CN104497633B - 一种纳米碳酸钙的表面处理方法 - Google Patents
一种纳米碳酸钙的表面处理方法 Download PDFInfo
- Publication number
- CN104497633B CN104497633B CN201410685319.2A CN201410685319A CN104497633B CN 104497633 B CN104497633 B CN 104497633B CN 201410685319 A CN201410685319 A CN 201410685319A CN 104497633 B CN104497633 B CN 104497633B
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- nano
- fatty acid
- kiln gas
- conditioning agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (3)