CN103601970B - 一种高强度透明塑料桶 - Google Patents
一种高强度透明塑料桶 Download PDFInfo
- Publication number
- CN103601970B CN103601970B CN201310522740.7A CN201310522740A CN103601970B CN 103601970 B CN103601970 B CN 103601970B CN 201310522740 A CN201310522740 A CN 201310522740A CN 103601970 B CN103601970 B CN 103601970B
- Authority
- CN
- China
- Prior art keywords
- compound
- transparent plastic
- component
- temperature
- plastic barrel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种高强度透明塑料桶,涉及化工技术领域,由以下重量百分比的组分组成,聚丙烯50-80%、玻璃纤维5-40%、增塑剂1-5%、再生地膜1-10%、透明剂0.1-5%、阻燃剂0.5-1%、高强度变性淀粉1-5%、光亮剂0.5-1%。本发明组分简单,成本低,外形美观,能够使用部分再生料作为原料,提高了资源利用率,同时由于改变了传统的生产工艺,增加冷冻这一环节,提高了制品的安全性,韧度更强,在较高的温度下仍然具有较好的稳定性能。
Description
技术领域
本发明涉及化工技术领域,具体涉及一种高强度透明塑料桶及其制备工艺。
背景技术
塑料桶多用于各种液体的储存和运输,对特殊的危险品包装具有良好的特性,它有不易碎、不生锈、质轻等特点,而且耐油、耐强腐蚀性能,多用于需要保温、防潮、耐压、抗腐蚀的危险品包装。塑料桶的材料多采用聚乙烯、聚丙烯、聚酯等塑料吹塑、注塑、吸塑、滚塑而成,多用于盛装化工、农药、医药、食品、五金电子、机电等行业液体、固体物品。生产塑料桶的主要原料是聚乙烯(Polyethylene,PE),简称PE,是乙烯进行加聚而成的高分子有机化合物。聚乙烯是世界上公认的接触食品最佳材料,无毒、无味、无臭,符合食品包装卫生标准。聚乙烯薄膜,轻盈透明,具有防潮、抗氧、耐酸、耐碱、气密性一般,热封性优异等性能,素有“塑料之花”的美称,是塑料包装印刷用量最多、最重要的材料。
发明内容
本发明所要解决的技术问题在于提供一种配方简单,产品质量稳定的高强度透明塑料桶及其制备工艺。
本发明所要解决的技术问题采用以下技术方案来实现:
一种高强度透明塑料桶,由以下重量百分比的组分组成,
各组分的最佳重量百分比为:
制备方法如下:
1)按上述重量比称取各组分;
2)将聚丙烯、再生地膜及高强度变性淀粉置于搅拌机中,在80-120℃的温度下搅拌30分钟,混合均匀;
3)将混合均匀的混合料置于冷冻设备中,在-10℃的温度下冷冻6小时;
4)取出冷冻后的混合料,依次加入计量后的玻璃纤维、增塑剂、透明剂、阻燃剂和光亮剂,搅拌混合成混合料;
5)将混合料置于锥形双螺杆挤出机料斗中,挤出塑料颗粒;
6)将塑料颗粒置于挤出中空吹塑成型机料斗中,挤出管状坯料;
7)将管状坯料放入挤出中空吹塑成型机模具中,控制模具温度和压缩空气压力,中空吹制成透明塑料桶。
本发明的有益效果是:本发明组分简单,成本低,外形美观,能够使用部分再生料作为原料,提高了资源利用率,同时由于改变了传统的生产工艺,增加冷冻这一环节,提高了制品的安全性,韧度更强,在较高的温度下仍然具有较好的稳定性能。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
一种高强度透明塑料桶,由以下重量百分比的组分组成,
制备方法如下:
1)按上述重量比称取各组分;
2)将聚丙烯、再生地膜及高强度变性淀粉置于搅拌机中,在80-120℃的温度下搅拌30分钟,混合均匀;
3)将混合均匀的混合料置于冷冻设备中,在-10℃的温度下冷冻6小时;
4)取出冷冻后的混合料,依次加入计量后的玻璃纤维、增塑剂、透明剂、阻燃剂和光亮剂,搅拌混合成混合料;
5)将混合料置于锥形双螺杆挤出机料斗中,挤出塑料颗粒;
6)将塑料颗粒置于挤出中空吹塑成型机料斗中,挤出管状坯料;
7)将管状坯料放入挤出中空吹塑成型机模具中,控制模具温度和压缩空气压力,中空吹制成透明塑料桶。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (1)
1.一种高强度透明塑料桶,其特征在于,由以下重量百分比的组分制成:
制备方法如下:
1)按上述重量比称取各组分;
2)将聚丙烯、再生地膜及高强度变性淀粉置于搅拌机中,在80-120℃的温度下搅拌30分钟,混合均匀;
3)将混合均匀的混合料置于冷冻设备中,在-10℃的温度下冷冻6小时;
4)取出冷冻后的混合料,依次加入计量后的玻璃纤维、增塑剂、透明剂、阻燃剂和光亮剂,搅拌混合成混合料;
5)将混合料置于锥形双螺杆挤出机料斗中,挤出塑料颗粒;
6)将塑料颗粒置于挤出中空吹塑成型机料斗中,挤出管状坯料;
7)将管状坯料放入挤出中空吹塑成型机模具中,控制模具温度和压缩空气压力,中空吹制成透明塑料桶。