15份、碳酸钙6~8份、改性凹凸棒土8~12份、抗氧剂0.5~2份、硬脂酸正丁酯0.5~2份、钛酸酯偶联剂1~3份、壳聚糖4~7份。
进一步,其优选方案为所述的抗氧剂为抗氧剂264。
进一步,其优选方案为所述的钛酸酯偶联剂为三异硬酯酸钛酸异丙酯。
进一步,其优选方案为所述的改性凹凸棒土的制备方法为:将凹凸棒土用质量分数为12~14%的盐酸浸泡2~3小时,再用质量分数为12~15%氢氧化钠的溶液浸泡2~3小时,然后用去离子水洗涤至中性,烘干,即可得到改性凹凸棒土。
本发明还提供一种抗菌微孔PHA保鲜膜的制备方法,包括如下步骤:
(1)将PHA树脂、碳酸钙和改性凹凸棒土粉碎至150~200目;
(2)将粉碎后的PHA树脂、碳酸钙和改性凹凸棒土置于高速混合机中,并向其中加入乙酰柠檬酸三乙酯、抗氧剂、硬脂酸正丁酯、钛酸酯偶联剂和壳聚糖,混合均匀,得到混合物料;
(3)将混合物料加入到挤出机中挤出,然后经压延出片、引离、拉伸、冷却、牵引和卷曲,最后分切得到抗菌微孔PHA保鲜膜。
本发明与现有技术相比,其有益效果为:(1)本发明产品结构稳定,透气性好,在贮藏期间,即使有温度波动,也不易产生结露;(2)原料中添加了壳聚糖,不仅起到抗菌作用,同时还对果蔬具有一定的保鲜作用;(3)具有O2和CO2的双向调节作用,对O2、CO2、水蒸气、乙烯等气体具有较强的吸附作用和透过能力;(4)本发明制备工艺简单,制得的抗菌微孔PHA保鲜膜可生物降解,避免了以乙烯母料为原材料的保鲜膜对环境的污染。
具体实施例
一种抗菌微孔PHA保鲜膜,包括按照重量份数计的如下原料:PHA树脂100~120份、乙酰柠檬酸三乙酯8~15份、碳酸钙6~8份、改性凹凸棒土8~12份、抗氧剂0.5~2份、硬脂酸正丁酯0.5~2份、钛酸酯偶联剂1~3份、壳聚糖4~7份。
所述的改性凹凸棒土的制备方法为:将凹凸棒土用质量分数为12~14%的盐酸浸泡2~3小时,再用质量分数为12~15%氢氧化钠的溶液浸泡2~3小时,然后用去离子水洗涤至中性,烘干,即可得到改性凹凸棒土。
该抗菌微孔PHA保鲜膜的制备方法,包括如下步骤:
(1)将PHA树脂、碳酸钙和改性凹凸棒土粉碎至150~200目;
(2)将粉碎后的PHA树脂、碳酸钙和改性凹凸棒土置于高速混合机中,并向其中加入乙酰柠檬酸三乙酯、抗氧剂、硬脂酸正丁酯、钛酸酯偶联剂和壳聚糖,混合均匀,得到混合物料;
(3)将混合物料加入到挤出机中挤出,然后经压延出片、引离、拉伸、冷却、牵引和卷曲,最后分切得到抗菌微孔PHA保鲜膜。
下面结合实施例对本发明作进一步的详细描述。
实施例1
一种抗菌微孔PHA保鲜膜,包括按照重量份数计的如下原料:PHA树脂100份、乙酰柠檬酸三乙酯8份、碳酸钙6份、改性凹凸棒土8份、抗氧剂264 0.5份、硬脂酸正丁酯0.5份、三异硬酯酸钛酸异丙酯1份、壳聚糖4份。
所述的改性凹凸棒土的制备方法为:将凹凸棒土用质量分数为12%的盐酸浸泡2小时,再用质量分数为15%氢氧化钠的溶液浸泡3小时,然后用去离子水洗涤至中性,烘干,即可得到改性凹凸棒土。
该抗菌微孔PHA保鲜膜的制备方法,包括如下步骤:
(1)将PHA树脂、碳酸钙和改性凹凸棒土粉碎至150~200目;
(2)将粉碎后的PHA树脂、碳酸钙和改性凹凸棒土置于高速混合机中,并向其中加入乙酰柠檬酸三乙酯、抗氧剂、硬脂酸正丁酯、钛酸酯偶联剂和壳聚糖,混合均匀,得到混合物料;
(3)将混合物料加入到挤出机中挤出,然后经压延出片、引离、拉伸、冷却、牵引和卷曲,最后分切得到抗菌微孔PHA保鲜膜。
 
实施例2
一种抗菌微孔PHA保鲜膜,包括按照重量份数计的如下原料:PHA树脂120份、乙酰柠檬酸三乙酯15份、碳酸钙8份、改性凹凸棒土12份、抗氧剂264 2份、硬脂酸正丁酯2份、三异硬酯酸钛酸异丙酯3份、壳聚糖7份。
所述的改性凹凸棒土的制备方法为:将凹凸棒土用质量分数为14%的盐酸浸泡3小时,再用质量分数为12%氢氧化钠的溶液浸泡2小时,然后用去离子水洗涤至中性,烘干,即可得到改性凹凸棒土。
本实施例的抗菌微孔PHA保鲜膜的制备方法与实施例1相同。
 
实施例3
一种抗菌微孔PHA保鲜膜,包括按照重量份数计的如下原料:PHA树脂110份、乙酰柠檬酸三乙酯12份、碳酸钙7份、改性凹凸棒土10份、抗氧剂264 1.2份、硬脂酸正丁酯1.6份、三异硬酯酸钛酸异丙酯2.2份、壳聚糖5.8份。
所述的改性凹凸棒土的制备方法为:将凹凸棒土用质量分数为13%的盐酸浸泡2.2小时,再用质量分数为14%氢氧化钠的溶液浸泡2.8小时,然后用去离子水洗涤至中性,烘干,即可得到改性凹凸棒土。
本实施例的抗菌微孔PHA保鲜膜的制备方法与实施例1相同。
 
性能检测
采用实施例1~3产品以及普通市售保鲜膜为对照,对灵武长枣包装在20℃下存放90天,其检测结果如表1所示。
 
表1 产品性能检测数据
  失重率 可溶性固形物 坏果率% 转红率% 硬度105Pa 褐变指数
实施例1 0.65 21.8 0.5 100 9.62 0.04
实施例2 0.63 21.7 0 100 9.61 0.03
实施例3 0.58 22.0 0 100 9.58 0.03
对照组 1.5 20.75 8 100 9.72 0.09
检测结果说明,本发明产品具有良好的调节作用,是一种理想的果蔬保鲜用品。

Claims (5)

1.一种抗菌微孔PHA保鲜膜,其特征在于包括按照重量份数计的如下原料:PHA树脂100~120份、乙酰柠檬酸三乙酯8~15份、碳酸钙6~8份、改性凹凸棒土8~12份、抗氧剂0.5~2份、硬脂酸正丁酯0.5~2份、钛酸酯偶联剂1~3份、壳聚糖4~7份。
2.根据权利要求1所述的抗菌微孔PHA保鲜膜,其特征在于所述的抗氧剂为抗氧剂264。
3.根据权利要求1所述的抗菌微孔PHA保鲜膜,其特征在于所述的钛酸酯偶联剂为三异硬酯酸钛酸异丙酯。
4.根据权利要求1所述的抗菌微孔PHA保鲜膜,其特征在于所述的改性凹凸棒土的制备方法为:将凹凸棒土用质量分数为12~14%的盐酸浸泡2~3小时,再用质量分数为12~15%氢氧化钠的溶液浸泡2~3小时,然后用去离子水洗涤至中性,烘干,即可得到改性凹凸棒土。
5.如权利要求1所述的抗菌微孔PHA保鲜膜的制备方法,其特征在于包括如下步骤:
(1)将PHA树脂、碳酸钙和改性凹凸棒土粉碎至150~200目;
(2)将粉碎后的PHA树脂、碳酸钙和改性凹凸棒土置于高速混合机中,并向其中加入乙酰柠檬酸三乙酯、抗氧剂、硬脂酸正丁酯、钛酸酯偶联剂和壳聚糖,混合均匀,得到混合物料;
(3)将混合物料加入到挤出机中挤出,然后经压延出片、引离、拉伸、冷却、牵引和卷曲,最后分切得到抗菌微孔PHA保鲜膜。
CN201310351928.XA 2013-08-14 2013-08-14 一种抗菌微孔pha保鲜膜及其制备方法 Active CN103467940B (zh)