CN104419251A - 一种环保型银色刮开油墨的制备方法 - Google Patents

一种环保型银色刮开油墨的制备方法 Download PDF

Info

Publication number
CN104419251A
CN104419251A CN201310418761.4A CN201310418761A CN104419251A CN 104419251 A CN104419251 A CN 104419251A CN 201310418761 A CN201310418761 A CN 201310418761A CN 104419251 A CN104419251 A CN 104419251A
Authority
CN
China
Prior art keywords
environment
ink
friendly type
scratch ink
silver color
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310418761.4A
Other languages
English (en)
Other versions
CN104419251B (zh
Inventor
许钧强
郑玉峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaoguan Lianbang Environmentally Friendly New Materials Co ltd
Original Assignee
SHENZHEN QUANFENGSHENG CHEMICAL Co Ltd
SHENZHEN SHENJINGDA INK CHEMICAL Co Ltd
NANXIONG LIANBANG CHEMICAL PETROLEUM TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENZHEN QUANFENGSHENG CHEMICAL Co Ltd, SHENZHEN SHENJINGDA INK CHEMICAL Co Ltd, NANXIONG LIANBANG CHEMICAL PETROLEUM TECHNOLOGY Co Ltd filed Critical SHENZHEN QUANFENGSHENG CHEMICAL Co Ltd
Priority to CN201310418761.4A priority Critical patent/CN104419251B/zh
Publication of CN104419251A publication Critical patent/CN104419251A/zh
Application granted granted Critical
Publication of CN104419251B publication Critical patent/CN104419251B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种环保型银色刮开油墨的制备方法，按质量百分比由以下组分组成：丙烯酸树脂3％～15％、氯醋树脂4％～10％、铝银浆25％～40％、气相二氧化硅6％～15％、助剂2％～8％、溶剂25％～40％；本发明制得的环保型银色刮开油墨在贮存时不沉淀，铝粉漂浮性好、光泽高；不糊版、不粘版，粘性适中，流动流平性好，印刷性能优良；有很好的耐热性、耐磨性、稳定性、耐折度，使印制的成品在运输、销售中不易破损、划伤；且无毒、无异味，是真正的环保健康型刮开油墨；广泛应用于各种类型的彩票、奖券、票据、电话充值卡，游戏点卡、上网卡、抽奖卡、学习卡、电码防伪标识卡、速显册及儿童刮画等印刷。

Description

一种环保型银色刮开油墨的制备方法
技术领域
本发明属于印刷包装材料技术领域，涉及一种环保型银色刮开油墨，本发明还涉及该种银色刮开油墨的制备方法。
背景技术
随着市场经济的发展和人们物质文化生活水平的提高，各种类型的彩票、奖券、票据等大量出现，印制彩票、奖券、票据时的油墨也在不断增长，其中刮开油墨的用量也越来越大，除彩票、奖券、票据外，在电信、IT、商业和教育等行业也越来越广泛，如电信行业的电话充值卡，游戏点卡、上网卡、抽奖卡、学习卡、电码防伪标识卡、速显册及儿童刮画等领域。
目前市面上刮开油墨存在耐磨性、耐折度较差，光泽、遮盖力低或刮开时油墨去不尽；还有的在制造刮开油墨时所选树脂的要求要用芳烃类或酮类溶剂，油墨干后仍残留有害的芳烃类或酮类溶剂，对人体和环境必然造成严重的危害，因此开发一种环保型刮开油墨尤其必要。
发明内容
为了解决上面所述的技术问题，本发明采取以下技术方案：本发明涉及一种环保型银色刮开油墨，按质量百分比由以下组分组成：丙烯酸树脂3％～15％、氯醋树脂4％～10％、铝银浆25％～40％、气相二氧化硅6％～15％、助剂2％～8％、溶剂25％～40％。
其中，丙烯酸树脂选用分子量在5000～10000热塑型丙烯酸树脂。
氯醋树脂选用酯溶型三元氯醋树脂。
铝银浆选用平均粒径在8～15μm、325目筛留物＜0.1％的片状漂浮型铝银浆。
助剂至少包括润湿分散剂、流平剂、微细蜡浆的一种或其组合。
溶剂选取用醋酸丁酯、醋酸乙酯、PMA、DBE、乙二醇丁醚、丙二醇丁醚、脱芳D40溶剂的一种或其组合。
本发明提出一种环保型银色刮开油墨的制备方法，其制备工艺如下：按配方重量比计，把部分溶剂加入分散釜中，加入丙烯酸树脂、氯醋树脂溶解均匀，加入润湿分散剂、气相二氧化硅、铝银浆，高速分散30～40min，在低速搅拌下加入蜡浆、流平剂和剩余的溶剂，搅拌调节好粘度，过滤包装即制得一种环保型银色刮开油墨。
本发明制得的环保型银色刮开油墨在贮存时不沉淀，铝粉漂浮性好、光泽高；不糊版、不粘版，粘性适中，流动流平性好，印刷性能优良；有很好的耐热性、耐磨性、稳定性、耐折度，使印制的成品在运输、销售中不易破损、划伤；且无毒、无异味，是真正的环保健康型刮开油墨。广泛应用于各种类型的彩票、奖券、票据、电话充值卡，游戏点卡、上网卡、抽奖卡、学习卡、电码防伪标识卡、速显册及儿童刮画等印刷。
具体实施方式
按照表1的组分配方准备材料实施。
表1：三个实施例组分配方   质量份
实施例1：
按照表1中实例1按配方重量比把混合溶剂25份加入分散釜中，加入丙烯酸树脂12份、氯醋树脂10份溶解均匀，加入润湿分散剂1.5份、气相二氧化硅10份、铝银浆23份，高速分散30～40min，在低速搅拌下加入细蜡浆5.5份、流平剂1份和剩余的溶剂12份，搅拌调节好粘度，过滤包装即制得一种环保型银色刮开油墨。
实施例2，实施例3制备步骤参照实施例1。
按照国家相关标准，对本发明的环保型银色刮开油墨的性能进行检测，测试结果如表2所示。
表2环保型银色刮开油墨性能测试结果
测试项目 标准要求 测试结果
外观 银灰色 银灰色
细度μm ≤30 15
表干mm/min 11～13 12
实干min／100mm 15～20 16
透光点cm2， ≤10 2
刮开度g 8～11 9
在室温水中浸泡48h 刮开度基本不变 合格
在50℃，湿度90％放置48h 刮开度基本不变 合格
在-20℃放置48h 刮开度基本不变 合格
芳烃含量mg·kg-1 ≤0.1 0.05
游离甲醛mg·kg-1 ≤0.1 0.01
可溶性铅mg·kg-1 ≤90 ≤15
可溶性镉mg·kg-1 ≤75 ≤12
可溶性铬mg·kg-1 ≤60 ≤10
可溶性汞mg·kg-1 ≤60 未检出
尽管本发明已作了详细说明并引证了实施例，但对于本领域的普通技术人员，显然可以按照上述说明而做出的各种方案、修改和改动，都应该包括在权利要求的范围之内。

Claims (7)

1.一种环保型银色刮开油墨，其特征在于：以质量百分比计，包括如下组分：丙烯酸树脂3％～15％、氯醋树脂4％～10％、铝银浆25％～40％、气相二氧化硅6％～15％、助剂2％～8％、溶剂25％～40％。
2.如权利要求1所述的一种环保型银色刮开油墨，其特征在于：所述的丙烯酸树脂选用分子量在5000～10000热塑型丙烯酸树脂。
3.如权利要求1所述的一种环保型银色刮开油墨，其特征在于：所述的氯醋树脂选用酯溶型三元氯醋树脂。
4.如权利要求1所述的一种环保型银色刮开油墨，其特征在于：所述的铝银浆选用平均粒径在8～15μm、325目筛留物＜0.1％的片状漂浮型铝银浆。
5.如权利要求1所述的一种环保型银色刮开油墨，其特征在于：所述的助剂至少包括润湿分散剂、流平剂、微细蜡浆的一种或其组合。
6.如权利要求1所述的一种环保型银色刮开油墨，其特征在于：所述的溶剂选取用醋酸丁酯、醋酸乙酯、PMA、DBE、乙二醇丁醚、丙二醇丁醚、脱芳D40溶剂的一种或其组合。
7.一种如权利要求1所述的一种环保型银色刮开油墨的制备方法，其特征在于：所述制备方法，其制备工艺如下：按配方重量比计，把部分溶剂加入分散釜中，加入丙烯酸树脂、氯醋树脂溶解均匀，加入润湿分散剂、气相二氧化硅、铝银浆，高速分散30～40min，在低速搅拌下加入蜡浆、流平剂和剩余的溶剂，搅拌调节好粘度，过滤包装即制得一种环保型银色刮开油墨。
CN201310418761.4A 2013-09-10 2013-09-10 一种环保型银色刮开油墨的制备方法 Expired - Fee Related CN104419251B (zh)