CN104267001B - 环氧底漆托油性快速测试方法 - Google Patents

环氧底漆托油性快速测试方法 Download PDF

Info

Publication number
CN104267001B
CN104267001B CN201410462930.9A CN201410462930A CN104267001B CN 104267001 B CN104267001 B CN 104267001B CN 201410462930 A CN201410462930 A CN 201410462930A CN 104267001 B CN104267001 B CN 104267001B
Authority
CN
China
Prior art keywords
measured
oiliness
support
glass plate
epoxy primer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410462930.9A
Other languages
English (en)
Other versions
CN104267001A (zh
Inventor
李永强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU DEWEI PAINT Co Ltd
Original Assignee
JIANGSU DEWEI PAINT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU DEWEI PAINT Co Ltd filed Critical JIANGSU DEWEI PAINT Co Ltd
Priority to CN201410462930.9A priority Critical patent/CN104267001B/zh
Publication of CN104267001A publication Critical patent/CN104267001A/zh
Application granted granted Critical
Publication of CN104267001B publication Critical patent/CN104267001B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了环氧底漆托油性快速测试方法，包括以下步骤：a、制备测试液：用100质量份的乙酸仲丁酯溶剂溶解28‑32质量份的硝化棉，然后加入38‑42质量份的环氧树脂搅匀；b、将待测环氧底漆按照主剂和固化剂配比配制好，在玻璃板上用湿膜制备器刮涂涂膜，放入干燥箱干燥3‑5小时待测；c、用湿膜制备器在经b步骤刮涂涂膜的玻璃板上刮涂测试液，然后将玻璃板放置在48‑52℃干燥箱中干燥25‑35分钟，取出玻璃板自然冷却3‑5分钟；d、测试样板光泽，此光泽即为待测底漆的托油性。通过在待测环氧底漆上刮涂自干测试液，干燥后测量光泽度来测试底漆的托油性，操作简便，快速，准确。

Description

环氧底漆托油性快速测试方法
技术领域
本发明涉及一种环氧底漆托油性快速测试方法。
背景技术
在环氧防腐漆中经常出现在不同的底漆上喷涂同一面漆时会出现不同的光泽，这种能托住面漆光泽的性能称为托油性。托油性测试作为在生产中一项重要的质量测试指标。如何快速、简便、准确的测试底漆的托油性是一项难题。因此，需要提供一种新的技术方案来解决上述问题。
发明内容
为解决上述问题，本发明提供一种快速、简便、准确的环氧底漆托油性快速测试方法。
本发明采用的技术方案：
环氧底漆托油性快速测试方法，包括以下步骤：
a、制备测试液：用100质量份的乙酸仲丁酯溶剂溶解28-32质量份的硝化棉，然后加入38-42质量份的环氧树脂搅匀；
b、将待测环氧底漆按照主剂和固化剂配比配制好，在玻璃板上用湿膜制备器刮涂涂膜，放入干燥箱干燥3-5小时待测；
c、用湿膜制备器在经b步骤刮涂涂膜的玻璃板上刮涂测试液，然后将玻璃板放置在48-52℃干燥箱中干燥25-35分钟，取出玻璃板自然冷却3-5分钟；
d、采用光泽度仪测试样板光泽，此光泽即为待测底漆的托油性。
所述环氧树脂为环氧当量为475的双酚A型环氧树脂，环氧树脂内含质量百分含量25%二甲苯溶剂。
所述硝化棉为硝化纤维素，硝化棉内含质量百分含量30%的乙醇。
本发明的有益效果是：通过在待测环氧底漆上刮涂自干测试液，干燥后测量光泽度来测试底漆的托油性，操作简便，快速，准确。
具体实施方式
下述实施例仅用于说明本发明，但并不能限定本发明的保护范围。
实施例1
环氧底漆托油性快速测试方法，包括以下步骤：
a、制备测试液：用100g的乙酸仲丁酯溶剂溶解28g的硝化棉，然后加入38g的环氧树脂搅匀；
b、将待测环氧底漆按照主剂和固化剂配比配制好，在玻璃板上用湿膜制备器刮涂涂膜，放入干燥箱干燥3小时待测；
c、用湿膜制备器在经b步骤刮涂涂膜的玻璃板上刮涂测试液，然后将玻璃板放置在48℃干燥箱中干燥25分钟，取出玻璃板自然冷却3分钟；
d、采用光泽度仪测试样板光泽，此光泽即为待测底漆的托油性。
环氧树脂为环氧当量为475的双酚A型环氧树脂，环氧树脂内含质量百分含量25%二甲苯溶剂；硝化棉为硝化纤维素，硝化棉内含质量百分含量30%的乙醇。
实施例2
环氧底漆托油性快速测试方法，包括以下步骤：
a、制备测试液：用100g的乙酸仲丁酯溶剂溶解30g的硝化棉，然后加入40g的环氧树脂搅匀；
b、将待测环氧底漆按照主剂和固化剂配比配制好，在玻璃板上用湿膜制备器刮涂涂膜，放入干燥箱干燥4小时待测；
c、用湿膜制备器在经b步骤刮涂涂膜的玻璃板上刮涂测试液，然后将玻璃板放置在50℃干燥箱中干燥30分钟，取出玻璃板自然冷却4分钟；；
d、采用光泽度仪测试样板光泽，此光泽即为待测底漆的托油性。
环氧树脂为环氧当量为475的双酚A型环氧树脂，环氧树脂内含质量百分含量25%二甲苯溶剂；硝化棉为硝化纤维素，硝化棉内含质量百分含量30%的乙醇。
实施例3
环氧底漆托油性快速测试方法，包括以下步骤：
a、制备测试液：用100g的乙酸仲丁酯溶剂溶解32g的硝化棉，然后加入42g的环氧树脂搅匀；
b、将待测环氧底漆按照主剂和固化剂配比配制好，在玻璃板上用湿膜制备器刮涂涂膜，放入干燥箱干燥5小时待测；
c、用湿膜制备器在经b步骤刮涂涂膜的玻璃板上刮涂测试液，然后将玻璃板放置在52℃干燥箱中干燥35分钟，取出玻璃板自然冷却5分钟；
d、采用光泽度仪测试样板光泽，此光泽即为待测底漆的托油性。
环氧树脂为环氧当量为475的双酚A型环氧树脂，环氧树脂内含质量百分含量25%二甲苯溶剂；硝化棉为硝化纤维素，硝化棉内含质量百分含量30%的乙醇。
通过在待测环氧底漆上刮涂自干测试液，干燥后测量光泽度来测试底漆的托油性，操作简便，快速，准确。
上述的环氧树脂中的二甲苯作为稀释剂，市场上大量存在以二甲苯为溶剂的环氧树脂，可以直接购买使用，同时用二甲苯配合乙酸仲丁酯对整个测试液体系具有很好的溶解性，有利于成膜。硝化棉密封阴凉干燥避光保存，加入乙醇作为湿润剂，以保安全。
托油性的测试机理：首先上述乙酸仲丁酯溶剂、硝化棉、环氧树脂，这3种混合制得的测试液刮涂后能够形成自干的涂膜，不同的底漆刮涂测试液会产生不同的光泽，把这个光泽就定义为改底漆的托油性。

Claims (2)

1.环氧底漆托油性快速测试方法，其特征在于，包括以下步骤：
a、制备测试液：用100质量份的乙酸仲丁酯溶剂溶解28-32质量份的硝化棉，然后加入38-42质量份的环氧树脂搅匀；环氧树脂为环氧当量为475的双酚A型环氧树脂，环氧树脂内含质量百分含量25%二甲苯溶剂；
b、将待测环氧底漆按照主剂和固化剂配比配制好，在玻璃板上用湿膜制备器刮涂涂膜，放入干燥箱干燥3-5小时待测；
c、用湿膜制备器在经b步骤刮涂涂膜的玻璃板上刮涂测试液，然后将玻璃板放置在48-52℃干燥箱中干燥25-35分钟，取出玻璃板自然冷却3-5分钟；
d、采用光泽度仪测试样板光泽，此光泽即为待测底漆的托油性。
2.根据权利要求1所述的环氧底漆托油性快速测试方法，其特征在于：所述硝化棉为硝化纤维素，硝化棉内含质量百分含量30%的乙醇。
CN201410462930.9A 2014-09-12 2014-09-12 环氧底漆托油性快速测试方法 Active CN104267001B (zh)