CN104264001A - 一种原位自生颗粒增强的铝基复合材料及其制备方法 - Google Patents
一种原位自生颗粒增强的铝基复合材料及其制备方法 Download PDFInfo
- Publication number
- CN104264001A CN104264001A CN201410472154.0A CN201410472154A CN104264001A CN 104264001 A CN104264001 A CN 104264001A CN 201410472154 A CN201410472154 A CN 201410472154A CN 104264001 A CN104264001 A CN 104264001A
- Authority
- CN
- China
- Prior art keywords
- preparation
- particle
- aluminum
- matrix composite
- tib
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (9)