CN103980596B - 一种聚乙烯橡胶及其加工方法 - Google Patents
一种聚乙烯橡胶及其加工方法 Download PDFInfo
- Publication number
- CN103980596B CN103980596B CN201410200113.6A CN201410200113A CN103980596B CN 103980596 B CN103980596 B CN 103980596B CN 201410200113 A CN201410200113 A CN 201410200113A CN 103980596 B CN103980596 B CN 103980596B
- Authority
- CN
- China
- Prior art keywords
- polyethylene
- polyethylene rubber
- minutes
- rubber
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于橡胶技术领域,具体涉及一种聚乙烯橡胶及其加工方法。本发明中所述聚乙烯橡胶的原料配方按照下列重量份组成:超支化聚乙烯100份、炭黑50~80份、过氧化物交联剂2~5份、氧化锌0~6份、润滑剂0~5份、促进剂0.3~0.5份、硫磺0~0.2份。本发明的有益效果是:将具有高度支化结构聚乙烯(HBPE)用过氧化物硫化体系进行硫化,经应力-应变性能测试具有良好的力学性能,具备橡胶高弹性特征。与现有的氯化聚乙烯橡胶和氯磺化聚乙烯橡胶的制备方法完全不同。本发明打破了聚乙烯只能用做塑料制品的限制,扩大了聚乙烯的应用领域,大幅度提高了乙烯均聚物的附加值。
Description
技术领域
本发明属于橡胶技术领域,具体涉及一种聚乙烯橡胶及其加工方法。
背景技术
合成橡胶无疑是最早发展起来的合成高分子。在所有的合成高分子当中,合成橡胶是唯一具有高弹性的物质,广泛用于汽车、建筑、机械、电力、信息、航空、制药、健康以及日用品等行业。目前,制备合成橡胶通常需要双烯烃(如丁二烯、异戊二烯或乙叉降冰片烯)或特殊的单体(如二异氰酸酯或二甲基二氯硅烷)。这些原材料的价格较高,导致合成橡胶的价格居高不下。
乙烯是最简单、最便宜的单体。随着页岩气的开发利用,乙烯的来源将越来越丰富,价格也会越来越便宜。目前,美国利用页岩气中的乙烷资源制备的乙烯的价格仅为我国用石脑油制备的乙烯价格的1/3。如果能够将乙烯进行均聚制备玻璃化转变温度足够低、分子量足够高的无定形聚烯烃,就可以通过更加经济的方法制备一种新型的合成橡胶。因为除了乙烯的价格低之外,聚合工艺也可以得到大幅度的简化。
通常乙烯的均聚物是高度结晶的,只能用作塑料。自从1995年美国北卡州立大学的Brookhart教授首先报道了具有链行走(chainwalking)能力的(α-二亚胺)镍催化剂可以制备高分子量、带支链的聚乙烯,即超支化聚乙烯(HBPE)。人们开始致力于提高这类催化剂的热稳定性(Catal.Sci.Technol.2013,3,1172;Macromolecules42,2009,7789;Angew.Chem.Int.Ed.2004,43,1821;J.Am.Chem.Soc.2013,135,16316;Organometallics23,2004,3276-3283)。二十年来,这类催化剂的热稳定性得到了明显的改善,但是催化剂的链行走能力也得到了限制,由这些催化剂制备的聚乙烯的支化度不够高,导致聚乙烯的玻璃化转变温度高于–53℃。而通用橡胶的使用温度要求在–250~–60℃温度范围内。
我们在中国发明专利CN102827311A和CN102827312A中提供了几种新型的(α-二亚胺)镍催化剂。在后续的研究中,我们发现这些催化剂不仅有较好的热稳定性,催化剂链行走的能力也得到了很好地保留。在合适的条件下,用它们催化乙烯均聚,可以制备玻璃化转变温度为–61℃~–67℃、重均分子量为9.2万~42万的HBPE。
发明内容
本发明要解决的技术问题是,克服现有技术中的不足,以HBPE为原料提供一种聚乙烯橡胶及其加工方法。
为解决技术问题,本发明的解决方案是:
提供一种聚乙烯橡胶,所述聚乙烯橡胶的原料配方按照下列重量份组成:超支化聚乙烯100份、炭黑50~80份、过氧化物交联剂2~5份、氧化锌0~6份、润滑剂0~5份、促进剂0.3~0.5份、硫磺0~0.2份。
本发明中,所述超支化聚乙烯的支化度为106~125个支链/1000个碳、玻璃化转变温度为–67℃~–61℃、重均分子量为9.2万~42万、门尼粘度ML(1+4)125℃为2.12~86.63;其中所述超支化聚乙烯的支化度106~125个支链/1000个碳中甲基含量为48.7~64.5mol%、乙基含量为7.4~20.3mol%、丙基含量为1.8~6.7mol%、丁基含量为2.8~5.6mol%、戊基含量为2.1~3.7mol%、碳数≥6支链含量为11.5~23.5mol%。
本发明中,所述炭黑为炭黑N330、炭黑N550或炭黑N990。
本发明中,所述过氧化物交联剂为过氧化二异丙苯(DCP)。
本发明中,所述促进剂为N-环己基-2-苯并噻唑次磺酰胺(CZ)、二硫化二苯并噻唑(DM)或者三烯丙基异三聚氰酸酯(TAIC)中的一种或几种组成。
本发明中,所述润滑剂为硬脂酸、石蜡或者N,N’-亚乙基双硬脂酰胺(EBS)中的一种或几种组成。
本发明中,还提供一种基于所述聚乙烯橡胶的加工方法,如下步骤:
步骤(1):设置密炼机初始温度40℃,转子速度为50转/分钟,待温度稳定后保持10分钟;
步骤(2):将超支化聚乙烯加入密炼机中塑炼1.5分钟,再加入ZnO、润滑剂,混炼1.5分钟,然后加入炭黑,混炼3分钟,最后加入过氧化物交联剂、促进剂、助交联剂,混炼2.5分钟后出胶,得到混炼胶;
步骤(3):将混炼胶在辊距为0.8毫米、辊温40℃的开炼机上打三角包薄通4次,将辊距调到2.4毫米,投入胶料包辊,待表面光滑无气泡,下片;并在室温下放置20小时;
步骤(4):用平板硫化机在150℃~175℃、10MPa下硫化10~15分钟,室温下停放16小时,获得所述聚乙烯橡胶。
与现有技术相比,本发明的有益效果是:
本发明将具有高度支化结构的聚乙烯(HBPE)用过氧化物硫化体系进行硫化,经应力-应变性能测试发现它具有良好的力学性能,具备了橡胶高弹性的特征。我们将这样的新型合成橡胶定义为聚乙烯橡胶,是因为它是由乙烯均聚而制得的,与现有的氯化聚乙烯橡胶和氯磺化聚乙烯橡胶的制备方法完全不同。本发明打破了聚乙烯只能用做塑料制品的限制,扩大了聚乙烯的应用领域,大幅度提高了乙烯均聚物的附加值。
具体实施方式
下面给出实施例以对本发明做进一步说明,但不用来限制本发明的范围,该领域的技术熟练人员根据发明内容对本发明做出的一些非本质的改进和调整仍属于本发明的保护范围。
本发明的实施例中所用的原料除超支化聚乙烯(HBPE)外均为市售产品,实施例中所用的技术手段为本领域技术人员所熟知的常规手段。
本发明中所述超支化聚乙烯可通过现有专利公开的技术方案制备,其具体制备方法在专利(CN102827312A和CN102827311A)中已公开。通过利用几种新型(α-二亚胺)镍催化剂催化乙烯均聚,可获得本发明所述的超支化聚乙烯(HBPE)。
聚乙烯橡胶的性能测试方法如下:
本专利采用支化度为106~125个支链/1000个碳、玻璃化转变温度为–67℃~–61℃、重均分子量为9.2万~42万、门尼粘度ML(1+4)125℃为2.12~86.63的超支化聚乙烯(HBPE)作为研究对象。
门尼粘度测试:按照GB/T1232.1-2000,试样制备按照GB/T15340-1994。测定结果以ML(1+4)125℃表示。
拉伸强度测试:采用哑铃型样品,根据GB/T528-1998规定测定。
实施例1
表一实施例1的加工配方
以支化度为106个支链/1000个碳(其中甲基含量为50.6mol%、乙基含量为13.2mol%、丙基含量为6.7mol%、丁基含量为4.9mol%、戊基含量为3.7mol%、碳数≥6的支链含量为20.8mol%)、玻璃化转变温度为–65℃、重均分子量为25万、门尼粘度ML(1+4)125℃为16.75的超支化聚乙烯(HBPE-1)为主要原料,加工配方的组成成份和各组成成份的重量份如表一所示。
加工步骤如下:
步骤(1)设置密炼机的初始温度40℃,设定转子速度为50转/分钟,待温度稳定后保持10分钟。
步骤(2)加入100重量份聚乙烯塑炼1.5分钟后,加入3重量份ZnO,2重量份硬脂酸,混炼1.5分钟。然后加入50重量份N330炭黑,混炼3分钟。最后加入2重量份交联剂DCP,0.3重量份促进剂DM,0.2重量份硫磺(S),混炼2.5分钟后出胶,得到混炼胶。
步骤(3)将混炼胶在辊距为0.8毫米,辊温40℃的开炼机上打三角包薄通4次,将辊距调到2.4毫米,投入胶料包辊,待表面光滑无气泡,下片;室温下停放20小时。
步骤(4)在175℃,10MPa下硫化10分钟,室温下停放16小时。
步骤(5)裁成拉伸测试样条,拉伸速度为50毫米/分钟。
实施例2
将实施例1中的步骤(5)的拉伸速度改为500毫米/分钟,其他条件不变。
实施例3
将实施例2中步骤(4)的硫化温度改为170℃,硫化时间改为15分钟,其他条件不变。
实施例4
将实施例2中步骤(2)的DM和硫磺改成TAIC,加工配方如表二所示,其他条件不变。
表二实施例4的加工配方
实施例5
以支化度为108个支链/1000个碳(其中甲基含量为50.5mol%、乙基含量为12.9mol%、丙基含量为5.2mol%、丁基含量为4.8mol%、戊基含量为3.6mol%、碳数≥6的支链含量为23.0mol%)、玻璃化转变温度为–66℃、重均分子量为20万、门尼粘度ML(1+4)125℃为10.58的超支化聚乙烯(HBPE-2)为主要原料,硫化配方、加工方法、硫化条件以及测试方法与实施例4相同。
实施例6
将实施例5的步骤(4)中的硫化温度改为170℃,其他条件不变。
实施例7
在实施例5的步骤(2)中不添加ZnO和硬脂酸,其他条件不变。
实施例8
在实施例5的步骤(2)中将硬脂酸改为石蜡,N330炭黑改为N550炭黑,其他条件不变。
实施例9
在实施例5的步骤(2)中将TAIC改为N-环己基-2-苯并噻唑次磺酰胺,硬脂酸改为N,N’-亚乙基双硬脂酰胺,N330炭黑改为N990炭黑,其他条件不变。
实施例10
以支化度为108个支链/1000个碳(其中甲基含量为48.7mol%、乙基含量为14.9mol%、丙基含量为4.5mol%、丁基含量为5.6mol%、戊基含量为2.8mol%、碳数≥6的支链含量为23.5mol%)、玻璃化转变温度为–67℃、重均分子量为12.4万、门尼粘度ML(1+4)125℃为3.88的超支化聚乙烯(HBPE-3)为主要原料,硫化配方、加工方法、硫化条件以及测试方法与实施例4相同。
实施例11
以支化度为125个支链/1000个碳(其中甲基含量为64.5mol%、乙基含量为7.4mol%、丙基含量为2.4mol%、丁基含量为2.8mol%、戊基含量为2.1mol%、碳数≥6的支链含量为20.8mol%)、玻璃化转变温度为–61℃、重均分子量为42万、门尼粘度ML(1+4)125℃为86.63的超支化聚乙烯(HBPE-4)为主要原料,硫化配方、加工方法、硫化条件以及测试方法与实施例4相同。
实施例12
以支化度为119个支链/1000个碳(其中甲基含量为59.8mol%、乙基含量为20.3mol%、丙基含量为1.8mol%、丁基含量为4.5mol%、戊基含量为2.1mol%、碳数≥6的支链含量为11.5mol%)、玻璃化转变温度为–63℃、重均分子量为9.2万、门尼粘度ML(1+4)125℃为2.12的超支化聚乙烯(HBPE-5)为主要原料,硫化配方、加工方法、硫化条件以及测试方法与实施例4相同。
实施例13
将实施例2中步骤(2)改为加入100重量份聚乙烯塑炼1.5分钟后,加入4重量份ZnO,5重量份硬脂酸,混炼1.5分钟。然后加入80重量份N330炭黑,混炼3分钟。最后加入5重量份交联剂DCP,0.4重量份促进剂DM,0.1重量份硫磺,混炼2.5分钟后出胶,得到混炼胶,其他条件不变。
实施例14
将实施例2中步骤(2)改为加入100重量份聚乙烯塑炼1.5分钟后,加入6重量份ZnO,3重量份硬脂酸,混炼1.5分钟。然后加入70重量份N330炭黑,混炼3分钟。最后加入4重量份交联剂DCP,0.3重量份促进剂DM,0.2重量份硫磺,混炼2.5分钟后出胶,得到混炼胶,其他条件不变。
为了更好地说明本发明中聚乙烯橡胶的性能,以实施例1和实施例2做了相应的对照例1和对照例2,以实施例4做了相应的对照例3。对比例中生胶选用的三元乙丙橡胶和天然橡胶均为市售,其中三元乙丙橡胶重均分子量为15万,乙烯含量70wt%左右,乙叉降冰片烯含量0.5wt%左右,门尼粘度ML(1+4)125℃为45。天然橡胶为云南生产的微生物凝固天然胶,门尼粘度ML(1+4)125℃为93.9。
对照例1
以三元乙丙橡胶为主要原料,硫化配方、加工方法、硫化条件以及测试方法与实施例1相同。
对照例2
以三元乙丙橡胶为主要原料,硫化配方、加工方法、硫化条件以及测试方法与实施例2相同。
对照例3
表三对照例3的加工配方
以天然橡胶为主要原料,加工配方的组成成份和各组成成份的重量份如表三所示。
加工步骤如下:
步骤(1)密炼机的初始温度50℃,设定转子速度为50转/分钟,待温度稳定后保持10分钟。
步骤(2)加入100重量份天然橡胶塑炼1.5分钟后,加入6重量份ZnO,5重量份硬脂酸,混炼1.5分钟;然后加入80重量份炭黑,混炼3分钟。最后加入2重量份交联剂硫磺,0.5重量份促进剂M,2重量份防老剂4010NA,混炼2.5分钟后出胶,得到混炼胶。
步骤(3)将混炼胶在辊距为0.8毫米,辊温50℃的开炼机上打三角包薄通4次,将辊距调到2.4毫米左右,投入胶料包辊,待表面光滑无气泡,下片。
步骤(4)在150~160℃、10MPa下硫化15分钟。
步骤(5)裁成拉伸测试样条,拉伸速度为500毫米/分钟。
实施例1~7与对照例1~3的力学性能指标如表四所示。
表四实施例1~7与对照例1~3的力学性能
从表四中可以看出,本发明提供的聚乙烯橡胶具备了橡胶高弹性的特征,表现出了很好的弹性和强度。由实施例1和实施例2可知,采用不同的拉伸速度,拉伸强度有所不同。由实施例1与对照例1、实施例2和对照例2比较可知,聚乙烯橡胶,无论在50毫米/分钟还是500毫米/分钟的拉伸速度下,拉伸强度和断裂伸长率都明显高于三元乙丙橡胶。由实施例7和对照例2比较可知,分子量较低的聚乙烯橡胶的拉伸强度略低于三元乙丙橡胶,断裂伸长率稍高于三元乙丙橡胶。由实施例3和对照例3比较可知,聚乙烯橡胶的拉伸强度与天然橡胶的拉伸强度接近,断裂伸长率稍微高于天然橡胶。
因此,本发明的实际范围不仅包括所公开的实施例,还包括在权利要求书之下实施或者执行本发明的所有等效方案。
Claims (7)
1.一种聚乙烯橡胶,其特征在于,所述聚乙烯橡胶的原料配方按照下列重量份组成:超支化聚乙烯100份、炭黑50~80份、过氧化物交联剂2~5份、氧化锌0~6份、润滑剂0~5份、促进剂0.3~0.5份、硫磺0~0.2份。
2.根据权利要求1中所述的聚乙烯橡胶,其特征在于,所述超支化聚乙烯的支化度为106~125个支链/1000个碳、玻璃化转变温度为–67℃~–61℃、重均分子量为9.2万~42万、门尼粘度ML(1+4)125℃为2.12~86.63;其中所述超支化聚乙烯的支化度106~125个支链/1000个碳中甲基含量为48.7~64.5mol%、乙基含量为7.4~20.3mol%、丙基含量为1.8~6.7mol%、丁基含量为2.8~5.6mol%、戊基含量为2.1~3.7mol%、碳数≥6支链含量为11.5~23.5mol%。
3.根据权利要求1中所述的聚乙烯橡胶,其特征在于,所述炭黑为炭黑N330、炭黑N550或炭黑N990。
4.根据权利要求1中所述的聚乙烯橡胶,其特征在于,所述过氧化物交联剂为过氧化二异丙苯。
5.根据权利要求1中所述的聚乙烯橡胶,其特征在于,所述促进剂为N-环己基-2-苯并噻唑次磺酰胺、二硫化二苯并噻唑或者三烯丙基异三聚氰酸酯中的一种或几种组成。
6.根据权利要求1中所述的聚乙烯橡胶,其特征在于,所述润滑剂为硬脂酸、石蜡或者N,N’-亚乙基双硬脂酰胺中的一种或几种组成。
7.一种基于权利要求1中所述聚乙烯橡胶的加工方法,其特征在于,具体步骤如下所述:
步骤(1):设置密炼机初始温度40℃,转子速度为50转/分钟,待温度稳定后保持10分钟;
步骤(2):将超支化聚乙烯加入密炼机中塑炼1.5分钟,再加入ZnO、润滑剂,混炼1.5分钟,然后加入炭黑,混炼3分钟,最后加入过氧化物交联剂、促进剂、硫磺,混炼2.5分钟后出胶,得到混炼胶;
步骤(3):将混炼胶在辊距为0.8毫米、辊温40℃的开炼机上打三角包薄通4次,将辊距调到2.4毫米,投入胶料包辊,待表面光滑无气泡,下片;并在室温下放置20小时;
步骤(4):用平板硫化机在150℃~175℃、10MPa下硫化10~15分钟,室温下停放16小时,获得所述聚乙烯橡胶。